CN108545956A - A kind of processing method of silver pearl glassware - Google Patents

A kind of processing method of silver pearl glassware Download PDF

Info

Publication number
CN108545956A
CN108545956A CN201810686841.0A CN201810686841A CN108545956A CN 108545956 A CN108545956 A CN 108545956A CN 201810686841 A CN201810686841 A CN 201810686841A CN 108545956 A CN108545956 A CN 108545956A
Authority
CN
China
Prior art keywords
silver
colored
glassware
pearl
blank
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810686841.0A
Other languages
Chinese (zh)
Inventor
朱建功
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201810686841.0A priority Critical patent/CN108545956A/en
Publication of CN108545956A publication Critical patent/CN108545956A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of processing methods of silver-colored pearl glassware, include the following steps：1) it stocks up：High-boron-silicon glass pipe and filamentary silver are selected, filamentary silver is cut into silver-colored section, high-boron-silicon glass pipe, which is carried out high temperature, cuts pipe；2) base：Step 1) will be passed through, and treated that high-boron-silicon glass pipe is placed on slewing, is heated in rotation by widening burner flame, is heated to 1,200 1400 DEG C, high-boron-silicon glass pipe one end softening, drawing seal forms vessel bottom, blank is made；3) it merges；4) it is molded；5) it anneals：The molding vessel body of semi-finished product is put into 520 580 DEG C of annealing furnaces and is made annealing treatment, annealing time is 1.5 3h, finally obtains silver-colored pearl glassware finished product.The process steps of the silver-colored pearl glassware of the present invention are simple, it is easy to operate, silver-colored pearl and glassware is set to be merged, the inner wall of made glassware is protruding with several silver-colored pearls, and the processing method of the silver-colored pearl glassware is suitable for large-scale promotion application.

Description

A kind of processing method of silver pearl glassware
Technical field
The present invention relates to a kind of processing methods of silver-colored pearl glassware.
Background technology
It is well known that silver has certain health-care effect, because silver has suction-operated, micro- life to the microorganism in liquid After object is adsorbed by silver, the enzyme for playing respiration just loses effect, and microorganism will be rapid dead.As long as and every liter of water contains hundreds of millions points Two milligrams of silver ion can kill in water most of bacterium.Silver can sterilize, for example silverware ware can be killed in water Mushroom, but for transparent glassware, silver layer is difficult to process on glass material, and silver-colored material is made to be applied in glassware There are certain technical difficulties.
Invention content
In order to solve the above technical problems, the present invention provides a kind of processing method of silver-colored pearl glassware.
The processing method of the silver-colored pearl glassware of the present invention, includes the following steps：
1) it stocks up：High-boron-silicon glass pipe and filamentary silver are selected, filamentary silver is cut into silver-colored section, high-boron-silicon glass pipe, which is carried out high temperature, to be cut Pipe；
2) base：Step 1) will be passed through, and treated that high-boron-silicon glass pipe is placed on slewing, passes through in rotation Widen burner flame to be heated, is heated to 1200-1400 DEG C, high-boron-silicon glass pipe one end softening, drawing seal forms vessel Blank is made in bottom；
3) it merges：The silver-colored section in step 1) is added into blank open end, blank is added by widening burner flame Blank is warming up to 1200-1400 DEG C by heat, heating time 10-40 second, and silver-colored section is melted into silver after burning red softening in the middle part of blank Pearl, silver-colored pearl rotate in glass tube with glass tube, since the density of the density ratio glass of silver is big, silver-colored pearl under gravity Glass inside pipe wall can be penetrated into, silver-colored pearl is made to combine closely to form the silver-colored pearl blank that inner wall has silver point with blank inner wall；
4) it is molded：The silver-colored pearl blank of step 3) is preheated using flame spray head, mould is used again after the softening of silver-colored pearl blank Have compression moulding vessel bottom and oral area, is made annealing treatment molding vessel body to obtain semi-finished product；
5) it anneals：The molding vessel body of semi-finished product is put into 520-580 DEG C of annealing furnace and is made annealing treatment, annealing time For 1.5-3h, silver-colored pearl glassware finished product is finally obtained.
The processing method of the silver-colored pearl glassware of the present invention, in step 1)：A diameter of 1-3mm of the filamentary silver, silver-colored section Length be 1-3mm.
The processing method of the silver-colored pearl glassware of the present invention, in step 1)：By high-boron-silicon glass when the high temperature section pipe Tube edge rotates side and carries out local heating, until it is 1200-1400 DEG C to be heated to temperature, glass tube softening, from intermediate position pinch off It opens, completes high-boron-silicon glass pipe and cut pipe.
Beneficial effects of the present invention are compared with prior art：The process steps letter of the silver-colored pearl glassware of the present invention It is single, it is easy to operate, so that silver-colored pearl and glassware is merged, the inner wall of made glassware is protruding with several Silver-colored pearl, silver pearl can be in direct contact with liquid when use, have bactericidal effect, the processing method of the silver-colored pearl glassware suitable Suitable large-scale promotion application.
Specific implementation mode
With reference to embodiment, the embodiment of the present invention is furthur described in detail.Following embodiment is used for Illustrate the present invention, but is not limited to the scope of the present invention.
A kind of processing method of silver pearl glassware, includes the following steps：
1) it stocks up：High-boron-silicon glass pipe and filamentary silver are selected, filamentary silver is cut into silver-colored section, high-boron-silicon glass pipe, which is carried out high temperature, to be cut Pipe；
2) base：Step 1) will be passed through, and treated that high-boron-silicon glass pipe is placed on slewing, passes through in rotation Widen burner flame to be heated, is heated to 1200-1400 DEG C, high-boron-silicon glass pipe one end softening, drawing seal forms vessel Blank is made in bottom；
3) it merges：The silver-colored section in step 1) is added into blank open end, blank is added by widening burner flame Blank is warming up to 1200-1400 DEG C by heat, heating time 10-40 second, and silver-colored section is melted into silver after burning red softening in the middle part of blank Pearl, silver-colored pearl rotate in glass tube with glass tube, since the density of the density ratio glass of silver is big, silver-colored pearl under gravity Glass inside pipe wall can be penetrated into, silver-colored pearl is made to combine closely to form the silver-colored pearl blank that inner wall has silver point with blank inner wall；
4) it is molded：The silver-colored pearl blank of step 3) is preheated using flame spray head, mould is used again after the softening of silver-colored pearl blank Have compression moulding vessel bottom and oral area, is made annealing treatment molding vessel body to obtain semi-finished product；
5) it anneals：The molding vessel body of semi-finished product is put into 520-580 DEG C of annealing furnace and is made annealing treatment, annealing time For 1.5-3h, silver-colored pearl glassware finished product is finally obtained.
The processing method of the silver-colored pearl glassware of the present invention, in step 1)：A diameter of 1-3mm of the filamentary silver, silver-colored section Length be 1-3mm.
The processing method of the silver-colored pearl glassware of the present invention, in step 1)：By high-boron-silicon glass when the high temperature section pipe Tube edge rotates side and carries out local heating, until it is 1200-1400 DEG C to be heated to temperature, glass tube softening, from intermediate position pinch off It opens, completes high-boron-silicon glass pipe and cut pipe.
The process steps of the silver-colored pearl glassware of the present invention are simple, easy to operate, enable silver-colored pearl and glassware It is merged, the inner wall of made glassware is protruding with several silver-colored pearls, and silver pearl can directly connect with liquid when use It touches, there is bactericidal effect, the processing method of the silver-colored pearl glassware is suitable for large-scale promotion application.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art For member, without departing from the technical principles of the invention, several improvements and modifications, these improvements and modifications can also be made Also it should be regarded as protection scope of the present invention.

