CN1091125C - 一种无机涂料粘结剂 - Google Patents

一种无机涂料粘结剂 Download PDF

Info

Publication number
CN1091125C
CN1091125C CN97106316A CN97106316A CN1091125C CN 1091125 C CN1091125 C CN 1091125C CN 97106316 A CN97106316 A CN 97106316A CN 97106316 A CN97106316 A CN 97106316A CN 1091125 C CN1091125 C CN 1091125C
Authority
CN
China
Prior art keywords
adhesive
inorganic coating
aminoethyl
coating adhesive
bingjisanjiayangjiguiwan
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN97106316A
Other languages
English (en)
Other versions
CN1193030A (zh
Inventor
钱宗渊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN97106316A priority Critical patent/CN1091125C/zh
Publication of CN1193030A publication Critical patent/CN1193030A/zh
Application granted granted Critical
Publication of CN1091125C publication Critical patent/CN1091125C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种粘结剂，特别是一种无机涂料粘结剂，其特征在于还包括-N(β氨乙基)-γ-氨丙基三甲氧基硅烷，各组分的重量百分比是：硅酸钾45-55% 硅溶胶 25-35%-N(β氨乙基)-γ-氨丙基三甲氧基硅烷 1-10%其余为水。本发明的优点是采用了-N(β氨乙基)-γ-氨丙基三甲氧基硅烷，使置备好的粘结剂状态稳定，该粘结剂与锌粉混合后产生的涂料实干快、固化时间短，粘结力大能满足快速施工的要求。

Description

一种无机涂料粘结剂
本发明涉及一种粘结剂，特别是一种无机涂料粘结剂。
目前，中国高科集团开发LW-1型水性无机富锌涂料，该涂料的粘结剂由低摩数锂水玻璃制成，涂料固化时在一定湿度情况下需另涂刷固化剂，表干时间24分钟、实干时间24小时、固化时间7-14天、粘结力1.4mpa，数值较低，且金属锂成本高。
本发明的目的是提供一种能使涂料实干快、固化时间短，粘结力大的无机涂料粘结剂。
本发明的技术方案是设计一种无机涂料粘结剂，包括硅酸钾、硅溶胶，其特征在于还包括-N(β氨乙基)-γ-氨丙基三甲氧基硅烷，各组分的重量百分比是：
硅酸钾     45-55％           硅溶胶     25-35％
-N(β氨乙基)-γ-氨丙基三甲氧基硅烷      1-10％其余为水。
本发明的优点是采用了-N(β氨乙基)-γ-氨丙基三甲氧基硅烷，使置备好的粘结剂状态稳定，该粘结剂与锌粉混合后产生的涂料实干快、固化时间短，粘结力大能满足快速施工的要求。
下面结合实施例对本发明作进一步地描述：
实施例一：
称重1000克摩数3.3的钾水玻璃，以300克蒸馏水稀释搅拌，温度控制在30度到50度，沉淀后滤去杂质，称重700克浓度为23％的硅溶胶和80克-N(β氨乙基)-γ-氨丙基三甲氧基硅烷。将经稀释的钾水玻璃慢慢加入滤清的硅溶胶中边搅拌边线状滴加，加完后继续搅拌30分钟，温度保持在30度到50度，滴加-N(β氨乙基)-γ-氨丙基三甲氧基硅烷，再加入240克蒸馏水，加完后继续搅拌1-2小时。
配置好的粘结剂与超细锌粉以1比2.5的比例混合后，喷涂于钢材表面，表干时间20-35分钟、实干时间2.5小时、固化时间26小时、粘结力1.9mpa。
实施例二：
称重1000克摩数3.3的钾水玻璃，以300克蒸馏水稀释搅拌，温度控制在35度到50度，沉淀后滤去杂质，称重650克浓度为23％的硅溶胶和60克-N(β氨乙基)-γ-氨丙基三甲氧基硅烷。将经稀释的钾水玻璃慢慢加入滤清的硅溶胶中边搅拌边线状滴加，加完后继续搅拌30分钟，温度保持在30度到50度，滴加-N(β氨乙基)-γ-氨丙基三甲氧基硅烷，再加入200克蒸馏水，保持温度40度，加完后继续搅拌1-2小时。
配置好的粘结剂与超细锌粉以1比2.5的比例混合后，喷涂于钢材表面，表干时间15-30分钟、实干2小时结硬、固化时间24小时、粘结力3.5mpa。
在粘结剂中硅酸钾含量低于45％，粘结力减小，高于55％，调配的涂料太厚，难以从喷枪中喷出。硅溶胶含量低于25％，粘结力减小，大于35％调配的涂料太厚，且成本高。-N(β氨乙基)-γ-氨丙基三甲氧基硅烷含量低于1％，粘结剂不稳定，大于10％成本太高。本发明采用了-N(β氨乙基)-γ-氨丙基三甲氧基硅烷，防止聚合，使置备好的粘结剂状态稳定，与超细锌粉混合后产生的涂料实干快、固化时间短，粘结力大能满足快速施工的要求。

Claims (1)

  1. 一种无机富磷锌涂料用的粘结剂，包括硅酸钾、硅溶胶，其特征在于还包括-N(β氨乙基)-γ-氨丙基三甲氧基硅烷，各组分的重量百分比是：
    硅酸钾     45-55％               硅溶胶    25-35％
    -N(β氨乙基)-γ-氨丙基三甲氧基硅烷          1-10％其余为水。
CN97106316A 1997-03-11 1997-03-11 一种无机涂料粘结剂 Expired - Fee Related CN1091125C (zh)