CN109262943B - High-toughness plastic and ruler made of same - Google Patents
High-toughness plastic and ruler made of same Download PDFInfo
- Publication number
- CN109262943B CN109262943B CN201811049326.8A CN201811049326A CN109262943B CN 109262943 B CN109262943 B CN 109262943B CN 201811049326 A CN201811049326 A CN 201811049326A CN 109262943 B CN109262943 B CN 109262943B
- Authority
- CN
- China
- Prior art keywords
- bamboo
- ruler
- splits
- powder
- toughness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses high-toughness plastic and a ruler made of the high-toughness plastic, and belongs to the field of preparation of school supplies. The invention firstly makes bamboo splints into bamboo splits, then soaks the bamboo splits with biogas slurry, uses enzyme generated by microorganism in the biogas slurry to activate bamboo fibers, then carries out sun exposure and aging to further reduce the bonding force between the fibers, then uses NaOH solution to mix with the bamboo splits at high temperature to promote the microfiber silk layer to slide and swell, then uses liquid nitrogen to process to form ice crystals in fiber cells, then carries out stone grinding to break the ice crystals in cell walls under the action of pressure to separate the fibers into micro-nano fiber whiskers, mixes the micro-nano fiber whiskers with special-shaped polyethylene powder obtained by polymerization under the condition of an electric field according to a proportion, carries out injection molding, and prints scales after grinding to obtain the high-toughness plastic ruler. The ruler disclosed by the invention has the advantages of high toughness of bamboo fibers, high impact strength, difficulty in breaking, greatly prolonged service life compared with the traditional plastic ruler, and capability of being popularized and used on a large scale.
Description
Technical Field
The invention discloses high-toughness plastic and a ruler made of the high-toughness plastic, and belongs to the field of preparation of school supplies.
Background
The ruler is used for measuring length and is widely applied to mathematics, measurement, engineering and other subjects. The ruler is a ruler-shaped gauge with accurate straight edges, is also called a space ruler and is a very common length measuring instrument, and the stationery is common. At present, use more ruler and divide according to the material and mainly have: 1. the alloy ruler is long in service life, but is difficult to recover after being bent and deformed, and the production cost is relatively high compared with other materials, the accuracy is reduced after abrasion, and the ruler cannot be repaired; 2. the wooden ruler is light in weight, convenient to carry, limited in service life, easy to crack after meeting water, poor in flexibility and easy to break; 3. the plastic ruler has the advantages that the elastic modulus of plastic is between that of rubber and that of fiber, the plastic ruler can deform to a certain degree under stress, the common plastic ruler is composed of hard plastic and soft plastic, the elastic modulus of the soft plastic is close to that of the rubber, the hard plastic is close to that of the fiber, the hardness of the soft plastic is low, the plastic ruler is easy to deform under stress, the application range is limited, the hard plastic has certain hardness, the preparation process is simple, the materials are cheap and easy to obtain, the plasticity is strong, the plastic ruler is widely used as the ruler material in study articles at present, but the plastic is easy to age and yellow, if the use frequency is too high, the scales and the like of the plastic ruler are easy to wear, the toughness is poor, the plastic ruler is easy to break, corners are easy.
Disclosure of Invention
Aiming at the problems of poor toughness, brittleness, low impact strength, easy occurrence of stress fracture and short service life of the traditional plastic ruler in the preparation and use processes, the invention provides a preparation method of a high-toughness plastic ruler, which comprises the steps of firstly forming bamboo splits from bamboo chips, then soaking the bamboo splits with methane liquid, activating bamboo fibers by using enzyme generated by microorganisms in the methane liquid, then exposing and aging by sunlight to further reduce the bonding force among the fibers, then mixing the bamboo splits with NaOH solution at high temperature to promote the sliding and swelling of a microfiber fiber layer, then treating with liquid nitrogen to form ice crystals in fiber cells, and finally grinding by a stone mill to crack the ice crystals in cell walls under the action of pressure to separate the fibers into micro-nano fiber whiskers, and mixing the special-shaped polyethylene powder obtained by polymerization under the condition of an electric field in proportion, performing injection molding, polishing, and then printing scales to obtain the high-toughness plastic ruler. The ruler disclosed by the invention has the advantages of high toughness of bamboo fibers, high impact strength, difficulty in breaking, greatly prolonged service life compared with the traditional plastic ruler, and capability of being popularized and used on a large scale.
