CN109181136A - A kind of super soft screen protecting film of optical grade 2.5D - Google Patents
A kind of super soft screen protecting film of optical grade 2.5D Download PDFInfo
- Publication number
- CN109181136A CN109181136A CN201810581271.9A CN201810581271A CN109181136A CN 109181136 A CN109181136 A CN 109181136A CN 201810581271 A CN201810581271 A CN 201810581271A CN 109181136 A CN109181136 A CN 109181136A
- Authority
- CN
- China
- Prior art keywords
- parts
- protecting film
- super soft
- agent
- screen protecting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of super soft screen protecting film of optical grade 2.5D, and the protective film includes the ingredient of following parts by weight: polyvinyl chloride: 30 ~ 40 parts, polycarbonate: 20 ~ 30 parts; polypropylene: 10 ~ 15 parts; epoxy resin: 5 ~ 10 parts, polyether polyol: 5 ~ 10 parts, hollow glass micro mist: 5 ~ 10 parts; polyethyleneglycol diacrylate: 5 ~ 10 parts; silane coupling agent: 1 ~ 5 part, curing agent: 1 ~ 5 part, anti-aging agent: 1 ~ 5 part; plasticizer: 1 ~ 5 part, organic solvent: 50 ~ 60 parts.Rationally, simple production process, flexibility is high, and hardness is strong, and production cost is low, good in economic efficiency for the protection film component collocation.
Description
Technical field
The invention belongs to protect technical field of membrane, and in particular, to a kind of super soft screen protecting film of optical grade 2.5D.
Background technique
Screen protecting film is also known as mobile phone cosmetic membrane, safeguard film for cellular phone, is a kind of cold lamination film for mounting mobile phone screen.
The characteristics of PVC material protective film is texture softness itself, and is pasted conveniently, but this material is thicker, light transmission
It spends bad, screen is made to seem dimmer.Also the marking of glue can be left after tearing on the screen.This material also compares simultaneously
It is easier to the change with temperature and turns over yellow fuel-displaced, service life is shorter.So being substantially not visible this protective film on the market
?.
On the market can it is seen that a kind of PVC improvement version protective film, solve that previously thick and heavy and translucency is bad asks
Topic but still cannot solve the problems, such as to be easy to turn over yellow fuel-displaced, and should be noted this material of PVC and do not have anti-scratch
Ability, just will appear apparent scratch on protective film after a period of use, the display effect for influencing screen also influences hand
Other PVC of aesthetics of machine entirety itself is a kind of toxic material, contains heavy metal component, stops making comprehensively in Europe
It is sold in the market with the screen protecting film of this PVC improvement plate matter than wide, feature is hand held to feel very soft
Soft, many well-known protective film producers have also stopped using this material.
PET material protective film is current one of the most common type protector on the market, the entitled mylar .PET material of chemistry
The characteristics of protective film is that quality is harder, compares scratch resistance and use for a long time will not turn over yellow fuel-displaced as PVC material
But the protective film of general PET is easier to blister and fall off, even if but having fallen off in clear water by Electrostatic Absorption
In wash and may be reused .PET material protective film price ratio PVC it is expensive many.Many famous foreign brand mobile phones
When factory, what is configured at random is PET material protector, smart compared with packaging using PET material protector patch workmanship
Beauty has and carrys out tailor-made protector exclusively for hot buy mobile phone model, and not needing to cut can be used directly.
