CN109136901A - 压铸铝合金耐中性盐雾试验无铬钝化剂及制备方法 - Google Patents
压铸铝合金耐中性盐雾试验无铬钝化剂及制备方法 Download PDFInfo
- Publication number
- CN109136901A CN109136901A CN201811283361.6A CN201811283361A CN109136901A CN 109136901 A CN109136901 A CN 109136901A CN 201811283361 A CN201811283361 A CN 201811283361A CN 109136901 A CN109136901 A CN 109136901A
- Authority
- CN
- China
- Prior art keywords
- acid
- added
- salt spray
- spray test
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种压铸铝合金耐中性盐雾试验无铬钝化剂,所用原料及质量百分比如下:双氨基硅烷低聚物8~15%、KH‑560偶联剂9~20%、乳酸0.5~2%、冰醋酸0.5~2%,氟钛酸或氟锆酸0.2~1%、偏钒酸盐1~3%、磷酸盐1~5%、改性消泡剂0.01~0.03%及水余量。制备方法依次按照如下步骤进行:取纯水置于反应釜中,开启搅拌60转/分,加入双氨基硅烷低聚物搅拌30min;再加入KH‑560偶联剂搅拌10h;加入乳酸、冰醋酸搅拌2h;加入氟钛酸或氟锆酸后,再用热水溶解偏钒酸盐缓慢加入,最后加入磷酸盐及改性消泡剂,搅拌1h;过滤即可。
Description
技术领域
本发明涉及压铸铝合金以及铝合金表面处理领域,尤其涉及一种压铸铝合金耐中性盐雾试验无铬钝化剂及制备方法。
背景技术
铝合金压铸件广泛用于汽车、电子、家电以及飞机船舶等行业中,对其表面处理的要求也越来越高。传统的六价铬钝化膜虽然能满足压铸铝表面高耐腐蚀性的要求(耐中性盐雾试验),但由于其本身的不环保性、致癌性等原因已经被国家所限制。目前主流的无铬钝化主要是硅烷处理、钛锆盐钝化、钼酸盐钝化等,虽然可以满足涂装前的要求,保证工件与漆层的附着力及马丘试验等,但是裸膜的耐腐蚀性都不理想,中性盐雾试验一般都不超过2h。
发明内容
本发明是为了解决现有技术所存在的上述技术问题,提供一种压铸铝合金耐中性盐雾试验无铬钝化剂及制备方法。
本发明的技术解决方案是:一种压铸铝合金耐中性盐雾试验无铬钝化剂,其特征在于所用原料及质量百分比如下:双氨基硅烷低聚物8~15%、KH-560偶联剂 9~20%、乳酸0.5~2%、冰醋酸0.5~2%,氟钛酸或氟锆酸0.2~1%、偏钒酸盐1~3%、磷酸盐1~5%、改性消泡剂0.01~0.03%及水余量。
上述压铸铝合金耐中性盐雾试验无铬钝化剂的制备方法,其特征在于依次按照如下步骤进行:称取纯水置于反应釜中,开启搅拌,60转/分,加入双氨基硅烷低聚物,搅拌30min;再加入KH-560偶联剂搅拌10h;加入乳酸、冰醋酸,搅拌2h;加入氟钛酸或氟锆酸后,再用热水溶解偏钒酸盐缓慢加入,最后加入磷酸盐及改性消泡剂,搅拌1h;过滤即可。
本发明不仅可以满足涂装前的要求,保证工件与漆层的附着力及马丘试验等,而且中性盐雾试验优于现有技术(不超过2h)。对于大部分压铸铝工件,本发明原液使用能满足48h中性盐雾试验,对于铝型材工件只需质量浓度5~10%的工作液就能满足72h以上中性盐雾试验。
具体实施方式
实施例1:
本发明的压铸铝合金耐中性盐雾试验无铬钝化剂,所用原料及质量百分比如下:双氨基硅烷低聚物15%、KH-560偶联剂 9%、乳酸2%、冰醋酸0.5%,氟钛酸1%、偏钒酸盐1%、磷酸盐5%、改性消泡剂0.01%及水余量。
制备方法依次按照如下步骤进行:称取纯水置于反应釜中,开启搅拌,60转/分,加入双氨基硅烷低聚物,搅拌30min;再加入KH-560偶联剂搅拌10h;加入乳酸、冰醋酸,是液体呈弱酸性,搅拌2h;加入氟钛酸或氟锆酸后,再用热水溶解偏钒酸盐缓慢加入,最后加入磷酸盐及改性消泡剂,搅拌1h;过滤得滤液即可。
实施例2:
本发明的压铸铝合金耐中性盐雾试验无铬钝化剂,所用原料及质量百分比如下:双氨基硅烷低聚物8%、KH-560偶联剂20%、乳酸0.5%、冰醋酸2%,氟锆酸0.2%、偏钒酸盐3%、磷酸盐1%、改性消泡剂0.03%及水余量。
制备方法同实施例1。
实施例3:
本发明的压铸铝合金耐中性盐雾试验无铬钝化剂,所用原料及质量百分比如下:双氨基硅烷低聚物10%、KH-560偶联剂 15%、乳酸1%、冰醋酸1%,氟钛酸0.6%、偏钒酸盐2%、磷酸盐3%、改性消泡剂0.02及水余量。
制备方法同实施例1。
本发明实施例1、2、3的产品为微黄色均匀液体,pH值4.0~5.0。
本发明实施例1、2、3的产品原液使用,浸泡压铸铝合金工件2~5min,压铸铝合金表面不变色,80~120℃烘干30min,耐中性盐雾试验可以满足48h以上。
Claims (2)
1.一种压铸铝合金耐中性盐雾试验无铬钝化剂,其特征在于所用原料及质量百分比如下:双氨基硅烷低聚物8~15%、KH-560偶联剂 9~20%、乳酸0.5~2%、冰醋酸0.5~2%,氟钛酸或氟锆酸0.2~1%、偏钒酸盐1~3%、磷酸盐1~5%、改性消泡剂0.01~0.03%及水余量。
2.一种如权利要求1所述压铸铝合金耐中性盐雾试验无铬钝化剂的制备方法,其特征在于依次按照如下步骤进行:称取纯水置于反应釜中,开启搅拌,60转/分,加入双氨基硅烷低聚物,搅拌30min;再加入KH-560偶联剂搅拌10h;加入乳酸、冰醋酸,搅拌2h;加入氟钛酸或氟锆酸后,再用热水溶解偏钒酸盐缓慢加入,最后加入磷酸盐及改性消泡剂,搅拌1h;过滤即可。