CN106590374A - Back plate, side plate used paint and front plate used paint used for guitar painting and painting method of guitar - Google Patents
Back plate, side plate used paint and front plate used paint used for guitar painting and painting method of guitar Download PDFInfo
- Publication number
- CN106590374A CN106590374A CN201710004239.XA CN201710004239A CN106590374A CN 106590374 A CN106590374 A CN 106590374A CN 201710004239 A CN201710004239 A CN 201710004239A CN 106590374 A CN106590374 A CN 106590374A
- Authority
- CN
- China
- Prior art keywords
- guitar
- parts
- paint
- side plate
- backboard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses back plate, side plate used paint and front plate used paint used for guitar painting. The back plate, side plate used paint is prepared from 35-50 parts of synthetic fatty acid resin, 35-50 parts of acrylic resin, 8-15 parts of n-butyl acetate, 10-15 parts of PMA, 0.1-0.3 part of antiforming agent and 0.2-0.5 part of flatting agent; the front plate used paint is prepared from 25-40 parts of cotton liquid, 20-30 parts of castor oil, 25-35 parts of n-butyl acetate and 15-25 parts of PMA. According to the back plate, side plate used paint and front plate used paint used for guitar painting, the obtained back plate, side plate used paint and the front plate used paint can make the surface of the guitar form paint films which have good performance and are safe and environmentally friendly, and the matching of the back plate, side plate paint film and the front plate paint film make the guitar generate good vibration and sound making so as to generate good sound quality and tone. In addition, the painting method is more beneficial to the best matching constituted by the formed back plate, side plate paint film and the formed front plate paint film so as to be beneficial to the vibration and the sound making of the guitar, and the painting method makes the paint films formed on the surface of the guitar have more excellent performance.
Description
Technical field
The present invention relates to guitar application techniques field, the more particularly, to backboard of guitar application, side plate paint and positive plate
With paint, meanwhile, further relate to use the coating process of the backboard, side plate paint and positive plate paint application guitar.
Background technology
In guitar manufacturing process, the application of paint vehicle is very big for the impact of guitar quality, and the paint film formed by paint vehicle is not only
Brightness, richness, hardness, anti-wear performance and the mirror effect on guitar surface are directly affected, but also shaking for guitar can be affected
The dynamic and assimilation effect to high pitch, and then affect the tone color of guitar；Additionally, the application thickness and coating process of paint vehicle also can affect
The tonequality and tamber effect of guitar.In prior art, a kind of water-borne wood coating for electric guitar surface and its painting are disclosed
Coating method, can obtain the paint film effect that richness is good, hardness is high, mirror effect is good, and the advantage with safety and environmental protection.But mesh
The front research for guitar paint film concentrates on impact of the paint film property to guitar surface, and sound, tone color of the paint film for guitar
Etc. aspect influence research it is less.
The content of the invention
To solve the deficiency that prior art is present, the invention provides the backboard for guitar application, the side that use cooperatively
Plate is painted and positive plate paint, is painted and matching that positive plate is painted by backboard, side plate, not only makes guitar backboard, side plate and positive plate
Surface is respectively formed the paint film of excellent performance and safety and environmental protection, and makes guitar have good tonequality and tone color.
For achieving the above object, the invention provides a kind of backboard for guitar application, side plate paint and positive plate are painted,
The backboard, side plate enamel-cover include following raw material component：Synthctic fat acid resin 35-50 parts, acrylic resin 35-50
Part, butyl acetate 8-15 parts, PMA10-15 parts, defoamer 0.1-0.3 parts, levelling agent 0.2-0.5 parts；The positive plate is included with enamel-cover
Following raw material component：Cotton liquid 25-40 parts, castor oil 20-30 parts, butyl acetate 25-35 parts, PMA15-25 parts.
