CN109291539A - Antibacterial health-care fabric and preparation method thereof - Google Patents
Antibacterial health-care fabric and preparation method thereof Download PDFInfo
- Publication number
- CN109291539A CN109291539A CN201810960096.4A CN201810960096A CN109291539A CN 109291539 A CN109291539 A CN 109291539A CN 201810960096 A CN201810960096 A CN 201810960096A CN 109291539 A CN109291539 A CN 109291539A
- Authority
- CN
- China
- Prior art keywords
- fabric
- care
- layer
- inner layer
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This application discloses a kind of antibacterial health-care fabrics, including the inner layer fabric, antibiotic health care layer and outer shell fabric set gradually；The ingredient of the inner layer fabric includes 35~40 parts of cotton yarns, 25~30 parts of zein fibers, 20~25 parts of bamboo fibres and 15~20 parts of chitin fibers by weight；The antibiotic health care layer includes that nano-silver ionic fibrous layer and several equally distributed magnetic particles positioned at the nano-silver ionic fibrous layer both side surface, the area of the magnetic particle account for the 40~50% of nano-silver ionic fibrous layer；The outer shell fabric is nylon layer.Antibacterial health-care fabric of the invention can have both antimicrobial health care function and comfortable warmth retention property simultaneously.
Description
Technical field
The application belongs to garment material processing technique field, more particularly to a kind of antibacterial health-care fabric and its preparation side
Method.
Background technique
With the improvement of the quality of life, requirement of the people to dress-goods is also higher and higher, in addition to fashionable, also requires
With certain functionality.It is not limited solely to the range that clothing covers body, the research for functions such as comfort level, the health cares of fabric
Gradually deeply, but the research of fabric antibacterial health care ability is need to be improved, people can wear clothes on various occasions daily
Study, work, life, will touch various bacteriums between unconscious, long-term accumulated enrichment can generate danger to the health of human body
Evil.
Therefore, a kind of antibacterial health-care fabric is needed, can solve the demand of antibiotic health care.
Summary of the invention
The purpose of the present invention is to provide antibacterial health-care fabrics and preparation method thereof, with overcome the deficiencies in the prior art.
To achieve the above object, the invention provides the following technical scheme:
The embodiment of the present application discloses a kind of antibacterial health-care fabric, including inner layer fabric, the antibiotic health care layer set gradually
And outer shell fabric；
The ingredient of the inner layer fabric includes 35~40 parts of cotton yarns, 25~30 parts of zein fibers, 20~25 parts by weight
Bamboo fibre and 15~20 parts of chitin fibers；
The antibiotic health care layer include nano-silver ionic fibrous layer and be located at the nano-silver ionic fibrous layer both side surface
Several equally distributed magnetic particles, the area of the magnetic particle accounts for the 40~50% of nano-silver ionic fibrous layer；
The outer shell fabric is nylon layer.
Preferably, the shape of the magnetic particle includes one of spherical, sheet and tetrahedron or a variety of.
Preferably, the magnetic particle and the nano-silver ionic fibrous layer are bonded by adhesive.
Preferably, the inner layer fabric with a thickness of 0.15~0.25mm.
Preferably, the antibiotic health care layer with a thickness of 0.1~0.15mm.
The embodiment of the present application also discloses a kind of preparation method of antibacterial health-care fabric, comprising the following steps:
Inner layer fabric is blended and peroxide technique: choosing 35~40 parts of cotton yarns, 25~30 parts of zein fibers, 20~25 parts of bamboo fibres
Dimension and 15~20 parts of chitin fibers, progress is blended, then carries out peroxide processing with aqueous peroxygen solutions, obtains inner layer fabric；
Inner layer fabric boiling: the inner layer fabric is placed in water-bath and carries out kiering, is once washed later
Drying；
Inner layer fabric bleaching process: the inner layer fabric after primary washing drying is bleached under alkaline condition, later
Carry out secondary washing drying；
Antibiotic health care layer preparation process: several equally distributed magnetic particles are set on nano-silver ionic fibrous layer, are obtained
Obtain antibiotic health care layer；
Bonding process: utilizing adhesive, by inner layer fabric, antibiotic health care layer and the outer shell fabric phase after secondary washing drying
Bonding obtains antibacterial health-care fabric.
