CN109097908A - A kind of glass fiber reinforcement bonded fabric and its preparation process - Google Patents
A kind of glass fiber reinforcement bonded fabric and its preparation process Download PDFInfo
- Publication number
- CN109097908A CN109097908A CN201811131276.8A CN201811131276A CN109097908A CN 109097908 A CN109097908 A CN 109097908A CN 201811131276 A CN201811131276 A CN 201811131276A CN 109097908 A CN109097908 A CN 109097908A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- fibre
- woven fabrics
- bonded fabric
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of glass fiber reinforcement bonded fabrics, it is made of following parts by weight of component: PP material particle 70-90 mass parts, polypropylene fiber 20-40 mass parts, carbon fiber 20-30 mass parts, glass fibre 20-30 mass parts, ceramic fibre 20-30 mass parts, polyester fiber 20-40 mass parts, phenyl-diformyl phenylenediamine 10-30 mass parts, polyamide fibre chemical fibre 20-40 mass parts, polymethyl methacrylate 8-10 mass parts, viscose rayon 20-30 mass parts, polycarbonate 7-9 mass parts, ammonium polyphosphate 10-20 mass parts, brightening agent 2-4 mass parts, softening agent 2-4 mass parts and compatilizer 2-4 mass parts, the present invention relates to bonded fabric technical fields.The glass fiber reinforcement bonded fabric, glass fibre, carbon fiber and ceramic fibre have stronger wear-resisting property, to increase the wearability of non-woven fabrics, improve the service life of non-woven fabrics, and glass fibre has stronger corrosion resistance and fire protecting performance, to improve the comprehensive performance of non-woven fabrics entirety.
Description
Technical field
The present invention relates to field of nonwoven fabric technology, specially a kind of glass fiber reinforcement bonded fabric and its preparation process.
Background technique
Non-woven fabrics have it is moisture-proof, ventilative, flexible, light, not combustion-supporting, be easy decompose, it is nontoxic it is nonirritant, rich in color,
The features such as cheap, recyclable.Such as mostly using polypropylene (pp material) pellet is raw material, through high-temperature fusion, spinneret, paving
Guiding principle, hot pressing are batched continuous one-step and are produced.
Non-woven fabrics does not have latitude and longitude, cuts out and sews and is all very convenient, and light easy sizing, deep by manual fan
Like.Because it is a kind of fabric for not needing spinning and weaving and being formed, only textile staple or long filament are determined
To or random alignment, form fibre net structure, then reinforced using the methods of mechanical, hot sticky or chemical.It is not by one
One yarns interwoven is knitted together, but what the method that fiber is directly passed through to physics was bonded together, so, when
When you take the viscous title in your clothes, it finds that, it is the end of a thread that can not taken out one by one.Non-woven cloth breaches traditional spinning
Principle is knitted, and there is the features such as process flow is short, throughput rate is fast, and yield is high, at low cost, purposes is wide, raw material sources are more.
Bonded fabric good, nontoxic non-stimulated, the lower-price characteristic that only has a flexibility at present, but wear-resisting property is poor, knot
Structure intensity is small, is not suitable for packing article use.
Summary of the invention
(1) the technical issues of solving
In view of the deficiencies of the prior art, the present invention provides a kind of glass fiber reinforcement bonded fabric and its preparation processes, solve
It is good that current bonded fabric only has a flexibility, nontoxic non-stimulated, lower-price characteristic, but wear-resisting property is poor, structural strength
It is small, be not suitable for the problem of packing article uses.
(2) technical solution
In order to achieve the above object, the present invention is achieved by the following technical programs: a kind of glass fiber reinforcement bonded fabric, by
Following parts by weight of component is made: PP material particle 70-90 mass parts, polypropylene fiber 20-40 mass parts, carbon fiber 20-30 mass
Part, glass fibre 20-30 mass parts, ceramic fibre 20-30 mass parts, polyester fiber 20-40 mass parts, phenyl-diformyl phenylenediamine
10-30 mass parts, polyamide fibre chemical fibre 20-40 mass parts, polymethyl methacrylate 8-10 mass parts, viscose rayon 20-30 mass
Part, polycarbonate 7-9 mass parts, ammonium polyphosphate 10-20 mass parts, brightening agent 2-4 mass parts, softening agent 2-4 mass parts and phase
Hold agent 2-4 mass parts.
