CN106634302A - Explosion-proof film applied to mobile phone screen - Google Patents
Explosion-proof film applied to mobile phone screen Download PDFInfo
- Publication number
- CN106634302A CN106634302A CN201611141924.9A CN201611141924A CN106634302A CN 106634302 A CN106634302 A CN 106634302A CN 201611141924 A CN201611141924 A CN 201611141924A CN 106634302 A CN106634302 A CN 106634302A
- Authority
- CN
- China
- Prior art keywords
- parts
- explosion
- mobile phone
- coating
- proof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an explosion-proof film applied to mobile phone screen. The explosion-proof film comprises a PET carrier layer. One surface of the PET carrier layer is covered by an explosion-proof layer formed by painting a paint, which comprises the following components in parts by weight: 5 to 25 parts of active carbon prepared from walnut shells, 15 to 90 parts of ethyl acetate, 20 to 60 parts of nano silicon dioxide, 0.1 to 8 parts of siloxane acrylate, 1 to 20 parts of nano titanium dioxide, 1 to 20 parts of polystyrene, 5 to 25 parts of ethylene/vinyl alcohol copolymer, 20 to 100 parts of light cured acrylic glue, and 5 to 35 parts of polyvinylidene fluoride. The provided explosion-proof film has the advantages f high transparency, good UV resisting effect, and high surface hardness, can relieve various impacts and protect the screen, and can be applied to the field of mobile phone films.
Description
Technical field
The present invention relates to thin film technique field, specifically a kind of explosion-proof thin film being used on mobile phone screen.
Background technology
Sticking film for mobile phone also known as mobile phone cosmetic membrane, safeguard film for cellular phone be can be used for mounting handset surface, screen and other
A kind of cold lamination film of visible object, species is various, and sticking film for mobile phone is not limited only to mounting mobile phone, additionally can with mounting MP3,
MP4, computer screen, mouse, audio amplifier and it is any need to do the physical item protected, because it is initially widely used in the beauty of mobile phone, because
This and gain the name " sticking film for mobile phone ", can take on an entirely new look because of the mobile phone after sticking film for mobile phone mounting, light it is brilliant, not only can rise
To the effect of old machine renovation, and can with waterproof, prevent dust from entering keyboard, screen, play a part of protection, therefore people are again
Custom is called mobile phone cosmetic membrane, safeguard film for cellular phone.But existing mobile phone is it sometimes appear that blast, very big wound is caused to human body
Evil, existing sticking film for mobile phone does not possess alleviation and collides function, it is impossible to protect screen not rupture.
The content of the invention
It is an object of the invention to provide a kind of transparency is high, preventing ultraviolet effect is good, case hardness is high is used in handss
Explosion-proof thin film on machine screen, to solve the problems, such as above-mentioned background technology in propose.
For achieving the above object, the present invention provides following technical scheme:
A kind of explosion-proof thin film being used on mobile phone screen, including pet vector layer, the one side of pet vector layer has by applying
The explosion-proof layer that material coating is formed, the coating includes according to the raw material of weight portion:Walnut shell activated carbon 5-25 parts, ethyl acetate
15-90 parts, nano silicon 20-60 parts, silicone acrylate 0.1-8 parts, nano titanium oxide 1-20 parts, polystyrene
1-20 parts, ethylene/vinyl alcohol copolymer 5-25 parts, light-cured acrylic glue 20-100 parts, Kynoar 5-35 parts.
As further scheme of the invention:The coating includes according to the raw material of weight portion:Walnut shell activated carbon 8-20
Part, ethyl acetate 20-85 part, nano silicon 25-55 parts, silicone acrylate 0.1-6 parts, nano titanium oxide 3-15
Part, polystyrene 1-15 parts, ethylene/vinyl alcohol copolymer 8-20 parts, light-cured acrylic glue 25-95 parts, Kynoar
10-30 parts.
As further scheme of the invention:The coating, includes according to the raw material of weight portion:Walnut shell activated carbon 10-
15 parts, ethyl acetate 25-80 part, nano silicon 30-50 parts, silicone acrylate 0.2-5 parts, nano titanium oxide 5-
10 parts, polystyrene 2-10 parts, ethylene/vinyl alcohol copolymer 10-15 parts, light-cured acrylic glue 30-90 parts, polyvinylidene fluoride
Alkene 15-25 parts.
The preparation method of the explosion-proof thin film being used on mobile phone screen, comprises the following steps:Coating is configured:By Semen Juglandiss
Shell activated carbon, ethyl acetate, nano silicon, silicone acrylate, nano titanium oxide, polystyrene, ethylene/vinyl
It is sufficiently stirred for after alcohol copolymer, light-cured acrylic glue, Kynoar mixing, standing obtains final product coating in more than 12 hours.Apply
Cloth:The coating for preparing is spread evenly across into the laminated formation explosion-proof layer of pet vector, coating linear speed is 15-25m/s, coating thickness
For 2-15 μm, baking, UV sizings obtain final product explosion-proof thin film.
