CN109231794A - Special-shaped dog-ear plate curved tempered glass production technology - Google Patents
Special-shaped dog-ear plate curved tempered glass production technology Download PDFInfo
- Publication number
- CN109231794A CN109231794A CN201811378629.4A CN201811378629A CN109231794A CN 109231794 A CN109231794 A CN 109231794A CN 201811378629 A CN201811378629 A CN 201811378629A CN 109231794 A CN109231794 A CN 109231794A
- Authority
- CN
- China
- Prior art keywords
- glass
- cullet
- tempered glass
- mold
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to tempered glass technical fields, and disclose special-shaped dog-ear plate curved tempered glass production technology, the following steps are included: the cullet of recycling is handled, cullet is put into cleaning equipment first, cleaning equipment is sorted using air and is removed light impurities, light impurities removal cleans the cullet in cleaning equipment after finishing, it is put into Magnetic Isolation machine in the cullet after will be cleaned, the metal impurities mixed in Magnetic Isolation machine removal cullet, such as, there is metal cover etc. to be likely to form the oxide of interference smelting furnace operation in cullet.The abnormal shape dog-ear plate curved tempered glass production technology, pass through formula adjustment and fusion temperature adjustment, special raw mixture is added in tempered glass production, prodan or fluorite are not added, the generation of pernicious gas is avoided, and is able to satisfy production requirement, reduces environmental pollution, the cost of glass production is reduced, while so that glass is absorbed heat when heating.
Description
Technical field
The present invention relates to tempered glass technical field, specially special-shaped dog-ear plate curved tempered glass production technology.
Background technique
Tempered glass belongs to safety glass, and tempered glass is prestressed glass in fact, for the intensity for improving glass, usually makes
With method chemically or physically, compression is formed in glass surface, glass bears to offset skin stress first when external force, to mention
High bearing capacity, reinforcing glass itself anti-wind pressure.
With the development of society, requirement of the people to glass is higher and higher, the requirement such as people to strength of glass, to glass
The requirement of hardness, and High-strength compression resistant glass just refer under certain compression shock glass overall structure still guarantee it is complete and
The special glass not ruptured, and tempering is exactly the technique further strengthened to the intensity of glass, still, present high intensity
The reason of resistance to compression tempered glass is not easy to produce, and is not easy to production is not can guarantee glass thermally equivalent, to be unfavorable for guaranteeing
The quality of glass, while being unfavorable for rationally utilizing thermal energy, so be unfavorable for it is energy saving, so propose the curved tempering of special-shaped dog-ear plate
Process of glass solves the problems, such as above-mentioned propose.
Summary of the invention
(1) the technical issues of solving
In view of the deficiencies of the prior art, the present invention provides special-shaped dog-ear plate curved tempered glass production technology, have and adding
The advantages of capable of making glass thermally equivalent when hot, solves present High-strength compression resistant tempered glass and is not easy to produce, inconvenient
It is that not can guarantee glass thermally equivalent in the reason of production, to be unfavorable for guaranteeing the quality of glass, while is unfavorable for reasonable benefit
With thermal energy, and then it is unfavorable for energy saving problem.
