CN109135669A - For bonding plastics and the bonding agent of concrete and preparation method thereof - Google Patents
For bonding plastics and the bonding agent of concrete and preparation method thereof Download PDFInfo
- Publication number
- CN109135669A CN109135669A CN201810936537.7A CN201810936537A CN109135669A CN 109135669 A CN109135669 A CN 109135669A CN 201810936537 A CN201810936537 A CN 201810936537A CN 109135669 A CN109135669 A CN 109135669A
- Authority
- CN
- China
- Prior art keywords
- weight
- bonding
- parts
- concrete
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of for bonding plastics and the bonding agent of concrete and preparation method thereof, it is related to bonding agent field, the raw material of bonding agent includes: the thixotropic agent of the mixed solvent of 5-20 parts by weight, the SBS modified pitch of 10-30 parts by weight, the coupling agent of 3-10 parts by weight, the pigment of 5-15 parts by weight, the filler of 5-15 parts by weight, the aromatic solvent of 20-30 parts by weight, the color of 10-15 parts by weight and 5-10 parts by weight, it being capable of effectively bonding plastics and concrete, simultaneously at it in frosting formation composite layer, effective damp proof leakproof of waterproof.For the preparation method of bonding plastics and the bonding agent of concrete, operation is controllable, can be produced on a large scale.
Description
Technical field
The present invention relates to bonding agent fields, and in particular to a kind of bonding agent and its system for bonding plastics and concrete
Preparation Method.
Background technique
Plastic conduit plays a part of trandfer fluid, gas medium.In actual use, plastic conduit is generally positioned at
In concrete, for carrying out conveying water or other fluids.
But it is existing generally only with directly burial, while in the way of gap location filling filler, generally fill mortar
Way, but existing way suffers from the drawback that
Due to the corrosion of medium or atmosphere, therefore plastic conduit usually leaks, and thereby results in material leakage, and to life
Production brings insecurity factor, and the discharge of some hazardous mediums also causes environmental pollution.Existing mortar etc. functions only as filler,
It can not effectively carry out waterproof leakproof.Individual problem can only be solved to plastic conduit provisional leak stopping repairing simultaneously, for tight
The pipeline of aging again, leakage problem is not the problem of leak stopping can solve often, if pipeline is all replaced, to life
Influence caused by production can not be estimated.
Meanwhile existing bonding agent is general only individually for concrete bonding or plastic pipe bonding, for that can have simultaneously
Research between effect bonding concrete and plastic pipe is less.
Summary of the invention
The purpose of the present invention is to provide a kind of bonding agents for bonding plastics and concrete, can effectively be bonded modeling
Material and concrete, while at it in frosting formation composite layer, effective damp proof leakproof of waterproof.
Another object of the present invention is to provide a kind of preparation method for bonding plastics and the bonding agent of concrete,
Operation is controllable, can be produced on a large scale.
The present invention solves its technical problem and adopts the following technical solutions to realize.
The present invention proposes that a kind of bonding agent for bonding plastics and concrete, raw material include: the mixed of 5-20 parts by weight
Bonding solvent, the SBS modified pitch of 10-30 parts by weight, the coupling agent of 3-10 parts by weight, the pigment of 5-15 parts by weight, 5-15 weight
Part filler, the aromatic solvent of 20-30 parts by weight, the color of 10-15 parts by weight and 5-10 parts by weight thixotropic agent.
The present invention proposes a kind of above-mentioned preparation method for bonding plastics and the bonding agent of concrete comprising:
Mixed solvent is mixed with SBS modified pitch, 119-122 DEG C is heated to, obtains the mixed liquor of thawing.
Coupling agent, pigment, filler, aromatic solvent, color and thixotropic agent are added in mixed liquor, it is cold after mixing evenly
But.
The beneficial effect for the bonding agent of bonding plastics and concrete and preparation method thereof of the embodiment of the present invention is:
By the rational proportion of above-mentioned each raw material, it is effectively improved for the cementability between plastic material and concrete,
Composite layer, and then the effectively damp proof leakproof of waterproof are formed on the surface of plastics and/or concrete simultaneously.
Preparation method, operation is controllable, can be produced on a large scale.
Specific embodiment
It in order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below will be in the embodiment of the present invention
Technical solution be clearly and completely described.The person that is not specified actual conditions in embodiment, according to normal conditions or manufacturer builds
The condition of view carries out.Reagents or instruments used without specified manufacturer is the conventional production that can be obtained by commercially available purchase
Product.