Compared with prior art, the invention has the beneficial effects as follows:
The explosion-proof thin film that the present invention is provided has the advantages that transparency is high, preventing ultraviolet effect is good, case hardness is high, and
It is also equipped with alleviating and collides function, screen can be protected not rupture, can be used for sticking film for mobile phone field.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than the embodiment of whole.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
Embodiment 1
In the embodiment of the present invention, a kind of explosion-proof thin film being used on mobile phone screen, including pet vector layer, pet vector layer
One side there is the explosion-proof layer that formed by coatings, the coating includes according to the raw material of weight portion:Walnut shell activated carbon 5
Part, 15 parts of ethyl acetate, 20 parts of nano silicon, 0.1 part of silicone acrylate, 1 part of nano titanium oxide, polystyrene
1 part, 5 parts of ethylene/vinyl alcohol copolymer, 20 parts of light-cured acrylic glue, 5 parts of Kynoar.
The preparation method of the explosion-proof thin film being used on mobile phone screen, comprises the following steps:
1) coating configuration:By walnut shell activated carbon, ethyl acetate, nano silicon, silicone acrylate, nanometer two
It is sufficiently stirred for after titanium oxide, polystyrene, ethylene/vinyl alcohol copolymer, light-cured acrylic glue, Kynoar mixing,
Standing obtains final product coating in more than 12 hours.
2) it is coated with:By step 1) coating for preparing is spread evenly across the laminated formation explosion-proof layer of pet vector, and coating linear speed is
15m/s, coating thickness is 2 μm, baking, UV sizings, obtains final product explosion-proof thin film.
Embodiment 2
In the embodiment of the present invention, a kind of explosion-proof thin film being used on mobile phone screen, including pet vector layer, pet vector layer
One side there is the explosion-proof layer that formed by coatings, the coating includes according to the raw material of weight portion:Walnut shell activated carbon 25
Part, 90 parts of ethyl acetate, 60 parts of nano silicon, 8 parts of silicone acrylate, 20 parts of nano titanium oxide, polystyrene
20 parts, 25 parts of ethylene/vinyl alcohol copolymer, 100 parts of light-cured acrylic glue, 35 parts of Kynoar.
The preparation method of the explosion-proof thin film being used on mobile phone screen, comprises the following steps:
1) coating configuration:By walnut shell activated carbon, ethyl acetate, nano silicon, silicone acrylate, nanometer two
It is sufficiently stirred for after titanium oxide, polystyrene, ethylene/vinyl alcohol copolymer, light-cured acrylic glue, Kynoar mixing,
Standing obtains final product coating in more than 12 hours.
2) it is coated with:By step 1) coating for preparing is spread evenly across the laminated formation explosion-proof layer of pet vector, and coating linear speed is
25m/s, coating thickness is 15 μm, baking, UV sizings, obtains final product explosion-proof thin film.
Embodiment 3
In the embodiment of the present invention, a kind of explosion-proof thin film being used on mobile phone screen, including pet vector layer, pet vector layer
One side there is the explosion-proof layer that formed by coatings, the coating includes according to the raw material of weight portion:Walnut shell activated carbon 8
Part, 20 parts of ethyl acetate, 25 parts of nano silicon, 0.1 part of silicone acrylate, 3 parts of nano titanium oxide, polystyrene
1 part, 8 parts of ethylene/vinyl alcohol copolymer, 25 parts of light-cured acrylic glue, 10 parts of Kynoar.
The preparation method of the explosion-proof thin film being used on mobile phone screen, comprises the following steps:
1) coating configuration:By walnut shell activated carbon, ethyl acetate, nano silicon, silicone acrylate, nanometer two
It is sufficiently stirred for after titanium oxide, polystyrene, ethylene/vinyl alcohol copolymer, light-cured acrylic glue, Kynoar mixing,
Standing obtains final product coating in more than 12 hours.
2) it is coated with:By step 1) coating for preparing is spread evenly across the laminated formation explosion-proof layer of pet vector, and coating linear speed is
18m/s, coating thickness is 5 μm, baking, UV sizings, obtains final product explosion-proof thin film.
Embodiment 4
In the embodiment of the present invention, a kind of explosion-proof thin film being used on mobile phone screen, including pet vector layer, pet vector layer
One side there is the explosion-proof layer that formed by coatings, the coating includes according to the raw material of weight portion:Walnut shell activated carbon 20
Part, 85 parts of ethyl acetate, 55 parts of nano silicon, 6 parts of silicone acrylate, 15 parts of nano titanium oxide, polystyrene
15 parts, 20 parts of ethylene/vinyl alcohol copolymer, 95 parts of light-cured acrylic glue, 30 parts of Kynoar.
The preparation method of the explosion-proof thin film being used on mobile phone screen, comprises the following steps:
1) coating configuration:By walnut shell activated carbon, ethyl acetate, nano silicon, silicone acrylate, nanometer two
It is sufficiently stirred for after titanium oxide, polystyrene, ethylene/vinyl alcohol copolymer, light-cured acrylic glue, Kynoar mixing,
Standing obtains final product coating in more than 12 hours.
