CN109280504A - A kind of reflectorized material and preparation method thereof - Google Patents
A kind of reflectorized material and preparation method thereof Download PDFInfo
- Publication number
- CN109280504A CN109280504A CN201811017066.6A CN201811017066A CN109280504A CN 109280504 A CN109280504 A CN 109280504A CN 201811017066 A CN201811017066 A CN 201811017066A CN 109280504 A CN109280504 A CN 109280504A
- Authority
- CN
- China
- Prior art keywords
- layer
- adhesive
- base
- reflective
- superficial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of reflectorized materials, including base, superficial layer, glass microballoon, adhesive layer, reflective layer and gum layer, the base is the hyaline layer body membrane body made of PET, the adhesive layer is to be coated in substrate surface by adhesive sticker to be formed by a layer body, the glass microballoon is uniformly adhered to bonding layer surface, the superficial layer is made of transparent membrane and hot melt adhesive, and superficial layer is adhered on the outside of glass microballoon, the reflective layer is located at the base other side, and the gum layer is located at reflective layer back.The present invention produces superficial layer by the way of prefabricated, it can get out the superficial layer of different colours in advance, when needing to produce different reflective membranes, superficial layer and base need to only be pressed together by process for pressing, without changing production technology, compared with the preparation method of traditional reflective membrane, the present invention is greatly improved the quality of production of product.
Description
Technical field
The invention belongs to reflectorized material manufacturing fields, more specifically more particularly to a kind of reflectorized material.Meanwhile this hair
A kind of bright preparation method for further relating to reflectorized material.
Background technique
Reflectorized material, also referred to as retroreflecting material or reflecting material, including reflective membrane, reflective ink, reflecting sign
Line paint, reflective fabric, reflective leather, light-reflection fabric ribbon and reflection safety sex pilus fabric etc..Its principle is drawn on corresponding material surface
Enter the glass microballoon or the micro- lattice structure of prism of a kind of high refractive index.Reflective membrane be it is a kind of film has been made can be direct applied
Reflecting material, and a kind of reflecting material being most widely used.Common reflective membrane include superficial layer, glass microballoon,
Base and reflective layer first apply one layer of adhesive sticker in base to form superficial layer when production, then uniformly spread glass microballoon
In superficial layer, one layer of reflective layer then is plated at the glass microballoon back side, it, can be on surface if necessary to different reflective colors
Different dyestuffs is dissolved in material, and different reflective colors can be obtained.In the actual production process, change reflective material each time
The reflective color of material, requires to be adjusted production technology, serious to affect production technology, we need a kind of life thus
More efficient reflective membrane preparation method is produced to solve the above problems.
Summary of the invention
The purpose of the present invention is to provide a kind of reflectorized materials and preparation method thereof, to solve to propose in above-mentioned background technique
The problem of.
To achieve the above object, the invention provides the following technical scheme:
A kind of reflectorized material, including base, superficial layer, glass microballoon, adhesive layer, reflective layer and gum layer, the base be by
Hyaline layer body membrane body made of PET, the adhesive layer are to be coated in substrate surface by adhesive sticker to be formed by a layer body, the glass
Microballon is uniformly adhered to bonding layer surface, and the superficial layer is made of transparent membrane and hot melt adhesive, and superficial layer is adhered to glass
On the outside of glass microballon, the reflective layer is located at the base other side, and the gum layer is located at reflective layer back.
Preferably, the base with a thickness of 20-30 microns.
Preferably, the gum layer side is equipped with peeling layer.
A kind of preparation method of reflectorized material, includes the following steps:
S1, superficial layer processing: different dyestuffs being put into different hot melt adhesive and mixed, so that the different heat of color be made
Then hot melt adhesive is coated on the inside of transparent membrane by melten gel by coating machine, so that the different superficial layer of color is made, at it
After processing is completed, according to the different by its classification storage of color;
S2, it plants pearl: adhesive sticker is uniformly coated on by coating machine by PET film surface, then it is carried out by dryer
Drying, after the completion of to be dried, PET film surface will form one layer of adhesive layer, and glass microballoon is directly then spread in adhesive layer
Surface;
S3, aluminize: will by planting pearl treated that PET film is sent to vacuum aluminum-plating machine, carried on the back by vacuum aluminum-plating machine in base
It plates one layer of aluminium film and plants pearl mould to obtain aluminizing to form reflective layer in portion;
S4 pressing: the superficial layer of different colours is selected according to the demand of client, baking oven is first passed through and comes to the hot melt on superficial layer
Glue is heated, and superficial layer and aluminizing then is planted pearl molding by pressing machine and is combined, thus formed with it is coloured instead
Light film.
Preferably, the drying temperature of adhesive sticker is 30-45 DEG C in the step S2, and drying time is 2-5 minutes.
Preferably, the diameter of the glass microballoon is 40-60 microns.
It compared with prior art, can the beneficial effects of the present invention are: the present invention produces superficial layer by the way of prefabricated
It gets out the superficial layer of different colours in advance, it, only need to be by process for pressing by superficial layer when needing to produce different reflective membranes
It is pressed together with base, without changing production technology, compared with the preparation method of traditional reflective membrane, the present invention
It is greatly improved the quality of production of product.