(2) technical solution
To realize the above-mentioned purpose that can make glass thermally equivalent when heating, the invention provides the following technical scheme:
Special-shaped dog-ear plate curved tempered glass production technology, comprising the following steps:
1) cullet of recycling is handled, cullet is put into cleaning equipment first, cleaning equipment utilizes air
Light impurities are removed by sorting, and light impurities removal cleans the cullet in cleaning equipment after finishing, and are being incited somebody to action
Cullet after cleaned is put into Magnetic Isolation machine, the metal impurities mixed in Magnetic Isolation machine removal cullet, for example,
There is metal cover etc. to be likely to form the oxide of interference smelting furnace operation in cullet, it is miscellaneous that hand-sorted is mixed into the native stone class in cullet
Remaining cullet is carried out color separation sorting, mainly by optical sensing, uses compressed air by matter, ceramic-like impurity and organic matter
It is sorted, is finally crushed the cullet for handling rear qualification well, then smashed cullet is collected storage；
2) cullet is added in the equipment with blender and condenser, from 0 DEG C~600 DEG C continuous heatings, is heating
Engineering in cullet is stirred and can be sufficiently heated, accelerate the softening rate of cullet, heating 600 DEG C~1200
DEG C, to cullet be completely dissolved together after adding raw materials mixture, raw mixture contain 50~60 parts, feldspar 2.5~
3.5 parts, 8~10 parts of dolomite, 8~10 parts of lime stone, 17~19 parts of soda ash and 3.5~4.5 parts of small powder, contain in raw mixture
There is fluorine amount 0.5~1.0%, then is stirred mixing；
3) glass metal after mixing pours into glass mold, and glass mold is bending mold, and condenser makes glass in mold
Glass liquid is quickly cooled down into simple glass, and simple glass is taken out from the inside of mold, will be on the front and back sides of glass to be cut
Spread acid proof protective film, reserve the position of cutting mouth, then corrosive liquid is sprinkled upon tow sides, wait 60 minutes or so when
Between simple glass can be carried out cutting and polishing treatment, so that simple glass is processed into the shape of needs；
4) simple glass after well cutting is put into heating device, then from 0 DEG C~700 DEG C continuous heatings, when common
Glass is heated to 700 DEG C or so close to softening point, and simple glass eliminates internal stress by the deformation of itself and becomes tempering glass
Then tempered glass is removed mold by glass, then high pressure cold air is blowed to the two sides of tempered glass with bull nozzle, makes tempering glass
Glass is rapidly and uniformly cooled to room temperature.
(3) beneficial effect
Compared with prior art, the present invention provides special-shaped dog-ear plate curved tempered glass production technology, have following beneficial
Effect:
The abnormal shape dog-ear plate curved tempered glass production technology, is suitably adjusted by the dispensing ratio to original mixture
It is whole, it is added in tempered glass production and matches different raw mixtures, obtain the tempered glass of varying strength different demands, steel
Change in the production of glass and does not add prodan or fluorite, not only can be to avoid the generation of pernicious gas, but also be able to satisfy
The production requirement of tempered glass reduces pollution of tempered glass when production to environment, to reduce glass production
Cost, while it is more uniform during Glass Transition to heat in the way of stirring glass raw material, sufficiently make plus
Glass raw material in hot equipment absorbs heat, increases the efficiency of Glass Transition, to improve the quality of production of tempered glass, reduces
The yield of unqualified tempered glass.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical solution in the embodiment of the present invention is clearly and completely retouched
It states, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on the present invention
In embodiment, every other implementation obtained by those of ordinary skill in the art without making creative efforts
Example, shall fall within the protection scope of the present invention.
Embodiment one: special-shaped dog-ear plate curved tempered glass production technology, comprising the following steps:
1) cullet of recycling is handled, cullet is put into cleaning equipment first, cleaning equipment utilizes air
Light impurities are removed by sorting, and light impurities removal cleans the cullet in cleaning equipment after finishing, and are being incited somebody to action
Cullet after cleaned is put into Magnetic Isolation machine, the metal impurities mixed in Magnetic Isolation machine removal cullet, for example,
There is metal cover etc. to be likely to form the oxide of interference smelting furnace operation in cullet, it is miscellaneous that hand-sorted is mixed into the native stone class in cullet
Remaining cullet is carried out color separation sorting, mainly by optical sensing, uses compressed air by matter, ceramic-like impurity and organic matter
It is sorted, is finally crushed the cullet for handling rear qualification well, then smashed cullet is collected storage；
2) cullet is added in the equipment with blender and condenser, from 0 DEG C~600 DEG C continuous heatings, is heating
Engineering in cullet is stirred and can be sufficiently heated, accelerate the softening rate of cullet, heating 600 DEG C~1200
DEG C, adding raw materials mixture after being completely dissolved together to cullet, raw mixture contains 50 parts, 2.5 parts of feldspar, white clouds
8 parts of stone, 8 parts of lime stone, 17 parts of soda ash and 3.5 parts of small powder contain fluorine amount 0.5%, then are stirred mixing in raw mixture；
3) glass metal after mixing pours into glass mold, and glass mold is bending mold, and condenser makes glass in mold
Glass liquid is quickly cooled down into simple glass, and simple glass is taken out from the inside of mold, will be on the front and back sides of glass to be cut
Spread acid proof protective film, reserve the position of cutting mouth, then corrosive liquid is sprinkled upon tow sides, wait 60 minutes or so when
Between simple glass can be carried out cutting and polishing treatment, so that simple glass is processed into the shape of needs；
4) simple glass after well cutting is put into heating device, then from 0 DEG C~700 DEG C continuous heatings, when common
Glass is heated to 700 DEG C or so close to softening point, and simple glass eliminates internal stress by the deformation of itself and becomes tempering glass
Then tempered glass is removed mold by glass, then high pressure cold air is blowed to the two sides of tempered glass with bull nozzle, makes tempering glass
Glass is rapidly and uniformly cooled to room temperature.
