CN109160827A - A kind of red glaze golden flower paper decoration firing method of low temperature - Google Patents
A kind of red glaze golden flower paper decoration firing method of low temperature Download PDFInfo
- Publication number
- CN109160827A CN109160827A CN201811288475.XA CN201811288475A CN109160827A CN 109160827 A CN109160827 A CN 109160827A CN 201811288475 A CN201811288475 A CN 201811288475A CN 109160827 A CN109160827 A CN 109160827A
- Authority
- CN
- China
- Prior art keywords
- low temperature
- red glaze
- golden flower
- firing method
- red
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to ceramic technology fields, and in particular to red pigment and varnish are uniformly mixed by a kind of red glaze golden flower paper decoration firing method of low temperature, and grinding is used as colorant spare after reaching standard;By bottom flower printing to the surface of greenwave;It is toasted after the surface printing colorant of greenwave, toasts 600-620 DEG C, then republish gold paste afterwards, 720-750 DEG C of baking temperature, baking is completed up to the red glaze golden flower paper product of low temperature.The red glaze golden flower paper decoration firing method of a kind of low temperature provided by the invention, fired temperature is and golden yellow bright up to 720-750 DEG C on the red glaze of low temperature, without cracking phenomena.It is used with 720-750 DEG C of serial pigment collocation, pigment gloss degree is strong, and acid-fast alkali-proof is anti-oxidant, improves product specification and effect.
Description
Technical field
The invention belongs to ceramic technology fields, and in particular to a kind of red glaze golden flower paper decoration firing method of low temperature.
Background technique
The barbecue of the red glaze of low temperature is 750-800 DEG C at glaze temperature at present, and since temperature is lower, red glaze initial melting temperature is lower,
Golden flower paper fired temperature general control is between 540-560 DEG C.More than 560 DEG C, then gold is easily pulled open by red glaze, and temperature is higher, gold
Cracking phenomena is more serious.Therefore corresponding can only also be roasted together with gold to other colors for using of gold collocation, can only use intolerant to
Soda acid pigment, lustrous surface is not strong, and easily aoxidizes, and according to being burnt into twice, higher cost and is unfavorable for operating.
Summary of the invention
In view of the above technical problems, the present invention provides a kind of red glaze golden flower paper decoration firing method of low temperature.
A kind of red glaze golden flower paper decoration firing method of low temperature, comprising the following steps:
Red pigment and varnish are uniformly mixed, grinding is used as colorant spare after reaching standard;
By bottom flower printing to the surface of greenwave;Toasted after the surface printing colorant of greenwave, toast 600-620 DEG C, then after
Gold paste is republished, 720-750 DEG C of baking temperature, baking is completed up to the red glaze golden flower paper product of low temperature.
Also added with cracking -resistant material and diluent in the gold paste, with after 250 mesh screen cloths for printing.
The red glaze golden flower paper decoration firing method of a kind of low temperature provided by the invention, fired temperature is up to 720- on the red glaze of low temperature
750 DEG C, and it is golden yellow bright, without cracking phenomena.It is used with 720-750 DEG C of serial pigment collocation, pigment gloss degree is strong, acid-fast alkali-proof
It is anti-oxidant, improve product specification and effect.
Specific embodiment
It is described in conjunction with the embodiments the specific technical solution of the present invention.
A kind of red glaze golden flower paper decoration firing method of low temperature, comprising the following steps:
Red pigment and varnish are uniformly mixed, grinding is used as colorant spare after reaching standard;
By bottom flower printing to the surface of greenwave;Toasted after the surface printing colorant of greenwave, toast 600-620 DEG C, then after
Gold paste is republished, 720-750 DEG C of baking temperature, baking is completed up to the red glaze golden flower paper product of low temperature.
Also added with cracking -resistant material and diluent in the gold paste, with after 250 mesh screen cloths for printing.
Claims (2)
1. a kind of red glaze golden flower paper decoration firing method of low temperature, it is characterised in that: the following steps are included:
Red pigment and varnish are uniformly mixed, grinding is used as colorant spare after reaching standard;
By bottom flower printing to the surface of greenwave;Toasted after the surface printing colorant of greenwave, toast 600-620 DEG C, then after
Gold paste is republished, 720-750 DEG C of baking temperature, baking is completed up to the red glaze golden flower paper product of low temperature.
2. the red glaze golden flower paper decoration firing method of a kind of low temperature according to claim 1, it is characterised in that: in the gold paste also
Added with cracking -resistant material and diluent, with after 250 mesh screen cloths for printing.