In order to solve the technical problems, the technical scheme adopted by the invention is as follows:
(1) taking 4-6 bamboos with the diameter of 3-5 cm and the length of 1.2-1.5 m, manually slicing the bamboos into thin bamboo strips, collecting the thin bamboo strips, soaking the thin bamboo strips in biogas slurry for 24-36 h, taking out the thin bamboo strips, washing the thin bamboo strips for 3-5 times by using deionized water, uniformly spreading the thin bamboo strips under the sunlight, and exposing the thin bamboo strips for 7-10 days;
(2) after the insolation is finished, cutting the bamboo skin into 3-5 cm short bamboo skin by a chopper, pouring the short bamboo skin into a beaker filled with 1-2L of 6-8% sodium hydroxide solution, then turning the beaker into a digital display speed measurement constant temperature magnetic stirrer, stirring and reacting for 30-45 min at a constant temperature under the conditions that the temperature is 160-180 ℃ and the rotating speed is 600-800 r/min, filtering, removing filtrate, and washing filter residues with deionized water until the washing water is neutral;
(3) cooling the obtained filter residue by using liquid nitrogen for 40-60 s, then quickly paving the filter residue on the surface of a millstone of a stone mill, grinding for 10-15 min, and sieving by using a sieve of 400-600 meshes after grinding to obtain micro-nano bamboo powder for later use;
(4) adding 4-6 g of sodium dodecyl benzene sulfonate into a quartz reaction kettle containing 300-400 mL of deionized water, starting a reaction kettle stirrer, stirring and mixing at the rotating speed of 300-500 r/min for 10-20 min, starting a reaction kettle heater, heating to 70-80 ℃, inserting a copper electrode into emulsion of the reaction kettle, communicating the copper electrode with a pressure resistance tester, setting the direct-current voltage to be 220-380V, sequentially adding 0.4-0.6 g of potassium persulfate and 80-100 mL of styrene under the constant-temperature constant-voltage stirring state, reacting for 4-6 h, transferring the obtained material into an oven, drying for 6-8 h at the temperature of 80-90 ℃, and grinding into powder by using a mortar to obtain special-shaped polystyrene powder;
(5) weighing 35-40 parts by weight of the micro-nano bamboo powder for standby in the step (3) and 60-80 parts by weight of the obtained special-shaped polystyrene powder in sequence, adding the obtained special-shaped polystyrene powder into a mixer, stirring and mixing the obtained special-shaped polystyrene powder for 30-45 min at the rotating speed of 600-800 r/min, adding the obtained mixed material into a screw injection molding machine, heating to melt the mixed material, injecting the melted material into a cavity of a ruler mold through a screw, shaping and cooling, manually polishing to remove burrs, and then printing scales on a polished ruler blank through a screen printing to obtain the high-toughness plastic ruler.
Physical properties of the present invention: the density of the high-toughness plastic ruler is 1.05-1.08 g/cm3, the tensile strength is 49.6-50.6 MPa, the bending strength is 96.2-97.6 MPa, the elongation at break is 1.6-2.0%, the Vicat softening point is 230-240 DEG F, and the service life of the ruler can be prolonged by 12-24 months compared with that of a traditional plastic ruler.
The invention has the beneficial effects that:
(1) the high-toughness plastic ruler disclosed by the invention is high in toughness, not easy to break, and greatly prolonged in service life compared with the traditional plastic ruler, and the problem of white pollution to the environment after being discarded can be reduced;
(2) the modified bamboo fiber is adopted as the toughening fiber, the raw materials are cheap and easy to obtain, the plasticity is strong, the preparation process is simple, and the obtained plastic ruler can be widely used as a school supply.