Preferably, a kind of glass fiber reinforcement bonded fabric, is made of following parts by weight of component: 80 mass of PP material particle
Part, 30 mass parts of polypropylene fiber, 25 mass parts of carbon fiber, 25 mass parts of glass fibre, 25 mass parts of ceramic fibre, polyester fiber
30 mass parts, 20 mass parts of phenyl-diformyl phenylenediamine, 30 mass parts of polyamide fibre chemical fibre, 9 mass parts of polymethyl methacrylate, viscose glue
25 mass parts of fiber, 8 mass parts of polycarbonate, 15 mass parts of ammonium polyphosphate, 3 mass parts of brightening agent, 3 mass parts of softening agent and phase
Hold 3 mass parts of agent.
A kind of preparation process of glass fiber reinforcement bonded fabric, comprising the following steps:
Step 1: into cylinder-shaped blender be added PP material particle, polypropylene fiber, glass fibre, carbon fiber, ceramic fibre,
Polyester fiber, viscose rayon and polyamide fibre chemical fibre, the added material by the way of being added while stirring obtain high strength non-woven fabric original
Material;
Step 2: the high strength non-woven fabric raw material obtained to step 1 sequentially adds phenyl-diformyl phenylenediamine, polymethylacrylic acid
Methyl esters, polycarbonate, ammonium polyphosphate, brightening agent, softening agent and compatilizer, while being added also in compliance with the mode being added while stirring
The principle of material obtains non-woven fabrics mixing extruded material;
Step 3: carrying out preliminarily dried to non-woven fabrics mixing extruded material is obtained, then dried to its vacuum drum drying equipment
It is dry;
Step 4: the non-woven fabrics mixing extruded material after drying, is uniformly transmitted to screw extruder, so that raw material is uniformly sent to
In filament spinning component equipped with filter screen, filters out impurity and sprayed from spinneret later, form as-spun fibre;
Step 5: as-spun fibre is uniformly laid on lapper lace curtaining after the cooling drawing-off of air-flow by diffusor duct, formation
Filament web, hot rolling, winding become non-woven fabrics after cutting;
Step 6: the non-woven fabrics quality after qualitative detects, qualified product carries out class wrapping.
Preferably, the mixing temperature setting in the step 1 is 160 DEG C -180 DEG C.
Preferably, it in the step 2 after the completion of added material, first stirs 30min, after static 10min, then it is carried out
Stir 1h.
Preferably, the temperature setting of preliminarily dried is 120-150 DEG C in the step 3.
Preferably, the temperature setting of vacuum drum drying equipment drying is 160-180 DEG C in the step 3.
The beneficial effects of the present invention are: glass fibre, carbon fiber and ceramic fibre are added into non-woven fabrics, glass fibre,
There is stronger wear-resisting property to improve the use of non-woven fabrics to increase the wearability of non-woven fabrics for carbon fiber and ceramic fibre
Service life, and glass fibre has stronger corrosion resistance and fire protecting performance, to improve the comprehensive performance of non-woven fabrics entirety.
Specific embodiment
In order to be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, tie below
Specific embodiment is closed, the present invention is further explained.
Embodiment one
A kind of glass fiber reinforcement bonded fabric, is made of following parts by weight of component: 70 mass parts of PP material particle, polypropylene fiber
20 mass parts, 20 mass parts of carbon fiber, 20 mass parts of glass fibre, 20 mass parts of ceramic fibre, 20 mass parts of polyester fiber, benzene
Two formyl phenylenediamines, 10 mass parts, 20 mass parts of polyamide fibre chemical fibre, 8 mass parts of polymethyl methacrylate, 20 mass of viscose rayon
Part, 7 mass parts of polycarbonate, 10 mass parts of ammonium polyphosphate, 2 mass of 2 mass parts of brightening agent, 2 mass parts of softening agent and compatilizer
Part.
A kind of preparation process of glass fiber reinforcement bonded fabric, comprising the following steps:
Step 1: into cylinder-shaped blender be added PP material particle, polypropylene fiber, glass fibre, carbon fiber, ceramic fibre,
Polyester fiber, viscose rayon and polyamide fibre chemical fibre, the added material by the way of being added while stirring obtain high strength non-woven fabric original
Material;
Step 2: the high strength non-woven fabric raw material obtained to step 1 sequentially adds phenyl-diformyl phenylenediamine, polymethylacrylic acid
Methyl esters, polycarbonate, ammonium polyphosphate, brightening agent, softening agent and compatilizer, while being added also in compliance with the mode being added while stirring
The principle of material obtains non-woven fabrics mixing extruded material;
Step 3: carrying out preliminarily dried to non-woven fabrics mixing extruded material is obtained, then dried to its vacuum drum drying equipment
It is dry;
Step 4: the non-woven fabrics mixing extruded material after drying, is uniformly transmitted to screw extruder, so that raw material is uniformly sent to
In filament spinning component equipped with filter screen, filters out impurity and sprayed from spinneret later, form as-spun fibre;
Step 5: as-spun fibre is uniformly laid on lapper lace curtaining after the cooling drawing-off of air-flow by diffusor duct, formation
Filament web, hot rolling, winding become non-woven fabrics after cutting;
Step 6: the non-woven fabrics quality after qualitative detects, qualified product carries out class wrapping.
