CN106865965A - A kind of processing technology of tempering single-glass - Google Patents
A kind of processing technology of tempering single-glass Download PDFInfo
- Publication number
- CN106865965A CN106865965A CN201710177801.9A CN201710177801A CN106865965A CN 106865965 A CN106865965 A CN 106865965A CN 201710177801 A CN201710177801 A CN 201710177801A CN 106865965 A CN106865965 A CN 106865965A
- Authority
- CN
- China
- Prior art keywords
- glass
- raw material
- cutting
- mixing
- edging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of processing technology of tempering single-glass, the processing technology is comprised the following steps：Technological process：Raw material crushes → mixing → fusing → shaping → cutting → edging → cleaning → heating → packaging.A kind of processing technology of tempering single-glass of the invention, the smoothness of glass edge can be increased, reduce the trouble of secondary operation after dispatching from the factory, and with good translucency, suitable for different use environments, the overall structure of glass will not be damaged during processing, the service life of safety glass can be extended, with good promotional value.
Description
Technical field
The present invention relates to tempering single-glass processing technique field, more particularly to a kind of processing work of tempering single-glass
Skill.
Background technology
Safety glass（Tempered glass/Reinforced glass）Belong to safety glass.Safety glass is in fact
A kind of prestressed glass, to improve the intensity of glass, usually using method chemically or physically, forming pressure in glass surface should
Power, glass is born to offset skin stress first during external force, and so as to improve bearing capacity, reinforcing glass itself anti-wind pressure is trembled with fear
Heat, impact etc., note being distinguished with fiberglass.The safety glass impact strength of condition of equivalent thickness is the 3 of simple glass
~5 times, bending strength is 3~5 times of simple glass, and safety glass has good heat endurance, and the temperature difference that can be born is general
3 times of logical glass, can bear 300 DEG C of difference variation, and after toughened glass crushing, fragment can be broken into uniform little particle simultaneously
And without the wedge angle of universal glass knife-like, be widely used in so as to be referred to as safety glass among automobile, interior decoration, Yi Jigao
The window that floor is externally opened.
The content of the invention
It is an object of the invention to provide a kind of processing technology of tempering single-glass.
A kind of processing technology of tempering single-glass, its specific procedure of processing is：
（1）, raw material crush：Raw material should select silica sand, soda ash, feldspar, dolomite, lime stone and saltcake, and it should be made when broken
Particle is less than 0.1mm, is crushed in closed space, reduces waving for dust, while clearing up wherein mixing the impurity for containing.
（2）, mixing：To be mixed between the raw material and additive of broken powdering so that additive can be uniform
It is dispersed in powder raw material, by observing its concrete form during mixing, judges whether to be well mixed.
（3）, fusing：The raw material after the completion of mixing is sent in glass melting furnace, now adjust temperature in molten cellar for storing things to
1700 °, the molten cellar for storing things of closed structure can reduce the loss of heat, heat can be reflected by melting the sheet tin on the outside of cellar for storing things, through 30 minutes
It is fused into glass metal.
（4）, shaping：Glass metal under molten condition is placed into corresponding shaped device, different shape can be formed
And the glass metal of thickness, then lowered the temperature rapidly by heat-conducting plate so that glass metal completed solidification in 10 minutes, it is ensured that glass
The stability of form, the glass metal overflowed during this should be struck off in time.
（5）, cutting：Glass after cooling is placed on cutting plate, glass is fixed by fixing device, then used
Measurement apparatus mark the size and shape for needing cutting, are cut by giant, should be stopped by protective cover during cutting and flown
The chip for splashing, it is to avoid cause injury to personnel.
（6）, edging：The glass after the completion of cutting is placed into edge polisher, by the depth and length that manually control edging
Degree, the chip of edging is collected by dust storage chamber, is then polished again by sand paper, makes glass edge more smooth flat
It is whole.
（7）, cleaning：By the glass after edging, separate transmission is carried out according to different shape size, the warm water using 40 DEG C enters
The two-sided cleaning of row, should ensure that the stationarity of glass, while entering to the impurity in small, broken bits that glass surface is adhered to by tweed during cleaning
Row is erased.