Detailed Description
Taking 4-6 bamboos with the diameter of 3-5 cm and the length of 1.2-1.5 m, manually slicing the bamboos into thin bamboo strips, collecting the thin bamboo strips, soaking the thin bamboo strips in biogas slurry for 24-36 h, taking out the thin bamboo strips, washing the thin bamboo strips for 3-5 times by using deionized water, uniformly spreading the thin bamboo strips under the sunlight, and exposing the thin bamboo strips for 7-10 days; after the insolation is finished, cutting the bamboo skin into 3-5 cm short bamboo skin by a chopper, pouring the short bamboo skin into a beaker filled with 1-2L of 6-8% sodium hydroxide solution, then turning the beaker into a digital display speed measurement constant temperature magnetic stirrer, stirring and reacting for 30-45 min at a constant temperature under the conditions that the temperature is 160-180 ℃ and the rotating speed is 600-800 r/min, filtering, removing filtrate, and washing filter residues with deionized water until the washing water is neutral; cooling the obtained filter residue by using liquid nitrogen for 40-60 s, then quickly paving the filter residue on the surface of a millstone of a stone mill, grinding for 10-15 min, and sieving by using a sieve of 400-600 meshes after grinding to obtain micro-nano bamboo powder for later use; adding 4-6 g of sodium dodecyl benzene sulfonate into a quartz reaction kettle containing 300-400 mL of deionized water, starting a reaction kettle stirrer, stirring and mixing at the rotating speed of 300-500 r/min for 10-20 min, starting a reaction kettle heater, heating to 70-80 ℃, inserting a copper electrode into emulsion of the reaction kettle, communicating the copper electrode with a pressure resistance tester, setting the direct-current voltage to be 220-380V, sequentially adding 0.4-0.6 g of potassium persulfate and 80-100 mL of styrene under the constant-temperature constant-voltage stirring state, reacting for 4-6 h, transferring the obtained material into an oven, drying for 6-8 h at the temperature of 80-90 ℃, and grinding into powder by using a mortar to obtain special-shaped polystyrene powder; weighing 35-40 parts of standby micro-nano bamboo powder and 60-80 parts of the obtained special-shaped polystyrene powder in sequence by weight, adding the obtained special-shaped polystyrene powder into a mixer, stirring and mixing the obtained mixture for 30-45 min at the rotating speed of 600-800 r/min, adding the obtained mixture into a screw injection molding machine, heating to melt the mixture, injecting the melted material into a cavity of a ruler mold through a screw, shaping and cooling, manually polishing to remove burrs, and then printing scales on a polished ruler blank through a screen printing manner to obtain the high-toughness plastic ruler.
Example 1
Taking 4 bamboos with the diameter of 3cm and the length of 1.2m, manually slicing the bamboos into bamboo splits, collecting the bamboo splits, soaking the bamboo splits in biogas liquid for 24 hours, taking out the bamboo splits, washing the bamboo splits with deionized water for 3 times, and then uniformly spreading the bamboo splits in the sun and exposing the bamboo splits to the sun for 7 days; after the insolation is finished, cutting the bamboo skin into 3cm short bamboo skin by a chopper, pouring the short bamboo skin into a beaker filled with 1L of sodium hydroxide solution with the mass concentration of 6%, then turning the beaker into a digital display speed measurement constant temperature magnetic stirrer, stirring and reacting for 30min at the constant temperature of 160 ℃ and the rotating speed of 600r/min, filtering, removing filtrate, and washing filter residue with deionized water until washing water is neutral; cooling the obtained filter residue with liquid nitrogen for 40s, rapidly spreading on the surface of a millstone of a stone mill, grinding for 10min, and sieving with a 400-mesh sieve to obtain micro-nano bamboo powder for later use; adding 4g of sodium dodecyl benzene sulfonate into a quartz reaction kettle containing 300mL of deionized water, starting a reaction kettle stirrer, stirring and mixing at the rotating speed of 300r/min for 10min, starting a reaction kettle heater, heating to 70 ℃, then inserting a copper electrode into emulsion of the reaction kettle, communicating the copper electrode with a pressure resistance tester, setting the direct-current voltage to be 220V, sequentially adding 0.4g of potassium persulfate and 80mL of styrene under the constant-temperature constant-voltage stirring state, reacting for 4h, transferring the obtained material into an oven, drying for 6h under the condition of 80 ℃, and grinding into powder by using a mortar to obtain special-shaped polystyrene powder; weighing 35 parts of standby micro-nano bamboo powder and 60 parts of the obtained special-shaped polystyrene powder in sequence according to parts by weight, adding the obtained special-shaped polystyrene powder into a mixer, stirring and mixing the obtained mixture for 30min at a rotating speed of 600r/min, adding the obtained mixture into a screw injection molding machine, heating to melt the mixture, injecting the melted material into a ruler mold cavity through a screw, carrying out shaping and cooling, manually polishing to remove burrs, and then carrying out silk-screen printing on a polished ruler blank to obtain the high-toughness plastic ruler.
