CN104553101A - Reimpression protective film - Google Patents

Reimpression protective film Download PDF

Info

Publication number
CN104553101A
CN104553101A CN201310467015.4A CN201310467015A CN104553101A CN 104553101 A CN104553101 A CN 104553101A CN 201310467015 A CN201310467015 A CN 201310467015A CN 104553101 A CN104553101 A CN 104553101A
Authority
CN
China
Prior art keywords
coating
layer
cloudy
release
polymer solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310467015.4A
Other languages
Chinese (zh)
Other versions
CN104553101B (en
Inventor
金闯
张庆杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Stick new materials Polytron Technologies Inc
Original Assignee
Suzhou Sidike New Material Science and Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to CN201610574835.7A priority Critical patent/CN106183317A/en
Priority to CN201610795667.4A priority patent/CN106398571A/en
Priority to CN201310467015.4A priority patent/CN104553101B/en
Priority to CN201610795668.9A priority patent/CN106398572A/en
Priority to CN201610795761.XA priority patent/CN106381082A/en
Priority to CN201610795610.4A priority patent/CN106318261A/en
Priority to CN201610792081.2A priority patent/CN106381081A/en
Priority to CN201610574885.5A priority patent/CN106189888A/en
Application filed by Suzhou Sidike New Material Science and Technology Co Ltd filed Critical Suzhou Sidike New Material Science and Technology Co Ltd
Priority to CN201610792022.5A priority patent/CN106318260A/en
Publication of CN104553101A publication Critical patent/CN104553101A/en
Application granted granted Critical
Publication of CN104553101B publication Critical patent/CN104553101B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

A reimpression protective film contains a substrate layer, a reimpression coating, an organosilicon pressure-sensitive adhesive layer and matt release paper. The matt release paper is formed by successively stacking a first lamination layer, a release paper raw paper layer, a second lamination layer, a matt coating and a release agent coating. The lamination layers are respectively coated with a matt coating agent. The reimpression protective film is obtained by the following technology: 0.3-1 part of nano-SiO2 powder, 0.2-0.6 part of nano-Al2O3 powder and 0.3-1 part of a silane coupling agent are added into 8-10 parts of toluene and ultrasonic treatment is carried out to obtain a pre-dispersion liquid; 100 parts of vinyl siloxane and 0.3-1 part of hydrosiloxane are added into 120-150 parts of butanone and mechanical agitation is performed to obtain a polymer solution; the pre-dispersion liquid and the polymer solution are mixed, and mechanical agitation and ultrasonic agitation are successively carried out; and 0.2-0.5 part of platinum is added into the modulated polymer solution, and mechanical agitation and ultrasonic agitation are successively carried out. By the use of the reimpression protective film, the organosilicon rubber surface has a good haze effect, and the rubber surface achieves a low-reflectivity effect. In addition, surface roughness uniformity of the matt coating which contacts with the release agent coating is enhanced.