The embodiment of the present invention is carried out specifically for bonding agent of bonding plastics and concrete and preparation method thereof below
Explanation.
The present invention background technique there are aiming at the problem that, provide a kind of bonding with concrete dedicated for bonding plastics
Agent, specifically, the raw material for being used for the bonding agent of bonding plastics and concrete include: the mixed solvent of 5-20 parts by weight, 10-30
The SBS modified pitch of parts by weight, the coupling agent of 3-10 parts by weight, the pigment of 5-15 parts by weight, 5-15 parts by weight filler, 20-
The thixotropic agent of the aromatic solvent of 30 parts by weight, the color of 10-15 parts by weight and 5-10 parts by weight.Pass through the conjunction of above-mentioned each raw material
Reason proportion, effectively improves it for the cementability between plastic material and concrete, wherein plastic material is preferably plastic tube
Material, the bonding agent provided through the invention can effectively bonding plastics tubing and concrete, while in the surface shape of plastic pipe
At composite layer, and then the effectively damp proof leakproof of waterproof.
Wherein, mixed solvent is selected from least one of butyl ester, ethyl ester and ethylene glycol monobutyl ether, it is preferable that mixing is molten
Agent includes butyl ester, ethyl ester and ethylene glycol monobutyl ether, and solute effect is good, such as wherein butyl ester, ethyl ester and ethylene glycol monobutyl ether
The ratio between additive amount be 1-15:1-15:1-15.
But other raw materials, such as thixotropic agent etc. are limited in the dissolution of in the mixed solvent, therefore pass through addition aromatic solvent
It is effectively increased in the dissolubility of in the mixed solvent, the mobility of bonding agent is improved, is more convenient for being bonded.Preferably, the present invention compared with
In good embodiment, aromatic solvent is selected from least one of toluene and dimethylbenzene, and preferably aromatic solvent is toluene and diformazan
The mixture of benzene.
SBS modified pitch refers to the pitch emulsion modified through SBS, with preferable high temperature resistant and waterproof performance, leads to
The cooperation with other auxiliary agents is crossed, effectively between the surface of chemical pipeline and concrete, forms one layer of organic composite material layer,
Can not only close adhesion on duct wall and concrete, while can also be used as the functional polymer that a kind of endurance can be special
Material layer is used to extend the service life of plastic pipe by whole or local coating plastic tubing, and then effectively prevent leak.
The reasonable addition of SBS modified pitch effectively improves adhesive property, quick-drying and the resistance to low temperature of bonding agent.
Coupling agent can react in bonding agent with certain groups on the surfaces such as reinforcing material, such as filler, and can be with
The reaction of SBS modified pitch, forms a boundary layer between reinforcing material and resin matrix, and boundary layer can transmit stress, thus
Adhesive strength between reinforcing material and SBS modified pitch is enhanced, the performance of bonding agent is improved, interface shape can also be improved
State improves the ageing-resistant of bonding agent, proof stress and wearability, and then improves between bonding agent and plastic pipe and concrete
Cementability.
Preferably, in preferred embodiments of the present invention, coupling agent is selected from γ-(the third oxygen of 2.3- epoxy) propyl trimethoxy silicon
Alkane, γ-methacryloxypropyl trimethoxy silane, vinyl three ('beta '-methoxy ethyoxyl) silane, γ-aminopropyl three
In ester modified dose of amido polyol of Ethoxysilane, vinyltrimethoxysilane, triethoxysilylpropyl tetrasulfide and end
At least one；Such as coupling agent is γ-methacryloxypropyl trimethoxy silane and (the 'beta '-methoxy second of vinyl three
Oxygroup) silane mixture or coupling agent be gamma-aminopropyl-triethoxy-silane, vinyltrimethoxysilane, triethoxy
The mixture of ester modified dose of amido polyol of silicon propyl tetrasulfide and end.
Preferably, in preferred embodiments of the present invention, coupling agent is vinyltrimethoxysilane.It effectively improves bonding
The cementability of agent and plastic pipe, concrete, while cooperating with SBS modified pitch, effectively improve the durability of bonding agent.
In order to make the workability of bonding agent more preferably, while there can be higher consistency when static, in external force
The lower substance for becoming low consistency fluid again of effect, convenient for being applied to target position.It is fine that thixotropic agent is selected from gas-phase silica, carboxymethyl
Tie up at least one of plain sodium, precipitated silica and organobentonite；Preferably, thixotropic agent is sodium carboxymethylcellulose.
