CN109263217A - A kind of film breathed freely for fresh-keeping of vegetables - Google Patents
A kind of film breathed freely for fresh-keeping of vegetables Download PDFInfo
- Publication number
- CN109263217A CN109263217A CN201811060884.4A CN201811060884A CN109263217A CN 109263217 A CN109263217 A CN 109263217A CN 201811060884 A CN201811060884 A CN 201811060884A CN 109263217 A CN109263217 A CN 109263217A
- Authority
- CN
- China
- Prior art keywords
- parts
- film
- inner membrance
- outer membrane
- fresh
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of films breathed freely for fresh-keeping of vegetables, including the inner membrance being integrated, basement membrane and the outer membrane of being combined with each other by combination process;It is consisted of the following compositions according to the mass percent of material: the mass percent of the material of outer membrane and inner membrance composition and its material are as follows: 15-35 parts of polyethylene, 4-7 parts of Arabic gum, 1-2 parts of polylactic acid, 1-2 parts of glycerol, 1-2 parts of chitosan, 1-3 parts of glacial acetic acid, 1-4 parts of antioxidant, 1-3 parts of preservative, 1-2 parts of antibacterial agent.The present invention has rational design, includes metallocene and auxiliary agent in basement membrane, improves the oxygen permeating amount of film entirety, can achieve 1500 film oxygen permeating amount, to meet the fresh-keeping needs such as vegetables, meet the needs of market.
Description
Technical field
The invention belongs to preservative film fields, more specifically to a kind of film breathed freely for fresh-keeping of vegetables.
Background technique
Vegetables are one of food sources important in people's diet, it is possible to provide the multivitamin and mine of needed by human body
The nutriments such as substance, the 60% of 90%, the VA of the VC of needed by human body derive from vegetables, therefore effective ingredient and water in vegetables
Point holding be a critically important project, its aerobic respiration should be allowed, and cannot allow its complete anoxic.
Therefore, the prior art is to be improved.
Summary of the invention
In view of the deficiencies of the prior art, the present invention intends to provide it is a kind of for fresh-keeping of vegetables breathe freely
Film, design rationally, include metallocene and auxiliary agent in basement membrane, improve the oxygen permeating amount of film entirety, can achieve 1500 film oxygen flow
Amount, to meet the fresh-keeping needs such as vegetables, meets the needs of market.
To achieve the above object, the present invention provides the following technical scheme that
A kind of film breathed freely for fresh-keeping of vegetables, it is characterised in that: be integrated including being combined with each other by combination process
Inner membrance, basement membrane and outer membrane;Consisted of the following compositions according to the mass percent of material: the material of outer membrane and inner membrance composition and its
The mass percent of material are as follows: 15-35 parts of polyethylene, 4-7 parts of Arabic gum, 1-2 parts of polylactic acid, 1-2 parts of glycerol,
1-2 parts of chitosan, 1-3 parts of glacial acetic acid, 1-4 parts of antioxidant, 1-3 parts of preservative, 1-2 parts of antibacterial agent;Basement membrane
It is the basement membrane made of metallocene LLDPE and auxiliary agent;The thickness ratio of the inner membrance, basement membrane and outer membrane is (1-2): (2-3): (1-
2)。
As a kind of technical solution of optimization, the material composition of the outer membrane and inner membrance and its mass percent of material
Are as follows: 26 parts of polyethylene, 6 parts of Arabic gum, 1.4 parts of polylactic acid, 1.5 parts of glycerol, 1.8 parts of chitosan, 1.6 parts
Glacial acetic acid, 1.7 parts of antioxidant, 2 parts of preservative, 1.4 parts of antibacterial agent.
As a kind of technical solution of optimization, the material composition of the outer membrane and inner membrance and its mass percent of material
Are as follows: 30 parts of polyethylene, 6 parts of Arabic gum, 2 parts of polylactic acid, 1 part of glycerol, 1.8 parts of chitosan, 2 parts of ice vinegar
Acid, 3 parts of antioxidant, 3 parts of preservative, 2 parts of antibacterial agent.
As a kind of technical solution of optimization, the material composition of the outer membrane and inner membrance and its mass percent of material
Are as follows: 22 parts of polyethylene, 4 parts of Arabic gum, 1 part of polylactic acid, 1 part of glycerol, 1 part of chitosan, 3 parts of glacial acetic acid, 2
Antioxidant, 2 parts of the preservative, 1 part of antibacterial agent of part.