By the way that the minimum and glass raw material mixing of raw mixture is added, the high tempering glass of intensity is obtained after being evenly heated
Glass reduces the manufacturing cost of tempered glass.
Embodiment two: special-shaped dog-ear plate curved tempered glass production technology, comprising the following steps:
1) cullet of recycling is handled, cullet is put into cleaning equipment first, cleaning equipment utilizes air
Light impurities are removed by sorting, and light impurities removal cleans the cullet in cleaning equipment after finishing, and are being incited somebody to action
Cullet after cleaned is put into Magnetic Isolation machine, the metal impurities mixed in Magnetic Isolation machine removal cullet, for example,
There is metal cover etc. to be likely to form the oxide of interference smelting furnace operation in cullet, it is miscellaneous that hand-sorted is mixed into the native stone class in cullet
Remaining cullet is carried out color separation sorting, mainly by optical sensing, uses compressed air by matter, ceramic-like impurity and organic matter
It is sorted, is finally crushed the cullet for handling rear qualification well, then smashed cullet is collected storage；
2) cullet is added in the equipment with blender and condenser, from 0 DEG C~600 DEG C continuous heatings, is heating
Engineering in cullet is stirred and can be sufficiently heated, accelerate the softening rate of cullet, heating 600 DEG C~1200
DEG C, adding raw materials mixture after being completely dissolved together to cullet, raw mixture contains 52 parts, 2.7 parts of feldspar, white clouds
8.5 parts of stone, 8.5 parts of lime stone, 17.5 parts of soda ash and 3.7 parts of small powder contain fluorine amount 0.7%, then are stirred in raw mixture
Mix mixing；
3) glass metal after mixing pours into glass mold, and glass mold is bending mold, and condenser makes glass in mold
Glass liquid is quickly cooled down into simple glass, and simple glass is taken out from the inside of mold, will be on the front and back sides of glass to be cut
Spread acid proof protective film, reserve the position of cutting mouth, then corrosive liquid is sprinkled upon tow sides, wait 60 minutes or so when
Between simple glass can be carried out cutting and polishing treatment, so that simple glass is processed into the shape of needs；
4) simple glass after well cutting is put into heating device, then from 0 DEG C~700 DEG C continuous heatings, when common
Glass is heated to 700 DEG C or so close to softening point, and simple glass eliminates internal stress by the deformation of itself and becomes tempering glass
Then tempered glass is removed mold by glass, then high pressure cold air is blowed to the two sides of tempered glass with bull nozzle, makes tempering glass
Glass is rapidly and uniformly cooled to room temperature.
Dosage by increasing raw mixture keeps the intensity of tempered glass more hard, improves the steady of tempered glass
It is qualitative.
