CN107857951A - A kind of explosion-proof pad pasting of cell phone screen glass - Google Patents
A kind of explosion-proof pad pasting of cell phone screen glass Download PDFInfo
- Publication number
- CN107857951A CN107857951A CN201711043334.7A CN201711043334A CN107857951A CN 107857951 A CN107857951 A CN 107857951A CN 201711043334 A CN201711043334 A CN 201711043334A CN 107857951 A CN107857951 A CN 107857951A
- Authority
- CN
- China
- Prior art keywords
- parts
- explosion
- pad pasting
- proof pad
- phone screen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of plastic sheeting, and in particular to a kind of explosion-proof pad pasting of cell phone screen glass, belongs to safeguard film for cellular phone technical field.Explosion-proof pad pasting, include each component of following parts by weight:20 30 parts of acrylic resin, 40 50 parts of polyvinyl chloride, 6 10 parts of calcium phosphate, 2 12 parts of silica, 17 parts of phenmethylol, 5 10 parts of two molybdenum of boronation, 38 parts of glass fibre element, 26 parts of 2 hydroxyl, 4 methoxy benzophenone, 25 parts of polyphenylene sulfide, 49 parts of titanium dioxide.The present invention passes through acrylic resin, polyvinyl chloride, calcium phosphate; silica, phenmethylol, the molybdenum of boronation two; glass fibre element; the methoxy benzophenone of 2 hydroxyl 4, polyphenylene sulfide, the compounding of titanium dioxide; by being acted synergistically between raw material; explosion-proof film provided by the invention has the advantages that transparency is high, preventing ultraviolet effect is good, case hardness is high, and is also equipped with alleviating and collides function, screen can be protected not rupture.
Description
Technical field
The present invention relates to a kind of plastic sheeting, and in particular to a kind of explosion-proof pad pasting of cell phone screen glass, belongs to mobile phone guarantor
Cuticula technical field.
Background technology
With expanding economy, people become increasingly to be unable to do without mobile phone, and mobile phone has become the one of people's life
Part, but the screen of mobile phone influences the service life of mobile phone, therefore, sticking film for mobile phone becomes necessity, and mobile phone is protected intolerant to scratch
Cuticula is a kind of cold lamination film available for mounting handset surface, screen and other visible objects, and species is various.Diaphragm rises
To effect be exactly to protect, spent some months, film taken off, mobile phone or brand-new!There is no any abrasion and spot!But market
On pad pasting, generally existing is easily broken, wear-resisting low intensity, the shortcomings that easily scratch, be have impact on the service life of pad pasting, is influenceed simultaneously
The feel of user.
The content of the invention
Gathered it is an object of the invention to provide a kind of cell phone screen glass with explosion-proof pad pasting, the present invention by acrylic resin
Vinyl chloride, calcium phosphate, silica, phenmethylol, the molybdenum of boronation two, glass fibre element, ESCALOL 567, gather
Diphenyl sulfide, the compounding of titanium dioxide, by being acted synergistically between raw material, explosion-proof film provided by the invention have transparency it is high,
The advantages that preventing ultraviolet effect is good, case hardness is high, and be also equipped with alleviating and collide function, screen can be protected not rupture.
The purpose of the present invention is achieved through the following technical solutions, a kind of explosion-proof pad pasting of cell phone screen glass, and it is special
Sign is that the explosion-proof pad pasting of Mobile phone screen film glass includes each component of following parts by weight:Acrylic resin 20-30 parts, polychlorostyrene second
Alkene 40-50 parts, calcium phosphate 6-10 parts, silica 2-12 parts, phenmethylol 1-7 parts, the molybdenum 5-10 parts of boronation two, glass fibers
Tie up plain 3-8 parts, ESCALOL 567 2-6 parts, polyphenylene sulfide 2-5 parts, titanium dioxide 4-9 parts.
Preferably, the explosion-proof pad pasting of Mobile phone screen film glass includes each component of following parts by weight:Acrylic resin
20.8-29.3 parts, polyvinyl chloride 41.7-49.2 parts, calcium phosphate 6.6-9.5 parts, silica 2.4-11.2 parts, phenmethylol
1.5-6.4 parts, the molybdenum 5.3-9.6 parts of boronation two, glass fibre element 3.6-7.4 parts, ESCALOL 567
2.2-5.7 parts, polyphenylene sulfide 2.3-4.6 parts, titanium dioxide 4.8-8.6 parts.
