CN109107859A - A kind of plastics honeycomb boards plating wax method - Google Patents
A kind of plastics honeycomb boards plating wax method Download PDFInfo
- Publication number
- CN109107859A CN109107859A CN201811035881.5A CN201811035881A CN109107859A CN 109107859 A CN109107859 A CN 109107859A CN 201811035881 A CN201811035881 A CN 201811035881A CN 109107859 A CN109107859 A CN 109107859A
- Authority
- CN
- China
- Prior art keywords
- honeycomb boards
- plastics
- plastics honeycomb
- wax
- beeswax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of plastics honeycomb boards to plate wax method, firstly, pre-processing to plastics honeycomb boards；Then, beeswax solution is prepared；Then, pretreated plastics honeycomb boards are put into beeswax solution and are impregnated；It is fumigated secondly, the plastics honeycomb boards after immersion are put into heating room；Finally, taking out plastics honeycomb boards from heating room and drying.Plastics honeycomb plate surface passes through cleaning treatment in plastics honeycomb boards plating wax method disclosed by the invention, and surface smoothness height can preferably adhere to beeswax film；And plastics honeycomb boards integrally pass through the pre-heat treatment, can be consistent with the beeswax solution temperature prepared in the double-deck paraffin pot, realize that beeswax is preferably merged with plastics honeycomb boards；Furthermore plastics honeycomb boards are stifling by heating room, so that beeswax film is uniformly distributed in plastics honeycomb plate surface and avoids blocked up beeswax film that beeswax is caused to waste.
Description
Technical field
The invention belongs to apiary's equipment fields, particularly, are related to a kind of plastics honeycomb boards plating wax method.
Background technique
Tradition bee-keeping make honey beekeeper all be need honeycomb is put into beehive, general honeycomb needs first to be processed with four
Scantling nail on composition frame with iron nail, put on iron wire, tighten, installing by beeswax support artificial septum, integrally put
Enter in beehive, has been made after honey takes honey using centrifuge every time, often had breakage, honeybee needs to repair honeycomb again, existing
The integrated honeycomb very good solution above problem, can guarantee the intensity of honeycomb itself, when especially the honeybee winter stops in winter,
Integrated plastics honeycomb boards avoid infested mildew, can repeatedly utilize.
But since integrated honeycomb is made by plastic material, hence it is evident that the beeswax material of difference and existing artificial septum
Matter, it is not high for the acceptance of Plastic nest base to result in honeybee, influences honey overall yield, provides honeybee for plastics honeycomb boards
Acceptance be to have to solve the problems, such as.
Summary of the invention
In order to solve the above-mentioned technical problems, the present invention provides a kind of plastics honeycomb boards to plate wax method, which is characterized in that
Step 100: plastics honeycomb boards are pre-processed；
Step 200: preparation beeswax solution；
Step 300: pretreated plastics honeycomb boards being partially placed into beeswax solution and are impregnated；
Step 400: the plastics honeycomb boards after immersion being put into heating room and heats or fumigates；
Step 500: taking out plastics honeycomb boards from heating room and dry.
It is preferably, pretreated to the progress of plastics honeycomb boards in the step 100 that steps are as follows:
Step 110: the dirt and spot inside plastics honeycomb plate surface and honeycomb are removed with neutral cleaning solution；
Step 120: being rinsed inside plastics honeycomb plate surface and honeycomb with clear water；
Step 130: drying up or dry plastics honeycomb boards using air, hot gas；
Preferably, steps are as follows for preparation beeswax solution in the step 200:
Step 210: beeswax being put in people's paraffin pot, then the water for being equivalent to beeswax about 1/2 will be added by the size of pot, heating is molten
Change beeswax, wax liquid temperature must not cross 100 DEG C；
Step 220: the wax liquor that will have been melted stands about 50 minutes, impurity in wax is made to be sunken to bottom, above clean wax liquor
It is stored for future use after cooling agglomeration；
Step 230: clean wax stone being cut into small pieces, heat preservation is put into and dips in wax cauldron, suitable quantity of water, heating, wax liquor is added
Temperature is maintained at about 70~90 DEG C.
Preferably, whole be vertically quickly put into of pretreated plastics honeycomb boards honeycomb is dipped in into wax in the step 300
It in the wax liquor of pot, is quickly pulled out after impregnating about 10 seconds, one layer of thicker wax layer is adhered on each surface of honeycomb.
By the nest hole of plastics honeycomb boards eat dishes without rice or wine one down or towards side, quickly pull plastics honeycomb boards out in wax liquor,
Reduce the residual beeswax liquid in honeycomb.
There are the honeycomb boards of honeycomb on two sides, and vertical position quickly removes honeycomb boards, reduces the residual in the honeycomb of two sides
Wax liquor.