Embodiment three: special-shaped dog-ear plate curved tempered glass production technology, comprising the following steps:
1) cullet of recycling is handled, cullet is put into cleaning equipment first, cleaning equipment utilizes air
Light impurities are removed by sorting, and light impurities removal cleans the cullet in cleaning equipment after finishing, and are being incited somebody to action
Cullet after cleaned is put into Magnetic Isolation machine, the metal impurities mixed in Magnetic Isolation machine removal cullet, for example,
There is metal cover etc. to be likely to form the oxide of interference smelting furnace operation in cullet, it is miscellaneous that hand-sorted is mixed into the native stone class in cullet
Remaining cullet is carried out color separation sorting, mainly by optical sensing, uses compressed air by matter, ceramic-like impurity and organic matter
It is sorted, is finally crushed the cullet for handling rear qualification well, then smashed cullet is collected storage；
2) cullet is added in the equipment with blender and condenser, from 0 DEG C~600 DEG C continuous heatings, is heating
Engineering in cullet is stirred and can be sufficiently heated, accelerate the softening rate of cullet, heating 600 DEG C~1200
DEG C, adding raw materials mixture after being completely dissolved together to cullet, raw mixture contains 54 parts, 3 parts of feldspar, dolomite
9 parts, 9 parts of lime stone, 18 parts of soda ash and 4 parts of small powder contain fluorine amount 0.8%, then are stirred mixing in raw mixture；
3) glass metal after mixing pours into glass mold, and glass mold is bending mold, and condenser makes glass in mold
Glass liquid is quickly cooled down into simple glass, and simple glass is taken out from the inside of mold, will be on the front and back sides of glass to be cut
Spread acid proof protective film, reserve the position of cutting mouth, then corrosive liquid is sprinkled upon tow sides, wait 60 minutes or so when
Between simple glass can be carried out cutting and polishing treatment, so that simple glass is processed into the shape of needs；
4) simple glass after well cutting is put into heating device, then from 0 DEG C~700 DEG C continuous heatings, when common
Glass is heated to 700 DEG C or so close to softening point, and simple glass eliminates internal stress by the deformation of itself and becomes tempering glass
Then tempered glass is removed mold by glass, then high pressure cold air is blowed to the two sides of tempered glass with bull nozzle, makes tempering glass
Glass is rapidly and uniformly cooled to room temperature.
Manufacturing cost substantially reduces, and reduces the use of raw material, and by reducing fusion temperature, also greatly saves
The energy, while producing the discharge amount of noxious material and usage amount is reduced, protect environment.
Example IV: special-shaped dog-ear plate curved tempered glass production technology, comprising the following steps:
1) cullet of recycling is handled, cullet is put into cleaning equipment first, cleaning equipment utilizes air
Light impurities are removed by sorting, and light impurities removal cleans the cullet in cleaning equipment after finishing, and are being incited somebody to action
Cullet after cleaned is put into Magnetic Isolation machine, the metal impurities mixed in Magnetic Isolation machine removal cullet, for example,
There is metal cover etc. to be likely to form the oxide of interference smelting furnace operation in cullet, it is miscellaneous that hand-sorted is mixed into the native stone class in cullet
Remaining cullet is carried out color separation sorting, mainly by optical sensing, uses compressed air by matter, ceramic-like impurity and organic matter
It is sorted, is finally crushed the cullet for handling rear qualification well, then smashed cullet is collected storage；
2) cullet is added in the equipment with blender and condenser, from 0 DEG C~600 DEG C continuous heatings, is heating
Engineering in cullet is stirred and can be sufficiently heated, accelerate the softening rate of cullet, heating 600 DEG C~1200
DEG C, adding raw materials mixture after being completely dissolved together to cullet, raw mixture contains 56 parts, 3.2 parts of feldspar, white clouds
9.5 parts of stone, 9.5 parts of lime stone, 18.5 parts of soda ash and 4.2 parts of small powder contain fluorine amount 0.9%, then are stirred in raw mixture
Mix mixing；
3) glass metal after mixing pours into glass mold, and glass mold is bending mold, and condenser makes glass in mold
Glass liquid is quickly cooled down into simple glass, and simple glass is taken out from the inside of mold, will be on the front and back sides of glass to be cut
Spread acid proof protective film, reserve the position of cutting mouth, then corrosive liquid is sprinkled upon tow sides, wait 60 minutes or so when
Between simple glass can be carried out cutting and polishing treatment, so that simple glass is processed into the shape of needs；
4) simple glass after well cutting is put into heating device, then from 0 DEG C~700 DEG C continuous heatings, when common
Glass is heated to 700 DEG C or so close to softening point, and simple glass eliminates internal stress by the deformation of itself and becomes tempering glass
Then tempered glass is removed mold by glass, then high pressure cold air is blowed to the two sides of tempered glass with bull nozzle, makes tempering glass
Glass is rapidly and uniformly cooled to room temperature.
