CN109266208A - A kind of guitar paint special and preparation method thereof - Google Patents
A kind of guitar paint special and preparation method thereof Download PDFInfo
- Publication number
- CN109266208A CN109266208A CN201811110163.XA CN201811110163A CN109266208A CN 109266208 A CN109266208 A CN 109266208A CN 201811110163 A CN201811110163 A CN 201811110163A CN 109266208 A CN109266208 A CN 109266208A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- guitar
- paint
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of guitar paint special, it calculates by weight, including 35-50 parts of synthctic fat acid resin, 35-50 parts of hydroxyl polyacrylic resin, 40-50 parts of isocyanate addition product, 35-50 parts of acrylic resin, 20-30 parts of ethyl acetate, 10-20 parts of polyketone resin, 10-20 parts of propylene glycol methyl ether acetate, 8-15 parts of butyl acetate, 10-18 parts of phenolic aldehyde ethanol, 10-18 parts of dimethylbenzene, PMA10-15 parts, 20-30 parts of castor oil, 1-5 parts of defoaming agent, 2-8 parts of levelling agent, efficient flatting silica 10-20 parts, 10-20 parts of drier.The solution have the advantages that, using the above formula and its manufacturing method, it can be improved rate of drying of the coating in film forming procedure, it avoids in the overlong time for waiting guitar dry, prevent the beauty for being influenced and being destroyed guitar musical instrument by external environment in prolonged drying process, and the present invention can keep paint color for a long time, be not in fall the case where painting.
Description
Technical field
The present invention relates to paint field, in particular to a kind of guitar paint special and preparation method thereof.
Background technique
It after the completion of guitar production, will paint to other, the generally existing large viscosity of guitar paint at this stage, paint film are dry
Dry effect undesirable problem needs to stand the problems such as dry for a long time after spraying, and is easy after guitar long-time use
Now fall the case where painting, influences guitar beauty and service life.
Summary of the invention
The purpose of the present invention is to provide a kind of guitar paint specials and preparation method thereof, are remarkably improved the dry speed of guitar
Rate, and guitar is not in the situation for falling paint during prolonged use.
Technical solution of the present invention: a kind of guitar paint special calculates by weight, including synthctic fat acid resin 35-50
Part, 35-50 parts of hydroxyl polyacrylic resin, 40-50 parts of isocyanate addition product, 35-50 parts of acrylic resin, ethyl acetate
20-30 parts, 10-20 parts of polyketone resin, 10-20 parts of propylene glycol methyl ether acetate, 8-15 parts of butyl acetate, phenolic aldehyde ethanol 10-
18 parts, 10-18 parts of dimethylbenzene, PMA10-15 parts, 20-30 parts of castor oil, 1-5 parts of defoaming agent, 2-8 parts of levelling agent, efficient delustring
10-20 parts of powder, 10-20 parts of drier.
Aforementioned guitar paint special, parts by weights calculate, including 40-45 parts of synthctic fat acid resin, hydroxyl polyacrylic acid tree
40-45 parts of rouge, 45-48 parts of isocyanate addition product, 40-45 parts of acrylic resin, 22-28 parts of ethyl acetate, polyketone resin 12-
18 parts, 12-18 parts of propylene glycol methyl ether acetate, 10-14 parts of butyl acetate, 12-16 parts of phenolic aldehyde ethanol, 12-16 parts of dimethylbenzene,
PMA12-14 parts, 22-28 parts of castor oil, 2-4 parts of defoaming agent, 3-6 parts of levelling agent, efficient flatting silica 12-15 parts, drier 12-
15 parts.
Aforementioned guitar paint special, parts by weights calculate, it is characterised in that: including 42 parts of synthctic fat acid resin, hydroxyl is poly-
42 parts of acrylic resin, 46 parts of isocyanate addition product, 42 parts of acrylic resin, 25 parts of ethyl acetate, 15 parts of polyketone resin, third
15 parts of glycol methyl ether acetate, 13 parts of butyl acetate, 14 parts of phenolic aldehyde ethanol, 14 parts of dimethylbenzene, PMA13 parts, 25 parts of castor oil,
3 parts of defoaming agent, 5 parts of levelling agent, 13 parts of efficient flatting silica, 13 parts of drier.