Preferably, in the step 400 by the plastics honeycomb boards after immersion be put into heating room in heat or fumigating step such as
Under:
Several plastics honeycomb boards are hung up in heating room, heats in room and is fumigated using hot wind, heat radiation or water vapour, added
Hot temperature is not less than 70 degree, every time heating about 5 minutes, grafting wax disk is provided with below the plastics honeycomb boards, for recycling fusing
The beeswax to drip.
When heating, honeycomb boards nest hole is downward, flows out honeycomb convenient for the residual beeswax in honeycomb, honeycomb inner wall is only residual
Stay micro ultra-thin wax coating.
Two-sided on one side first downward, heating about after five minutes, then changes other one down when having honeycomb, continues heating about
5 minutes, until the two-sided honeycomb inner wall only ultra-thin wax coating of residual minim.
Compared with the existing technology, the invention has the following beneficial effects:
1. plastics honeycomb plate surface passes through cleaning treatment, surface smoothness height can preferably adhere to beeswax film；
2. plastics honeycomb boards integrally pass through the pre-heat treatment, can be kept with the beeswax solution temperature prepared in the double-deck paraffin pot
Unanimously, realize that beeswax is preferably merged with plastics honeycomb boards；
3. plastics honeycomb boards are stifling by heating room, so that beeswax film is uniformly distributed and avoids in plastics honeycomb plate surface
Blocked up beeswax film causes beeswax to waste.
Detailed description of the invention
Plastics honeycomb boards plate wax method flow schematic diagram in Fig. 1 one embodiment of the present invention.
Specific embodiment
Tradition bee-keeping make honey beekeeper all be need honeycomb is put into beehive, general honeycomb needs first to be processed with four
Scantling nail on composition frame with iron nail, put on iron wire, tighten, installing by beeswax support artificial septum, integrally put
Enter in beehive, has been made after honey takes honey using centrifuge every time, often had breakage, honeybee needs to repair honeycomb again, existing
The integrated honeycomb very good solution above problem, can guarantee the intensity of honeycomb itself, when especially the honeybee winter stops in winter,
Integrated plastics honeycomb boards avoid infested mildew, can repeatedly utilize.
But since integrated honeycomb is made by plastic material, hence it is evident that the beeswax material of difference and existing artificial septum
Matter, it is not high for the acceptance of Plastic nest base to result in honeybee, influences honey overall yield, provides honeybee for plastics honeycomb boards
Acceptance be to have to solve the problems, such as.
In order to solve the above-mentioned technical problems, the present invention provides a kind of plastics honeycomb boards to plate wax method,
Step 100: plastics honeycomb boards are pre-processed；
It is pretreated to the progress of plastics honeycomb boards in step 100 that steps are as follows:
Step 110: the dirt and spot inside plastics honeycomb plate surface and honeycomb are removed with neutral cleaning solution；
Step 120: being rinsed inside plastics honeycomb plate surface and honeycomb with clear water；
Step 130: drying up plastics honeycomb boards using air, hot gas or directly dry plastics honeycomb boards；
Plastics honeycomb plate surface passes through cleaning treatment, and surface smoothness height can preferably adhere to beeswax film；
Step 140: by plastics honeycomb boards be placed into heating room in preheat, heating temperature to 68 °~75 °, due to
There are more organic substances in beeswax, and the unsuitable temperature of beeswax heating is excessively high, and the melt temperature of general beeswax is 68 °~75 °, modeling
Expect that honeycomb boards keep the mutually synthermal combination for being conducive to beeswax and plastics honeycomb plate surface with beeswax, plastics honeycomb boards integrally pass through
The pre-heat treatment can be consistent with the beeswax solution temperature prepared in the double-deck paraffin pot, realize beeswax and plastics honeycomb boards more
Good fusion.
In one particular embodiment of the present invention, steps are as follows for preparation beeswax solution in step 200:
Step 210: smashing into beeswax to pieces egg size and put in people's paraffin pot, then the water that 1/3 will be added by the size of pot, heat
Beeswax is melted, wax liquid temperature must not cross 100 DEG C；
Step 220: the wax liquor melted is stood about 50 minutes, impurity in wax is made to be sunken to bottom, above clean wax liquor
It is stored for future use after cooling agglomeration；
Or scoop the wax liquor melted in people's wax melting tank, a small amount of alimentary acetic acid of people is dripped, 5~6 hours is stood, makes miscellaneous in wax
Matter is sunken to bottom, and wax liquor clean above is scooped bilayer and is dipped in paraffin pan；
Step 230: clean wax stone being cut into the fritter or about 1 × 1 × 1cm cube of little finger finger belly size, is put into
Heat preservation is dipped in wax cauldron, and suitable quantity of water, heating is added, and wax liquid temperature is maintained at about 70~90 DEG C；
Or paraffin pan heating is dipped in bilayer, wherein outer pot water temperature is maintained at 70~90 DEG C, and the wax liquid temperature of interior pot is maintained at
68~75 DEG C.
In the specific embodiment of the present invention,
Preferably, whole be vertically quickly put into of pretreated plastics honeycomb boards honeycomb is dipped in into paraffin pan in step 300
It in wax liquor, is quickly pulled out after impregnating about 10 seconds, one layer of thicker wax layer is adhered on each each surface of honeycomb.