In order to enable obtained bonding agent can be perfectly identical as the color of plastic pipe or concrete, or effectively dress
Decorations, color are selected from silver-colored aluminium powder, silver-colored aluminium paste, bronze, iron oxide red, iron oxide black, graphite, carbon black color, bavin woods bright green and titanium white
At least one of powder；Since the color of existing concrete is grey black, it is preferred that color is carbon black color.
It holds, adds pigment, assist the color of color, while for cooperating with filler, filling caking agent series, improving it
Consistency, while adjusting the cementability of bonding agent.
Preferably, in preferred embodiments of the present invention, pigment in mica powder, carbonate and kaolin at least one
Kind；Preferably, pigment is mica powder, and filler is talcum powder, cooperates filling effect and good with the fiting effect of color.
The present invention also provides a kind of above-mentioned preparation methods for bonding plastics and the bonding agent of concrete comprising:
S1. mixed solvent is mixed with SBS modified pitch, is heated to 119-122 DEG C, obtain the mixed liquor of thawing.
Wherein it should be noted that mixed solvent is mixed in emulsion pot with SBS modified pitch, opens steam and slowly add
Heat.Optionally, it heats with 3-5 DEG C/min heating, is sufficiently mixed SBS modified pitch in mixed solvent, improves the later period
Adhesive property.
S2. coupling agent, pigment, filler, aromatic solvent, color and thixotropic agent are added in mixed liquor, after mixing evenly
It is cooling.
Specifically, the step of coupling agent, pigment, filler, aromatic solvent, color and thixotropic agent are added in mixed liquor is wrapped
It includes:
When mixeding liquid temperature is 118-130 DEG C, coupling agent, pigment and filler are first sequentially added in mixed liquor, this temperature
Under the conditions of degree, coupling agent, pigment and filler can be made to be sufficiently mixed in mixed liquor, improve the stability of subsequent bonding agent, together
The effect of Shi Tigao coupling agent improves stability and connectivity between a substance, improves adhesive effect.
After mixing evenly, aromatic solvent, color and thixotropic agent are sequentially added, is stirred to no particle, sequentially adding can
The dispersion degree for effectively improving color and thixotropic agent improves the homogeneity of the quality of last bonding agent.Wherein, preferably stir with
The condition of 600r/min carries out.
In preferred embodiments of the present invention, it is cooled to 30-35 DEG C.It is then possible to carry out packaging and other steps, do not do herein superfluous
It states.
Feature and performance of the invention are described in further detail with reference to embodiments.
Embodiment 1
A kind of bonding agent for bonding plastics and concrete, is made by following methods:
S1. raw material is configured, wherein raw material includes: the mixed solvent of 15 parts by weight, the SBS modified pitch of 20 parts by weight, 7 weights
The amount vinyltrimethoxysilane of part, the mica powder of 10 parts by weight, talcum powder, the aromatic hydrocarbons of 22 parts by weight of 10 parts by weight are molten
The sodium carboxymethylcellulose of agent, the carbon black color of 13 parts by weight and 7 parts by weight.
Wherein, mixed solvent is butyl ester, ethyl ester and ethylene glycol monobutyl ether according to middle amount than the mixture for 1:1:1, virtue
Hydrocarbon solvent is the mixture of toluene and dimethylbenzene.
S2. mixed solvent is mixed with SBS modified pitch, is heated to 120 DEG C, obtain the mixed liquor of thawing.
S3. when mixeding liquid temperature is 125 DEG C, vinyltrimethoxysilane, mica are first sequentially added in mixed liquor
Powder and talcum powder sequentially add aromatic solvent, carbon black color and sodium carboxymethylcellulose, stirring to nothing after mixing evenly
Particle is cooled to after 30 DEG C to obtain the final product.
Embodiment 2
A kind of bonding agent for bonding plastics and concrete, is made by following methods:
S1. raw material is configured, wherein raw material includes: the mixed solvent of 17 parts by weight, the SBS modified pitch of 24 parts by weight, 5 weights
Measure the vinyltrimethoxysilane of part, the mica powder of 7 parts by weight, the talcum powder of 8 parts by weight, 23 parts by weight aromatic solvent,
The carbon black color of 12 parts by weight and the sodium carboxymethylcellulose of 7 parts by weight.
Wherein, mixed solvent is butyl ester, ethyl ester and ethylene glycol monobutyl ether according to middle amount than the mixture for 1:3:2, virtue
Hydrocarbon solvent is the mixture of toluene and dimethylbenzene.
S2. mixed solvent is mixed with SBS modified pitch, is heated to 120 DEG C, obtain the mixed liquor of thawing.