For screen protecting film, the current country is primarily present following patent document:
The Chinese patent of Publication No. CN107857951A discloses a kind of plastic film, and in particular to a kind of cell phone screen glass
With explosion-proof pad pasting, belong to safeguard film for cellular phone technical field.Explosion-proof pad pasting, each component including following parts by weight: acrylic resin
20-30 parts, 40-50 parts of polyvinyl chloride, 6-10 parts of calcium phosphate, 2-12 parts of silica, 1-7 parts of benzyl alcohol, two molybdenum 5-10 of boronation
Part, 3-8 parts of glass fibre element, 2-6 parts of ESCALOL 567,2-5 parts of polyphenylene sulfide, 4-9 parts of titanium dioxide.This
Invention passes through acrylic resin, polyvinyl chloride, calcium phosphate, silica, benzyl alcohol, two molybdenum of boronation, glass fibre element, 2- hydroxyl
Base -4- methoxy benzophenone, polyphenylene sulfide, the compounding of titanium dioxide are provided by the invention by acting synergistically between raw material
Explosion-proof film has many advantages, such as that transparency is high, ultraviolet ray preventing effect is good, surface hardness is high, and is also equipped with alleviation and collides function,
Screen can be protected not rupture.However, explosion-proof pad pasting provided by the patent, hardness is higher, causes flexibility poor.
Summary of the invention
Above-mentioned to solve the problems, such as, the purpose of the present invention is to provide a kind of super soft screen protections of optical grade 2.5D
Film, rationally, simple production process, flexibility is high, and hardness is strong, and production cost is low, good in economic efficiency for the protection film component collocation.
In order to achieve the above objectives, the technical scheme is that
A kind of super soft screen protecting film of optical grade 2.5D, the protective film includes the ingredient of following parts by weight: polyvinyl chloride: 30 ~
40 parts, polycarbonate: 20 ~ 30 parts, polypropylene: 10 ~ 15 parts, epoxy resin: 5 ~ 10 parts, polyether polyol: 5 ~ 10 parts, hollow glass
Glass micro mist: 5 ~ 10 parts, polyethyleneglycol diacrylate: 5 ~ 10 parts, silane coupling agent: 1 ~ 5 part, curing agent: 1 ~ 5 part, anti-aging agent:
1 ~ 5 part, plasticizer: 1 ~ 5 part, organic solvent: 50 ~ 60 parts.
Further, the protective film includes the ingredient of following parts by weight: polyvinyl chloride: 30 ~ 35 parts, polycarbonate: 25 ~
30 parts, polypropylene: 10 ~ 13 parts, epoxy resin: 5 ~ 7 parts, polyether polyol: 5 ~ 8 parts, hollow glass micro mist: 6 ~ 10 parts, poly- second
Omega-diol diacrylate: 7 ~ 10 parts, silane coupling agent: 1 ~ 3 part, curing agent: 2 ~ 5 parts, anti-aging agent: 1 ~ 3 part, plasticizer: 3 ~ 5
Part, organic solvent: 55 ~ 60 parts.
Further, the protective film includes the ingredient of following parts by weight: polyvinyl chloride: 35 parts, polycarbonate: and 25 parts,
Polypropylene: 13 parts, epoxy resin: 6 parts, polyether polyol: 7 parts, hollow glass micro mist: 8 parts, polyethyleneglycol diacrylate: 7
Part, silane coupling agent: 2 parts, curing agent: 3 parts, anti-aging agent: 3 parts, plasticizer: 4 parts, organic solvent: 55 parts.
Further, plasticizer is three fourth of dioctyl phthalate, diisobutyl phthalate or acetyl tributyl citrate
Ester.
Further, the anti-aging agent is anti-aging agent 4040.
Further, the curing agent is aminoethyl piperazine, trimethylhexamethylenediamine or m-xylene diamine.
Further, the silane coupling agent is gamma-amino propyl trimethoxy silicane, gamma-amino propyl triethoxy
Silane or beta-aminoethyl-gamma-amino hydroxypropyl methyl diethoxy silane.
Further, the organic solvent is ethyl alcohol or propylene glycol solution.
Further, the preparation method of the super soft screen protecting film of the optical grade 2.5D includes the following steps: according to the proportion
Claim polyvinyl chloride, polycarbonate, polypropylene, epoxy resin melting mixing at 200 ~ 250 DEG C respectively, it is stirred to react 20 ~
40min adds polyether polyol, hollow glass micro mist, polyethyleneglycol diacrylate and 20 ~ 30 weight parts organic solvents,
10 ~ 15min is stirred under 300 ~ 400 revs/min of revolving speed, is uniformly mixed, then mixture is transferred in kneading machine, and silicon is added
Alkane coupling agent, curing agent, anti-aging agent, plasticizer and remaining organic solvent, are kneaded 10 ~ 20min, form to get the protective film.