Social a large amount of glass wastes have been recycled, have saved part resource, and make manufacturing enterprise's production cost significantly
Decline.
The beneficial effects of the present invention are: the abnormal shape dog-ear plate curved tempered glass production technology, by original mixture
Dispensing ratio carries out appropriate adjustment, is added in tempered glass production and matches different raw mixtures, obtains varying strength not
With the tempered glass of demand, prodan or fluorite are not added in the production of tempered glass, it not only can be to avoid pernicious gas
Generation, and be able to satisfy the production requirement of tempered glass, reduce pollution of tempered glass when production to environment,
To reduce the cost of glass production, while heat glass raw material in the way of stirring during Glass Transition
It is more uniform, so that the glass raw material in heating equipment is absorbed heat, increases the efficiency of Glass Transition, to improve tempering glass
The quality of production of glass reduces the yield of unqualified tempered glass, solves present High-strength compression resistant tempered glass and is not easy to give birth to
The reason of producing, being not easy to production is not can guarantee glass thermally equivalent, to be unfavorable for guaranteeing the quality of glass, is unfavorable for simultaneously
Thermal energy is rationally utilized, and then is unfavorable for energy saving problem.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (1)
1. special-shaped dog-ear plate curved tempered glass production technology, which comprises the following steps:
1) cullet of recycling is handled, cullet is put into cleaning equipment first, cleaning equipment is sorted using air
Light impurities are removed, light impurities removal cleans the cullet in cleaning equipment after finishing, and will clean
Cullet after good is put into Magnetic Isolation machine, the metal impurities mixed in Magnetic Isolation machine removal cullet, for example, in broken glass
There is metal cover etc. to be likely to form the oxide of interference smelting furnace operation in glass, hand-sorted be mixed into native stone class impurity in cullet,
Remaining cullet is carried out color separation sorting, mainly by optical sensing, is carried out with compressed air by ceramic-like impurity and organic matter
The cullet for handling rear qualification well is finally crushed, then smashed cullet is collected storage by sorting；
2) cullet is added in the equipment with blender and condenser, from 0 DEG C~600 DEG C continuous heatings, in the work of heating
Cullet is stirred and can be sufficiently heated in journey, accelerates the softening rate of cullet, is heated up 600 DEG C~1200 DEG C, to
Cullet be completely dissolved together after adding raw materials mixture, raw mixture contain 50~60 parts, 2.5~3.5 parts of feldspar,
8~10 parts of dolomite, 8~10 parts of lime stone, 17~19 parts of soda ash and 3.5~4.5 parts of small powder contain fluorine amount in raw mixture
0.5~1.0%, then it is stirred mixing；
3) glass metal after mixing pours into glass mold, and glass mold is bending mold, and condenser makes glass metal in mold
It is quickly cooled down into simple glass, simple glass is taken out from the inside of mold, will be spread on the front and back sides of glass to be cut
Acid proof protective film reserves the position of cutting mouth, then corrosive liquid is sprinkled upon tow sides, waits 60 minutes or so time just
Cutting and polishing treatment can be carried out to simple glass, and simple glass is made to be processed into the shape of needs；
4) simple glass after well cutting is put into heating device, then from 0 DEG C~700 DEG C continuous heatings, works as simple glass
700 DEG C or so close to softening point are heated to, simple glass eliminates internal stress by the deformation of itself and becomes tempered glass, so
Tempered glass is removed into mold afterwards, then high pressure cold air is blowed to the two sides of tempered glass with bull nozzle, keeps tempered glass fast
Speed and be equably cooled to room temperature.