CN109208146A - The method for weaving of cotton and the blended hollow yarn man textile fabric of polyvinyl - Google Patents
The method for weaving of cotton and the blended hollow yarn man textile fabric of polyvinyl Download PDFInfo
- Publication number
- CN109208146A CN109208146A CN201710541325.4A CN201710541325A CN109208146A CN 109208146 A CN109208146 A CN 109208146A CN 201710541325 A CN201710541325 A CN 201710541325A CN 109208146 A CN109208146 A CN 109208146A
- Authority
- CN
- China
- Prior art keywords
- yarn
- desizing
- cotton
- spinning
- weaving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of method for weaving of cotton and the blended hollow yarn man textile fabric of polyvinyl of the present invention.It includes the following steps: 1) water-soluble poval spinning: carrying out spinning to polyvinyl alcohol by dry spinning method, the poly-vinyl alcohol solution of concentration 30~40% is passed through into device for spinning, from spinning head aperture indentation hot-air channel, the water evaporation in poly-vinyl alcohol solution is fallen using hot-air, poly-vinyl alcohol solution thread is made to be frozen into silk fiber；2) spinning of covering yarn；3) it weaves: by a temperature of starching of the covering yarn at 50~75 DEG C made from Quality Pure Cotton Yarn Production and step 2, fabric being weaved by spaced mode；4) it desizing and moves back dimension: the fabric that step 3 obtains being subjected to desizing simultaneously and moves back dimension, in 90~98 DEG C of desizing liquids 30~45min of heat preservation, obtain thorough desizing, move back dimension fabric.Effect is good, yarn strength is high for the dimension of moving back of present invention covering yarn in weaving process.
Description
Technical field
The present invention relates to the method for weaving of a kind of textile fabric, especially disclose a kind of cotton and the blended hollow yarn home textile of polyvinyl
The method for weaving of fabric.
Background technique
Water soluble vinylon is soluble easily in water, is easy to degrade, tasteless, nontoxic, has been widely used in traditional textile, medical treatment, has made
The fields such as paper, supatex fabric exploitation, the production of disposable production, penelope.
Hollow yarn is utilization of the doughnut concept on yarn, makees covering yarn using water soluble vinylon and cotton fiber, will
Molten remove can form pure cotton hollow yarn to polyvinyl core filaments in the hot water.The volume for thus substantially increasing storage air in yarn contains
Amount.Yarn core dissolves away in hollow yarn, quality mitigate, it can be achieved that yarn thin specialization and family's textile fabric it is lightening.With hollow yarn plus
Family's textile fabric of work has good warmth retention property, hydroscopic fast-drying, and fabric fluffy degree is high, and elasticity is good, and soft.Mesh
Before, it is more about research of the hollow yarn in terms of towel cloth, knitted fabric, still, applied in terms of woven fabric about hollow yarn
Product it is less, while there is also many problems in process of production.
For example, a kind of hollow yarn is disclosed, by water-soluble fibre and spinning application No. is 03220439.6 patent application
Textured fiber mixing, drawing-off, twisting spin, and fiber is twisted at spiral, and the intermediate position for the yarn body being twisted together is in hollow shape.Its
Advantage is that have high specific surface area, and the covering surface of yarn is big；Has the effect of high resiliency, super soft；Due to there is air insulated
The presence of film, this yarn have good thermal insulation property.But it is mixed using the short fine item that carries out of water soluble vinylon, moves back dimension rear yarn
The hollow effect of line is unobvious to be easy to collapse.
For another example: application No. is 200710019777.2 patents of invention to disclose a kind of soft warming type hollow yarn production
Side carries out technique processing to the cotton fiber of selection first, including distributes cotton, cotton carding, drafting, combing, drafting, rove, spun yarn, network
The process that cylinder, loose formula move back dimension；Secondly, being to select water-soluble fibre for blend fibre, then carry out work to the water-soluble fibre of selection
Skill processing, step include at least scutching cotton and cotton carding；Although its product obtained has many advantages, such as, but manufacturing procedure is excessively numerous
Miscellaneous, production efficiency is low.
For another example, application No. is 201210371990.0 patents of invention to disclose a kind of high degree of hollowness core-spun yarn work
Skill, covering yarn obtained and the cored weaving yarns towel technique is utilized, is 4.1~7.3tex by two root thickness cotton yarns and number
Water soluble vinylon filament composite twist, be made with cotton fiber cladding water soluble vinylon filament spun yarn；It then will be described water-soluble
Property the hydrolysis of polyvinyl long filament, and obtain the high degree of hollowness covering yarn；The disadvantages of this method are: gained fabric is empty in use
Heart effect easily collapses, to weaken the excellent performance of hollow yarn.
