CN109291135A - Cover plate for drilling hole - Google Patents
Cover plate for drilling hole Download PDFInfo
- Publication number
- CN109291135A CN109291135A CN201811204497.3A CN201811204497A CN109291135A CN 109291135 A CN109291135 A CN 109291135A CN 201811204497 A CN201811204497 A CN 201811204497A CN 109291135 A CN109291135 A CN 109291135A
- Authority
- CN
- China
- Prior art keywords
- water
- cover plate
- drilling hole
- fat composition
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of cover plate for drilling hole, including a metal foil and at least one layer of hydrophilic resin fat composition layer, wherein the hydrophilic resin fat composition layer is incorporated into the metal foil, and the reaction heat enthalpy of the hydrophilic resin fat composition layer is between 10~40 (J/g), and fusing point is that can form resin twisting cohesion on preferable Hole Wall Roughness and less drill bit between 48~70 DEG C.
Description
This case be a divisional application, female case be the applying date be on October 22nd, 2014, application No. is
201410566017.3, the Chinese invention patent application of entitled " cover plate for drilling hole ".
Technical field
The present invention is in relation to a kind of cover plate for drilling hole, espespecially a kind of brill that can be used for the fields such as IC support plate, PCB, BGA plate and use
Hole cover board has the advantages that structure is simple, can form preferable Hole Wall Roughness and resin twisting cohesion on less drill bit.
Background technique
In recent years, electronic product tend to it is frivolous, multi-functional and at high speed develop so that printed circuit board in micropore quantity with
Density content rapidly increases, and based under this trend, drilling quality, hole location precision and drill point service life and other effects are so important finger
Mark, however traditional accessory plate such as traditional cover boards such as aluminium foil or phenolic resin, be not suitable for already this demand using upper, if making reluctantly
Occurred partially with bad missings such as drill point abrasions with then easy broken needle, hole.
Now, drilled metal cover board (Aluminum cover is most) consequentiality that different kenels are constituted, but stablize and undoubtedly by
Application it is seldom, it is mainly complicated in lubrication layer formula and in buffering drilling inferior horn pressure, lubrication drill point (reducing drill point abrasion)
It is functionally all inadequate with adherence metal foil (drill point heat sinking function) etc..Such as to belong to water-soluble lubricating mixture, synthetic wax
With perforated plate made by the scraps of paper, but there is drill point that can not radiate and stickiness problem;It is glutinous with polyethylene glycol or the improvement of polyethers esters
Property problem, but have drill point can not chip removal and the inclined problem in hole;Film, glue is made with water-soluble resin mixing water-insoluble lubricant
It is coated with thermosetting resin between the composite wood of piece and aluminium foil, film, aluminium foil, the drilling cover board of totally three kinds of various combinations construction, but matched
Side is all complicated with production and the thermoset resin layer that combines, and because hardness is high it is easier that drill point skids due to hole deviates or broken needle.
Summary of the invention
A kind of structure is simple, can form preferable Hole Wall Roughness and less drill bit providing for the main object of the present invention
The cover plate for drilling hole of upper resin twisting cohesion.
In order to achieve the above object, a kind of cover plate for drilling hole set by the present invention, including a metal foil and at least one layer of
Hydrophilic resin fat composition layer, wherein the hydrophilic resin fat composition layer is incorporated into the metal foil, and the hydrophilic resin group
At the reaction heat enthalpy of nitride layer between 10~40 (J/g), and fusing point is between 48~70 DEG C.
When implementation, the metal foil with a thickness of 0.05mm~0.2mm.
When implementation, the hydrophilic resin fat composition layer with a thickness of 0.02mm~0.15mm.
When implementation, which is selected from polypropylene oxide, polyethylene oxide including one, gathers and stretch fourth two
Alcohol, polyolefin glycol polyester, carboxymethyl cellulose, polyvinyl pyrrolidone, polyacrylamide and Sodium Polyacrylate wherein one
Kind has crystalline water-soluble resin;Or, hydrophilic resin fat composition layer includes one selected from polyethylene glycol phenolic ether, poly- second
The alcohol ethers such as glycol alkyl ether have crystalline water-soluble resin;Or, the hydrophilic resin fat composition layer is selected from including one
There is crystalline water-soluble resin in alcohols such as hexitol, propylene glycol, glycerine.
When implementation, which is separately mixed with an inorganic compound, a defoaming agent and an interfacial agent, to be formed
The hydrophilic resin fat composition layer.
When implementation, which is talcum powder, molybdenum disulfide, zinc molybdate, calcium carbonate, graphite, boron nitride, nitridation
The one of which such as aluminium, aluminium oxide, aluminium hydroxide or two or more substances.