Mixing temperature setting in step 1 is 160 DEG C -180 DEG C.In step 2 after the completion of added material, first stir
After 30min, static 10min, then 1h is stirred to it.The temperature setting of preliminarily dried is 120-150 DEG C in step 3.Step
The temperature setting of vacuum drum drying equipment drying is 160-180 DEG C in rapid three.
Embodiment two
A kind of glass fiber reinforcement bonded fabric, is made of following parts by weight of component: 80 mass parts of PP material particle, polypropylene fiber
30 mass parts, 25 mass parts of carbon fiber, 25 mass parts of glass fibre, 25 mass parts of ceramic fibre, 30 mass parts of polyester fiber, benzene
Two formyl phenylenediamines, 20 mass parts, 30 mass parts of polyamide fibre chemical fibre, 9 mass parts of polymethyl methacrylate, 25 mass of viscose rayon
Part, 8 mass parts of polycarbonate, 15 mass parts of ammonium polyphosphate, 3 mass of 3 mass parts of brightening agent, 3 mass parts of softening agent and compatilizer
Part.
A kind of preparation process of glass fiber reinforcement bonded fabric, comprising the following steps:
Step 1: into cylinder-shaped blender be added PP material particle, polypropylene fiber, glass fibre, carbon fiber, ceramic fibre,
Polyester fiber, viscose rayon and polyamide fibre chemical fibre, the added material by the way of being added while stirring obtain high strength non-woven fabric original
Material;
Step 2: the high strength non-woven fabric raw material obtained to step 1 sequentially adds phenyl-diformyl phenylenediamine, polymethylacrylic acid
Methyl esters, polycarbonate, ammonium polyphosphate, brightening agent, softening agent and compatilizer, while being added also in compliance with the mode being added while stirring
The principle of material obtains non-woven fabrics mixing extruded material;
Step 3: carrying out preliminarily dried to non-woven fabrics mixing extruded material is obtained, then dried to its vacuum drum drying equipment
It is dry;
Step 4: the non-woven fabrics mixing extruded material after drying, is uniformly transmitted to screw extruder, so that raw material is uniformly sent to
In filament spinning component equipped with filter screen, filters out impurity and sprayed from spinneret later, form as-spun fibre;
Step 5: as-spun fibre is uniformly laid on lapper lace curtaining after the cooling drawing-off of air-flow by diffusor duct, formation
Filament web, hot rolling, winding become non-woven fabrics after cutting;
Step 6: the non-woven fabrics quality after qualitative detects, qualified product carries out class wrapping.
Mixing temperature setting in step 1 is 160 DEG C -180 DEG C.In step 2 after the completion of added material, first stir
After 30min, static 10min, then 1h is stirred to it.The temperature setting of preliminarily dried is 120-150 DEG C in step 3.Step
The temperature setting of vacuum drum drying equipment drying is 160-180 DEG C in rapid three.
Embodiment three
A kind of glass fiber reinforcement bonded fabric, is made of following parts by weight of component: 90 mass parts of PP material particle, polypropylene fiber
40 mass parts, 30 mass parts of carbon fiber, 30 mass parts of glass fibre, 30 mass parts of ceramic fibre, 40 mass parts of polyester fiber, benzene
Two formyl phenylenediamines, 30 mass parts, 40 mass parts of polyamide fibre chemical fibre, 10 mass parts of polymethyl methacrylate, 30 mass of viscose rayon
Part, 9 mass parts of polycarbonate, 20 mass parts of ammonium polyphosphate, 4 mass of 4 mass parts of brightening agent, 4 mass parts of softening agent and compatilizer
Part.