S3. when mixeding liquid temperature is 124 DEG C, vinyltrimethoxysilane, mica are first sequentially added in mixed liquor
Powder and talcum powder sequentially add aromatic solvent, carbon black color and sodium carboxymethylcellulose, stirring to nothing after mixing evenly
Particle is cooled to after 35 DEG C to obtain the final product.
Embodiment 3
A kind of bonding agent for bonding plastics and concrete, is made by following methods:
S1. raw material is configured, wherein raw material includes: the mixed solvent of 11 parts by weight, the SBS modified pitch of 19 parts by weight, 7 weights
Measure the vinyltrimethoxysilane of part, the mica powder of 13 parts by weight, the talcum powder of 8 parts by weight, 24 parts by weight aromatic solvent,
The carbon black color of 14 parts by weight and the sodium carboxymethylcellulose of 8 parts by weight.
Wherein, mixed solvent is butyl ester, ethyl ester and ethylene glycol monobutyl ether according to middle amount than the mixture for 7:12:3, virtue
Hydrocarbon solvent is the mixture of toluene and dimethylbenzene.
S2. mixed solvent is mixed with SBS modified pitch, is heated to 122 DEG C, obtain the mixed liquor of thawing.
S3. when mixeding liquid temperature is 126 DEG C, vinyltrimethoxysilane, mica are first sequentially added in mixed liquor
Powder and talcum powder sequentially add aromatic solvent, carbon black color and sodium carboxymethylcellulose, stirring to nothing after mixing evenly
Particle is cooled to after 33 DEG C to obtain the final product.
Embodiment 4
A kind of bonding agent for bonding plastics and concrete, is made by following methods:
S1. raw material is configured, wherein raw material includes: the mixed solvent of 20 parts by weight, the SBS modified pitch of 30 parts by weight, 10
The vinyltrimethoxysilane of parts by weight, the mica powder of 15 parts by weight, the talcum powder of 13 parts by weight, the aromatic hydrocarbons of 29 parts by weight are molten
The sodium carboxymethylcellulose of agent, the carbon black color of 13 parts by weight and 10 parts by weight.
Wherein, mixed solvent is butyl ester, ethyl ester and ethylene glycol monobutyl ether according to middle amount than the mixture for 1:1:1, virtue
Hydrocarbon solvent is the mixture of toluene and dimethylbenzene.
S2. mixed solvent is mixed with SBS modified pitch, is heated to 120 DEG C, obtain the mixed liquor of thawing.
S3. when mixeding liquid temperature is 120 DEG C, vinyltrimethoxysilane, mica are first sequentially added in mixed liquor
Powder and talcum powder sequentially add aromatic solvent, carbon black color and sodium carboxymethylcellulose, stirring to nothing after mixing evenly
Particle is cooled to after 30 DEG C to obtain the final product.
Embodiment 5
A kind of bonding agent for bonding plastics and concrete, is made by following methods:
S1. raw material is configured, wherein raw material includes: the mixed solvent of 10 parts by weight, the SBS modified pitch of 10 parts by weight, 3 weights
Measure the vinyltrimethoxysilane of part, the mica powder of 6 parts by weight, the talcum powder of 5 parts by weight, 25 parts by weight aromatic solvent,
The carbon black color of 10 parts by weight and the sodium carboxymethylcellulose of 7 parts by weight.
Wherein, mixed solvent is butyl ester, ethyl ester and ethylene glycol monobutyl ether according to middle amount than the mixture for 1:1:1, virtue
Hydrocarbon solvent is the mixture of toluene and dimethylbenzene.
S2. mixed solvent is mixed with SBS modified pitch, is heated to 122 DEG C, obtain the mixed liquor of thawing.
S3. when mixeding liquid temperature is 122 DEG C, vinyltrimethoxysilane, mica are first sequentially added in mixed liquor
Powder and talcum powder sequentially add aromatic solvent, carbon black color and sodium carboxymethylcellulose, stirring to nothing after mixing evenly
Particle is cooled to after 32 DEG C to obtain the final product.
Test example
It chooses similar products common on the market: being usually used in solvent type grey colloid, the solvent type carbon black glue of Decoration Industry
Successively 1-2, the bonding agent provided using the embodiment of the present invention 1 carry out the measurement of physicochemical property as test group to body as a control group.
The results are shown in Table 1.