Summary of the invention
It is an object of the invention to overcome defect existing in the prior art, provides in a kind of weaving process and move back dimension effect
It is good, yarn strength is high, family's textile fabric product of preparation is frivolous, warmth retention property is good, hydroscopic fast-drying is good, fluffy degree is high, elasticity is good and
The method for weaving of soft cotton and the blended hollow yarn man textile fabric of polyvinyl.
The present invention is implemented as follows: the method for weaving of a kind of cotton and the blended hollow yarn man textile fabric of polyvinyl, feature exist
In: include the following steps:
1) water-soluble poval spinning: spinning is carried out to polyvinyl alcohol by dry spinning method, by the poly- second of concentration 30~40%
Enolate solution passes through device for spinning, will be in poly-vinyl alcohol solution using hot-air from spinning head aperture indentation hot-air channel
Water evaporation is fallen, and poly-vinyl alcohol solution thread is made to be frozen into silk fiber, and wherein poly-vinyl alcohol solution average degree of polymerization is 1750 ± 50；
To nascent silk fiber carry out hot-stretch processing, 180 ± 10 DEG C of draft temperature, 3~6 times of draw ratio；Obtain water-soluble polyethylene
Alcohol fiber filament；
2) spinning of covering yarn: the water-soluble polyvinyl alcohol fibers silk that step 1 is obtained, will by ring spinner as heart yarn
Cotton fiber is coated on the outer surface of heart yarn, and when cladding, the tension of cotton fiber is less than heart yarn tension；The unit time output of heart yarn
Speed is less than the speed of cotton fiber unit time output；The cotton fiber unit time output speed be 10~16m/min, heart yarn,
Tension difference between cotton fiber is 20~40cN, and the speed difference of unit time output is 2~4m/min, and covering yarn is finally made；
3) it weaves: by covering yarn made from Quality Pure Cotton Yarn Production and step 2 in 50~75 DEG C of at a temperature of starching, passing through spaced side
Formula weaves fabric；
4) it desizing and moves back dimension: the fabric that step 3 obtains being subjected to desizing simultaneously and moves back dimension, in 90~98 DEG C of desizing liquids heat preservation 30
~45min obtains thorough desizing, moves back dimension fabric.
In step 3, the slurry of the starching is PVA starch mixed slurry.
Spaced arrangement in step 3 is alternatively arranged for the warp and weft of gained covering yarn and Quality Pure Cotton Yarn Production.
The component of the desizing liquid of desizing in step 4 is in mass ratio are as follows: 0.3% ~ 0.5% desizing enzyme, 0.2% ~ 0.4%
Enzyme activity promoter, 0.3% ~ 0.6% detergent, 0.02% ~ 0.03% defoaming agent, remaining mixes for water；Bath raio be 1:8~
1:11.
Desizing in step 4 moves back dimension process as loose formula desizing.
Desizing liquid injection form in step 4 is overflow desizing.
The beneficial effects of the present invention are: effect is good, yarn strength is high for the dimension of moving back of present invention covering yarn in weaving process, system
Standby family's textile fabric product has that frivolous, warmth retention property is good, hydroscopic fast-drying is good, fluffy degree is high, elasticity is good and soft excellent
Point.
Specific embodiment
A kind of method for weaving of cotton and the blended hollow yarn man textile fabric of polyvinyl of the present invention, includes the following steps:
1) water-soluble poval spinning: spinning is carried out to polyvinyl alcohol by dry spinning method, by the poly- second of concentration 30~40%
Enolate solution passes through device for spinning, will be in poly-vinyl alcohol solution using hot-air from spinning head aperture indentation hot-air channel
Water evaporation is fallen, and poly-vinyl alcohol solution thread is made to be frozen into silk fiber, and wherein poly-vinyl alcohol solution average degree of polymerization is 1750 ± 50；
To nascent silk fiber carry out hot-stretch processing, 180 ± 10 DEG C of draft temperature, 3~6 times of draw ratio；Obtain water-soluble polyethylene
Alcohol fiber filament；
2) spinning of covering yarn: the water-soluble polyvinyl alcohol fibers silk that step 1 is obtained, will by ring spinner as heart yarn
Cotton fiber is coated on the outer surface of heart yarn, and when cladding, the tension of cotton fiber is less than heart yarn tension；The unit time output of heart yarn
Speed is less than the speed of cotton fiber unit time output；The cotton fiber unit time output speed be 10~16m/min, heart yarn,
Tension difference between cotton fiber is 20~40cN, and the speed difference of unit time output is 2~4m/min, and covering yarn is finally made；
3) it weaves: by covering yarn made from Quality Pure Cotton Yarn Production and step 2 in 50~75 DEG C of at a temperature of starching, passing through spaced side
Formula weaves fabric；Wherein, the slurry of the starching is PVA starch mixed slurry.The spaced arrangement is gained covering yarn
It is alternatively arranged with the warp and weft of Quality Pure Cotton Yarn Production.
