CN109161222A - A kind of sweat-steaming house plank and preparation method thereof - Google Patents
A kind of sweat-steaming house plank and preparation method thereof Download PDFInfo
- Publication number
- CN109161222A CN109161222A CN201811101047.1A CN201811101047A CN109161222A CN 109161222 A CN109161222 A CN 109161222A CN 201811101047 A CN201811101047 A CN 201811101047A CN 109161222 A CN109161222 A CN 109161222A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- sweat
- mixture
- steaming house
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of sweat-steaming house plank and preparation method thereof, the raw material including following parts by weight: 5.2-7.6 parts of oligofructose, 16.3-19.5 parts of Tourmaline powder, 30.6-35.8 parts of wood powder, 15.4-21.3 parts of stalk powder, 9.4-10.8 parts of epoxy resin powder, 6.8-11.6 parts of low density polyethylene (LDPE), 3.4-5.7 parts of negative ion powder, 4.4-6.2 parts of zinc stearate, 38-41.2 parts of cyclohexanol, 3.3-4.5 parts of coupling agent, 14.2-16.5 parts of diatomite, 5.6-8.1 parts of crystal salt and 8.2-10.3 parts of slag.This product raw material sources are extensive, preparation process is simple, by crystal salt, the Tourmaline powder of far infrared, the negative ion powder that anion can be discharged, wood powder, slag can be discharged etc. and be used cooperatively, it can use anion, far infrared promotes the metabolism of human body, there is repair function to human body, meets the use demand of sweat-steaming house.
Description
Technical field
The present invention relates to sweat-steaming house field, specifically a kind of sweat-steaming house plank.
Background technique
With the increase and the improvement of people's living standards of people's income, more and more people like in leisure time
Be Myself Cup of tea feelings, and sweat steaming is exactly wherein common one kind.
Sweat steaming is a kind of leisure project, is one kind of thermotherapy, with a long history, deep to be liked by the common people, is the Yi great Te of South Korea
Color.The steaming of Korean style sweat is to heat yellow mud and various stones, people or seat or is lain, and for wind dispelling, Eradicates is cold, warm body promoting blood circulation, the beautiful face of warm skin,
Ancient times are the privilege enjoyment of noble or imperial family, and cultural origin is deep.With the prevalence of Korean Culture, sweat steaming also follows South Korean TV soaps closely,
Clothes, makeup, beautifying technique into China and are promptly approved and are connect by Chinese within short several years together
By, and it is increasingly becoming a kind of casual health mode that people are keen to and pursue.
Sweat-steaming house is the place for carrying out sweat steaming, mostly uses the plank production of the covering with paint paint of coating addition negative ion powder, this
Although kind of a plank can discharge a certain amount of anion, the negative ion powder of excessive addition is unable in paint, this will lead to oil
Adhesive force and the photocuring ability for painting itself die down, and contain formaldehyde components in paint, draw while accordingly generating anion
Enter air pollution, this is just that the use of people brings inconvenience.
Summary of the invention
The purpose of the present invention is to provide a kind of sweat-steaming house planks, to solve the problems mentioned in the above background technology.
To achieve the above object, the invention provides the following technical scheme:
A kind of sweat-steaming house plank, the raw material including following parts by weight: 5.2-7.6 parts of oligofructose, Tourmaline powder 16.3-
19.5 parts, 30.6-35.8 parts of wood powder, 15.4-21.3 parts of stalk powder, 9.4-10.8 parts of epoxy resin powder, low density polyethylene (LDPE)
6.8-11.6 parts, 3.4-5.7 parts of negative ion powder, 4.4-6.2 parts of zinc stearate, 38-41.2 parts of cyclohexanol, coupling agent 3.3-4.5
Part, 14.2-16.5 parts of diatomite, 5.6-8.1 parts of crystal salt and 8.2-10.3 parts of slag.
As a further solution of the present invention: the relative molecular weight of oligofructose is 480-860.
As a further solution of the present invention: stalk powder includes rice straw powder, soybean stalk powder, corn stover
At least two in powder and broomcorn straw powder.
As a further solution of the present invention: the partial size of slag is 0.12-0.27mm, negative ion powder and Tourmaline powder
Partial size is 860-950nm.
The preparation method of the sweat-steaming house plank, the specific steps are as follows:
Step 1, by Tourmaline powder, negative ion powder, crystal salt and slag 560-750 degrees Celsius calcining 80-110 minutes, so
After be uniformly mixed, obtain the first mixture；
Epoxy resin powder and low density polyethylene (LDPE) are heated to molten condition by step 2, then with the first mixture ball milling, obtain
To the second mixture；
Wood powder, stalk powder, zinc stearate and diatomite are added into cyclohexanol and ultrasonic wave are uniformly dispersed by step 3,
Obtain third mixture；
Step 4 stirs evenly oligofructose, the second mixture, third mixture and coupling agent in high-speed mixer,
Then it squeezes out, cooling and shaping, cuts after drawing to get finished product is arrived in double screw extruder.