The backboard of the present invention, side plate are painted using synthetic fatty acid resin-bonded acrylic resin as main film forming substance,
Be equipped with butyl acetate, PMA, then in addition a small amount of defoamer, levelling agent as auxiliary agent, the painting at the backboard as guitar and side plate
Paint, the paint film of formation has a characteristic that hardness is high, transparency is high, richness is good, and can firmly be attached to guitar backboard,
At side plate, preferable wearability is formed.But because the air film that this backboard, side plate paint film are formed is too hard, it is unfavorable for sending out for guitar
Sound, therefore the present invention used using cotton liquid, castor oil as main film forming substance in the positive plate surface of guitar, is equally equipped with butyl acetate
And PMA, the positive plate paint film good to form pliability, and then form softer air film, beneficial to the sounding of guitar, and with backboard, side
Cooperation, the sounding of joint effect guitar and vibration, and the absorption to high pitch are formed between plate paint film, so that guitar has preferably
Tonequality and tone color.Therefore, the backboard for guitar application of the invention, side plate paint and positive plate paint, paint in backboard, side plate
Under cooperation with positive plate paint, can not only make guitar surface that there is good performance, but also it is good to have can guitar
Sounding and tonequality, tone color；Additionally, the guitar paint film safety and environmental protection for being formed, on human body without impact.
Used as the further restriction to above-mentioned technical proposal, the backboard, side plate enamel-cover include following raw material group
Point：40 parts of synthctic fat acid resin, 40 parts of acrylic resin, 10 parts of butyl acetate, PMA10 parts, 0.2 part of defoamer, levelling agent
0.3 part；The positive plate enamel-cover includes following raw material component：30 parts of cotton liquid, 20 parts of castor oil, 30 parts of butyl acetate,
PMA20 parts.
Used as the further restriction to above-mentioned technical proposal, the defoamer adopts defoamer 2030；
Used as the further restriction to above-mentioned technical proposal, the levelling agent adopts levelling agent 3130.
The optimum feed stock component proportion for further limiting backboard, side plate paint and positive plate paint of the invention, and defoamer, stream
The species of flat agent, so that the paint film property and tonequality of guitar are more excellent.
Meanwhile, present invention also offers a kind of coating process of guitar, comprises the following steps：
A, guitar backboard, the application of side plate：
A1, by backboard as above, side plate paint with curing agent, diluent press 1:(0.6-0.8):(1-1.2) weight
Amount proportioning mixing, stirs, and obtains backboard, side plate paint vehicle；
A2, by backboard, side plate paint vehicle even application on the backboard and side plate of guitar, coating one layer after stand 2-2.5 it is little
When, then with 800-1000 mesh sand paperings, spray again afterwards, ten layers of spraying are altogether carried out, complete to guitar backboard, side plate
Application；
The application of the positive plate of b, guitar：
B1,1 will be pressed with diluent by positive plate paint as above:(1-1.2) weight proportion mixing, stirs, and obtains
To positive plate paint vehicle；
B2, by positive plate paint vehicle even application on the positive plate of guitar, coating one layer after stand 2-2.5 hours, Ran Houyong
800-1000 mesh sand paperings, spray again afterwards, and three layers of spraying are carried out altogether, complete the application to the positive plate of guitar.
In the coating process of guitar, application is separately carried out to guitar backboard, side plate and positive plate, the backboard of employing, side plate are used
Paint, via spraying guitar backboard and side plate after being mixed and made into backboard, side plate paint vehicle with curing agent, diluent, and limits coating
The interval time of the number of plies and every layer of spraying operation；Using positive plate paint, via with diluent be mixed after positive plate paint vehicle spray
Apply the positive plate of guitar, the interval time of the same number of plies and every layer of spraying operation for limiting coating, but backboard, side plate paint vehicle and coat
Number, from positive plate paint vehicle and coating the number of plies it is different so that backboard, side plate formation paint film and positive plate shape into paint film between constitute most
The vibration of good cooperation, more conducively guitar and sounding, form more preferable tonequality and tone color, and make the paint film of guitar surface formation
Can be more excellent.
Used as the further restriction to above-mentioned technical proposal, the curing agent presses 1 by TDI curing agent and HDI curing agent:
(0.9-1.1) weight proportion is mixed to get.
Used as the further restriction to above-mentioned technical proposal, the diluent presses 1 by butyl ester and PMA:(0.9-1.1) weight
Amount proportioning is mixed to get.
The raw material components and component proportion of curing agent and diluent are further limited, is more conducive to form the spray of paint vehicle and paint vehicle
Apply.