When implementation, which is modified polysiloxanes (Polysiloxane) resin and its relevant derivative, silicon
The one of which such as power health (Silicone) and its fatty acid, fatty acid amine, polyether compound or two or more substances.
When implementation, which is to have hydrophily (hydrophilic part) part and lipophilicity in a molecule
The compound that (lipophilic part) partly coexists, wherein the hydrophilic portion then has carbonate, sulfate etc., the lipophilic
Even property part has direct steel, side refining cyclic aromatic hydrocarbon radical.
When implementation, which is the water-soluble resin of number average molecular weight 300000 to 400000
20 parts by weight after being dissolved in water with 60 parts by weight of water-soluble resin of number average molecular weight 10000 to 80000, add 8 weights
The inorganic compound of amount part stirs and is allowed to be fully dispersed in water-soluble resin aqueous solution, then adds disappearing for 2 parts by weight again
It is stirred after infusion and the interfacial agent of 2 parts by weight and is allowed to be fully dispersed in formed in water-soluble resin aqueous solution.
When implementation, which is the water-soluble resin of number average molecular weight 200000 to 300000
20 parts by weight, after being dissolved in water with 60 parts by weight of water-soluble resin of number average molecular weight 300000 to 400000, addition 8
The inorganic compound of parts by weight stirs and is allowed to be fully dispersed in water-soluble resin aqueous solution, then adds 2 parts by weight again
It is stirred after defoaming agent and the interfacial agent of 2 parts by weight and is allowed to be fully dispersed in formed in water-soluble resin aqueous solution.
When implementation, a primer layer is equipped between the metal foil and the hydrophilic resin fat composition layer.
When implementation, which is any in thermoplastic resin thermosetting resin or two kinds are used in mixed way.
To further appreciate that the present invention, preferred embodiment is lifted below, cooperates schema, figure number, by specific structure of the invention
At content and its it is reached the effect of detailed description are as follows.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of cover plate for drilling hole of the embodiment of the present invention;
Fig. 2 is that the embodiment of the present invention adds the structural schematic diagram after primer layer.
Description of symbols: 1, metal foil;2, hydrophilic resin fat composition layer;3- primer layer.
Specific embodiment
It is embodiment below, but the contents of the present invention are not limited to the range of these embodiments.
Referring to Fig. 1, it is an a kind of embodiment of cover plate for drilling hole of the present invention comprising a metal foil 1 and at least
One layer of hydrophilic resin fat composition layer 2.
The metal foil 1 is aluminium foil, with a thickness of 0.05mm~0.2mm.
The hydrophilic resin fat composition layer 2 is with a thickness of 0.02mm~0.15mm, for being incorporated into the metal foil 1, and the parent
Water-base resin forms the reaction heat enthalpy of nitride layer 2 between 10~40 (J/g), and fusing point is between 48~70 DEG C.
Wherein, which includes one selected from polypropylene oxide, polyethylene oxide, poly- stretches fourth two
Alcohol, polyolefin glycol polyester, carboxymethyl cellulose, polyvinyl pyrrolidone, polyacrylamide and Sodium Polyacrylate wherein one
Kind has crystalline water-soluble resin;Or, hydrophilic resin fat composition layer includes one selected from polyethylene glycol phenolic ether, poly- second
The alcohol ethers such as glycol alkyl ether have crystalline water-soluble resin;Or, the hydrophilic resin fat composition layer is selected from including one
There is crystalline water-soluble resin in alcohols such as hexitol, propylene glycol, glycerine.
And best mode for carrying out the invention is that the water-soluble resin is separately mixed with an inorganic compound, a defoaming agent and one
Interfacial agent, to form the hydrophilic resin fat composition layer 2.Wherein, which is talcum powder, molybdenum disulfide, molybdenum
The substance of the one of which such as sour zinc, calcium carbonate, graphite, boron nitride, aluminium nitride, aluminium oxide, aluminium hydroxide.The defoaming agent system is to change
Polysiloxanes (Polysiloxane) resin and its relevant derivative, silicon power health (Silicone) and its fatty acid, rouge of property
The one of which substance such as fat acid amide, polyether compound.The interfacial agent is to have hydrophily (hydrophilic in a molecule
Part) the compound partly partly coexisted with lipophilicity (lipophilic part), wherein the hydrophilic portion then has carbonic acid
Salt, sulfate etc., even lipophilicity part has direct steel, side refining cyclic aromatic hydrocarbon radical.