Description

New print diaphragm
Technical field
The present invention relates to a kind of diaphragm, particularly a kind of new print diaphragm.
Background technology
The products such as film face-plate is Mobile phone touch button such as, thin film switch are in carrying and use procedure, and its surface is easily subject to contact staining or polishing scratch scratches, and usually adopt diaphragm to cover its surface and make it from damage and pollute.Diaphragm is generally made up of substrate layer and the adhesive layer be coated on this substrate layer.When diaphragm is used for protecting various film face-plate such as Mobile phone touch button, during the products such as thin film switch surperficial, need printing word, pattern etc. on diaphragm, traditional diaphragm is general all not through wear-resisting new print process, is therefore difficult to carry out presswork on diaphragm; Secondly; when in new print diaphragm, release liners attaches with the pad pasting being coated with trowel adhesive; the mould release coating in release liners is easily caused to be taken away by the adhesive that adhesion is larger; thus form in the local surfaces of pad pasting the mould release coating area being difficult to clean out, destroy pure, the uniformity of pad pasting entirety.
Summary of the invention
The invention provides a kind of new print diaphragm, this new print diaphragm makes organic silica gel face mist degree effective, makes glue face reach low reflecting effect; And improve the cloudy surface Coating Surface Roughness uniformity with mould release coating layer touch, solve the leaching membrane layer of release liners and the technical problem of mould release coating binding force instability, be conducive to peeling off and avoiding residual pressure sensitive adhesive and mould release is residued on pressure-sensitive adhesive layer.
For achieving the above object, the technical solution used in the present invention is: a kind of new print diaphragm, comprise a substrate layer, this substrate layer applied atop one is for the new print coating of printing-ink, this substrate layer lower surface is bonded with a cloudy-surface release paper by silicone pressure sensitive glue-line and is connected, described cloudy-surface release paper is stacked gradually by the first leaching membrane layer, release liners original paper layer, the second leaching membrane layer, cloudy surface coating and mould release coating and forms, and described cloudy surface coating is 2.821um ~ 3.324um towards the surface roughness on the surface of described mould release coating; Described preparation technology forms primarily of the following step:
The first step: in the both side surface of release liners body paper, with film machine each film one deck leaching membrane layer, then cools;
Second step: apply the cloudy surface coating agent that a layer thickness is 0.2 ~ 2 micron on any leaching membrane layer, this cloudy surface coating agent obtains further by following technique:
Step 1. is by 0.3 ~ 1 part of Nano-meter SiO_2 2powder, 0.2 ~ 0.6 part of nanometer Al 2o 3powder and 0.3 ~ 1 part of silane coupler add in 8 ~ 10 parts of toluene and carry out ultrasonic wave process and obtain pre-dispersed liquid;
100 parts of vinylsiloxanes, 0.3 ~ 1 part of hydrogen-containing siloxane add in 120 ~ 150 parts of butanone by step 2. to carry out mechanical agitation and obtains polymer solution;
The mixing of the polymer solution of the pre-dispersed liquid of step 1, step 2 is also carried out mechanical agitation to step 3. successively and ultrasonic wave stirs, thus obtain the polymer solution after modulation;
The polymer solution of step 4. after described modulation adds 0.2 ~ 0.5 part of platinum and carries out mechanical agitation and the release solvent of the ultrasonic wave stirring described cloudy surface of acquisition successively;
3rd step: the cloudy surface coating agent of release liners is carried out polymerisation by baking and obtains cloudy surface coating;
4th step: apply one deck mould release coating on the surface of described cloudy surface coating.
The technical scheme improved further in technique scheme is as follows:
1. in such scheme, described Nano-meter SiO_2 2the diameter range of powder is 10 ~ 15nm, described nanometer Al 2o 3the diameter range of powder is 25 ~ 35nm.
2., in such scheme, the material of first, second leaching membrane layer described is PETG, polypropylene, polyethylene or polyvinyl chloride.
Because technique scheme is used, the present invention compared with prior art has following advantages and effect:
New print diaphragm of the present invention, the Nano-meter SiO_2 of special diameter and content 2powder, nanometer Al 2o 3powder under solvent with silane coupler through ultrasonic wave acting in conjunction, and mechanical agitation and ultrasonic wave stir combination, are conducive to Nano-meter SiO_2 2powder, Al 2o 3powder is evenly distributed, and specific polymer solution and pre-dispersed liquid adopt different solvents, reduces Nano-meter SiO_2 2powder, Al 2o 3the surface energy of particle, be beneficial to powder granule dispersion in a solvent further, improve the cloudy surface Coating Surface Roughness uniformity with mould release coating layer touch, solve the leaching membrane layer of release liners and the technical problem of mould release coating binding force instability, be conducive to peeling off and avoiding residual pressure sensitive adhesive and mould release is residued on pressure-sensitive adhesive layer.
Accompanying drawing explanation
Accompanying drawing 1 is new print diaphragm structural representation of the present invention;
Accompanying drawing 2a is cloudy surface coating microscopic appearance SEM resolution chart in existing new print diaphragm;
Accompanying drawing 2b is cloudy surface coating microscopic appearance SEM resolution chart in new print diaphragm of the present invention.
In above accompanying drawing: 1, substrate layer; 2, new print coating; 3, silicone pressure sensitive glue-line; 4, cloudy-surface release paper; 5, the first leaching membrane layer; 6, release liners original paper layer; 7, the second leaching membrane layer; 8, cloudy surface coating; 9, mould release coating.
Detailed description of the invention
Below in conjunction with drawings and Examples, the invention will be further described:
Embodiment 1 ~ 5: a kind of new print diaphragm, comprise a substrate layer 1, this substrate layer 1 applied atop one is for the new print coating 2 of printing-ink, this substrate layer 1 lower surface is bonded with a cloudy-surface release paper 4 by silicone pressure sensitive glue-line 3 and is connected, described cloudy-surface release paper 4 is stacked gradually by the first leaching membrane layer 5, release liners original paper layer 6, second leaching membrane layer 7, cloudy surface coating 8 and mould release coating 9 and forms, and described cloudy surface coating is 2.821um ~ 3.324um towards the surface roughness on the surface of mould release coating; Described preparation technology forms primarily of the following step:
The first step: in the both side surface of release liners body paper, with film machine each film one deck leaching membrane layer, then cools;
Second step: apply the cloudy surface coating agent that a layer thickness is 0.2 ~ 2 micron on any leaching membrane layer, this cloudy surface coating agent obtains further by following technique:
Step 1. is by 0.3 ~ 1 part of Nano-meter SiO_2 2powder, 0.2 ~ 0.6 part of nanometer Al 2o 3powder and 0.3 ~ 1 part of silane coupler add in 8 ~ 10 parts of toluene and carry out ultrasonic wave process and obtain pre-dispersed liquid;
100 parts of vinylsiloxanes, 0.3 ~ 1 part of hydrogen-containing siloxane add in 120 ~ 150 parts of butanone by step 2. to carry out mechanical agitation and obtains polymer solution;
The mixing of the polymer solution of the pre-dispersed liquid of step 1, step 2 is also carried out mechanical agitation to step 3. successively and ultrasonic wave stirs, thus obtain the polymer solution after modulation;
The polymer solution of step 4. after described modulation adds 0.2 ~ 0.5 part of platinum and carries out mechanical agitation and the release solvent of the ultrasonic wave stirring described cloudy surface of acquisition successively;
The each ingredients weight parts content of embodiment 1 ~ 5 cloudy surface coating is in table 1.
Table 1
Embodiment one Embodiment two Embodiment three Embodiment four Embodiment five
Vinylsiloxane 100 parts 100 parts 100 parts 100 parts 100 parts
Hydrogen-containing siloxane 0.3 part 0.5 part 0.4 part 0.35 part 0.9 part
Nano-meter SiO_2 2Powder 0.5 part 0.6 part 1 part 0.8 part 0.4 part
Nanometer Al 2O 3Powder 0.45 part 0.25 part 0.2 part 0.5 part 0.6 part
Silane coupler 0.35 part 1 part 0.4 part 0.45 part 0.9 part
Toluene 8 ~ 10 parts 8 parts 8.5 part 9 parts 8 parts
Butanone 120 parts 125 parts 150 parts 135 parts 130 parts
3rd step: the cloudy surface coating agent of release liners is carried out polymerisation by baking and obtains cloudy surface coating;
4th step: apply one deck mould release coating on the surface of described cloudy surface coating.
Above-mentioned Nano-meter SiO_2 2the diameter range of powder is 12nm, described nanometer Al 2o 3the diameter range of powder is 30nm.
In above-described embodiment 1, the material of first, second leaching membrane layer is respectively PETG, polypropylene, in embodiment 2, the material of first, second leaching membrane layer is respectively polypropylene, polyethylene, in embodiment 3, the material of first, second leaching membrane layer is respectively polypropylene, in embodiment 4, the material of first, second leaching membrane layer is respectively polyethylene, polyvinyl chloride, and in embodiment 5, the material of first, second leaching membrane layer is respectively PETG, polyvinyl chloride.
Above-described embodiment, only for technical conceive of the present invention and feature are described, its object is to person skilled in the art can be understood content of the present invention and implement according to this, can not limit the scope of the invention with this.All equivalences done according to Spirit Essence of the present invention change or modify, and all should be encompassed within protection scope of the present invention.