The preparation method of aforementioned guitar paint special, comprising the following steps:
It (1) will include synthctic fat acid resin, hydroxyl polyacrylic resin, isocyanate addition product, acrylic resin, acetic acid second
Ester, polyketone resin, which is added to the container, to be dispersed to stir evenly under 600-800 revs/min of speed；
(2) in order by propylene glycol methyl ether acetate under the speed of 600-800r/min, butyl acetate, phenolic aldehyde ethanol, two
Toluene, PMA are added in said vesse, then disperse to stir evenly under the speed of 1000-1200r/min；
(3) in order by castor oil under the speed of 600-800r/min, defoaming agent, levelling agent, efficient flatting silica is added above-mentioned
Dispersion stirs evenly and is prepared into mian paint under the speed of 600-800r/min in container；
(4) mian paint of above-mentioned preparation is divided into two equal portions, then promotor is added thereto in a mian paint and is uniformly mixed, will be urged
Dry agent is added in another mian paint and is uniformly mixed, by above-mentioned two parts of mian paints after mixing to get finished product when use.
Compared with prior art, the solution have the advantages that, using the above formula and its manufacturing method, it can be improved painting
Expect the rate of drying in film forming procedure, avoids preventing in the overlong time for waiting guitar dry in prolonged drying process
In influenced and destroyed the beauty of guitar musical instrument by external environment, and the present invention can keep paint color for a long time, be not in fall
The case where paint, occurs.
Specific embodiment
Embodiment 1
A kind of guitar paint special, calculates by weight, including 35 parts of synthctic fat acid resin, and 35 parts of hydroxyl polyacrylic resin,
40 parts of isocyanate addition product, 35 parts of acrylic resin, 20 parts of ethyl acetate, 10 parts of polyketone resin, propylene glycol methyl ether acetate
10 parts, 8 parts of butyl acetate, 10 parts of phenolic aldehyde ethanol, 10 parts of dimethylbenzene, PMA10 parts, 20 parts of castor oil, 1 part of defoaming agent, levelling
2 parts of agent, 10 parts of efficient flatting silica, 10 parts of drier.
The preparation method of the guitar paint special, which comprises the following steps:
It (1) will include synthctic fat acid resin, hydroxyl polyacrylic resin, isocyanate addition product, acrylic resin, acetic acid second
Ester, polyketone resin, which is added to the container, to be dispersed to stir evenly under the speed of 600r/min；
(2) in order by propylene glycol methyl ether acetate under the speed of 600r/min, butyl acetate, phenolic aldehyde ethanol, dimethylbenzene,
PMA is added in said vesse, then disperses to stir evenly under the speed of 1000r/min；
(3) in order by castor oil, defoaming agent, levelling agent, efficient flatting silica addition said vesse under the speed of 600r/min
In under the speed of 600r/min dispersion stir evenly and be prepared into mian paint；
(4) mian paint of above-mentioned preparation is divided into two equal portions, then promotor is added thereto in a mian paint and is uniformly mixed, will be urged
Dry agent is added in another mian paint and is uniformly mixed, by above-mentioned two parts of mian paints after mixing to get finished product when use.
Embodiment 2
A kind of guitar paint special, calculates by weight, including 42 parts of synthctic fat acid resin, and 42 parts of hydroxyl polyacrylic resin,
46 parts of isocyanate addition product, 42 parts of acrylic resin, 25 parts of ethyl acetate, 15 parts of polyketone resin, propylene glycol methyl ether acetate
15 parts, 13 parts of butyl acetate, 14 parts of phenolic aldehyde ethanol, 14 parts of dimethylbenzene, PMA13 parts, 25 parts of castor oil, 3 parts of defoaming agent, levelling
5 parts of agent, 13 parts of efficient flatting silica, 13 parts of drier.
The preparation method of the guitar paint special, which comprises the following steps:
It (1) will include synthctic fat acid resin, hydroxyl polyacrylic resin, isocyanate addition product, acrylic resin, acetic acid second
Ester, polyketone resin, which is added to the container, to be dispersed to stir evenly under the speed of 700r/min；
(2) in order by propylene glycol methyl ether acetate under the speed of 700r/min, butyl acetate, phenolic aldehyde ethanol, dimethylbenzene,
PMA is added in said vesse, then disperses to stir evenly under the speed of 1100r/min；
(3) in order by castor oil, defoaming agent, levelling agent, efficient flatting silica addition said vesse under the speed of 700r/min
In under the speed of 700r/min dispersion stir evenly and be prepared into mian paint；
(4) mian paint of above-mentioned preparation is divided into two equal portions, then promotor is added thereto in a mian paint and is uniformly mixed, will be urged
Dry agent is added in another mian paint and is uniformly mixed, by above-mentioned two parts of mian paints after mixing to get finished product when use.