Therefore, when actual implementation, which can mitigate rushing from drill bit cutting portion using the aluminium foil of 98 or more purity
Hit, and improve the adaptation of drill point blade front end, the hydrophilic resin fat composition layer 2 be number average molecular weight 300000 to
400000 20 parts by weight of water-soluble resin, it is molten with 60 parts by weight of water-soluble resin of number average molecular weight 10000 to 80000
Solution in water after, addition 8 parts by weight inorganic compound stir and be allowed to be fully dispersed in water-soluble resin aqueous solution, then
It is stirred after adding the defoaming agent of 2 parts by weight and the interfacial agent of 2 parts by weight again and is allowed to be fully dispersed in water-soluble resin water
Formed in solution.Hydrophilic resin fat composition layer 2 after drying is made for the mode of 0.03mm, using double roller cylinder Comma
Coater is coated with this hydrophilic resin fat composition layer 2 after the metal foil 1 that single side forms thickness 0.01mm, and drying machine is recycled to make
Cooling, use to form cover plate for drilling hole of the invention (being above the 1st embodiment).
Also, number average molecular weight 200000 to 300000 also can be used in the present invention hydrophilic resin fat composition layer 2
20 parts by weight of water-soluble resin are dissolved in water with 60 parts by weight of water-soluble resin of number average molecular weight 300000 to 400000
In after, addition 8 parts by weight inorganic compound stir and be allowed to be fully dispersed in water-soluble resin aqueous solution, then add again
It is stirred after the defoaming agent of 2 parts by weight and the interfacial agent of 2 parts by weight and is allowed to be fully dispersed in water-soluble resin aqueous solution
It is formed, the hydrophilic resin fat composition layer 2 after drying is made for the mode of 0.03mm, using double roller cylinder Comma Coater
This hydrophilic resin fat composition layer 2 is coated with after the metal foil 1 that single side forms thickness 0.01mm, drying machine is recycled to be allowed to cold
But, it uses to form cover plate for drilling hole of the invention (being above the 2nd embodiment).
Therefore, by above-mentioned two embodiments cover plate for drilling hole obtained, after the copper-surfaced laminated plates of 6 thickness 0.1mm,
It is that upper mode is configured with the hydrophilic resin fat composition layer 2, on the downside of overlapped copper-surfaced laminated plates, configures lower bolster
(urea plate), with 0.105 Φ of drill bit (0.105mm*2.2mm), rotation speed 200000rpm, feed speed 25mm/sec, withdrawing speed
The condition of 423mm/sec drills to each drill point with 3000hits, shows that difference scans card meter with per minute by using heat
10 DEG C of heating rate measuring range is 40~80 DEG C and is measured, for any on the cover plate for drilling hole of above-described embodiment 1,2
3 different zones of selection carry out actual measurement, it is possible to find its heat enthalpy value is 17 (J/g), and fusing point is 60 DEG C, and thick by hole wall
Rugosity test (after drilling processing for process hole center section cutting grind, in a side of hole wall most
Big protrusion is measured with the distance until most deep recess portion.Measurement site be drill bit the 2999th hole processing hole do twice put down
As Hole Wall Roughness value), hole location precision test (using hole analyzer to bottom in the copper foil laminates being overlapped
The hole site of 3000hits and the offset of specified coordinate are measured in the back side of copper foil laminates, are calculated each drill point flat
Mean value and standard deviation (δ), calculate+3 δ of average value and maximum value, record 7 bit bores processing average value), resin volume
The judgement of attached amount degree (carries out observation phase to 7 drill points after 3000hits using the optical microscopy that multiplying power is 25 times respectively
Maximum diameter and drill bit axis direction length for the resin twisting cohesion of drill point diameter judge resin twisting cohesion amount degree) after can find, lead to
Resin twisting cohesion on preferable Hole Wall Roughness and less drill bit can be formed by crossing cover plate for drilling hole set by the present invention really.
In addition, as shown in Fig. 2, to increase the adaptation of the metal foil and the hydrophilic resin fat composition layer, it can be pre-
Primer layer 3 prior to forming 0.001~0.01mm of thickness in metal foil is most ideal.As long as the primer layer 3 can promote resin
The substance of constituent adaptation, other have no any restriction, also can be used any in thermoplasticity or thermosetting resin
A kind of or two kinds are used in mixed way, thermoplastic resin such as vinyl acetate condensate, Polyester condensate, acryloyl base system is poly-
Zoarium is the equal substances or mixture, the resin etc. of thermosetting resin such as epoxy base system resin and cyanate series.
Therefore, the boring Aluminum cover of the present invention has the heat content and fusing point of particular range by hydrophilic resin fat composition layer
Value, can provide heat dissipation appropriate and degree of lubrication for drill point, so Hole Wall Roughness and drill point when can be directed to drilling processing
Upper resin twisting cohesion is contributed.
