CN109249664A - A kind of PVC film modelled after an antique and preparation method thereof - Google Patents
A kind of PVC film modelled after an antique and preparation method thereof Download PDFInfo
- Publication number
- CN109249664A CN109249664A CN201810936084.8A CN201810936084A CN109249664A CN 109249664 A CN109249664 A CN 109249664A CN 201810936084 A CN201810936084 A CN 201810936084A CN 109249664 A CN109249664 A CN 109249664A
- Authority
- CN
- China
- Prior art keywords
- pvc
- parts
- temperature
- modelled
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of PVC film modelled after an antique of the present invention and preparation method thereof, including layer of PVC and ink layer, the ink layer raw material includes: 15-20 parts of polishes according to parts by weight, 2-5 parts of butanone, 3-6 parts of pigment, 0.1-0.3 parts of scratch resistance agent, preparation method, the following steps are included: 1) PVC base and PVC decorative layer are prepared first, printing ink layer on the PVC decorative layer；2) then PVC base and PVC decorative layer are bonded by make-up machine；3) finally ink layer is wiped using wiping agent, ink layer is wiped by wiping agent, so that ink layer shows decorative pattern and pattern modelled after an antique, there is antique effect, meet the needs of people.
Description
Technical field
The invention belongs to high-molecular compound technical fields, and in particular to a kind of PVC film modelled after an antique and preparation method thereof.
Background technique
Polyvinyl chloride English abbreviation PVC, with less toxic, fire-retardant, cold-resistant, the environmentally friendly excellent performance of PVC film, increasingly
To vast purposes, it is widely used in the fields such as certificate, Bao Ce, packaging, luggage, clothes, footwear, automobile decoration, develops to
Visible PVC product everywhere in daily life field.By a little as it can be seen that the demand of PVC film is increasing.
PVC film main ingredient is polyvinyl chloride, separately has and other compositions are added to enhance its heat resistance, toughness, ductility
Deng.PVC film be liked deeply in the world today, a kind of rather popular and synthetic material for being also widely used.PVC film
Global usage amount be in second in various synthetic materials.In the material that can produce three-dimensional table facial mask, PVC film is most
Suitable material.
Currently, and having part as the improvement of people's living standards, part population likes pursuing the home decoration of modernization
People likes the furniture decoration and ornament that have pseudo-classic style, and there is presently no the PVC films for meeting this demand of people.
Summary of the invention
The present invention overcomes the disadvantages of the prior art, provides a kind of PVC film modelled after an antique and preparation method thereof, has imitative
Ancient effect, meets the needs of people.
In order to solve the above-mentioned technical problem, the present invention is achieved by the following technical solutions:
A kind of PVC film modelled after an antique comprising layer of PVC and ink layer, the ink layer raw material includes: polishes according to parts by weight
15-20 parts, 2-5 parts of butanone, 3-6 parts of pigment, 0.1-0.3 parts of scratch resistance agent.
Further, the pigment includes red 0.87 part of R-122, and Y-21 is 2.75 parts, black 0.5 part of B-27 yellow.
A kind of preparation method of PVC film modelled after an antique, comprising the following steps:
1) PVC base and PVC decorative layer, printing ink layer on the PVC decorative layer are prepared first；
2) then PVC base and PVC decorative layer are bonded by make-up machine；
3) finally ink layer is wiped using wiping agent.
Further, according to parts by weight, the wiping agent is 40-70 parts of ethyl ester and 30-40 parts of butanone.
Further, in the step 2), the PVC base and PVC decorative layer pass through face preheating wheel and middle preheating first
Then wheel passes through embossed wheel, rubber tire, temperature refining wheel and cooling wheel then by main heat opinion and delivery wheel.
Further, the face preheating wheel speed is 11.742m/min, and temperature is 120 DEG C, and middle preheating wheel speed is
12.023m/min, temperature are 130 DEG C.
Further, it is 12.48m/min that the main heat, which discusses speed, and temperature is 155 DEG C, and conveying wheel speed is 12.156m/
Min, temperature are 160 DEG C.
Further, the embossing wheel speed is 11.102m/min, and temperature is 30 DEG C.
Further, the rubber tire temperature is ice water temperature, and temperature refining wheel speed is 12.256m/min, and temperature is 30 DEG C, cooling
Wheel speed is 12.368m/min, and temperature is ice water temperature.
Compared with prior art, the beneficial effects of the present invention are:
A kind of PVC film modelled after an antique of the present invention and preparation method thereof, including layer of PVC and ink layer, the ink layer raw material
It according to parts by weight include: 15-20 parts of polishes, 2-5 parts of butanone, 3-6 parts of pigment, 0.1-0.3 parts of scratch resistance agent, preparation method,
The following steps are included: 1) PVC base and PVC decorative layer are prepared first, printing ink layer on the PVC decorative layer；2) then logical
Make-up machine is crossed to be bonded PVC base and PVC decorative layer；3) finally ink layer is wiped using wiping agent, is passed through
Wiping agent wipes ink layer, so that ink layer shows decorative pattern and pattern modelled after an antique, has antique effect, meets people
Demand.