The present invention also provides a kind of films breathed freely for fresh-keeping of vegetables, it is characterised in that: preparation process is:
Include the following steps:
1), according to above-mentioned formula by polyethylene, Arabic gum, polylactic acid, glycerol, chitosan, glacial acetic acid and deionization
Water mixing, which is put into blender, stirs, and is fitted into mold and stands 10-15 hours, mixed material is made;
2), antioxidant, preservative, antibacterial agent are mixed 30 minutes and stand 12-18 hours, intermixture is made;
3) mixed material in step 1), is subjected to blown film under vacuum conditions, and it is small that dry 3-6 is placed in drying box
When take out;
4), the intermixture in step 2) is uniformly applied on any one film surface of step 3), under air drying environment
Standing 12-18 hours can outer membrane and inner membrance;
5), extruder that metallocene LLDPE and auxiliary agent are put into 250 DEG C to fusion plastification and is metered into runner point
It is squeezed out again through T-die after orchestration, is cast into sheet by 25 DEG C of sharp cooling rolls;Sheet carries out longitudinal stretching and cross directional stretch, indulges
It is 100 DEG C to stretching with preheating temperature stretching in the transverse direction, setting temperature is 120 DEG C, and stretching ratio is 1.2 times, and basement membrane is made;
6), that outer membrane, basement membrane and inner membrance is compound in one, preservative film is made.
By adopting the above-described technical solution, compared with prior art, the present invention has rational design, it include metallocene in basement membrane
And auxiliary agent, the oxygen permeating amount of film entirety is improved, can achieve 1500 film oxygen permeating amount, it is full to meet the fresh-keeping needs such as vegetables
The demand in sufficient market.
Specific embodiment
A kind of film breathed freely for fresh-keeping of vegetables, including the inner membrance being integrated, basement membrane of being combined with each other by combination process
And outer membrane, it is consisted of the following compositions according to the mass percent of material: the quality of the material of outer membrane and inner membrance composition and its material
Percentage are as follows: 15-35 parts of polyethylene, 4-7 parts of Arabic gum, 1-2 parts of polylactic acid, 1-2 parts of glycerol, 1-2 parts of shell
Glycan, 1-3 parts of glacial acetic acid, 1-4 parts of antioxidant, 1-3 parts of preservative, 1-2 parts of antibacterial agent.Basement membrane is by metallocene
Basement membrane made of LLDPE and auxiliary agent.The thickness ratio of the inner membrance, basement membrane and outer membrane is (1-2): (2-3): (1-2).
The present invention also provides a kind of film breathed freely for fresh-keeping of vegetables, preparation process includes the following steps:
1), according to above-mentioned formula by polyethylene, Arabic gum, polylactic acid, glycerol, chitosan, glacial acetic acid and deionization
Water mixing, which is put into blender, stirs, and is fitted into mold and stands 10-15 hours, mixed material is made;
2), antioxidant, preservative, antibacterial agent are mixed 30 minutes and stand 12-18 hours, intermixture is made;
3) mixed material in step 1), is subjected to blown film under vacuum conditions, and it is small that dry 3-6 is placed in drying box
When take out;
4), the intermixture in step 2) is uniformly applied on any one film surface of step 3), under air drying environment
Standing 12-18 hours can outer membrane and inner membrance;
5), extruder that metallocene LLDPE and auxiliary agent are put into 250 DEG C to fusion plastification and is metered into runner point
It is squeezed out again through T-die after orchestration, is cast into sheet by 25 DEG C of sharp cooling rolls;Sheet carries out longitudinal stretching and cross directional stretch, indulges
It is 100 DEG C to stretching with preheating temperature stretching in the transverse direction, setting temperature is 120 DEG C, and stretching ratio is 1.2 times, and basement membrane is made;
6), that outer membrane, basement membrane and inner membrance is compound in one, preservative film is made.
The present invention has rational design, includes metallocene and auxiliary agent in basement membrane, improves the oxygen permeating amount of film entirety, can achieve
1500 film oxygen permeating amount meets the needs of market to meet the fresh-keeping needs such as vegetables.
Embodiment 1
The mass percent of the material of outer membrane and inner membrance composition and its material are as follows: 26 parts of polyethylene, 6 parts of Arab
Glue, 1.4 parts of polylactic acid, 1.5 parts of glycerol, 1.8 parts of chitosan, 1.6 parts of glacial acetic acid, 1.7 parts of antioxidant, 2 parts
Preservative, 1.4 parts of antibacterial agent.
Embodiment 2
The mass percent of the material of outer membrane and inner membrance composition and its material are as follows: 30 parts of polyethylene, 6 parts of Arab
Glue, 2 parts of polylactic acid, 1 part of glycerol, 1.8 parts of chitosan, 2 parts of glacial acetic acid, 3 parts of antioxidant, 3 parts of preservative,
2 parts of antibacterial agent.