Preferably, the inner layer fabric boiling specifically includes: the inner layer fabric being placed in water-bath and is boiled
Practicing, 20~40min of kiering time, after kiering, impregnates 3~5min with the acetic acid of 1g/L at 75~80 DEG C by 90~98 DEG C of temperature,
Primary washing drying is carried out later.
Preferably, the inner layer fabric bleaching process specifically includes: by the inner layer fabric after primary washing drying in bleaching liquor
In bleached, the ingredient of bleaching liquor includes hydrogen peroxide, sodium metasilicate and refining agent, and bleaching temperature is maintained at 80~95 DEG C, the time
20~30min, pH value are 7~12, carry out secondary washing drying later.
Preferably, the antibiotic health care layer preparation process specifically includes: uniformly being glued several magnetic particles by adhesive
Knot obtains antibiotic health care layer on nano-silver ionic fibrous layer.
It preferably, further include that ironing processing is carried out to the antibacterial health-care fabric after the bonding process.
Compared with the prior art, the advantages of the present invention are as follows:
(1) antibacterial health-care fabric of the invention, including the inner layer fabric, antibiotic health care layer and outer shell fabric set gradually；
The ingredient of inner layer fabric includes cotton yarn, zein fiber, bamboo fibre and chitin fiber；Antibiotic health care layer includes nano-silver ionic fibre
Layer and several equally distributed magnetic particles positioned at the nano-silver ionic fibrous layer both side surface are tieed up, and outer shell fabric is Buddhist nun
Imperial layer can have both antimicrobial health care function and comfortable warmth retention property simultaneously.
(2) antibacterial health-care fabric of the invention, has antibiotic health care layer, and the external magnetic field variation of magnetic particle will affect people
The physiological function of body enhances body immunity so as to adjust the physiological function of human body.The magnetic particle can be to the difference of human body
Position carries out stimulation therapy, has and promotes blood circulation, activates body cell and eliminate the healthcare functions such as fatigue.
Specific embodiment
In one embodiment of the application, a kind of antibacterial health-care fabric is provided, including inner layer fabric, the antibiotic health care set gradually
Layer and outer shell fabric；
The ingredient of the inner layer fabric includes 35~40 parts of cotton yarns, 25~30 parts of zein fibers, 20~25 parts by weight
Bamboo fibre and 15~20 parts of chitin fibers；
The antibiotic health care layer include nano-silver ionic fibrous layer and be located at the nano-silver ionic fibrous layer both side surface
Several equally distributed magnetic particles, the area of the magnetic particle accounts for the 40~50% of nano-silver ionic fibrous layer；
The outer shell fabric is nylon layer.
Wherein, the shape of the magnetic particle includes one of spherical, sheet and tetrahedron or a variety of.
The magnetic particle and the nano-silver ionic fibrous layer are bonded by adhesive.
The inner layer fabric with a thickness of 0.15~0.25mm.The antibiotic health care layer with a thickness of 0.1~0.15mm.
The embodiment of the present application also discloses a kind of preparation method of antibacterial health-care fabric, comprising the following steps:
Inner layer fabric is blended and peroxide technique: choosing 35~40 parts of cotton yarns, 25~30 parts of zein fibers, 20~25 parts of bamboo fibres
Dimension and 15~20 parts of chitin fibers, progress is blended, then carries out peroxide processing with aqueous peroxygen solutions, obtains inner layer fabric；
Inner layer fabric boiling: the inner layer fabric is placed in water-bath and carries out kiering, is once washed later
Drying；
Inner layer fabric bleaching process: the inner layer fabric after primary washing drying is bleached under alkaline condition, later
Carry out secondary washing drying；
Antibiotic health care layer preparation process: several equally distributed magnetic particles are set on nano-silver ionic fibrous layer, are obtained
Obtain antibiotic health care layer；
Bonding process: utilizing adhesive, by inner layer fabric, antibiotic health care layer and the outer shell fabric phase after secondary washing drying
Bonding obtains antibacterial health-care fabric.
