CN109231801A - A kind of stained glass cup processing technology - Google Patents
A kind of stained glass cup processing technology Download PDFInfo
- Publication number
- CN109231801A CN109231801A CN201811297586.7A CN201811297586A CN109231801A CN 109231801 A CN109231801 A CN 109231801A CN 201811297586 A CN201811297586 A CN 201811297586A CN 109231801 A CN109231801 A CN 109231801A
- Authority
- CN
- China
- Prior art keywords
- embryo material
- stained glass
- processing technology
- particle
- cup processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to glass technology fields, refer in particular to a kind of stained glass cup processing technology, the processing technology is that color grains are added in hollow embryo material, make particle fusion inside embryo material by heating, and form embryo material by blowing, trimming is then carried out to embryo material by local heating, finally by stress relieving by annealing, the object of the present invention is to provide a kind of safe and healthy and low production cost stained glass cup processing technologys.
Description
Technical field
The invention belongs to glass technology fields, refer in particular to a kind of stained glass cup processing technology.
Background technique
Glass is Cup for drinking water most suitable in family life, opposed plastic cup, dixie cup, for ceramic cup, more strong
Health is safer, and cleaning is also very convenient, and moderate, glass is fired by inorganic silicic acid salt, in the process of firing
In be free of organic chemical substance, it is not necessary to worry that chemical substance is drunk into belly.And glass surface is smooth, it is easy to clean, bacterium and
Dirt is difficult to retain, and glass in the market is mostly colourless or has single color, seldom occurs having in cup body a variety of
The glass of color, be primarily due to multicolour glass need cup body molding after on cup body welding stained glass, add
Work complex process, production efficiency is low, or keeps cup body presentation colored by adding pigment in the process of processing and manufacturing, but pigment
In generally all contain heavy metal, influence user's health, there are also a kind of stained glass cup be to make in glass surface applique
It is easy to fall with middle surface covering.
Summary of the invention
The object of the present invention is to provide a kind of safe and healthy and low production cost stained glass cup processing technologys.
The object of the present invention is achieved like this:
A kind of stained glass cup processing technology, includes the following steps:
A, early-stage preparations one: production stained glass particulates;
B, early-stage preparations two: heating hollow glass tube localized hyperthermia, and divides and form several independent embryo materials;
C, it forming: weighing particle, particle is added in embryo material, high-temperature heating makes particles fuse and mutually merges with embryo material,
And form embryo material by blowing;
D, trimming is handled: molding embryo material locally being carried out circumference heating, carries out ends cutting to embryo material;
E, it anneals: glass being placed in annealing kiln and is annealed, eliminate stress;
Step b, heating temperature is 1200-1600 DEG C in c, d.
Particle diameter is 1-2mm in a.
The glass tube is with a thickness of 2-3mm.
In c high temperature heating process, embryo material merges particle uniformly on embryo material inner wall around axial rotation.
It in c high temperature heating process, is heated outside embryo material, embryo material first softens, and falls into particle in embryo material.
Embryo material one end sealing in step b, the other end of embryo material are provided with the opening for particle to be added.
The stained glass particulates are that stained glass stick crushes to be formed by pulverizer.
Using a kind of stained glass cup processing technology of the present invention, compared with prior art, it has the advantage that: logical
Cross in embryo material forming process, stained glass particulates be fused in embryo material, processing method is simple, high production efficiency, due to
Grain small volume, particle melts completely so that embryo material and particle connection structure stabilization, and due on glass in fusion process
Colour is melted by stained glass to be formed, adhesive-free and pigment on glass, therefore stained glass cup sanitation and hygiene, be conducive to using
The health of person.Preparation method of the present invention solve stained glass cup processing method in the prior art is simple, be unfavorable for using
The problem of person's health.It is simple with preparation process, high production efficiency, and stained glass cup sanitation and hygiene produced, be conducive to
The health of user.
Detailed description of the invention
Fig. 1 is process flow chart of the invention.