Embodiment 3
The mass percent of the material of outer membrane and inner membrance composition and its material are as follows: 22 parts of polyethylene, 4 parts of Arab
Glue, 1 part of polylactic acid, 1 part of glycerol, 1 part of chitosan, 3 parts of glacial acetic acid, 2 parts of antioxidant, 2 parts of preservative, 1
The antibacterial agent of part.
Protection scope of the present invention is not limited merely to above-described embodiment, and all technical solutions belonged under thinking of the present invention are equal
It belongs to the scope of protection of the present invention.It should be pointed out that for those skilled in the art, not departing from the present invention
Several improvements and modifications under the premise of principle, these modifications and embellishments should also be considered as the scope of protection of the present invention.
Claims (5)
1. a kind of film breathed freely for fresh-keeping of vegetables, it is characterised in that: be integrated including being combined with each other by combination process
Inner membrance, basement membrane and outer membrane;
It is consisted of the following compositions according to the mass percent of material:
The mass percent of the material of outer membrane and inner membrance composition and its material are as follows: 15-35 parts of polyethylene, 4-7 parts of Arab
Glue, 1-2 parts of polylactic acid, 1-2 parts of glycerol, 1-2 parts of chitosan, 1-3 parts of glacial acetic acid, 1-4 parts of antioxidant, 1-3
The preservative, 1-2 parts of antibacterial agent of part;
Basement membrane is the basement membrane made of metallocene LLDPE and auxiliary agent;
The thickness ratio of the inner membrance, basement membrane and outer membrane is (1-2): (2-3): (1-2).
2. a kind of film breathed freely for fresh-keeping of vegetables according to claim 1, it is characterised in that: the outer membrane and inner membrance
The mass percent of material composition and its material are as follows: 26 parts of polyethylene, 6 parts of Arabic gum, 1.4 parts of polylactic acid, 1.5 parts
Glycerol, 1.8 parts of chitosan, 1.6 parts of glacial acetic acid, 1.7 parts of antioxidant, 2 parts of preservative, 1.4 parts of antibacterial agent.
3. a kind of film breathed freely for fresh-keeping of vegetables according to claim 1, it is characterised in that: the outer membrane and inner membrance
The mass percent of material composition and its material are as follows: 30 parts of polyethylene, 6 parts of Arabic gum, 2 parts of polylactic acid, 1 part sweet
Oil, 1.8 parts of chitosan, 2 parts of glacial acetic acid, 3 parts of antioxidant, 3 parts of preservative, 2 parts of antibacterial agent.
4. a kind of film breathed freely for fresh-keeping of vegetables according to claim 1, it is characterised in that: the outer membrane and inner membrance
The mass percent of material composition and its material are as follows: 22 parts of polyethylene, 4 parts of Arabic gum, 1 part of polylactic acid, 1 part sweet
Oil, 1 part of chitosan, 3 parts of glacial acetic acid, 2 parts of antioxidant, 2 parts of preservative, 1 part of antibacterial agent.
5. a kind of film breathed freely for fresh-keeping of vegetables according to claim 1, it is characterised in that: the preparation process of film is:
Include the following steps:
1), polyethylene, Arabic gum, polylactic acid, glycerol, chitosan, glacial acetic acid and deionized water are mixed according to above-mentioned formula
Conjunction is put into blender and stirs, and is fitted into mold and stands 10-15 hours, and mixed material is made;
2), antioxidant, preservative, antibacterial agent are mixed 30 minutes and stand 12-18 hours, intermixture is made;
3), the mixed material in step 1) is subjected to blown film under vacuum conditions, and is placed in drying box dry 3-6 hours and takes
Out;
4), the intermixture in step 2) is uniformly applied on any one film surface of step 3), is stood under air drying environment
It 12-18 hours can outer membrane and inner membrance;
5), extruder that metallocene LLDPE and auxiliary agent are put into 250 DEG C, to fusion plastification and is metered into flow passage distributor
It is squeezed out again through T-die afterwards, is cast into sheet by 25 DEG C of sharp cooling rolls;Sheet carries out longitudinal stretching and cross directional stretch, Zong Xiangla
Stretching with preheating temperature stretching in the transverse direction is 100 DEG C, and setting temperature is 120 DEG C, and stretching ratio is 1.2 times, and basement membrane is made;
6), that outer membrane, basement membrane and inner membrance is compound in one, preservative film is made.