Specific embodiment
Hereinafter, preferred embodiments of the present invention will be described, it should be understood that preferred embodiment described herein is only used
In the description and interpretation present invention, it is not intended to limit the present invention.
A kind of PVC film modelled after an antique comprising layer of PVC and ink layer, ink layer raw material include: polyester resin according to parts by weight
50 parts, 35 parts of butyl glycol ether, 10 parts of filler, 2 parts of dispersing agent, 3 parts of defoaming agent, 19.2 parts of polishes TJ110,3.43 parts of butanone,
4.12 parts of pigment, 0.25 part of KA-910 scratch resistance agent, polishes TJ110 is for adjusting ink colors, wherein pigment includes R-122 red
0.87 part, Y-21 is 2.75 parts, black 0.5 part of B-27 yellow.
A kind of preparation method of PVC film modelled after an antique, comprising the following steps:
1) PVC base and PVC decorative layer, printing ink layer on the PVC decorative layer are prepared first；
2) then PVC base and PVC decorative layer are bonded by make-up machine；
3) finally ink layer is wiped using wiping agent, according to parts by weight, the ethyl ester that the wiping agent is 60 parts
With 36 parts of butanone.
Wherein, in step 2), then PVC base and PVC decorative layer pass through first by face preheating wheel and middle preheating wheel
Then main heat opinion and delivery wheel pass through embossed wheel, rubber tire, temperature refining wheel and cooling wheel.
It is 11.742m/min that face, which preheats wheel speed, and temperature is 120 DEG C, and middle preheating wheel speed is 12.023m/min, temperature
It is 130 DEG C.
It is 12.48m/min that main heat, which discusses speed, and temperature is 155 DEG C, and conveying wheel speed is 12.156m/min, temperature 160
℃。
Embossing wheel speed is 11.102m/min, and temperature is 30 DEG C.
Rubber tire temperature is ice water temperature, and temperature refining wheel speed is 12.256m/min, and temperature is 30 DEG C, and cooling wheel speed is
12.368m/min, temperature are ice water temperature.
The present invention makes pigment cooperate, then by using wiping agent to ink by above-mentioned specific speed and temperature
Layer is wiped, and the PVC film of pseudo-classic effect is obtained.
Finally, it should be noted that these are only the preferred embodiment of the present invention, it is not intended to restrict the invention, although
Referring to embodiment, invention is explained in detail, for those skilled in the art, still can be to aforementioned
Technical solution documented by each embodiment is modified or equivalent replacement of some of the technical features, but it is all
Within the spirit and principles in the present invention, any modification, equivalent replacement, improvement and so on should be included in protection of the invention
Within the scope of.
Claims (9)
1. a kind of PVC film modelled after an antique, which is characterized in that it includes layer of PVC and ink layer, and the ink layer raw material is according to parts by weight
It include: 15-20 parts of polishes, 2-5 parts of butanone, 3-6 parts of pigment, 0.1-0.3 parts of scratch resistance agent.
2. a kind of PVC film modelled after an antique according to claim 1, which is characterized in that the pigment includes red 0.87 part of R-122, Y-
21 is 2.75 parts, black 0.5 part of B-27 yellow.
3. a kind of preparation method of PVC film modelled after an antique according to claim 1, which comprises the following steps:
1) PVC base and PVC decorative layer, printing ink layer on the PVC decorative layer are prepared first；
2) then PVC base and PVC decorative layer are bonded by make-up machine；
3) finally ink layer is wiped using wiping agent.
4. a kind of preparation method of PVC film modelled after an antique according to claim 3, which is characterized in that according to parts by weight, the wiping
Wiping agent is 40-70 parts of ethyl ester and 30-40 parts of butanone.
5. a kind of preparation method of PVC film modelled after an antique according to claim 3, which is characterized in that described in the step 2)
PVC base and PVC decorative layer, then by main heat opinion and delivery wheel, then lead to first by face preheating wheel and middle preheating wheel
Cross embossed wheel, rubber tire, temperature refining wheel and cooling wheel.
6. a kind of preparation method of PVC film modelled after an antique according to claim 5, which is characterized in that the face preheats wheel speed and is
11.742m/min, temperature are 120 DEG C, and middle preheating wheel speed is 12.023m/min, and temperature is 130 DEG C.
7. a kind of preparation method of PVC film modelled after an antique according to claim 5, which is characterized in that the main heat by speed is
12.48m/min, temperature are 155 DEG C, and conveying wheel speed is 12.156m/min, and temperature is 160 DEG C.
8. a kind of preparation method of PVC film modelled after an antique according to claim 5, which is characterized in that the embossing wheel speed is
11.102m/min, temperature are 30 DEG C.
9. a kind of preparation method of PVC film modelled after an antique according to claim 4, which is characterized in that the rubber tire temperature is ice water
Temperature, temperature refining wheel speed are 12.256m/min, and temperature is 30 DEG C, and cooling wheel speed is 12.368m/min, and temperature is ice water temperature
Degree.