As a further solution of the present invention: the power of ultrasonic wave is 80-110W in step 3, and the frequency of ultrasonic wave is
25-33KHz。
Compared with prior art, the beneficial effects of the present invention are: this product raw material sources are extensive, preparation process is simple, will
Crystal salt, the cooperation such as can discharge the Tourmaline powder of far infrared, the negative ion powder that anion can be discharged, wood powder, slag
It uses, can use the metabolism of anion, far infrared promotion human body, have repair function to human body, meet sweat-steaming house
Use demand.
Specific embodiment
The technical solution of the patent is explained in further detail With reference to embodiment.
Embodiment 1
A kind of sweat-steaming house plank, the raw material including following parts by weight: 5.2 parts of oligofructose, 16.3 parts of Tourmaline powder, wood powder
30.6 parts, 15.4 parts of stalk powder, 9.4 parts of epoxy resin powder, 6.8 parts of low density polyethylene (LDPE), 3.4 parts of negative ion powder, stearic acid
4.4 parts of zinc, 38 parts of cyclohexanol, 3.3 parts of coupling agent, 14.2 parts of diatomite, 5.6 parts of crystal salt and 8.2 parts of slag.Stalk powder packet
Include the mixture of rice straw powder, soybean stalk powder and broomcorn straw powder.
The preparation method of the sweat-steaming house plank, the specific steps are as follows:
Step 1 calcines Tourmaline powder, negative ion powder, crystal salt and slag 90 minutes at 580 degrees Celsius, and then mixing is equal
It is even, obtain the first mixture；
Epoxy resin powder and low density polyethylene (LDPE) are heated to molten condition by step 2, then with the first mixture ball milling, obtain
To the second mixture；
Wood powder, stalk powder, zinc stearate and diatomite are added into cyclohexanol and ultrasonic wave are uniformly dispersed by step 3,
Obtain third mixture；
Step 4 stirs evenly oligofructose, the second mixture, third mixture and coupling agent in high-speed mixer,
Then it squeezes out, cooling and shaping, cuts after drawing to get finished product is arrived in double screw extruder.
Embodiment 2
A kind of sweat-steaming house plank, the raw material including following parts by weight: 6.3 parts of oligofructose, 17.4 parts of Tourmaline powder, wood powder
32.5 parts, 17.6 parts of stalk powder, 9.9 parts of epoxy resin powder, 8.4 parts of low density polyethylene (LDPE), 3.9 parts of negative ion powder, stearic acid
5.1 parts of zinc, 38.8 parts of cyclohexanol, 3.9 parts of coupling agent, 15.2 parts of diatomite, 6.3 parts of crystal salt and 9.1 parts of slag.The grain of slag
Diameter is 0.24mm, and the partial size of negative ion powder and Tourmaline powder is 880nm.
The preparation method of the sweat-steaming house plank, the specific steps are as follows:
Step 1 calcines Tourmaline powder, negative ion powder, crystal salt and slag 90 minutes at 720 degrees Celsius, and then mixing is equal
It is even, obtain the first mixture；
Epoxy resin powder and low density polyethylene (LDPE) are heated to molten condition by step 2, then with the first mixture ball milling, obtain
To the second mixture；
Wood powder, stalk powder, zinc stearate and diatomite are added into cyclohexanol and ultrasonic wave are uniformly dispersed by step 3,
The power of ultrasonic wave is 105W, and the frequency of ultrasonic wave is 28KHz, obtains third mixture；
Step 4 stirs evenly oligofructose, the second mixture, third mixture and coupling agent in high-speed mixer,
Then it squeezes out, cooling and shaping, cuts after drawing to get finished product is arrived in double screw extruder.
Embodiment 3
A kind of sweat-steaming house plank, the raw material including following parts by weight: 7.3 parts of oligofructose, 18.9 parts of Tourmaline powder, wood powder
34.7 parts, 20.6 parts of stalk powder, 10.6 parts of epoxy resin powder, 10.8 parts of low density polyethylene (LDPE), 5.2 parts of negative ion powder, tristearin
6 parts of sour zinc, 40.8 parts of cyclohexanol, 4.3 parts of coupling agent, 16.1 parts of diatomite, 7.7 parts of crystal salt and 9.9 parts of slag.Oligofructose
Relative molecular weight be 480-660.Stalk powder includes the mixture of rice straw powder and broomcorn straw powder.
