CN109252356A - A kind of fiber gauze production technology of high intensity - Google Patents
A kind of fiber gauze production technology of high intensity Download PDFInfo
- Publication number
- CN109252356A CN109252356A CN201810917262.2A CN201810917262A CN109252356A CN 109252356 A CN109252356 A CN 109252356A CN 201810917262 A CN201810917262 A CN 201810917262A CN 109252356 A CN109252356 A CN 109252356A
- Authority
- CN
- China
- Prior art keywords
- fiber
- gauze
- added
- water
- high intensity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of fiber gauze production technology of high intensity, 1) to chitin fiber modification;2) alginate fibre is prepared;3) cotton fiber is prepared;4) preparation self-control chitin fiber;5) raw material obtained above is subjected to antimicrobial treatment, gauze fabric is then made;6) fabric is immersed in desizing, scouring and bleaching combined machine slot, is first cleaned with 95-100 DEG C of water, then reduce temperature, finishing auxiliaries, cleaning is added in water cleaning;7) by above-mentioned fabric with temperature it is again that 105-110 DEG C of clear water boils, hydrophilic softening agent, cellulase, cloth outputting, dewatered drying is added.Hospital gauze preparation method of the invention, obtained gauze is antibacterial with conventional antimicrobial, cleaning function also has improvement blood circulation outside, it boosts metabolism, eliminate fatigue, the effect of inducing resuscitation brain tonic can speed up coagulation process, while form one layer of stable network gel in wound surface, the microenvironment for being conducive to tissue growth is built for wound, and then promotes wound healing.
Description
Technical field
The present invention relates to a kind of preparation methods of hospital gauze, and in particular to a kind of fiber gauze production work of high intensity
Skill.
Background technique
With going deep into researching wound healing, it was recognized that using the purpose of dressing far from order to cover wound
Face, dressing must also be able to promote wound healing.When causing defect of skin due to factors such as damage or diseases, the surface of a wound is often resulted in
Moisture, electrolyte and protein loss, the open surface of a wound also add the probability of infection, and the effective wound closure of getting up early can be reduced
The generation of above-mentioned complication.The flesh and blood that existing gauze is easy bonding wound is caused to paste and be torn, and not only cannot effectively be stopped blooding,
It is also possible to causing infected wound bacterium.
Summary of the invention
It causes to paste and tear the technical problem to be solved by the present invention is to the flesh and blood that existing gauze is easy bonding wound, no
Only cannot effectively it stop blooding, it is also possible to cause infected wound bacterium, and it is an object of the present invention to provide a kind of fiber gauze of high intensity produces
Technique, obtained gauze is antibacterial with conventional antimicrobial, cleaning function also has improvement blood circulation outside, boosts metabolism, eliminates
Fatigue, the effect of inducing resuscitation brain tonic, and gauze feel obtained is smooth, submissive pleasant, moisture absorption is ventilative, more comfort, Neng Goujia
Fast coagulation process, while one layer of stable network gel is formed in wound surface, one, which is built, for wound is conducive to tissue growth
Microenvironment, and then promote wound healing.
The present invention is achieved through the following technical solutions:
A kind of fiber gauze production technology of high intensity, the hospital gauze are gathered by alginate fibre, chitin fiber, modified shell
Sugared fiber and cotton fiber is blended forms, the weight ratio of the alginate fibre, chitin fiber, modified chitosan fiber and cotton fiber
For 30-35:40-50:15-25:75-85;The preparation method is as follows: 1) modification liquid is sprayed on the chitin fiber banked up, change
Property processing 12-24h;2) sodium alginate is added in deionized water, stirring at normal temperature, until being completely dissolved, obtains mass percent
For the sodium alginate soln of 2.4-3.6, nano-Ag particles are added in sodium alginate soln, stir evenly, blend spinning is made
Liquid prepares alginate fibre, coagulating bath post-tensioning winding using wet spinning technology, and naturally dry obtains alginate fibre;3) it will take off
Then rouge and cleaned cotton fiber first carries out extrusion pretreatment carries out carboxymethyl-modification processing, adds soluble silver salt,
Stabilizer isothermal reaction 30min at 28-55 DEG C is added, finally by processed cotton fiber in the isothermal reaction 1h at 28-55 DEG C
Successively through surfactant wash, passivation, then through clear water rinsing, dehydration, it is obtained by drying arrive cotton fiber;4) 30-40g silkworm chrysalis is weighed
Shell is put into the beaker with 60-80mL hydrochloric acid solution after mixing immersion, then addition 90-110mL sodium hydroxide is molten into beaker
Liquid is continuesd to mix and is embathed, and is obtained alkali cleaning substance, and rinse alkali cleaning substance with hydrogen peroxide, chitosan is made, by chitosan, ice vinegar
Acid solution and polyvinyl alcohol stirring obtain modified self-control chitosan solution, modified self-control chitosan solution are transported to more
Wire drawing in the bushing of hole obtains modified self-control chitin fiber;5) raw material obtained by step 1), 2), 3) He 4) carries out at antibacterial
Reason, is then made gauze fabric;6) solution is mixed in the fabric woven and modified nano-titanium dioxide and dimethicone
It immerses in the hot water storgae of desizing, scouring and bleaching combined machine, bath raio 1:25-30 first cleans 20-30min with 95-100 DEG C of water, then reduces
5-10 DEG C of temperature, water cleans 30-45min, and finishing auxiliaries are then added in water, and adjustment aqueous temperature is 65-75 DEG C, cleaning
40-50min;7) by above-mentioned fabric with temperature it is again that 105-110 DEG C of clear water boils 50-60min, adds hydrophilic softening agent, fiber
Enzyme continues to boil 30min, and cloth outputting is dehydrated, and 115-125 DEG C of drying obtains: fiber hospital gauze.