Specific embodiment
With specific embodiment, the invention will be further described with reference to the accompanying drawing:
A kind of stained glass cup processing technology, includes the following steps:
A, early-stage preparations one: different shaped particles can be made in stained glass by worker, and also can use pulverizer will
Stained glass stick is ground into particle, and stained glass particulates are that stained glass stick is formed by pulverizer processing in the present embodiment, excellent
Selecting particle diameter is 1-2mm, convenient for the melted by heat of particle;
B, early-stage preparations two: choosing hollow glass tube, heats to hollow glass tube localized hyperthermia, and heating and temperature control exists
1200-1600 DEG C, hollow glass tube heats hollow glass tube circumference around axial-rotation in heating process, and divides shape
At several independent embryo materials, with a thickness of 2-3mm, in the present embodiment, particle is crushed preferably glass tube by stained glass stick is formed, excellent
Embryo material one end is selected to seal, the other end of embryo material is provided with the opening for particle to be added, and produces and processes convenient for worker.
C, form: weigh particle, by particle be added embryo material in, high-temperature heating, heating and temperature control at 1200-1600 DEG C,
Make particles fuse and mutually merged with embryo material, the melting range of the stained glass particulates is less than or equal to the melting range of embryo material, preferably color
The melting range of color glass particle and the melting range of embryo material are identical, and stained glass particulates when processing is avoided only to fall into embryo material and unfused,
Keep glass rough, even results in user's injury, be also beneficial to that stained glass particulates is avoided to be only attached to glass table
Face, to keep stained glass particulates easy to fall off, hollow glass tube and particle are high-boron-silicon glass in the present embodiment, high-temperature heating
In the process, it is heated outside embryo material, embryo material first softens, and falls into particle in embryo material, is conducive to the glass table produced
Face is smooth, forms embryo material finally by blowing.
D, trimming is handled: molding embryo material locally being carried out circumference heating, heating and temperature control is high at 1200-1600 DEG C
In warm heating process, embryo material merges particle uniformly on embryo material inner wall around axial rotation, carries out ends cutting to embryo material;
E, it anneals: glass being placed in annealing kiln and is annealed, annealing temperature is controlled at 550-600 DEG C, eliminates stress.
Above-described embodiment is only presently preferred embodiments of the present invention, is not limited the scope of the invention according to this, therefore: it is all according to
The equivalence changes that structure of the invention, shape, principle are done, should all be covered by within protection scope of the present invention.
Claims (8)
1. a kind of stained glass cup processing technology, characterized by the following steps:
A, early-stage preparations one: production stained glass particulates;
B, early-stage preparations two: heating hollow glass tube localized hyperthermia, and divides and form several independent embryo materials;
C, it forms: weighing particle, particle is added in embryo material, high-temperature heating makes particles fuse and mutually merges with embryo material, and leads to
Crossing blowing forms embryo material;
D, trimming is handled: molding embryo material locally being carried out circumference heating, carries out ends cutting to embryo material;
E, it anneals: glass being placed in annealing kiln and is annealed, eliminate stress.
2. a kind of stained glass cup processing technology according to claim 1, it is characterised in that: step b, heat temperature in c, d
Degree is 1200-1600 DEG C.
3. a kind of stained glass cup processing technology according to claim 1 or 2, it is characterised in that: particle diameter is 1- in a
2mm。
4. a kind of stained glass cup processing technology according to claim 3, it is characterised in that: the glass tube is with a thickness of 2-
3mm。
5. a kind of stained glass cup processing technology according to claim 1 or 2 or 4, it is characterised in that: the heating of c high temperature
In the process, embryo material merges particle uniformly on embryo material inner wall around axial rotation.
6. a kind of stained glass cup processing technology according to claim 5, it is characterised in that: in c high temperature heating process,
It is heated outside embryo material, embryo material first softens, and falls into particle in embryo material.
7. a kind of stained glass cup processing technology according to claim 6, it is characterised in that: embryo material one end in step b
Sealing, the other end of embryo material are provided with the opening for particle to be added.
8. a kind of stained glass cup processing technology described according to claim 1 or 2 or 4 or 6 or 7, it is characterised in that: the coloured silk
Color glass particle is that stained glass stick crushes to be formed by pulverizer.