The preparation method of the sweat-steaming house plank, the specific steps are as follows:
Step 1 calcines Tourmaline powder, negative ion powder, crystal salt and slag 96 minutes at 720 degrees Celsius, and then mixing is equal
It is even, obtain the first mixture；
Epoxy resin powder and low density polyethylene (LDPE) are heated to molten condition by step 2, then with the first mixture ball milling, obtain
To the second mixture；
Wood powder, stalk powder, zinc stearate and diatomite are added into cyclohexanol and ultrasonic wave are uniformly dispersed by step 3,
Obtain third mixture；
Step 4 stirs evenly oligofructose, the second mixture, third mixture and coupling agent in high-speed mixer,
Then it squeezes out, cooling and shaping, cuts after drawing to get finished product is arrived in double screw extruder.
Embodiment 4
A kind of sweat-steaming house plank, the raw material including following parts by weight: 7.6 parts of oligofructose, 19.5 parts of Tourmaline powder, wood powder
35.8 parts, 21.3 parts of stalk powder, 10.8 parts of epoxy resin powder, 11.6 parts of low density polyethylene (LDPE), 5.7 parts of negative ion powder, tristearin
6.2 parts of sour zinc, 41.2 parts of cyclohexanol, 4.5 parts of coupling agent, 16.5 parts of diatomite, 8.1 parts of crystal salt and 10.3 parts of slag.It is oligomeric
The relative molecular weight of fructose is 520-780.Stalk powder includes rice straw powder, soybean stalk powder, maize straw powder
With the mixture of broomcorn straw powder.The partial size of slag is 0.16mm, and the partial size of negative ion powder and Tourmaline powder is
910nm。
The preparation method of the sweat-steaming house plank, the specific steps are as follows:
Step 1 calcines Tourmaline powder, negative ion powder, crystal salt and slag 88 minutes at 590 degrees Celsius, and then mixing is equal
It is even, obtain the first mixture；
Epoxy resin powder and low density polyethylene (LDPE) are heated to molten condition by step 2, then with the first mixture ball milling, obtain
To the second mixture；
Wood powder, stalk powder, zinc stearate and diatomite are added into cyclohexanol and ultrasonic wave are uniformly dispersed by step 3,
The power of ultrasonic wave is 85W, and the frequency of ultrasonic wave is 29KHz, obtains third mixture；
Step 4 stirs evenly oligofructose, the second mixture, third mixture and coupling agent in high-speed mixer,
Then it squeezes out, cooling and shaping, cuts after drawing to get finished product is arrived in double screw extruder.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (6)
1. a kind of sweat-steaming house plank, which is characterized in that the raw material including following parts by weight: 5.2-7.6 parts of oligofructose, Tuo Ma
It is 16.3-19.5 parts of beautiful jade powder, 30.6-35.8 parts of wood powder, 15.4-21.3 parts of stalk powder, 9.4-10.8 parts of epoxy resin powder, low
6.8-11.6 parts of density polyethylene, 3.4-5.7 parts of negative ion powder, 4.4-6.2 parts of zinc stearate, 38-41.2 parts of cyclohexanol, coupling
3.3-4.5 parts of agent, 14.2-16.5 parts of diatomite, 5.6-8.1 parts of crystal salt and 8.2-10.3 parts of slag.
2. sweat-steaming house plank according to claim 1, which is characterized in that the relative molecular weight of the oligofructose is
480-860。
3. sweat-steaming house plank according to claim 1, which is characterized in that the stalk powder includes rice straw powder
At least two in end, soybean stalk powder, maize straw powder and broomcorn straw powder.
4. sweat-steaming house plank according to claim 1, which is characterized in that the partial size of the slag is 0.12-0.27mm,
The partial size of negative ion powder and Tourmaline powder is 860-950nm.
5. a kind of preparation method of the sweat-steaming house plank as described in claim 1-4 is any, which is characterized in that specific steps are such as
Under:
Step 1, by Tourmaline powder, negative ion powder, crystal salt and slag 560-750 degrees Celsius calcining 80-110 minutes, so
After be uniformly mixed, obtain the first mixture；
Epoxy resin powder and low density polyethylene (LDPE) are heated to molten condition by step 2, then with the first mixture ball milling, obtain
To the second mixture；
Wood powder, stalk powder, zinc stearate and diatomite are added into cyclohexanol and ultrasonic wave are uniformly dispersed by step 3,
Obtain third mixture；
Step 4 stirs evenly oligofructose, the second mixture, third mixture and coupling agent in high-speed mixer,
Then it squeezes out, cooling and shaping, cuts after drawing to get finished product is arrived in double screw extruder.
6. the preparation method of sweat-steaming house plank according to claim 5, which is characterized in that ultrasonic wave in the step 3
Power be 80-110W, the frequency of ultrasonic wave is 25-33KHz.