（8）, heating：Glass after cleaning is transported in annealing furnace by conveyer, is heated through 450 DEG C of height
100s, then through 300 DEG C height heat 200s, chilling 100s is then carried out by cooling blower, after the completion of it is water cooled to normal temperature
Obtain final product individual layer safety glass finished product.
（9）, packaging：Finished product individual layer safety glass is wrapped up by soft continuous cloth, mounted box packaging is carried out, and opened up in mounted box
Air hole, it is ensured that the permeability of air in placement process.
Beneficial effect is：The individual layer safety glass produced using processing technology of the present invention, by increasing capacitance it is possible to increase glass edge
Smoothness, reduces the trouble of secondary operation after dispatching from the factory, and with good translucency, it is adaptable to different use environments, plus
Man-hour will not damage to the overall structure of glass, can extend the service life of safety glass.
Specific embodiment
Safety glass is in fact a kind of prestressed glass, to improve the intensity of glass, usually using side chemically or physically
Method, compression is formed in glass surface, and glass bears to offset skin stress first during external force, so as to improve bearing capacity, is increased
Strong glass itself anti-wind pressure, cold and heat, impact etc., when glass is destroyed by external force, fragment can be cellular blunt into being similar to
The broken little particle in angle, is difficult to cause serious injury human body.But different production technologies, can be to the using effect of safety glass
Cause serious influence.
A kind of processing technology of tempering single-glass, it is concretely comprised the following steps：
（1）, raw material crush：Raw material should select silica sand, soda ash, feldspar, dolomite, lime stone and saltcake, and it should be made when broken
Particle is less than 0.1mm, is crushed in closed space, reduces waving for dust, while clearing up wherein mixing the impurity for containing.
（2）, mixing：To be mixed between the raw material and additive of broken powdering so that additive can be uniform
It is dispersed in powder raw material, by observing its concrete form during mixing, judges whether to be well mixed.
（3）, fusing：The raw material after the completion of mixing is sent in glass melting furnace, now adjust temperature in molten cellar for storing things to
1700 °, the molten cellar for storing things of closed structure can reduce the loss of heat, heat can be reflected by melting the sheet tin on the outside of cellar for storing things, through 30 minutes
It is fused into glass metal.
（4）, shaping：Glass metal under molten condition is placed into corresponding shaped device, different shape can be formed
And the glass metal of thickness, then lowered the temperature rapidly by heat-conducting plate so that glass metal completed solidification in 10 minutes, it is ensured that glass
The stability of form, the glass metal overflowed during this should be struck off in time.
（5）, cutting：Glass after cooling is placed on cutting plate, glass is fixed by fixing device, then used
Measurement apparatus mark the size and shape for needing cutting, are cut by giant, should be stopped by protective cover during cutting and flown
The chip for splashing, it is to avoid cause injury to personnel.
（6）, edging：The glass after the completion of cutting is placed into edge polisher, by the depth and length that manually control edging
Degree, the chip of edging is collected by dust storage chamber, is then polished again by sand paper, makes glass edge more smooth flat
It is whole.
（7）, cleaning：By the glass after edging, separate transmission is carried out according to different shape size, the warm water using 40 DEG C enters
The two-sided cleaning of row, should ensure that the stationarity of glass, while entering to the impurity in small, broken bits that glass surface is adhered to by tweed during cleaning
Row is erased.
（8）, heating：Glass after cleaning is transported in annealing furnace by conveyer, is heated through 450 DEG C of height
100s, then through 300 DEG C height heat 200s, chilling 100s is then carried out by cooling blower, after the completion of it is water cooled to normal temperature
Obtain final product individual layer safety glass finished product.
（9）, packaging：Finished product individual layer safety glass is wrapped up by soft continuous cloth, mounted box packaging is carried out, and opened up in mounted box
Air hole, it is ensured that the permeability of air in placement process.