In sum, using technical scheme, the backboard for guitar application of acquisition, side plate are painted and positive plate
With paint, guitar surface can be made to form the paint film that brightness is high, transparency is high, richness is good, the paint film wearability is good and safety collar
Protect, and matched with positive plate paint film by backboard, side plate paint film, make the good vibration of guitar generation and sounding, and to high pitch
With good absorption, so as to form preferable tonequality and tone color.In addition, the coating process of the present invention, by limiting backboard, side
The preparation of plate paint vehicle and the coating number of plies, interval time, the preparation of positive plate paint vehicle and the coating number of plies, interval time, more conducively formed
Backboard, side plate paint film and positive plate paint film constitute best fit, be beneficial to vibration and the sounding of guitar, formed more preferable tonequality and
Tone color, and make the paint film property that guitar surface is formed more excellent.
Specific embodiment
Below in conjunction with embodiment, technical scheme is clearly and completely described, it is clear that described
Embodiment is only a part of embodiment of the invention, rather than the embodiment of whole.Based on the embodiment in the present invention, this area
The every other embodiment that those of ordinary skill is obtained under the premise of creative work is not made, belongs to protection of the present invention
Scope.
Embodiment one
The present embodiment is related to the backboard for guitar application, side plate paint and positive plate paint, and the coating process of guitar.
Embodiment 1.1
A kind of backboard, side plate paint for guitar application, including：40 parts of synthctic fat acid resin, acrylic resin 40
Part, 10 parts of butyl acetate, PMA10 parts, 2,030 0.2 parts of defoamer, 3,130 0.3 parts of levelling agent；With backboard, side plate paint phase
The positive plate matched somebody with somebody is included with enamel-cover：30 parts of cotton liquid (i.e. nitrocotton liquid), 20 parts of castor oil, 30 parts of butyl acetate, PMA20 parts；By as follows
Step carries out application：
A, guitar backboard, the application of side plate：
A1, by above-mentioned backboard, side plate paint with curing agent, diluent by weight ratio 1:0.8:1 mixing, stirs,
Obtain backboard, side plate paint vehicle；The curing agent is TDI curing agent and HDI curing agent by weight ratio 1:1 solidification being mixed to get
Agent；The diluent is solvent butyl ester and PMA by weight ratio 1:1 diluent being mixed to get；
A2, by backboard, side plate paint vehicle even application on the backboard and side plate of guitar, coating one layer after stand 2 hours, so
Afterwards with 1000 mesh sand paperings, spray again afterwards, ten layers of spraying are carried out altogether, complete the application to guitar backboard, side plate；
The application of the positive plate of b, guitar：
B1, by above-mentioned positive plate paint and diluent by weight ratio 1:1 mixing, stirs, and obtains positive plate paint vehicle；It is described
Diluent is solvent butyl ester and PMA by weight ratio 1:1 diluent being mixed to get；
B2, by positive plate paint vehicle even application on the positive plate of guitar, coating one layer after stand 2 hours, then use 1000 mesh
Sand papering, sprays again afterwards, and three layers of spraying are carried out altogether, completes the application to the positive plate of guitar.
After completing the application to guitar backboard, side plate and positive plate, brightness height, transparency are formed on guitar surface high, plentiful
The paint film spent, the paint film wearability is good and safety and environmental protection, and guitar can produce good vibration and sounding.
Embodiment 1.2
A kind of backboard, side plate paint for guitar application, including：45 parts of synthctic fat acid resin, acrylic resin 35
Part, 12 parts of butyl acetate, PMA12 parts, 2,030 0.3 parts of defoamer, 3,130 0.4 parts of levelling agent；With backboard, side plate paint phase
The positive plate matched somebody with somebody is included with enamel-cover：35 parts of cotton liquid (i.e. nitrocotton liquid), 25 parts of castor oil, 28 parts of butyl acetate, PMA23 parts；By as follows
Step carries out application：
A, guitar backboard, the application of side plate：
A1, by above-mentioned backboard, side plate paint with curing agent, diluent by weight ratio 1:0.6:1 mixing, stirs,
Obtain backboard, side plate paint vehicle；The curing agent is TDI curing agent and HDI curing agent by weight ratio 1:1.1 be mixed to get consolidate
Agent；The diluent is solvent butyl ester and PMA by weight ratio 1:1.1 diluents being mixed to get；
A2, by backboard, side plate paint vehicle even application on the backboard and side plate of guitar, coating one layer after stand 2 hours, so
Afterwards with 800 mesh sand paperings, spray again afterwards, ten layers of spraying are carried out altogether, complete the application to guitar backboard, side plate；
The application of the positive plate of b, guitar：
B1, by above-mentioned positive plate paint and diluent by weight ratio 1:1 mixing, stirs, and obtains positive plate paint vehicle；It is described
Diluent is solvent butyl ester and PMA by weight ratio 1:1.1 diluents being mixed to get；
B2, by positive plate paint vehicle even application on the positive plate of guitar, coating one layer after stand 2 hours, then with 800 mesh sand
Paper is polished, and is sprayed again afterwards, and three layers of spraying are carried out altogether, completes the application to the positive plate of guitar.