4) it desizing and moves back dimension: the fabric that step 3 obtains being subjected to desizing simultaneously and moves back dimension, in 90~98 DEG C of desizing liquids guarantor
30~45min of temperature, obtains thorough desizing, moves back dimension fabric.The component of the desizing liquid of the desizing is in mass ratio are as follows: 0.3% ~
0.5% desizing enzyme, the enzyme activity promoter of 0.2% ~ 0.4 %, 0.3% ~ 0.6% detergent, 0.02% ~ 0.03% defoaming agent, its
Yu Weishui is mixed；Bath raio is 1:8~1:11.The desizing moves back dimension process as loose formula desizing.The desizing liquid injects form
For overflow desizing.
In weaving process of the present invention in order to avoid dissolving away polyvinyl after, because of warp and weft interweaving state, postorder process and used
Hollow yarn, which collapses, in journey becomes flat and weakens hollow effect, and the present invention is alternatively arranged with Quality Pure Cotton Yarn Production using covering yarn to weave
Object.Wherein, Quality Pure Cotton Yarn Production plays skeleton function, to improve hollow effect reduction phenomenon.It spins matched pure with processed covering yarn
Cotton completes the weaving for being alternatively arranged hollow yarn woven fabric using low temperature starching technique.
Dyeing and finishing technology optimization: fabric desizing is tieed up while being carried out with moving back, and process is simplified, energy consumption reduces, sustainable development.Consider
Slurry to yarn sizing is PVA starch mixed slurry, in the hot water plus alkali desizing.Temperature when moving back dimension by optimizing, when
Between, the technological parameter of bath raio, keep hollow effect after moving back dimension good, while reducing and damaging to yarn strength.
Claims (6)
1. the method for weaving of a kind of cotton and the blended hollow yarn man textile fabric of polyvinyl, characterized by the following steps:
1) water-soluble poval spinning: spinning is carried out to polyvinyl alcohol by dry spinning method, by the poly- second of concentration 30~40%
Enolate solution passes through device for spinning, will be in poly-vinyl alcohol solution using hot-air from spinning head aperture indentation hot-air channel
Water evaporation is fallen, and poly-vinyl alcohol solution thread is made to be frozen into silk fiber, and wherein poly-vinyl alcohol solution average degree of polymerization is 1750 ± 50；
To nascent silk fiber carry out hot-stretch processing, 180 ± 10 DEG C of draft temperature, 3~6 times of draw ratio；Obtain water-soluble polyethylene
Alcohol fiber filament；
2) spinning of covering yarn: the water-soluble polyvinyl alcohol fibers silk that step 1 is obtained, will by ring spinner as heart yarn
Cotton fiber is coated on the outer surface of heart yarn, and when cladding, the tension of cotton fiber is less than heart yarn tension；The unit time output of heart yarn
Speed is less than the speed of cotton fiber unit time output；The cotton fiber unit time output speed be 10~16m/min, heart yarn,
Tension difference between cotton fiber is 20~40cN, and the speed difference of unit time output is 2~4m/min, and covering yarn is finally made；
3) it weaves: by covering yarn made from Quality Pure Cotton Yarn Production and step 2 in 50~75 DEG C of at a temperature of starching, passing through spaced side
Formula weaves fabric；
4) it desizing and moves back dimension: the fabric that step 3 obtains being subjected to desizing simultaneously and moves back dimension, in 90~98 DEG C of desizing liquids heat preservation 30
~45min obtains thorough desizing, moves back dimension fabric.
2. the method for weaving of the cotton and the blended hollow yarn man textile fabric of polyvinyl according to claim 1, it is characterised in that: step
In rapid 3, the slurry of the starching is PVA starch mixed slurry.
3. the method for weaving of the cotton and the blended hollow yarn man textile fabric of polyvinyl according to claim 1, it is characterised in that:
Spaced arrangement in step 3 is alternatively arranged for the warp and weft of gained covering yarn and Quality Pure Cotton Yarn Production.
4. the method for weaving of the cotton and the blended hollow yarn man textile fabric of polyvinyl according to claim 1, it is characterised in that:
The component of the desizing liquid of desizing in step 4 is in mass ratio are as follows: 0.3% ~ 0.5% desizing enzyme, 0.2% ~ 0.4% enzyme activity promote
Agent, 0.3% ~ 0.6% detergent, 0.02% ~ 0.03% defoaming agent, remaining mixes for water；Bath raio is 1:8~1:11.
5. the method for weaving of the cotton and the blended hollow yarn man textile fabric of polyvinyl according to claim 1, it is characterised in that:
Desizing in step 4 moves back dimension process as loose formula desizing.
6. the method for weaving of the cotton and the blended hollow yarn man textile fabric of polyvinyl according to claim 1, it is characterised in that:
Desizing liquid injection form in step 4 is overflow desizing.