Hospital gauze preparation method of the invention, be made gauze is antibacterial with conventional antimicrobial, outside cleaning function also with changing
Kind blood circulation, boosts metabolism, and eliminates fatigue, the effect of inducing resuscitation brain tonic, and gauze feel obtained is smooth, submissive to relax
Refreshing, moisture absorption is ventilative, more comfort, can speed up coagulation process, while forming one layer of stable network gel in wound surface,
The microenvironment for being conducive to tissue growth is built for wound, and then promotes wound healing.
The modification liquid is made of each raw material of following weight percentage: decis 2-3%, alkyl phosphate 5-
8%, glycerol 2-4%, ester based quaternary ammonium salt 0.1-0.3%, titanate coupling agent 5-7%, remaining as water;The modification of modification
Liquid measure is the 6-10% of chitin fiber weight, and then chitin fiber is sent into vaporium, steams 35-55min.
The mass ratio of sodium alginate soln and nano-Ag particles is 1:0.2-0.6.
The finishing auxiliaries are prepared from the following raw materials in parts by weight: being carried silver organo-sol 10-15, epoxychloropropane 3-6, resisted
Bacteria microcapsule 7-9, ethylene glycol 12-14, polyhexamethylene guanide 0.4-0.7, sodium citrate 2.1-2.6, alkyl phosphate 5-7, rouge
Fat alcohol polyoxyethylene ether 6-8 and nano silica 2-3;The antimicrobial component of the antibacterial microcapsule is with Econazole class high score
Based on sub- compound and pyrethroid class compound.
Antimicrobial treatment in the step 4) is as follows: the cotton gauze after washing being put into the water of bath raio 1:30, cotton is added
Then the antibacterial agent of the 6-7.8% of gauze weight increases temperature to about 50-55 DEG C, handles time 2h.
Compared with prior art, the present invention having the following advantages and benefits:
A kind of fiber gauze production technology of high intensity of the present invention, obtained gauze antibacterial, cleaning function with conventional antimicrobial
Also having outside improves blood circulation, boosts metabolism, and it is sliding to eliminate fatigue, the effect of inducing resuscitation brain tonic, and gauze feel obtained
Refreshing, submissive pleasant, moisture absorption is ventilative, more comfort, can speed up coagulation process, at the same wound surface formed one layer it is stable
Network gel builds the microenvironment for being conducive to tissue growth for wound, and then promotes wound healing.
Specific embodiment
To make the objectives, technical solutions, and advantages of the present invention clearer, below with reference to embodiment, the present invention is made
Further to be described in detail, exemplary embodiment of the invention and its explanation for explaining only the invention, are not intended as to this
The restriction of invention.