After completing the application to guitar backboard, side plate and positive plate, brightness height, transparency are formed on guitar surface high, plentiful
The paint film spent, the paint film wearability is good and safety and environmental protection, and guitar can produce good vibration and sounding.
Embodiment two
The present embodiment is related to impact of the paint film to guitar sound.
The guitar of non-application, its phonation volume is 90%, and the sounding duration of a sound is 95%；Jing backboards of the present invention, side plate paint and
Guitar of the positive plate after paint application, phonation volume is 78%, and the sounding duration of a sound is 83%；Using the guitar of conventional guitar paint application,
Generation volume is 60%, and the sounding duration of a sound is 65%.
Jing specialty tuners carry out audition to the guitar of Jing applications of the present invention, guitar obtained in the present invention range, accuracy in pitch,
Tone color aspect reaches good quality.
From the above results, the paint film on guitar surface has notable shadow for the sound size and sound quality of guitar
Ring, the guitar obtained using technical scheme has more preferable tonequality and tone color, it is ensured that the sound quality of guitar.
Claims (7)
1. a kind of backboard for guitar application, side plate paint and positive plate paint, it is characterised in that the backboard, side plate are painted
Including following raw material component：Synthctic fat acid resin 35-50 parts, acrylic resin 35-50 parts, butyl acetate 8-15
Part, PMA10-15 parts, defoamer 0.1-0.3 parts, levelling agent 0.2-0.5 parts；The positive plate enamel-cover includes following raw material
Component：Cotton liquid 25-40 parts, castor oil 20-30 parts, butyl acetate 25-35 parts, PMA15-25 parts.
2. backboard for guitar application according to claim 1, side plate paint and positive plate are painted, it is characterised in that：Institute
State backboard, side plate enamel-cover and include following raw material component：40 parts of synthctic fat acid resin, 40 parts of acrylic resin, acetic acid
10 parts of butyl ester, PMA10 parts, 0.2 part of defoamer, 0.3 part of levelling agent；The positive plate enamel-cover includes following raw material component：
30 parts of cotton liquid, 20 parts of castor oil, 30 parts of butyl acetate, PMA20 parts.
3. backboard for guitar application according to claim 1 and 2, side plate paint and positive plate are painted, it is characterised in that：
The defoamer adopts defoamer 2030.
4. backboard for guitar application according to claim 1 and 2, side plate paint and positive plate are painted, it is characterised in that：
The levelling agent adopts levelling agent 3130.
5. a kind of coating process of guitar, it is characterised in that comprise the following steps：
A, guitar backboard, the application of side plate：
A1, by backboard as claimed in claim 1, side plate paint with curing agent, diluent press 1:(0.6-0.8):(1-1.2)
Weight proportion mixes, and stirs, and obtains backboard, side plate paint vehicle；
A2, by backboard, side plate paint vehicle even application on the backboard and side plate of guitar, coating one layer after stand 2-2.5 hours, so
800-1000 mesh sand paperings are used afterwards, is sprayed again afterwards, ten layers of spraying are carried out altogether, complete the application to guitar backboard, side plate；
The application of the positive plate of b, guitar：
B1,1 will be pressed with diluent by positive plate paint as claimed in claim 1:(1-1.2) weight proportion mixing, stirs,
Obtain positive plate paint vehicle；
B2, by positive plate paint vehicle even application on the positive plate of guitar, coating one layer after stand 2-2.5 hours, then use 800-
1000 mesh sand paperings, spray again afterwards, and three layers of spraying are carried out altogether, complete the application to the positive plate of guitar.
6. the coating process of guitar according to claim 5, it is characterised in that：The curing agent is by TDI curing agent and HDI
Curing agent presses 1:(0.9-1.1) weight proportion is mixed to get.
7. the coating process of guitar according to claim 5, it is characterised in that：The diluent presses 1 by butyl ester and PMA:
(0.9-1.1) weight proportion is mixed to get.