Preferably, the explosion-proof pad pasting of Mobile phone screen film glass includes each component of following parts by weight:Acrylic resin
21.6-28.0 parts, polyvinyl chloride 42.5-48.4 parts, calcium phosphate 7.0-9.1 parts, silica 2.9-10.6 parts, phenmethylol
2.0-5.9 parts, the molybdenum 5.9-9.0 parts of boronation two, glass fibre element 4.1-6.8 parts, ESCALOL 567
2.8-5.0 parts, polyphenylene sulfide 2.7-4.2 parts, titanium dioxide 5.2-8.1 parts.
Preferably, the explosion-proof pad pasting of Mobile phone screen film glass includes each component of following parts by weight:Acrylic resin
23.2-26.4 parts, polyvinyl chloride 43.8-47.0 parts, calcium phosphate 7.4-8.6 parts, silica 4.2-9.3 parts, phenmethylol
2.8-5.1 parts, the molybdenum 6.4-8.2 parts of boronation two, glass fibre element 4.6-6.3 parts, ESCALOL 567
3.3-4.6 parts, polyphenylene sulfide 3.1-4.0 parts, titanium dioxide 5.8-7.5 parts.
Preferably, the explosion-proof pad pasting of Mobile phone screen film glass includes each component of following parts by weight:Acrylic resin
24.3-25.7 parts, polyvinyl chloride 44.5-46.3 parts, calcium phosphate 7.8-8.1 parts, silica 4.9-7.6 parts, phenmethylol
3.4-4.6 parts, the molybdenum 7.1-7.9 parts of boronation two, glass fibre element 5.0-5.8 parts, ESCALOL 567
3.9-4.3 parts, polyphenylene sulfide 3.3-3.8 parts, titanium dioxide 6.3-7.2 parts.
Compared with prior art, the invention has the advantages that:The present invention is by acrylic resin, polyvinyl chloride,
Calcium phosphate, silica, phenmethylol, the molybdenum of boronation two, glass fibre element, ESCALOL 567, polyphenylene sulfide,
The compounding of titanium dioxide, by being acted synergistically between raw material, explosion-proof film provided by the invention has transparency height, antiultraviolet
The advantages that effect is good, case hardness is high, and be also equipped with alleviating and collide function, screen can be protected not rupture.Mobile phone sticker of the present invention
Film has wearability effect, effectively prevents cut and scratch, has good toughness and wearability, effectively protects mobile phone, and
Cause relatively low.The present invention ensure screen glass surface it is smooth, without scratch;Lift the mechanical strength and hardness of screen glass, energy
The screen glass that output is bonded entirely, production is efficient, and product quality is stable.
Embodiment
Embodiment 1
A kind of explosion-proof pad pasting of cell phone screen glass, include each component of following percentage by weight:Acrylic resin 20-30 parts,
Polyvinyl chloride 40-50 parts, calcium phosphate 6-10 parts, silica 2-12 parts, phenmethylol 1-7 parts, the molybdenum 5-10 parts of boronation two,
Glass fibre element 3-8 parts, ESCALOL 567 2-6 parts, polyphenylene sulfide 2-5 parts, titanium dioxide 4-9 parts.
Embodiment 2
A kind of explosion-proof pad pasting of cell phone screen glass, include each component of following percentage by weight:Acrylic resin 20.8-
29.3 parts, polyvinyl chloride 41.7-49.2 parts, calcium phosphate 6.6-9.5 parts, silica 2.4-11.2 parts, phenmethylol 1.5-
6.4 parts, the molybdenum 5.3-9.6 parts of boronation two, glass fibre element 3.6-7.4 parts, ESCALOL 567 2.2-5.7
Part, polyphenylene sulfide 2.3-4.6 parts, titanium dioxide 4.8-8.6 parts.
Embodiment 3
A kind of explosion-proof pad pasting of cell phone screen glass, include each component of following percentage by weight:Acrylic resin 21.6-
28.0 parts, polyvinyl chloride 42.5-48.4 parts, calcium phosphate 7.0-9.1 parts, silica 2.9-10.6 parts, phenmethylol 2.0-
5.9 parts, the molybdenum 5.9-9.0 parts of boronation two, glass fibre element 4.1-6.8 parts, ESCALOL 567 2.8-5.0
Part, polyphenylene sulfide 2.7-4.2 parts, titanium dioxide 5.2-8.1 parts.