Embodiment
A kind of fiber gauze production technology of high intensity of the present invention, the hospital gauze by alginate fibre, chitin fiber, change
Property chitin fiber and cotton fiber is blended forms, the alginate fibre, chitin fiber, modified chitosan fiber and cotton fiber
Weight ratio is 30-35:40-50:15-25:75-85;The preparation method is as follows: 1) modification liquid to be sprayed to the chitin fiber banked up
On, modification 12-24h;2) sodium alginate is added in deionized water, stirring at normal temperature, until being completely dissolved, obtains quality hundred
Divide the sodium alginate soln than being 2.4-3.6, nano-Ag particles are added in sodium alginate soln, stir evenly, mixing is made
Spinning solution prepares alginate fibre, coagulating bath post-tensioning winding using wet spinning technology, and naturally dry obtains alginate fibre;3)
By degreasing and cleaned cotton fiber first carries out extrusion pretreatment, then carries out carboxymethyl-modification processing, adds solubility
Stabilizer isothermal reaction 30min at 28-55 DEG C is added in silver salt, the isothermal reaction 1h at 28-55 DEG C, finally will be processed
Cotton fiber successively through surfactant wash, passivation, then through clear water rinsing, dehydration, it is obtained by drying arrive cotton fiber;4) 30- is weighed
40g silkworm chrysalis shell is put into the beaker with 60-80mL hydrochloric acid solution after mixing immersion, then 90-110mL hydrogen-oxygen is added into beaker
Change sodium solution, continues to mix and embathe, obtains alkali cleaning substance, and rinse alkali cleaning substance with hydrogen peroxide, chitosan is made, shell is gathered
Sugar, glacial acetic acid solution and polyvinyl alcohol stirring obtain modified self-control chitosan solution, by modified self-control chitosan solution fortune
It is sent to wire drawing in porous bushing, obtains modified self-control chitin fiber;5) raw material obtained by step 1), 2), 3) He 4) carries out
Then gauze fabric is made in antimicrobial treatment;6) fabric woven and modified nano-titanium dioxide and dimethicone are mixed and is stirred
Solution is mixed to immerse in the hot water storgae of desizing, scouring and bleaching combined machine, bath raio 1:25-30 first cleans 20-30min with 95-100 DEG C of water,
5-10 DEG C of temperature is reduced again, and water cleans 30-45min, and finishing auxiliaries are then added in water, and adjustment aqueous temperature is 65-75
DEG C, clean 40-50min;7) by above-mentioned fabric with temperature it is again that 105-110 DEG C of clear water boils 50-60min, adds hydrophilic softness
Agent, cellulase continue to boil 30min, and cloth outputting is dehydrated, and 115-125 DEG C of drying obtains: fiber hospital gauze.
Hospital gauze preparation method of the invention, be made gauze is antibacterial with conventional antimicrobial, outside cleaning function also with changing
Kind blood circulation, boosts metabolism, and eliminates fatigue, the effect of inducing resuscitation brain tonic, and gauze feel obtained is smooth, submissive to relax
Refreshing, moisture absorption is ventilative, more comfort, can speed up coagulation process, while forming one layer of stable network gel in wound surface,
The microenvironment for being conducive to tissue growth is built for wound, and then promotes wound healing.
Preferably, the modification liquid is made of each raw material of following weight percentage: decis 2-3%, alkyl phosphorus
Acid esters 5-8%, glycerol 2-4%, ester based quaternary ammonium salt 0.1-0.3%, titanate coupling agent 5-7%, remaining as water;Modification is used
Modification liquid measure be chitin fiber weight 6-10%, then by chitin fiber be sent into vaporium in, steam 35-55min.
Preferably, the mass ratio of sodium alginate soln and nano-Ag particles is 1:0.2-0.6.
Preferably, the finishing auxiliaries are prepared from the following raw materials in parts by weight: carrying silver organo-sol 10-15, epoxy chloropropionate
Alkane 3-6, antibacterial microcapsule 7-9, ethylene glycol 12-14, polyhexamethylene guanide 0.4-0.7, sodium citrate 2.1-2.6, alkyl phosphoric acid
Ester 5-7, fatty alcohol polyoxyethylene ether 6-8 and nano silica 2-3;The antimicrobial component of the antibacterial microcapsule is with chlorobenzene miaow
Based on azole high-molecular compound and pyrethroid class compound.
Preferably, the antimicrobial treatment in the step 4) is as follows: the cotton gauze after washing is put into the water of bath raio 1:30,
The antibacterial agent of the 6-7.8% of cotton gauze weight is added, then increases temperature to about 50-55 DEG C, handles time 2h.
Above-described specific embodiment has carried out further the purpose of the present invention, technical scheme and beneficial effects
It is described in detail, it should be understood that being not intended to limit the present invention the foregoing is merely a specific embodiment of the invention
Protection scope, all within the spirits and principles of the present invention, any modification, equivalent substitution, improvement and etc. done should all include
Within protection scope of the present invention.