The inner layer fabric boiling specifically includes: the inner layer fabric is placed in water-bath and carries out kiering, kiering
20~40min of time, after kiering, impregnates 3~5min with the acetic acid of 1g/L at 75~80 DEG C by 90~98 DEG C of temperature, it is laggard
The primary washing drying of row.
The inner layer fabric bleaching process specifically includes: the inner layer fabric after primary washing drying is floated in bleaching liquor
White, the ingredient of bleaching liquor includes hydrogen peroxide, sodium metasilicate and refining agent, and bleaching temperature is maintained at 80~95 DEG C, and the time 20~
30min, pH value are 7~12, carry out secondary washing drying later.
The antibiotic health care layer preparation process specifically includes: by adhesive by several magnetic particle even adhesions in nanometer
On silver-ion fiber layer, antibiotic health care layer is obtained.
It further include that ironing processing is carried out to the antibacterial health-care fabric after the bonding process.
Antibacterial health-care fabric of the invention, has antibiotic health care layer, and the external magnetic field variation of magnetic particle will affect human body
Physiological function enhance body immunity so as to adjust the physiological function of human body.The magnetic particle can be to the different portions of human body
Position carries out stimulation therapy, has and promotes blood circulation, activates body cell and eliminate the healthcare functions such as fatigue.
To make the object, technical solutions and advantages of the present invention clearer, below to a specific embodiment of the invention into
Row is described in detail.Embodiments of the present invention are only exemplary, and the present invention is not limited to these embodiments.
Embodiment 1
Antibacterial health-care fabric, including the inner layer fabric, antibiotic health care layer and outer shell fabric set gradually.Inner layer fabric at
Divide includes 35 parts of cotton yarns, 25 parts of zein fibers, 25 parts of bamboo fibres and 20 parts of chitin fibers by weight.
If antibiotic health care layer includes nano-silver ionic fibrous layer and positioned at the nano-silver ionic fibrous layer both side surface
Equally distributed magnetic particle is done, the area of the magnetic particle accounts for the 40% of nano-silver ionic fibrous layer.
Outer shell fabric is nylon layer.
The shape of magnetic particle includes one of spherical, sheet and tetrahedron or a variety of.
Wherein, inner layer fabric with a thickness of 0.15mm.Antibiotic health care layer with a thickness of 0.1mm.
The preparation method of antibacterial health-care fabric, comprising the following steps:
Inner layer fabric is blended and peroxide technique: choosing 35 parts of cotton yarns, 25 parts of zein fibers, 25 parts of bamboo fibres and 20 parts of crusts
Cellulose fiber, progress is blended, then carries out peroxide processing with aqueous peroxygen solutions, obtains inner layer fabric；
Inner layer fabric boiling: the inner layer fabric being placed in water-bath and carries out kiering, kiering time 20min, temperature
98 DEG C of degree, after kiering, impregnates 5min with the acetic acid of 1g/L at 75 DEG C, carries out primary washing drying later；
Inner layer fabric bleaching process: the inner layer fabric after primary washing drying is bleached in bleaching liquor, bleaching liquor at
It point include hydrogen peroxide, sodium metasilicate and refining agent, bleaching temperature is maintained at 80~95 DEG C, 20~30min of time, and pH value is 7~
12, secondary washing drying is carried out later.
Antibiotic health care layer preparation process: by adhesive by several magnetic particle even adhesions in nano-silver ionic fibrous layer
On, obtain antibiotic health care layer；
Bonding process: utilizing adhesive, by inner layer fabric, antibiotic health care layer and the outer shell fabric phase after secondary washing drying
Bonding obtains antibacterial health-care fabric.
Finally, carrying out ironing processing to the antibacterial health-care fabric.
Embodiment 2
Antibacterial health-care fabric, including the inner layer fabric, antibiotic health care layer and outer shell fabric set gradually.Inner layer fabric at
Divide includes 40 parts of cotton yarns, 30 parts of zein fibers, 20 parts of bamboo fibres and 15 parts of chitin fibers by weight.
