CN109133635A - Surface has the Ceramic Tiles and its surface three-dimensional pattern processing method of space pattern - Google Patents
Surface has the Ceramic Tiles and its surface three-dimensional pattern processing method of space pattern Download PDFInfo
- Publication number
- CN109133635A CN109133635A CN201811237739.9A CN201811237739A CN109133635A CN 109133635 A CN109133635 A CN 109133635A CN 201811237739 A CN201811237739 A CN 201811237739A CN 109133635 A CN109133635 A CN 109133635A
- Authority
- CN
- China
- Prior art keywords
- ceramic brick
- processing method
- space pattern
- brick surface
- ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses Ceramic Tiles and its surface three-dimensional pattern processing method that a kind of surface has space pattern, wherein comprising steps of carving according to surface of the target pattern to Ceramic Tiles, forms surface texture, and once fired；It according to ceramic brick surface texture coating glass white glaze of the target pattern after primary fire, dries, then carries out secondary firing, form surface three-dimensional pattern.The present invention solves the problems, such as that ceramic brick surface space pattern durability is bad in the prior art.
Description
Technical field
The present invention relates to Ceramic Tiles and its surfaces that Ceramic Tiles technical field more particularly to a kind of surface have space pattern
Space pattern processing method.
Background technique
In ceramic tile production, various patterns are often made in ceramic brick surface by craft or machine, but it is existing
Technology production ceramic brick surface pattern otherwise no stereoscopic effect, although pattern have stereoscopic effect be easy dampness, it is mould
Become or fall off, durability is inadequate, has seriously affected the quality and service life of product.
Therefore, the existing technology needs to be improved and developed.
Summary of the invention
In view of above-mentioned deficiencies of the prior art, the purpose of the present invention is to provide the ceramics that a kind of surface has space pattern
Brick and its surface three-dimensional pattern processing method, it is intended to solve that ceramic brick surface space pattern durability is bad in the prior art asks
Topic.
Technical scheme is as follows:
A kind of ceramic brick surface space pattern processing method, wherein comprising steps of
It is carved according to surface of the target pattern to Ceramic Tiles, forms surface texture, and once fired；
It according to ceramic brick surface texture coating glass white glaze of the target pattern after primary fire, dries, then carries out secondary firing,
Form surface three-dimensional pattern.
The ceramic brick surface space pattern processing method a, wherein firing temperature is 1200 ~ 1300 DEG C, the time
For 45 ~ 65mins.
The ceramic brick surface space pattern processing method, wherein secondary firing temperature is 600 ~ 800 DEG C, the time 4
~6h。
The ceramic brick surface space pattern processing method, wherein the glass white glaze is by glass white glaze original glaze and camphor tree
Cerebrol reconciles by the volume ratio of 4:1.
The ceramic brick surface space pattern processing method, wherein glass white glaze is handled through mill glaze in advance using preceding.
The ceramic brick surface space pattern processing method, wherein it is described according to target pattern after primary fire
After the step of ceramic brick surface texture coating glass white glaze, further includes: according to the depth of picture color, distant relationships, to picture
Face locally carries out secondary toning.
The ceramic brick surface space pattern processing method, wherein after primary fire, further comprise the steps of: inspection
Ceramic brick surface crackle, and reclaim processing is carried out to cracks, then fired again.
A kind of surface has the Ceramic Tiles of space pattern, wherein is process by method as described above.
The utility model has the advantages that the present invention first carves out surface texture in ceramic brick surface according to target pattern, and once burnt
System, then the surface texture coating glass white glaze after primary fire to be to form target pattern, then after carrying out secondary firing, can
Waterproof, anticorrosive, long-lived ceramic brick surface space pattern are enough formed, it is three-dimensional to solve ceramic brick surface in the prior art
The bad problem of pattern durability.
Detailed description of the invention
Fig. 1 is the flow chart of ceramic brick surface space pattern processing method preferred embodiment of the present invention.
Specific embodiment
The present invention provides a kind of Ceramic Tiles and its surface three-dimensional pattern processing method of the surface with space pattern, to make this
The purpose of invention, technical solution and effect are clearer, define, and the present invention is described in more detail below.It should be appreciated that this
Locate described specific embodiment to be only used to explain the present invention, be not intended to limit the present invention.
Ceramic brick surface space pattern processing method of the present invention, as shown in Figure 1, comprising the following steps:
S1, it is carved according to surface of the target pattern to Ceramic Tiles, forms surface texture, and once fired；
S2, according to ceramic brick surface texture coating glass white glaze of the target pattern after primary fire, dry, then carry out secondary burning
System forms surface three-dimensional pattern.
The present invention first carves out surface texture in ceramic brick surface according to target pattern, and is once fired, and then exists
Surface texture coating glass white glaze forms target pattern, then after carrying out secondary firing, can form solid in ceramic brick surface
Pattern, the space pattern have waterproof, anticorrosive, long-lived characteristic.
It in the step S1, is carved, is formed corresponding with target pattern according to surface of the target pattern to Ceramic Tiles
Stereo structure surface texture.Preferably, target pattern can be gone out in the printout surface of Ceramic Tiles in advance, in order to preferably carve
Carve surface texture.
After carrying out surface texture engraving to Ceramic Tiles, once fired in the kiln that temperature is 1200 ~ 1300 DEG C,
Firing time is 45 ~ 65mins, with the ceramic brick surface after firm engraving.Preferably, a firing temperature is 1240 DEG C, fire
Time is 55mins.
After primary fire, ceramic brick surface is detected, detects the dark crackle in its surface, and a glaze is carried out to dark crackle
Then processing, this glaze processing glaze used can be fired again, wherein again for common ceramic glaze with covering the dark crackle
The condition of sintering procedure can be as a sintering procedure.