Embodiment 4
A kind of explosion-proof pad pasting of cell phone screen glass, include each component of following percentage by weight:Acrylic resin 23.2-
26.4 parts, polyvinyl chloride 43.8-47.0 parts, calcium phosphate 7.4-8.6 parts, silica 4.2-9.3 parts, phenmethylol 2.8-
5.1 parts, the molybdenum 6.4-8.2 parts of boronation two, glass fibre element 4.6-6.3 parts, ESCALOL 567 3.3-4.6
Part, polyphenylene sulfide 3.1-4.0 parts, titanium dioxide 5.8-7.5 parts.
Embodiment 5
A kind of explosion-proof pad pasting of cell phone screen glass, include each component of following percentage by weight:Acrylic resin 24.3-
25.7 parts, polyvinyl chloride 44.5-46.3 parts, calcium phosphate 7.8-8.1 parts, silica 4.9-7.6 parts, phenmethylol 3.4-
4.6 parts, the molybdenum 7.1-7.9 parts of boronation two, glass fibre element 5.0-5.8 parts, ESCALOL 567 3.9-4.3
Part, polyphenylene sulfide 3.3-3.8 parts, titanium dioxide 6.3-7.2 parts.
Claims (5)
1. a kind of explosion-proof pad pasting of cell phone screen glass, it is characterized in that, the explosion-proof pad pasting of Mobile phone screen film glass includes following heavy
Measure each component of part:Acrylic resin 20-30 parts, polyvinyl chloride 40-50 parts, calcium phosphate 6-10 parts, silica 2-12
Part, phenmethylol 1-7 parts, the molybdenum 5-10 parts of boronation two, glass fibre element 3-8 parts, ESCALOL 567 2-6
Part, polyphenylene sulfide 2-5 parts, titanium dioxide 4-9 parts.
2. a kind of explosion-proof pad pasting of cell phone screen glass according to claim 1, it is characterized in that, the Mobile phone screen film glass
Explosion-proof pad pasting includes each component of following parts by weight:Acrylic resin 20.8-29.3 parts, polyvinyl chloride 41.7-49.2 parts, phosphorus
Sour calcium 6.6-9.5 parts, silica 2.4-11.2 parts, phenmethylol 1.5-6.4 parts, the molybdenum 5.3-9.6 parts of boronation two, glass fibers
Tie up plain 3.6-7.4 parts, ESCALOL 567 2.2-5.7 parts, polyphenylene sulfide 2.3-4.6 parts, titanium dioxide
4.8-8.6 part.
3. a kind of explosion-proof pad pasting of cell phone screen glass according to claim 1, it is characterized in that, the Mobile phone screen film glass
Explosion-proof pad pasting includes each component of following parts by weight:Acrylic resin 21.6-28.0 parts, polyvinyl chloride 42.5-48.4 parts, phosphorus
Sour calcium 7.0-9.1 parts, silica 2.9-10.6 parts, phenmethylol 2.0-5.9 parts, the molybdenum 5.9-9.0 parts of boronation two, glass fibers
Tie up plain 4.1-6.8 parts, ESCALOL 567 2.8-5.0 parts, polyphenylene sulfide 2.7-4.2 parts, titanium dioxide
5.2-8.1 part.
4. a kind of explosion-proof pad pasting of cell phone screen glass according to claim 1, it is characterized in that, the Mobile phone screen film glass
Explosion-proof pad pasting includes each component of following parts by weight:Acrylic resin 23.2-26.4 parts, polyvinyl chloride 43.8-47.0 parts, phosphorus
Sour calcium 7.4-8.6 parts, silica 4.2-9.3 parts, phenmethylol 2.8-5.1 parts, the molybdenum 6.4-8.2 parts of boronation two, glass fibre
Plain 4.6-6.3 parts, ESCALOL 567 3.3-4.6 parts, polyphenylene sulfide 3.1-4.0 parts, titanium dioxide 5.8-
7.5 part.
5. a kind of explosion-proof pad pasting of cell phone screen glass according to claim 1, it is characterized in that, the Mobile phone screen film glass
Explosion-proof pad pasting includes each component of following parts by weight:Acrylic resin 24.3-25.7 parts, polyvinyl chloride 44.5-46.3 parts, phosphorus
Sour calcium 7.8-8.1 parts, silica 4.9-7.6 parts, phenmethylol 3.4-4.6 parts, the molybdenum 7.1-7.9 parts of boronation two, glass fibers
Tie up plain 5.0-5.8 parts, ESCALOL 567 3.9-4.3 parts, polyphenylene sulfide 3.3-3.8 parts, titanium dioxide
6.3-7.2 part.