The processing technology of tempering single-glass of the present invention has advantages below：
1st, raw material should select silica sand, soda ash, feldspar, dolomite, lime stone and saltcake, and when broken its particle should be less than
0.1mm, the size of particle decides the number of light transmittance, and the particle of 0.1mm can be increased safety glass translucent effect, and
And after clearing up the wherein mixed impurity for containing, cleanliness factor and aesthetics after glass processing can be lifted.
2nd, the glass after edging, separate transmission is carried out according to different shape size, is carried out using 40 DEG C of warm water two-sided clear
Wash, it is ensured that inside glass structural stability, prevent that temperature is too high to make glass hardened beforehand, it is viscous to glass surface by tweed
Attached impurity in small, broken bits is erased, and can reduce in subsequent handling has impurity to stick to the trouble that glass surface is difficult to clean off.
3rd, chilling 100s is carried out by cooling blower in heating process, after the completion of water cooled obtain final product individual layer tempering to normal temperature
Glass finished-product so that safety glass is cooled into a process for gradual change in proper order, by being quickly cooled to firm structure, then by
Water-cooled completes the hardening of various pieces, the effectively service life of lifting safety glass.
The basic principles, principal features and advantages of the present invention have been shown and described above.The technical staff of the industry should
Understand, the present invention is not limited to the above embodiments, simply original of the invention is illustrated described in above-described embodiment and specification
Reason, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes and improvements
All fall within the protetion scope of the claimed invention.The claimed scope of the invention is by appending claims and its Xiao Wu circle
It is fixed.
Claims (1)
1. a kind of processing technology of tempering single-glass, it is characterised in that：The specific procedure of processing of the tempering single-glass is：
（1）, raw material crush：Raw material should select silica sand, soda ash, feldspar, dolomite, lime stone and saltcake, and it should be made when broken
Particle is less than 0.1mm, is crushed in closed space, reduces waving for dust, while clearing up wherein mixing the impurity for containing;
（2）, mixing：To be mixed between the raw material and additive of broken powdering so that additive can uniformly disperse
In powder raw material, by observing its concrete form during mixing, judge whether to be well mixed;
（3）, fusing：The raw material after the completion of mixing is sent in glass melting furnace, now adjusts the temperature in molten cellar for storing things to 1700 °,
The molten cellar for storing things of closed structure can reduce the loss of heat, and heat can be reflected by melting the sheet tin on the outside of cellar for storing things, be fused into through 30 minutes
Glass metal;
（4）, shaping：Glass metal under molten condition is placed into corresponding shaped device, different shape and thickness can be formed
The glass metal of degree, is then lowered the temperature rapidly by heat-conducting plate so that glass metal completed solidification in 10 minutes, it is ensured that glass form
Stability, during this overflow glass metal should be struck off in time;
（5）, cutting：Glass after cooling is placed on cutting plate, glass is fixed by fixing device, measurement is then used
Device marks the size and shape for needing cutting, is cut by giant, should stop what is splashed by protective cover during cutting
Chip, it is to avoid cause injury to personnel;
（6）, edging：The glass after the completion of cutting is placed into edge polisher, by manually controlling the depth and length of edging, mill
The chip on side is collected by dust storage chamber, is then polished again by sand paper, makes glass edge more smooth;
（7）, cleaning：By the glass after edging, separate transmission is carried out according to different shape size, carried out using 40 DEG C of warm water double
Face is cleaned, and the stationarity of glass is should ensure that during cleaning, while being smeared to the impurity in small, broken bits that glass surface is adhered to by tweed
Remove;
（8）, heating：Glass after cleaning is transported in annealing furnace by conveyer, 100s is heated through 450 DEG C of height,
Heat 200s through 300 DEG C of height again, chilling 100s then carried out by cooling blower, after the completion of water cooled obtain final product list to normal temperature
Layer safety glass finished product;
（9）, packaging：Finished product individual layer safety glass is wrapped up by soft continuous cloth, mounted box packaging is carried out, and air is opened up in mounted box
Through hole, it is ensured that the permeability of air in placement process.