In the step S2, according to ceramic brick surface texture coating glass white glaze of the target pattern after primary fire, shape
At the color effect pattern as target pattern, then naturally dry, flash-off time can be 1h, then carry out secondary burning again
It makes, then natural cooling, it can form surface three-dimensional pattern.
Preferably, the temperature of the secondary firing is 600 ~ 800 DEG C, and the firing time is 4 ~ 6h, can be by glass white glaze jail
Jail fire on cubic texture surface, temperature it is too low or it is excessively high will affect sintering effect, and stablize it is excessively high will cause surface damage
Wound.More preferably, the temperature of secondary firing be 700 DEG C, time 5h.
Preferably, the step of ceramic brick surface texture coating glass white glaze according to target pattern after primary fire it
Afterwards, further includes: according to the depth of picture color, distant relationships, secondary toning is locally carried out to picture.
Wherein, the glass white glaze and camphorated oil reconcile by the volume ratio of 4:1, and mill glaze machine pair is utilized before reconciliation
Former glaze carries out mill glaze processing, and the processing time is that 12h or more is preferred.
Based on the above method, the present invention also provides the Ceramic Tiles that a kind of surface has space pattern, wherein the ceramics
Brick is process by method as described above.
It is described further below with reference to more detailed embodiment.
The surface of the present embodiment has the step of processing method of the Ceramic Tiles of space pattern as follows:
Step 1: target pattern original image PS is opened electronics manuscript base piece, carry out toning and extra undercolour removal, makes to beat
When print can it is more efficient and clear, the drawing handled well is divided into auxiliary line the size for needing to print monolithic drawing, then into
Row, which is cut, to be saved, and the monolithic drawing cut is converted into printer software format with U1traPrint software；
Step 2: opening PrintExp print software, the program converted is chosen to be printed, and directly on flat-panel printer
Pattern is printed upon on ceramic brick product；
Step 3: carrying out artificial hand engraving and creation according to the requirement of picture after product is printed；
It is fired on brandreth step 4: the product carved is placed on, bottom four corners brush aluminium oxide, and the product carved is used
Tricycle is fired in customization spring brandreth drawing to specified production line；
Step 5: Product transport is fired 55 minutes or so into hot-working line kiln and under the conditions of 1240 DEG C or so；
Step 6: product fired retract workshop classification detected secretly split, glaze paint the problems such as, and carry out a glaze to place is secretly split
Processing, then fired again；
Step 7: the good post-tensioning of product testing goes cutting area to cut, and put need to neatly be classified inspection it is good after, polishing splicing；
Step 8: colouring work carries out product coating glass white glaze according to the requirement of original image, and according to picture after product examination is good
The depth of color, distant relationships locally carry out secondary toning to picture；
Step 9: after product has coated glass white glaze, 1 hour of naturally dry；
Step 10: carrying out secondary firing 5 hours to product under the conditions of 700 DEG C, it is then naturally cooling to room temperature；
It is classified step 11: secondary burned product is drawn to finished product, it is thin to carry out the degree of deformation to brick, size, quantity, picture etc.
Save problem detection, it is ensured that massless problem；
Step 12: then being packaged with carton, foam and leatheroid, it is packed in storage.
In conclusion surface provided by the present invention has Ceramic Tiles and its surface three-dimensional pattern processing side of space pattern
Method, the present invention first carve out surface texture in ceramic brick surface according to target pattern and are once fired, then once fired
Surface texture coating glass white glaze afterwards can form waterproof, anti-corruption to form target pattern, then after carrying out secondary firing
Erosion, long-lived ceramic brick surface space pattern, it is bad to solve ceramic brick surface space pattern durability in the prior art
The problem of.
It should be understood that the application of the present invention is not limited to the above for those of ordinary skills can
With improvement or transformation based on the above description, all these modifications and variations all should belong to the guarantor of appended claims of the present invention
Protect range.
Claims (8)
1. a kind of ceramic brick surface space pattern processing method, which is characterized in that comprising steps of
It is carved according to surface of the target pattern to Ceramic Tiles, forms surface texture, and once fired；
It according to ceramic brick surface texture coating glass white glaze of the target pattern after primary fire, dries, then carries out secondary firing,
Form surface three-dimensional pattern.
2. ceramic brick surface space pattern processing method according to claim 1, which is characterized in that one time firing temperature is
1200 ~ 1300 DEG C, the time is 45 ~ 65mins.
3. ceramic brick surface space pattern processing method according to claim 1, which is characterized in that secondary firing temperature is
600 ~ 800 DEG C, the time is 4 ~ 6h.
4. ceramic brick surface space pattern processing method according to claim 1, which is characterized in that the glass white glaze with
Camphorated oil reconciles by the volume ratio of 4:1.
5. ceramic brick surface space pattern processing method according to claim 4, which is characterized in that glass white glaze is using
It is preceding to be handled in advance through mill glaze.
6. ceramic brick surface space pattern processing method according to claim 1, which is characterized in that described according to target figure
After case is the ceramic brick surface texture coating glass white glaze after primary fire the step of, further includes: according to the depth of picture color
Shallowly, distant relationships locally carry out secondary toning to picture.
7. ceramic brick surface space pattern processing method according to claim 1, which is characterized in that once firing it
Afterwards, it further comprises the steps of: and checks ceramic brick surface crackle, and glaze is carried out to cracks and is handled, then fired again.
8. the Ceramic Tiles that a kind of surface has space pattern, which is characterized in that added by the method as described in claim 1 ~ 7 is any
Work forms.