Embodiment 3
A kind of guitar paint special, calculates by weight, including 50 parts of synthctic fat acid resin, and 50 parts of hydroxyl polyacrylic resin,
50 parts of isocyanate addition product, 50 parts of acrylic resin, 30 parts of ethyl acetate, 20 parts of polyketone resin, propylene glycol methyl ether acetate
20 parts, 15 parts of butyl acetate, 18 parts of phenolic aldehyde ethanol, 18 parts of dimethylbenzene, PMA15 parts, 30 parts of castor oil, 5 parts of defoaming agent, levelling
8 parts of agent, 20 parts of efficient flatting silica, 20 parts of drier.
The preparation method of the guitar paint special, which comprises the following steps:
It (1) will include synthctic fat acid resin, hydroxyl polyacrylic resin, isocyanate addition product, acrylic resin, acetic acid second
Ester, polyketone resin, which is added to the container, to be dispersed to stir evenly under the speed of 800r/min；
(2) in order by propylene glycol methyl ether acetate under the speed of 800r/min, butyl acetate, phenolic aldehyde ethanol, dimethylbenzene,
PMA is added in said vesse, then disperses to stir evenly under the speed of 1200r/min；
(3) in order by castor oil, defoaming agent, levelling agent, efficient flatting silica addition said vesse under the speed of 800r/min
In under the speed of 800r/min dispersion stir evenly and be prepared into mian paint；
(4) mian paint of above-mentioned preparation is divided into two equal portions, then promotor is added thereto in a mian paint and is uniformly mixed, will be urged
Dry agent is added in another mian paint and is uniformly mixed, by above-mentioned two parts of mian paints after mixing to get finished product when use.
Claims (4)
1. a kind of guitar paint special, calculates by weight, it is characterised in that: including 35-50 parts of synthctic fat acid resin, hydroxyl is poly-
35-50 parts of acrylic resin, 40-50 parts of isocyanate addition product, 35-50 parts of acrylic resin, 20-30 parts of ethyl acetate, gather
10-20 parts of ketone resin, 10-20 parts of propylene glycol methyl ether acetate, 8-15 parts of butyl acetate, 10-18 parts of phenolic aldehyde ethanol, dimethylbenzene
It 10-18 parts, PMA10-15 parts, 20-30 parts of castor oil, 1-5 parts of defoaming agent, 2-8 parts of levelling agent, efficient flatting silica 10-20 parts, urges
It is agent 10-20 parts dry.
2. guitar paint special according to claim 1, parts by weights is calculated, it is characterised in that: including synthctic fat acid resin
40-45 parts, 40-45 parts of hydroxyl polyacrylic resin, 45-48 parts of isocyanate addition product, 40-45 parts of acrylic resin, acetic acid
22-28 parts of ethyl ester, 12-18 parts of polyketone resin, 12-18 parts of propylene glycol methyl ether acetate, 10-14 parts of butyl acetate, phenolic aldehyde ethyl alcohol
12-16 parts of liquid, 12-16 parts of dimethylbenzene, PMA12-14 parts, 22-28 parts of castor oil, 2-4 parts of defoaming agent, 3-6 parts of levelling agent, efficiently
12-15 parts of flatting silica, 12-15 parts of drier.
3. guitar paint special according to claim 1, parts by weights is calculated, it is characterised in that: including synthctic fat acid resin
42 parts, 42 parts of hydroxyl polyacrylic resin, 46 parts of isocyanate addition product, 42 parts of acrylic resin, 25 parts of ethyl acetate, polyketone
15 parts of resin, 15 parts of propylene glycol methyl ether acetate, 13 parts of butyl acetate, 14 parts of phenolic aldehyde ethanol, 14 parts of dimethylbenzene, PMA13 parts,
25 parts of castor oil, 3 parts of defoaming agent, 5 parts of levelling agent, 13 parts of efficient flatting silica, 13 parts of drier.
4. the preparation method of guitar paint special according to claim 1 to 3, which is characterized in that including following step
It is rapid:
It (1) will include synthctic fat acid resin, hydroxyl polyacrylic resin, isocyanate addition product, acrylic resin, acetic acid second
Ester, polyketone resin, which is added to the container, to be dispersed to stir evenly under 600-800 revs/min of speed；
(2) in order by propylene glycol methyl ether acetate under the speed of 600-800r/min, butyl acetate, phenolic aldehyde ethanol, two
Toluene, PMA are added in said vesse, then disperse to stir evenly under the speed of 1000-1200r/min；
(3) in order by castor oil under the speed of 600-800r/min, defoaming agent, levelling agent, efficient flatting silica is added above-mentioned
Dispersion stirs evenly and is prepared into mian paint under the speed of 600-800r/min in container；
(4) mian paint of above-mentioned preparation is divided into two equal portions, then promotor is added thereto in a mian paint and is uniformly mixed, will be urged
Dry agent is added in another mian paint and is uniformly mixed, by above-mentioned two parts of mian paints after mixing to get finished product when use.