Preferably, by the nest hole of plastics honeycomb boards eat dishes without rice or wine one down or towards side, quickly pull plastics out in wax liquor
Honeycomb boards reduce the residual beeswax liquid in honeycomb.
Preferably, there are the honeycomb boards of honeycomb on two sides, and vertical position quickly removes honeycomb boards, reduces in the honeycomb of two sides
Residual wax liquor.
In another embodiment of the invention,
Step 300: pretreated plastics honeycomb boards being put into beeswax solution and are impregnated；
Pretreated plastics honeycomb boards are inserted perpendicularly into bilayer in step 300 to dip in the wax liquor of paraffin pan, impregnate 2~3 points
It is taken out after clock, one layer of thin wax is respectively adhered on the two sides of plate.
In the specific embodiment of the present invention,
Step 400: the plastics honeycomb boards after immersion are put into heating fumigating in heating room, steps are as follows:
Several plastics honeycomb boards are hung up in heating room, heats in room and is fumigated using hot wind or heat radiation or water vapour,
Heating temperature is not less than 70 degree, every time heating about 5 minutes, and plastics honeycomb boards are stifling by heating room, so that beeswax film is being moulded
Material honeycomb plate surface is uniformly distributed and avoids blocked up beeswax film that beeswax is caused to waste.Grafting wax is provided with below plastics honeycomb boards
Disk, for recycling the beeswax for melting and dripping.
Preferably, when heating, honeycomb boards nest hole is downward, flows out honeycomb convenient for the residual beeswax in honeycomb；, honeycomb
The inner wall only ultra-thin wax coating of residual minim.
Two-sided on one side first downward, heating about after five minutes, then changes other one down when having honeycomb, continues heating about
5 minutes, until the two-sided honeycomb inner wall only ultra-thin wax coating of residual minim.
Step 500: taking out plastics honeycomb boards from heating room and dry.
So far, although those skilled in the art will appreciate that present invention has been shown and described in detail herein multiple shows
Example property embodiment still without departing from the spirit and scope of the present invention, still can according to the present disclosure directly
Determine or deduce out many other variations or modifications consistent with the principles of the invention.Therefore, the scope of the present invention is understood that and recognizes
It is set to and covers all such other variations or modifications.
Claims (5)
1. a kind of plastics honeycomb boards plate wax method, which is characterized in that
Step 100: plastics honeycomb boards are pre-processed；
Step 200: preparation beeswax solution；
Step 300: pretreated plastics honeycomb boards being partially placed into beeswax solution and are impregnated；
Step 400: the plastics honeycomb boards after immersion are put into heating fumigating in heating room；
Step 500: taking out plastics honeycomb boards from heating room and dry.
2. plastics honeycomb boards according to claim 1 plate wax method, which is characterized in that
It is pretreated to the progress of plastics honeycomb boards in the step 100 that steps are as follows:
Step 110: the dirt and spot inside plastics honeycomb plate surface and honeycomb are removed with neutral cleaning solution；
Step 120: being rinsed inside plastics honeycomb plate surface and honeycomb with clear water；
Step 130: using air, hot gas drying plastics honeycomb boards or drying plastics honeycomb boards.
3. plastics honeycomb boards according to claim 1 plate wax method, which is characterized in that
Beeswax solution is prepared in the step 200, and steps are as follows:
Step 210: beeswax is put in people's paraffin pot, then the water for being equivalent to beeswax about 1/2 will be added by the size of pot, heating fusing bee
Wax, wax liquid temperature must not cross 100 DEG C；
Step 220: the wax liquor that will have been melted stands 50 minutes, impurity in wax is made to be sunken to bottom, above the cooling knot of clean wax liquor
It is stored for future use after block；
Step 230: clean wax stone being cut into small pieces, heat preservation is put into and dips in paraffin pan, suitable quantity of water, heating is added, wax liquid temperature is protected
It holds at 70~90 DEG C.
4. plastics honeycomb boards according to claim 1 plate wax method, which is characterized in that
Pretreated plastics honeycomb boards honeycomb is integrally vertically quickly put into the wax liquor for dipping in paraffin pan in the step 300,
It is quickly pulled out after impregnating 10 seconds, wax layer is adhered on surface.
5. plastics honeycomb boards according to claim 1 plate wax method, which is characterized in that
In the step 400 by the plastics honeycomb boards after immersion be put into heating room in heating fumigating steps are as follows:
Several plastics honeycomb boards are hung up in heating room, stifling using hot wind or heat radiation or water vapour in room, heating is heated
Temperature is not less than 70 degree, heats 5 minutes, is provided with grafting wax disk below the plastics honeycomb boards, the bee dripped for recycling fusing
Wax,
When heating, honeycomb boards nest hole is downward, flows out honeycomb convenient for the residual beeswax in honeycomb.