The above is specific embodiments of the present invention and the technological means used, according to the exposure or introduction of this paper
Can derive and derive many change and amendment, still can be considered equivalent change made by conception of the invention, caused by make
It with the connotation still covered without departing from specification and schema, is regarded as within technology scope of the invention, closes first old
It is bright.
In conclusion the present invention really can reach the expected purpose of invention according to content disclosed above, a kind of drilling is provided
With cover board, the value utilized in great industry, whence proposes application for a patent for invention in accordance with the law.
Claims (14)
1. a kind of cover plate for drilling hole, it is characterised in that comprising:
One metal foil;And
At least one layer of hydrophilic resin fat composition layer, is incorporated into the metal foil, and the hydrophilic resin fat composition layer its
Reaction heat enthalpy is between 10~40J/g, and fusing point is between 48~70 DEG C.
2. cover plate for drilling hole as described in claim 1, wherein the metal foil with a thickness of 0.05mm~0.2mm.
3. cover plate for drilling hole as described in claim 1, wherein the hydrophilic resin fat composition layer with a thickness of 0.02mm~
0.15mm。
4. cover plate for drilling hole as described in claim 1, wherein the hydrophilic resin fat composition layer includes one selected from polycyclic oxygen
Propane, polyethylene oxide gather and stretch butanediol, polyolefin glycol polyester, carboxymethyl cellulose, polyvinyl pyrrolidone, poly- third
Acrylamide and Sodium Polyacrylate it is one of there is crystalline water-soluble resin.
5. cover plate for drilling hole as described in claim 1, wherein the hydrophilic resin fat composition layer includes one selected from poly- second two
Alcohol phenolic ether or polyethylene glycol alkyl ether have crystalline water-soluble resin.
6. cover plate for drilling hole as described in claim 1, wherein the hydrophilic resin fat composition layer include one selected from hexitol,
Propylene glycol or glycerine it is one of there is crystalline water-soluble resin.
7. the cover plate for drilling hole as described in claim 4,5 or 6, wherein the water-soluble resin be separately mixed with an inorganic compound,
One defoaming agent and an interfacial agent, to form the hydrophilic resin fat composition layer.
8. cover plate for drilling hole as claimed in claim 7, wherein the inorganic compound is talcum powder, molybdenum disulfide, zinc molybdate, carbon
Sour calcium, graphite, boron nitride, aluminium nitride, aluminium oxide or aluminium hydroxide is one of or the mixture of two or more arbitrary proportions.
9. cover plate for drilling hole as claimed in claim 7, wherein the defoaming agent is modified polyorganosiloxane resin and its relevant
The mixing of derivative, silicon power health and its fatty acid, fatty acid amine or polyether compound one of which or two or more arbitrary proportions
Object.
10. cover plate for drilling hole as claimed in claim 7, wherein the interfacial agent is to have hydrophilic portion and parent in a molecule
The compound that lipid part coexists, wherein the hydrophilic portion is selected from the mixture of carbonate, sulfate or its arbitrary proportion, should
Even lipophilicity part has direct steel, side refining cyclic aromatic hydrocarbon radical.
11. cover plate for drilling hole as claimed in claim 7, wherein the hydrophilic resin fat composition layer is number average molecular weight
300000 to 400,000 20 parts by weight of water-soluble resin, the water-soluble resin 60 with number average molecular weight 10000 to 80000
After parts by weight are dissolved in water, the inorganic compound of 8 parts by weight of addition stirs and is allowed to be fully dispersed in water-soluble resin water-soluble
In liquid, is stirred after then adding the defoaming agent of 2 parts by weight and the interfacial agent of 2 parts by weight again and be allowed to be fully dispersed in water-soluble
Formed in property resin aqueous solution.
12. cover plate for drilling hole as claimed in claim 7, wherein the hydrophilic resin fat composition layer is number average molecular weight
200000 to 300,000 20 parts by weight of water-soluble resin, the water-soluble resin with number average molecular weight 300000 to 400000
After 60 parts by weight are dissolved in water, the inorganic compound of 8 parts by weight of addition stirs and is allowed to be fully dispersed in water-soluble resin water
In solution, is stirred after then adding the defoaming agent of 2 parts by weight and the interfacial agent of 2 parts by weight again and be allowed to be fully dispersed in water
Formed in soluble resin aqueous solution.
13. cover plate for drilling hole as described in claim 1 is wherein equipped between the metal foil and the hydrophilic resin fat composition layer
One primer layer.
14. cover plate for drilling hole as claimed in claim 13, wherein the primer layer is in thermoplastic resin or thermosetting resin
Any or two kinds of arbitrary proportions mixture.