If antibiotic health care layer includes nano-silver ionic fibrous layer and positioned at the nano-silver ionic fibrous layer both side surface
Equally distributed magnetic particle is done, the area of the magnetic particle accounts for the 50% of nano-silver ionic fibrous layer.
Outer shell fabric is nylon layer.
The shape of magnetic particle includes one of spherical, sheet and tetrahedron or a variety of.
Wherein, inner layer fabric with a thickness of 0.25mm.Antibiotic health care layer with a thickness of 0.1mm.
The preparation method of antibacterial health-care fabric, comprising the following steps:
Inner layer fabric is blended and peroxide technique: choosing 40 parts of cotton yarns, 30 parts of zein fibers, 20 parts of bamboo fibres and 15 parts of crusts
Cellulose fiber, progress is blended, then carries out peroxide processing with aqueous peroxygen solutions, obtains inner layer fabric；
Inner layer fabric boiling: the inner layer fabric being placed in water-bath and carries out kiering, kiering time 40min, temperature
90 DEG C of degree, after kiering, impregnates 3min with the acetic acid of 1g/L at 80 DEG C, carries out primary washing drying later；
Inner layer fabric bleaching process: the inner layer fabric after primary washing drying is bleached in bleaching liquor, bleaching liquor at
It point include hydrogen peroxide, sodium metasilicate and refining agent, bleaching temperature is maintained at 80~95 DEG C, 20~30min of time, and pH value is 7~
12, secondary washing drying is carried out later.
Antibiotic health care layer preparation process: by adhesive by several magnetic particle even adhesions in nano-silver ionic fibrous layer
On, obtain antibiotic health care layer；
Bonding process: utilizing adhesive, by inner layer fabric, antibiotic health care layer and the outer shell fabric phase after secondary washing drying
Bonding obtains antibacterial health-care fabric.
Embodiment 3
Antibacterial health-care fabric, including the inner layer fabric, antibiotic health care layer and outer shell fabric set gradually.Inner layer fabric at
Divide includes 38 parts of cotton yarns, 27 parts of zein fibers, 22 parts of bamboo fibres and 18 parts of chitin fibers by weight.
If antibiotic health care layer includes nano-silver ionic fibrous layer and positioned at the nano-silver ionic fibrous layer both side surface
Equally distributed magnetic particle is done, the area of the magnetic particle accounts for the 45% of nano-silver ionic fibrous layer.
Outer shell fabric is nylon layer.
The shape of magnetic particle includes one of spherical, sheet and tetrahedron or a variety of.
Wherein, inner layer fabric with a thickness of 0.15mm.Antibiotic health care layer with a thickness of 0.15mm.
The preparation method of antibacterial health-care fabric is same as Example 1 in the present embodiment.
Comparative example 1
Choose the common fabric without antimicrobial health care function on the market.
Bacteriostasis property test is carried out to the fabric of Examples 1 to 3 and comparative example 1, as a result such as table 1.
| Test index | Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example 1 |
| Yellow golden staphylococci bacteriostasis rate | > 93% | > 92% | > 93% | >72 |
| Candida albicans bacteriostasis rate | > 95% | > 94% | > 95% | >74 |
| Escherichia coli bacteriostasis rate | > 89% | > 88% | > 89% | > 61% |
Table 1.
Magnetic induction intensity test is carried out to the fabric of Examples 1 to 3 and comparative example 1, as a result such as table 2.
| Test index | Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example 1 |
| Magnetic induction intensity/Gs | 0.963 | 0.919 | 0.921 | 0.003 |
Table 2.
From table 1 it follows that the bacteriostasis property of common fabric is low, and in the present invention antibacterial health-care fabric bacteriostasis rate compared with
It is high.
From Table 2, it can be seen that the magnetic induction intensity of common fabric is almost 0, and antibacterial health-care fabric table in the present invention
The range of face magnetic induction intensity is between 0.9~1.0Gs.Research shows that the magnetic induction intensity useful and harmless to human body be 0.8~
1.2Gs。
Antibacterial health-care fabric of the invention, in addition to bacteriostasis rate is higher, also have promote blood circulation, activate body cell and
Eliminate the healthcare functions such as fatigue.