The beneficial effects of the present invention are:
Rationally, simple production process, flexibility is high, and hardness is strong, and production cost is low, economic benefit for the protection film component collocation
It is good.
Specific embodiment
The super soft screen protecting film of a kind of optical grade 2.5D provided by the present invention, the protective film includes following parts by weight
Ingredient: polyvinyl chloride: 30 ~ 40 parts, polycarbonate: 20 ~ 30 parts, polypropylene: 10 ~ 15 parts, epoxy resin: 5 ~ 10 parts, polyethers is more
First alcohol: 5 ~ 10 parts, hollow glass micro mist: 5 ~ 10 parts, polyethyleneglycol diacrylate: 5 ~ 10 parts, silane coupling agent: 1 ~ 5 part, Gu
Agent: 1 ~ 5 part, anti-aging agent: 1 ~ 5 part, plasticizer: 1 ~ 5 part, organic solvent: 50 ~ 60 parts.
Further, the protective film includes the ingredient of following parts by weight: polyvinyl chloride: 30 ~ 35 parts, polycarbonate: 25 ~
30 parts, polypropylene: 10 ~ 13 parts, epoxy resin: 5 ~ 7 parts, polyether polyol: 5 ~ 8 parts, hollow glass micro mist: 6 ~ 10 parts, poly- second
Omega-diol diacrylate: 7 ~ 10 parts, silane coupling agent: 1 ~ 3 part, curing agent: 2 ~ 5 parts, anti-aging agent: 1 ~ 3 part, plasticizer: 3 ~ 5
Part, organic solvent: 55 ~ 60 parts.
Further, the protective film includes the ingredient of following parts by weight: polyvinyl chloride: 35 parts, polycarbonate: and 25 parts,
Polypropylene: 13 parts, epoxy resin: 6 parts, polyether polyol: 7 parts, hollow glass micro mist: 8 parts, polyethyleneglycol diacrylate: 7
Part, silane coupling agent: 2 parts, curing agent: 3 parts, anti-aging agent: 3 parts, plasticizer: 4 parts, organic solvent: 55 parts.
Further, plasticizer is three fourth of dioctyl phthalate, diisobutyl phthalate or acetyl tributyl citrate
Ester.
Further, the anti-aging agent is anti-aging agent 4040.
Further, the curing agent is aminoethyl piperazine, trimethylhexamethylenediamine or m-xylene diamine.
Further, the silane coupling agent is gamma-amino propyl trimethoxy silicane, gamma-amino propyl triethoxy
Silane or beta-aminoethyl-gamma-amino hydroxypropyl methyl diethoxy silane.
Further, the organic solvent is ethyl alcohol or propylene glycol solution.
Further, the preparation method of the super soft screen protecting film of the optical grade 2.5D includes the following steps: according to the proportion
Claim polyvinyl chloride, polycarbonate, polypropylene, epoxy resin melting mixing at 200 ~ 250 DEG C respectively, it is stirred to react 20 ~
40min adds polyether polyol, hollow glass micro mist, polyethyleneglycol diacrylate and 20 ~ 30 weight parts organic solvents,
10 ~ 15min is stirred under 300 ~ 400 revs/min of revolving speed, is uniformly mixed, then mixture is transferred in kneading machine, and silicon is added
Alkane coupling agent, curing agent, anti-aging agent, plasticizer and remaining organic solvent, are kneaded 10 ~ 20min, form to get the protective film.
It should be noted that the above examples are only used to illustrate the technical scheme of the present invention and are not limiting.Although referring to compared with
Good embodiment describes the invention in detail, those skilled in the art should understand that, it can be to the technology of invention
Scheme is modified or replaced equivalently, and without departing from the range of technical solution of the present invention, should all be covered in power of the invention
In sharp claimed range.