The density of the high-toughness plastic ruler is 1.05g/cm3, the tensile strength is 49.6MPa, the bending strength is 96.2MPa, the elongation at break is 1.6%, the Vicat softening point is 230 DEG F, and the service life of the ruler is prolonged by 12 months compared with that of the traditional plastic ruler.
Example 2
Taking 5 bamboos with the diameter of 4cm and the length of 1.4m, manually slicing the bamboos into bamboo splits, collecting the bamboo splits, soaking the bamboo splits in biogas liquid for 30h, taking out the bamboo splits, washing the bamboo splits with deionized water for 4 times, and then uniformly spreading the bamboo splits in the sun and exposing the bamboo splits to the sun for 8 days; after the insolation is finished, cutting the bamboo skin into 4cm short bamboo skin by a guillotine, pouring the short bamboo skin into a beaker filled with 1.5L of 7% sodium hydroxide solution, then turning the beaker into a digital display speed measurement constant temperature magnetic stirrer, stirring and reacting for 38min at the constant temperature of 170 ℃ and the rotating speed of 700r/min, filtering, removing filtrate, and washing filter residue with deionized water until the washing water is neutral; cooling the obtained filter residue with liquid nitrogen for 50s, rapidly spreading on the surface of a millstone of a stone mill, grinding for 12min, and sieving with a 500-mesh sieve to obtain micro-nano bamboo powder for later use; adding 5g of sodium dodecyl benzene sulfonate into a quartz reaction kettle containing 350mL of deionized water, starting a reaction kettle stirrer, stirring and mixing at the rotating speed of 400r/min for 15min, starting a reaction kettle heater, heating to 75 ℃, then inserting a copper electrode into emulsion of the reaction kettle, communicating the copper electrode with a pressure resistance tester, setting the direct-current voltage to 300V, sequentially adding 0.5g of potassium persulfate and 90mL of styrene under the constant-temperature constant-voltage stirring state, reacting for 5h, transferring the obtained material into an oven, drying for 7h at the temperature of 85 ℃, and grinding into powder by using a mortar to obtain special-shaped polystyrene powder; weighing 38 parts of standby micro-nano bamboo powder and 70 parts of the obtained special-shaped polystyrene powder in sequence according to parts by weight, adding the obtained special-shaped polystyrene powder into a mixer, stirring and mixing the mixture for 40min at the rotating speed of 700r/min, adding the obtained mixture into a screw injection molding machine, heating to melt the mixture, injecting the melted material into a ruler mold cavity through a screw, carrying out shaping and cooling, manually polishing to remove burrs, and then carrying out silk-screen printing on the polished ruler blank to obtain the high-toughness plastic ruler.
The density of the high-toughness plastic ruler is 1.06g/cm3, the tensile strength is 50MPa, the bending strength is 97MPa, the elongation at break is 1.8%, the Vicat softening point is 235 DEG F, and the service life of the ruler can be prolonged by 18 months compared with that of the traditional plastic ruler.