Claims (3)

1. a kind of processing method of silver pearl glassware, which is characterized in that include the following steps：
1) it stocks up：High-boron-silicon glass pipe and filamentary silver are selected, filamentary silver is cut into silver-colored section, high-boron-silicon glass pipe, which is carried out high temperature, cuts pipe；
2) base：Step 1) will be passed through, and treated that high-boron-silicon glass pipe is placed on slewing, in rotation by widening Burner flame is heated, and is heated to 1200-1400 DEG C, high-boron-silicon glass pipe one end softening, drawing seal forms vessel bottom Blank is made in portion；
3) it merges：The silver-colored section in step 1) is added into blank open end, blank is heated by widening burner flame, is added Hot time 10-40 seconds, blank is warming up to 1200-1400 DEG C, silver-colored section is melted into silver-colored pearl, silver-colored pearl after burning red softening in the middle part of blank It is rotated with glass tube in glass tube, since the density of the density ratio glass of silver is big, silver-colored pearl can permeate under gravity To glass inside pipe wall, silver-colored pearl is made to combine closely to form the silver-colored pearl blank that inner wall has silver point with blank inner wall；
4) it is molded：The silver-colored pearl blank of step 3) is preheated using flame spray head, again with mold pressure after the softening of silver-colored pearl blank Type vessel bottom and oral area is made, is made annealing treatment molding vessel body to obtain semi-finished product；
5) it anneals：The molding vessel body of semi-finished product is put into 520-580 DEG C of annealing furnace and is made annealing treatment, annealing time is 1.5-3h finally obtains silver-colored pearl glassware finished product.
2. the processing method of silver pearl glassware according to claim 1, which is characterized in that in step 1)：The silver The length of a diameter of 1-3mm of silk, silver-colored section are 1-3mm.
3. the processing method of silver pearl glassware according to claim 1, which is characterized in that in step 1)：The height High-boron-silicon glass tube edge rotation side is subjected to local heating when temperature cuts pipe, until it is 1200-1400 DEG C to be heated to temperature, glass tube Softening, is opened from intermediate position pinch off, is completed high-boron-silicon glass pipe and is cut pipe.
CN201810686841.0A 2018-06-28 2018-06-28 A kind of processing method of silver pearl glassware Pending CN108545956A (en)