Finally, it is to be noted that, the terms "include", "comprise" or its any other variant be intended to it is non-exclusive
Property include so that include a series of elements process, method, article or equipment not only include those elements, but also
Further include other elements that are not explicitly listed, or further include for this process, method, article or equipment it is intrinsic
Element.
Claims (10)
1. a kind of antibacterial health-care fabric, it is characterised in that: including the inner layer fabric, antibiotic health care layer and outer layer surface set gradually
Material；
The ingredient of the inner layer fabric includes 35~40 parts of cotton yarns, 25~30 parts of zein fibers, 20~25 parts of bamboo fibres by weight
Dimension and 15~20 parts of chitin fibers；
If the antibiotic health care layer includes nano-silver ionic fibrous layer and positioned at the nano-silver ionic fibrous layer both side surface
Equally distributed magnetic particle is done, the area of the magnetic particle accounts for the 40~50% of nano-silver ionic fibrous layer；
The outer shell fabric is nylon layer.
2. antibacterial health-care fabric according to claim 1, it is characterised in that: the shape of the magnetic particle include it is spherical,
One of sheet and tetrahedron are a variety of.
3. antibacterial health-care fabric according to claim 1, it is characterised in that: the magnetic particle and the nano-silver ionic
Fibrous layer is bonded by adhesive.
4. antibacterial health-care fabric according to claim 1, it is characterised in that: the inner layer fabric with a thickness of 0.15~
0.25mm。
5. antibacterial health-care fabric according to claim 1, it is characterised in that: the antibiotic health care layer with a thickness of 0.1~
0.15mm。
6. a kind of preparation method of antibacterial health-care fabric, which comprises the following steps:
Inner layer fabric is blended and peroxide technique: choose 35~40 parts of cotton yarns, 25~30 parts of zein fibers, 20~25 parts of bamboo fibres and
15~20 parts of chitin fibers, progress is blended, then carries out peroxide processing with aqueous peroxygen solutions, obtains inner layer fabric；
Inner layer fabric boiling: the inner layer fabric being placed in water-bath and carries out kiering, carries out primary washing drying later；
Inner layer fabric bleaching process: the inner layer fabric after primary washing drying is bleached under alkaline condition, is carried out later
Secondary washing drying；
Antibiotic health care layer preparation process: several equally distributed magnetic particles are set on nano-silver ionic fibrous layer, are resisted
Bacterium heath care layer；
Bonding process: utilizing adhesive, and inner layer fabric, antibiotic health care layer and the outer shell fabric after secondary washing drying are mutually glued
Knot obtains antibacterial health-care fabric.
7. the preparation method of antibacterial health-care fabric according to claim 6, which is characterized in that the inner layer fabric kiering work
Skill specifically includes: the inner layer fabric is placed in water-bath and carries out kiering, 20~40min of kiering time, and 90~98 DEG C of temperature,
After kiering, 3~5min is impregnated at 75~80 DEG C with the acetic acid of 1g/L, carries out primary washing drying later.
8. the preparation method of antibacterial health-care fabric according to claim 6, which is characterized in that the inner layer fabric bleaches work
Skill specifically includes: the inner layer fabric after primary washing drying is bleached in bleaching liquor, the ingredient of bleaching liquor include hydrogen peroxide,
Sodium metasilicate and refining agent, bleaching temperature are maintained at 80~95 DEG C, 20~30min of time, and pH value is 7~12, is carried out later secondary
Washing drying.
9. the preparation method of antibacterial health-care fabric according to claim 6, which is characterized in that the antibiotic health care layer preparation
Technique specifically includes: by adhesive by several magnetic particle even adhesions on nano-silver ionic fibrous layer, obtain antibacterial protect
Strong layer.
10. the preparation method of antibacterial health-care fabric according to claim 6, it is characterised in that: after the bonding process
It further include that ironing processing is carried out to the antibacterial health-care fabric.