2) it is coated with:By step 1) coating for preparing is spread evenly across the laminated formation explosion-proof layer of pet vector, and coating linear speed is
22m/s, coating thickness is 12 μm, baking, UV sizings, obtains final product explosion-proof thin film.
Embodiment 5
In the embodiment of the present invention, a kind of explosion-proof thin film being used on mobile phone screen, including pet vector layer, pet vector layer
One side there is the explosion-proof layer that formed by coatings, the coating includes according to the raw material of weight portion:Walnut shell activated carbon 10
Part, 25 parts of ethyl acetate, 30 parts of nano silicon, 0.2 part of silicone acrylate, 5 parts of nano titanium oxide, polystyrene
2 parts, 10 parts of ethylene/vinyl alcohol copolymer, 30 parts of light-cured acrylic glue, 15 parts of Kynoar.
The preparation method of the explosion-proof thin film being used on mobile phone screen, comprises the following steps:
1) coating configuration:By walnut shell activated carbon, ethyl acetate, nano silicon, silicone acrylate, nanometer two
It is sufficiently stirred for after titanium oxide, polystyrene, ethylene/vinyl alcohol copolymer, light-cured acrylic glue, Kynoar mixing,
Standing obtains final product coating in more than 12 hours.
2) it is coated with:By step 1) coating for preparing is spread evenly across the laminated formation explosion-proof layer of pet vector, and coating linear speed is
20m/s, coating thickness is 8 μm, baking, UV sizings, obtains final product explosion-proof thin film.
Embodiment 6
In the embodiment of the present invention, a kind of explosion-proof thin film being used on mobile phone screen, including pet vector layer, pet vector layer
One side there is the explosion-proof layer that formed by coatings, the coating includes according to the raw material of weight portion:Walnut shell activated carbon 15
Part, 80 parts of ethyl acetate, 50 parts of nano silicon, 5 parts of silicone acrylate, 10 parts of nano titanium oxide, polystyrene
10 parts, 15 parts of ethylene/vinyl alcohol copolymer, 90 parts of light-cured acrylic glue, 25 parts of Kynoar.
The preparation method of the explosion-proof thin film being used on mobile phone screen, comprises the following steps:
1) coating configuration:By walnut shell activated carbon, ethyl acetate, nano silicon, silicone acrylate, nanometer two
It is sufficiently stirred for after titanium oxide, polystyrene, ethylene/vinyl alcohol copolymer, light-cured acrylic glue, Kynoar mixing,
Standing obtains final product coating in more than 12 hours.
2) it is coated with:By step 1) coating for preparing is spread evenly across the laminated formation explosion-proof layer of pet vector, and coating linear speed is
20m/s, coating thickness is 10 μm, baking, UV sizings, obtains final product explosion-proof thin film.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of spirit or essential attributes without departing substantially from the present invention, the present invention can be in other specific forms realized.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit is required rather than described above is limited, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.
Moreover, it will be appreciated that although this specification is been described by according to embodiment, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of description is only that for clarity those skilled in the art should
Using description as an entirety, the technical scheme in each embodiment can also Jing it is appropriately combined, form those skilled in the art
Understandable other embodiment.
Claims (3)
1. a kind of explosion-proof thin film being used on mobile phone screen, including pet vector layer, the one side of pet vector layer has by coating
The explosion-proof layer that coating is formed, it is characterised in that the coating includes according to the raw material of weight portion:Walnut shell activated carbon 5-25 parts,
Ethyl acetate 15-90 part, nano silicon 20-60 parts, silicone acrylate 0.1-8 parts, nano titanium oxide 1-20 parts,
Polystyrene 1-20 parts, ethylene/vinyl alcohol copolymer 5-25 parts, light-cured acrylic glue 20-100 parts, Kynoar 5-
35 parts.
2. the explosion-proof thin film being used on mobile phone screen according to claim 1, it is characterised in that the coating is according to weight
The raw material of amount part includes:Walnut shell activated carbon 8-20 parts, ethyl acetate 20-85 part, nano silicon 25-55 parts, siloxanes
Acrylate 0.1-6 parts, nano titanium oxide 3-15 parts, polystyrene 1-15 parts, ethylene/vinyl alcohol copolymer 8-20 parts, light
Curing acrylic glue 25-95 parts, Kynoar 10-30 parts.
3. the explosion-proof thin film being used on mobile phone screen according to claim 2, it is characterised in that the coating, according to
The raw material of weight portion includes:Walnut shell activated carbon 10-15 parts, ethyl acetate 25-80 part, nano silicon 30-50 parts, silica
Alkane acrylate 0.2-5 parts, nano titanium oxide 5-10 parts, polystyrene 2-10 parts, ethylene/vinyl alcohol copolymer 10-15 parts,
Light-cured acrylic glue 30-90 parts, Kynoar 15-25 parts.