Claims (5)
1. a kind of fiber gauze production technology of high intensity, which is characterized in that the hospital gauze is fine by alginate fibre, chitin
Dimension, modified chitosan fiber and cotton fiber is blended forms, the alginate fibre, chitin fiber, modified chitosan fiber and cotton
The weight ratio of fiber is 30-35:40-50:15-25:75-85;The preparation method is as follows: 1) modification liquid to be sprayed to the crust banked up
On cellulose fiber, modification 12-24h;2) sodium alginate is added in deionized water, stirring at normal temperature, until being completely dissolved, is obtained
Mass percent is the sodium alginate soln of 2.4-3.6, and nano-Ag particles are added in sodium alginate soln, stir evenly, and is made
At blend spinning liquid, alginate fibre, coagulating bath post-tensioning winding are prepared using wet spinning technology, naturally dry obtains seaweed
Fiber;3) by degreasing and cleaned cotton fiber first carries out extrusion pretreatment, carboxymethyl-modification processing is then carried out, is added
Stabilizer isothermal reaction 30min at 28-55 DEG C is added in soluble silver salt, the isothermal reaction 1h at 28-55 DEG C, finally will place
The cotton fiber managed successively through surfactant wash, passivation, then through clear water rinsing, dehydration, it is obtained by drying arrive cotton fiber;4) claim
It takes 30-40g silkworm chrysalis shell to be put into the beaker with 60-80mL hydrochloric acid solution after mixing immersion, then 90- is added into beaker
110mL sodium hydroxide solution, continuess to mix and embathes, and obtains alkali cleaning substance, and rinse alkali cleaning substance with hydrogen peroxide, it is poly- that shell is made
Sugar stirs chitosan, glacial acetic acid solution and polyvinyl alcohol, obtains modified self-control chitosan solution, makes shell by oneself for modified
Glycan solution is transported to wire drawing in porous bushing, obtains modified self-control chitin fiber;5) it is obtained by step 1), 2), 3) He 4)
Raw material carry out antimicrobial treatment, gauze fabric is then made;6) by the fabric woven and modified nano-titanium dioxide and dimethyl
Silicone oil is mixed solution and immerses in the hot water storgae of desizing, scouring and bleaching combined machine, and bath raio 1:25-30 is first cleaned with 95-100 DEG C of water
20-30min, then 5-10 DEG C of temperature is reduced, water cleans 30-45min, and finishing auxiliaries are then added in water, adjusts aqueous solution temperature
Degree is 65-75 DEG C, cleans 40-50min;7) by above-mentioned fabric with temperature it is again that 105-110 DEG C of clear water boils 50-60min, adds
Hydrophilic softening agent, cellulase continue to boil 30min, and cloth outputting is dehydrated, and 115-125 DEG C of drying obtains: fiber hospital gauze.
2. a kind of fiber gauze production technology of high intensity according to claim 1, which is characterized in that the modification liquid is
It is made of each raw material of following weight percentage: decis 2-3%, alkyl phosphate 5-8%, glycerol 2-4%, ester group quaternary ammonium
Salt 0.1-0.3%, titanate coupling agent 5-7%, remaining as water;The modification liquid measure of modification is chitin fiber weight
6-10%, then by chitin fiber be sent into vaporium in, steam 35-55min.
3. a kind of fiber gauze production technology of high intensity according to claim 1, which is characterized in that sodium alginate soln
Mass ratio with nano-Ag particles is 1:0.2-0.6.
4. a kind of fiber gauze production technology of high intensity according to claim 1, which is characterized in that the arrangement helps
Agent is prepared from the following raw materials in parts by weight: carrying silver organo-sol 10-15, epoxychloropropane 3-6, antibacterial microcapsule 7-9, ethylene glycol
12-14, polyhexamethylene guanide 0.4-0.7, sodium citrate 2.1-2.6, alkyl phosphate 5-7, fatty alcohol polyoxyethylene ether 6-8 and
Nano silica 2-3;The antimicrobial component of the antibacterial microcapsule is with Econazole class high-molecular compound and pyrethroid
Based on class compound.
5. a kind of fiber gauze production technology of high intensity according to claim 1, which is characterized in that in the step 4)
Antimicrobial treatment it is as follows: the cotton gauze after washing is put into the water of bath raio 1:30, the anti-of the 6-7.8% of cotton gauze weight is added
Then microbial inoculum increases temperature to about 50-55 DEG C, handles time 2h.