1 physicochemical property of table
On plastic plate, at interval of spraying one to twice in 1 day, control group 1-2 and test group 1 are verified for cement element
Slurry, cement mortar, polymer premixing mortar and putty coating and plastic plate cementability, it is as a result as follows:
There is no affinity between control group 2 and lean concrete grout, cement mortar, adhesive effect is poor.Simultaneously by by control group 1
With test group coated at leak, the waterproof of discovery test group 1 is than 1 good waterproof performance of control group.
Tested simultaneously with embodiment 2-5 using the above method, obtain it is similar with test group 1 as a result, therefore, herein
It does not repeat them here.
According to above-mentioned test example, there is base's adaptability provided by the present invention for the bonding agent of bonding plastics and concrete
Extensively, the characteristics of cohesive force is good, affinity is good, water-tolerant.
To sum up, the bonding agent provided in an embodiment of the present invention for bonding plastics and concrete, can effectively be bonded modeling
Material and concrete, while at it in frosting formation composite layer, effective damp proof leakproof of waterproof.It is above-mentioned to be used for bonding plastics
With the preparation method of the bonding agent of concrete, operation is controllable, can be produced on a large scale.
Embodiments described above is a part of the embodiment of the present invention, instead of all the embodiments.Reality of the invention
The detailed description for applying example is not intended to limit the range of claimed invention, but is merely representative of selected implementation of the invention
Example.Based on the embodiments of the present invention, obtained by those of ordinary skill in the art without making creative efforts
Every other embodiment, shall fall within the protection scope of the present invention.
Claims (10)
1. a kind of bonding agent for bonding plastics and concrete, characterized in that it comprises: the mixing of 5-20 parts by weight is molten
Agent, the SBS modified pitch of 10-30 parts by weight, the coupling agent of 3-10 parts by weight, the pigment of 5-15 parts by weight, 5-15 parts by weight
Filler, the aromatic solvent of 20-30 parts by weight, the color of 10-15 parts by weight and 5-10 parts by weight thixotropic agent.
2. the bonding agent according to claim 1 for bonding plastics and concrete, which is characterized in that the aromatic solvent
Selected from least one of toluene and dimethylbenzene.
3. the bonding agent according to claim 1 for bonding plastics and concrete, which is characterized in that the mixed solvent
Selected from least one of butyl ester, ethyl ester and ethylene glycol monobutyl ether.
4. the bonding agent according to claim 1 for bonding plastics and concrete, which is characterized in that the coupling agent choosing
From γ-(the third oxygen of 2.3- epoxy) propyl trimethoxy silicane, γ-methacryloxypropyl trimethoxy silane, vinyl
Three ('beta '-methoxy ethyoxyl) silane, gamma-aminopropyl-triethoxy-silane, vinyltrimethoxysilane, triethoxysilicane third
At least one of ester modified dose of amido polyol of base tetrasulfide and end；
Preferably, the coupling agent is vinyltrimethoxysilane.
5. the bonding agent according to claim 1 for bonding plastics and concrete, which is characterized in that the thixotropic agent choosing
From at least one of gas-phase silica, sodium carboxymethylcellulose, precipitated silica and organobentonite；
Preferably, the thixotropic agent is sodium carboxymethylcellulose.
6. the bonding agent according to claim 1 for bonding plastics and concrete, which is characterized in that the color is selected from
At least one in silver-colored aluminium powder, silver-colored aluminium paste, bronze, iron oxide red, iron oxide black, graphite, carbon black color, bavin woods bright green and titanium dioxide
Kind；
Preferably, the color is carbon black color.
7. the bonding agent according to claim 1 for bonding plastics and concrete, which is characterized in that the pigment is selected from
At least one of mica powder, carbonate and kaolin；
Preferably, the pigment is mica powder, and the filler is talcum powder.
8. the preparation method described in a kind of claim 1-7 any one for bonding plastics and the bonding agent of concrete,
It is characterized in that, comprising:
Mixed solvent is mixed with SBS modified pitch, 119-122 DEG C is heated to, obtains the mixed liquor of thawing；
Be added in the mixed liquor coupling agent, the pigment, the filler, the aromatic solvent, the color and
The thixotropic agent, cools down after mixing evenly.
9. preparation method according to claim 8, which is characterized in that the coupling agent, institute are added in the mixed liquor
The step of stating pigment, the filler, the aromatic solvent, the color and the thixotropic agent include:
When mixeding liquid temperature is 118-130 DEG C, coupling agent, pigment and filler are first sequentially added in the mixed liquor, are stirred
After uniformly, the aromatic solvent, color and thixotropic agent, stirring to no particle are sequentially added.
10. preparation method according to claim 8, which is characterized in that be cooled to 30-35 DEG C.