Detailed description of the invention
Fig. 1 is the structural diagram of the present invention.
In figure: 1 base, 2 superficial layers, 3 glass microballoons, 4 adhesive layers, 5 reflective layers, 6 gum layers, 7 transparent membranes, 8 hot melts
Glue.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.
Referring to Fig. 1, the present invention provides a kind of reflectorized material, including base 1, superficial layer 2, glass microballoon 3, adhesive layer
4, reflective layer 5 and gum layer 6, the base 1 are the hyaline layer body membrane bodies made of PET, and the adhesive layer 4 is applied by adhesive sticker
It overlays on substrate surface and is formed by a layer body, the glass microballoon 3 is uniformly adhered to 4 surface of adhesive layer, and the superficial layer 2 is by saturating
Bright film 7 and hot melt adhesive 8 form, and superficial layer 2 is adhered to 3 outside of glass microballoon, and the reflective layer 5 is located at 1 other side of base,
The gum layer 6 is located at 5 back of reflective layer.
Specifically, the base 1 with a thickness of 20-30 microns.
Specifically, 6 side of gum layer is equipped with peeling layer.
A kind of preparation method of reflectorized material, includes the following steps:
S1, superficial layer processing: different dyestuffs being put into different hot melt adhesive and mixed, so that the different heat of color be made
Then hot melt adhesive is coated on the inside of transparent membrane by melten gel by coating machine, so that the different superficial layer of color is made, at it
After processing is completed, according to the different by its classification storage of color;
S2, it plants pearl: adhesive sticker is uniformly coated on by coating machine by PET film surface, then it is carried out by dryer
Drying, after the completion of to be dried, PET film surface will form one layer of adhesive layer, and glass microballoon is directly then spread in adhesive layer
Surface;
S3, aluminize: will by planting pearl treated that PET film is sent to vacuum aluminum-plating machine, carried on the back by vacuum aluminum-plating machine in base
It plates one layer of aluminium film and plants pearl mould to obtain aluminizing to form reflective layer in portion;
S4 pressing: the superficial layer of different colours is selected according to the demand of client, baking oven is first passed through and comes to the hot melt on superficial layer
Glue is heated, and superficial layer and aluminizing then is planted pearl molding by pressing machine and is combined, thus formed with it is coloured instead
Light film.
Specifically, the drying temperature of adhesive sticker is 30-45 DEG C in the step S2, drying time is 2-5 minutes.
Specifically, the diameter of the glass microballoon is 40-60 microns.
The present invention produces superficial layer by the way of prefabricated, can get out the superficial layer of different colours in advance, work as needs
When producing different reflective membranes, superficial layer and base need to only be pressed together by process for pressing, without changing
Production technology, compared with the preparation method of traditional reflective membrane, the present invention is greatly improved the quality of production of product.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (6)
1. a kind of reflectorized material, including base (1), superficial layer (2), glass microballoon (3), adhesive layer (4), reflective layer (5) and back
Glue-line (6), it is characterised in that: the base (1) is the hyaline layer body membrane body made of PET, and the adhesive layer (4) is by not doing
Glue is coated in substrate surface and is formed by a layer body, and the glass microballoon (3) is uniformly adhered to adhesive layer (4) surface, the table
Surface layer (2) is made of transparent membrane (7) and hot melt adhesive (8), and superficial layer (2) is adhered on the outside of glass microballoon (3), described reflective
Layer (5) is located at base (1) other side, and the gum layer (6) is located at reflective layer (5) back.
2. a kind of reflectorized material according to claim 1, it is characterised in that: the base (1) it is micro- with a thickness of 20-30
Rice.
3. a kind of reflectorized material according to claim 1, it is characterised in that: gum layer (6) side is equipped with peeling layer.
4. a kind of preparation method of reflectorized material described in claim 1, which comprises the steps of:
S1, superficial layer processing: different dyestuffs being put into different hot melt adhesive and mixed, so that the different heat of color be made
Then hot melt adhesive is coated on the inside of transparent membrane by melten gel by coating machine, so that the different superficial layer of color is made, at it
After processing is completed, according to the different by its classification storage of color;
S2, it plants pearl: adhesive sticker is uniformly coated on by coating machine by PET film surface, then it is carried out by dryer
Drying, after the completion of to be dried, PET film surface will form one layer of adhesive layer, and glass microballoon is directly then spread in adhesive layer
Surface;
S3, aluminize: will by planting pearl treated that PET film is sent to vacuum aluminum-plating machine, carried on the back by vacuum aluminum-plating machine in base
It plates one layer of aluminium film and plants pearl mould to obtain aluminizing to form reflective layer in portion;
S4 pressing: the superficial layer of different colours is selected according to the demand of client, baking oven is first passed through and comes to the hot melt on superficial layer
Glue is heated, and superficial layer and aluminizing then is planted pearl molding by pressing machine and is combined, thus formed with it is coloured instead
Light film.
5. a kind of preparation method of reflectorized material according to claim 4, it is characterised in that: adhesive sticker in the step S2
Drying temperature be 30-45 DEG C, drying time be 2-5 minutes.
6. a kind of preparation method of reflectorized material according to claim 4, it is characterised in that: the diameter of the glass microballoon
It is 40-60 microns.