Example 3
Taking 6 bamboos with the diameter of 5cm and the length of 1.5m, manually slicing the bamboos into bamboo splits, collecting the bamboo splits, soaking the bamboo splits in biogas liquid for 36h, taking out the bamboo splits, washing the bamboo splits with deionized water for 5 times, and then uniformly spreading the bamboo splits in the sun and exposing the bamboo splits to the sun for 10 days; after the insolation is finished, cutting the bamboo skin into 5cm short bamboo skin by a chopper, pouring the short bamboo skin into a beaker filled with 2L of sodium hydroxide solution with the mass concentration of 8%, then turning the beaker into a digital display speed measurement constant temperature magnetic stirrer, stirring and reacting for 45min at the constant temperature of 180 ℃ and the rotating speed of 800r/min, filtering, removing filtrate, and washing filter residue with deionized water until washing water is neutral; cooling the obtained filter residue with liquid nitrogen for 60s, rapidly spreading on the surface of a millstone of a stone mill, grinding for 15min, and sieving with a 600-mesh sieve to obtain micro-nano bamboo powder for later use; adding 6g of sodium dodecyl benzene sulfonate into a quartz reaction kettle containing 400mL of deionized water, starting a reaction kettle stirrer, stirring and mixing at the rotating speed of 500r/min for 20min, starting a reaction kettle heater, heating to 80 ℃, then inserting a copper electrode into emulsion of the reaction kettle, communicating the copper electrode with a pressure resistance tester, setting the direct-current voltage to 380V, sequentially adding 0.6g of potassium persulfate and 100mL of styrene under the constant-temperature constant-voltage stirring state, reacting for 6h, transferring the obtained material into an oven, drying for 8h at the temperature of 90 ℃, and grinding into powder by using a mortar to obtain special-shaped polystyrene powder; weighing 40 parts of standby micro-nano bamboo powder and 80 parts of the obtained special-shaped polystyrene powder in sequence according to parts by weight, adding the obtained special-shaped polystyrene powder into a mixer, stirring and mixing for 45min at the rotating speed of 800r/min, adding the obtained mixed material into a screw injection molding machine, heating to melt the mixed material, injecting the melted material into a ruler mold cavity through a screw, carrying out shaping and cooling, manually polishing to remove burrs, and then carrying out silk-screen printing on the polished ruler blank to obtain the high-toughness plastic ruler.
The density of the high-toughness plastic ruler is 1.08g/cm3, the tensile strength is 50.6MPa, the bending strength is 97.6MPa, the elongation at break is 2.0%, the Vicat softening point is 240 DEG F, and the service life of the ruler is prolonged by 24 months compared with that of the traditional plastic ruler.
Claims (1)
1. A preparation method of a high-toughness plastic ruler is characterized by comprising the following specific preparation steps:
(1) taking 6 bamboos with the diameter of 5cm and the length of 1.5m, manually slicing the bamboos into bamboo splits, collecting the bamboo splits, soaking the bamboo splits in biogas liquid for 36h, taking out the bamboo splits, washing the bamboo splits with deionized water for 5 times, and then uniformly spreading the bamboo splits in the sun and exposing the bamboo splits to the sun for 10 days;
(2) after the insolation is finished, cutting the bamboo skin into 5cm short bamboo skin by a chopper, pouring the short bamboo skin into a beaker filled with 2L of sodium hydroxide solution with the mass concentration of 8%, then turning the beaker into a digital display speed measurement constant temperature magnetic stirrer, stirring and reacting for 45min at the constant temperature of 180 ℃ and the rotating speed of 800r/min, filtering, removing filtrate, and washing filter residue with deionized water until washing water is neutral;
(3) cooling the obtained filter residue with liquid nitrogen for 60s, rapidly spreading on the surface of a millstone of a stone mill, grinding for 15min, and sieving with a 600-mesh sieve to obtain micro-nano bamboo powder for later use;
(4) adding 6g of sodium dodecyl benzene sulfonate into a quartz reaction kettle containing 400mL of deionized water, starting a reaction kettle stirrer, stirring and mixing at the rotating speed of 500r/min for 20min, starting a reaction kettle heater, heating to 80 ℃, then inserting a copper electrode into emulsion of the reaction kettle, communicating the copper electrode with a pressure resistance tester, setting the direct-current voltage to 380V, sequentially adding 0.6g of potassium persulfate and 100mL of styrene under the constant-temperature constant-voltage stirring state, reacting for 6h, transferring the obtained material into an oven, drying for 8h at the temperature of 90 ℃, and grinding into powder by using a mortar to obtain special-shaped polystyrene powder;
(5) weighing 40 parts by weight of standby micro-nano bamboo powder and 80 parts by weight of the obtained special-shaped polystyrene powder in turn, adding the obtained special-shaped polystyrene powder into a mixer, stirring and mixing the obtained mixture at the rotating speed of 800r/min for 45min, adding the obtained mixed material into a screw injection molding machine, and heating to melt the mixed material;
(6) and (3) injecting the molten material prepared in the step (5) into a cavity of the ruler die through a screw, after shaping and cooling, manually polishing to remove burrs, and then printing scales on the polished ruler blank through a screen printing to obtain the high-toughness plastic ruler.