Claims (9)
1. a kind of super soft screen protecting film of optical grade 2.5D, which is characterized in that the protective film includes the ingredient of following parts by weight:
Polyvinyl chloride: 30 ~ 40 parts, polycarbonate: 20 ~ 30 parts, polypropylene: 10 ~ 15 parts, epoxy resin: 5 ~ 10 parts, polyether polyol: 5
~ 10 parts, hollow glass micro mist: 5 ~ 10 parts, polyethyleneglycol diacrylate: 5 ~ 10 parts, silane coupling agent: 1 ~ 5 part, curing agent: 1
~ 5 parts, anti-aging agent: 1 ~ 5 part, plasticizer: 1 ~ 5 part, organic solvent: 50 ~ 60 parts.
2. the super soft screen protecting film of optical grade 2.5D according to claim 1, which is characterized in that the protective film includes such as
The ingredient of lower parts by weight: polyvinyl chloride: 30 ~ 35 parts, polycarbonate: 25 ~ 30 parts, polypropylene: 10 ~ 13 parts, epoxy resin: 5 ~ 7
Part, polyether polyol: 5 ~ 8 parts, hollow glass micro mist: 6 ~ 10 parts, polyethyleneglycol diacrylate: 7 ~ 10 parts, silane coupling agent:
1 ~ 3 part, curing agent: 2 ~ 5 parts, anti-aging agent: 1 ~ 3 part, plasticizer: 3 ~ 5 parts, organic solvent: 55 ~ 60 parts.
3. the super soft screen protecting film of optical grade 2.5D according to claim 1, which is characterized in that the protective film includes such as
The ingredient of lower parts by weight: polyvinyl chloride: 35 parts, polycarbonate: 25 parts, polypropylene: 13 parts, epoxy resin: 6 parts, polyether polyols
Alcohol: 7 parts, hollow glass micro mist: 8 parts, polyethyleneglycol diacrylate: 7 parts, silane coupling agent: 2 parts, curing agent: 3 parts, prevent old
Agent: 3 parts, plasticizer: 4 parts, organic solvent: 55 parts.
4. the super soft screen protecting film of optical grade 2.5D according to claim 1, which is characterized in that plasticizer is O-phthalic
Dioctyl phthalate, diisobutyl phthalate or tributyl 2-acetylcitrate.
5. the super soft screen protecting film of optical grade 2.5D according to claim 1, which is characterized in that the anti-aging agent is anti-old
Agent 4040.
6. the super soft screen protecting film of optical grade 2.5D according to claim 1, which is characterized in that the curing agent is ammonia second
Base piperazine, trimethylhexamethylenediamine or m-xylene diamine.
7. the super soft screen protecting film of optical grade 2.5D according to claim 1, which is characterized in that the silane coupling agent is
Gamma-amino propyl trimethoxy silicane, γ aminopropyltriethoxy silane or beta-aminoethyl-gamma-amino hydroxypropyl methyl two
Ethoxysilane.
8. the super soft screen protecting film of optical grade 2.5D according to claim 1, which is characterized in that the organic solvent is second
Alcohol or propylene glycol solution.
9. the super soft screen protecting film of optical grade 2.5D described according to claim 1 ~ any one of 8, which is characterized in that the light
The preparation method of the super soft screen protecting film of classes and grades in school 2.5D includes the following steps: to claim polyvinyl chloride, poly- carbonic acid respectively according to the proportion
Ester, polypropylene, the epoxy resin melting mixing at 200 ~ 250 DEG C, are stirred to react 20 ~ 40min, add polyether polyol, sky
Heart glass micro mist, polyethyleneglycol diacrylate and 20 ~ 30 weight parts organic solvents, are stirred under 300 ~ 400 revs/min of revolving speed
10 ~ 15min is uniformly mixed, then mixture is transferred in kneading machine, and silane coupling agent, curing agent, anti-aging agent, increasing is added
Agent and remaining organic solvent are moulded, 10 ~ 20min is kneaded, forms to get the protective film.