Claims (3)

1. a new print diaphragm, comprise a substrate layer (1), this substrate layer (1) applied atop one is for the new print coating (2) of printing-ink, this substrate layer (1) lower surface is bonded with a cloudy-surface release paper (4) by silicone pressure sensitive glue-line (3) and is connected, it is characterized in that: described cloudy-surface release paper (4) is by the first leaching membrane layer (5), release liners original paper layer (6), second leaching membrane layer (7), cloudy surface coating (8) and mould release coating (9) stack gradually formation, described cloudy surface coating is 2.821um ~ 3.324um towards the surface roughness on the surface of mould release coating, described preparation technology forms primarily of the following step:
The first step: in the both side surface of release liners body paper, with film machine each film one deck leaching membrane layer, then cools;
Second step: apply the cloudy surface coating agent that a layer thickness is 0.2 ~ 2 micron on any leaching membrane layer, this cloudy surface coating agent obtains further by following technique:
Step 1. is by 0.3 ~ 1 part of Nano-meter SiO_2 2powder, 0.2 ~ 0.6 part of nanometer Al 2o 3powder and 0.3 ~ 1 part of silane coupler add in 8 ~ 10 parts of toluene and carry out ultrasonic wave process and obtain pre-dispersed liquid;
100 parts of vinylsiloxanes, 0.3 ~ 1 part of hydrogen-containing siloxane add in 120 ~ 150 parts of butanone by step 2. to carry out mechanical agitation and obtains polymer solution;
The mixing of the polymer solution of the pre-dispersed liquid of step 1, step 2 is also carried out mechanical agitation to step 3. successively and ultrasonic wave stirs, thus obtain the polymer solution after modulation;
The polymer solution of step 4. after described modulation adds 0.2 ~ 0.5 part of platinum and carries out mechanical agitation and the release solvent of the ultrasonic wave stirring described cloudy surface of acquisition successively;
3rd step: the cloudy surface coating agent of release liners is carried out polymerisation by baking and obtains cloudy surface coating;
4th step: apply one deck mould release coating on the surface of described cloudy surface coating.
2. new print diaphragm according to claim 1, is characterized in that: described Nano-meter SiO_2 2the diameter range of powder is 10 ~ 15nm, described nanometer Al 2o 3the diameter range of powder is 25 ~ 35nm.
3. new print diaphragm according to claim 1, is characterized in that: the material of first, second leaching membrane layer described is PETG, polypropylene, polyethylene or polyvinyl chloride.
CN201310467015.4A 2013-10-09 2013-10-09 reimpression protective film Active CN104553101B (en)