A kind of preparation process of glass fiber reinforcement bonded fabric, comprising the following steps:
Step 1: into cylinder-shaped blender be added PP material particle, polypropylene fiber, glass fibre, carbon fiber, ceramic fibre,
Polyester fiber, viscose rayon and polyamide fibre chemical fibre, the added material by the way of being added while stirring obtain high strength non-woven fabric original
Material;
Step 2: the high strength non-woven fabric raw material obtained to step 1 sequentially adds phenyl-diformyl phenylenediamine, polymethylacrylic acid
Methyl esters, polycarbonate, ammonium polyphosphate, brightening agent, softening agent and compatilizer, while being added also in compliance with the mode being added while stirring
The principle of material obtains non-woven fabrics mixing extruded material;
Step 3: carrying out preliminarily dried to non-woven fabrics mixing extruded material is obtained, then dried to its vacuum drum drying equipment
It is dry;
Step 4: the non-woven fabrics mixing extruded material after drying, is uniformly transmitted to screw extruder, so that raw material is uniformly sent to
In filament spinning component equipped with filter screen, filters out impurity and sprayed from spinneret later, form as-spun fibre;
Step 5: as-spun fibre is uniformly laid on lapper lace curtaining after the cooling drawing-off of air-flow by diffusor duct, formation
Filament web, hot rolling, winding become non-woven fabrics after cutting;
Step 6: the non-woven fabrics quality after qualitative detects, qualified product carries out class wrapping.
Mixing temperature setting in step 1 is 160 DEG C -180 DEG C.In step 2 after the completion of added material, first stir
After 30min, static 10min, then 1h is stirred to it.The temperature setting of preliminarily dried is 120-150 DEG C in step 3.Step
The temperature setting of vacuum drum drying equipment drying is 160-180 DEG C in rapid three.
The embodiment of the present invention and the common non-woven fabric table of comparisons
Ignition point | Wear-resistant strength | |
Common non-woven fabric | 550℃ | It is extremely low |
Embodiment one | 630℃ | It is lower |
Embodiment two | 750℃ | It is higher |
Embodiment three | 800℃ | It is high |
From above table as can be seen that compared with common non-woven fabric, non-woven fabrics of the invention has good wear-resisting property and prevents
Fiery performance improves dual property by a kind of material of glass fibre, reduces the cost of nonwoven production.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (7)
1. a kind of glass fiber reinforcement bonded fabric, which is characterized in that be made of following parts by weight of component: PP material particle 70-
90 mass parts, polypropylene fiber 20-40 mass parts, carbon fiber 20-30 mass parts, glass fibre 20-30 mass parts, ceramic fibre
20-30 mass parts, polyester fiber 20-40 mass parts, phenyl-diformyl phenylenediamine 10-30 mass parts, polyamide fibre chemical fibre 20-40 mass
Part, polymethyl methacrylate 8-10 mass parts, viscose rayon 20-30 mass parts, polycarbonate 7-9 mass parts, ammonium polyphosphate
10-20 mass parts, brightening agent 2-4 mass parts, softening agent 2-4 mass parts and compatilizer 2-4 mass parts.
2. a kind of glass fiber reinforcement bonded fabric according to claim 1, which is characterized in that by following parts by weight of component
It is made: 80 mass parts of PP material particle, 30 mass parts of polypropylene fiber, 25 mass parts of carbon fiber, 25 mass parts of glass fibre, ceramics
25 mass parts of fiber, 30 mass parts of polyester fiber, 20 mass parts of phenyl-diformyl phenylenediamine, 30 mass parts of polyamide fibre chemical fibre, poly- methyl
9 mass parts of methyl acrylate, 25 mass parts of viscose rayon, 8 mass parts of polycarbonate, 15 mass parts of ammonium polyphosphate, 3 matter of brightening agent
Measure part, 3 mass parts of 3 mass parts of softening agent and compatilizer.
3. a kind of preparation process of glass fiber reinforcement bonded fabric, it is characterised in that: the following steps are included:
Step 1: into cylinder-shaped blender be added PP material particle, polypropylene fiber, glass fibre, carbon fiber, ceramic fibre,
Polyester fiber, viscose rayon and polyamide fibre chemical fibre, the added material by the way of being added while stirring obtain high strength non-woven fabric original
Material;
Step 2: the high strength non-woven fabric raw material obtained to step 1 sequentially adds phenyl-diformyl phenylenediamine, polymethylacrylic acid
Methyl esters, polycarbonate, ammonium polyphosphate, brightening agent, softening agent and compatilizer, while being added also in compliance with the mode being added while stirring
The principle of material obtains non-woven fabrics mixing extruded material;
Step 3: carrying out preliminarily dried to non-woven fabrics mixing extruded material is obtained, then dried to its vacuum drum drying equipment
It is dry;
Step 4: the non-woven fabrics mixing extruded material after drying, is uniformly transmitted to screw extruder, so that raw material is uniformly sent to
In filament spinning component equipped with filter screen, filters out impurity and sprayed from spinneret later, form as-spun fibre;
Step 5: as-spun fibre is uniformly laid on lapper lace curtaining after the cooling drawing-off of air-flow by diffusor duct, formation
Filament web, hot rolling, winding become non-woven fabrics after cutting;
Step 6: the non-woven fabrics quality after qualitative detects, qualified product carries out class wrapping.
4. a kind of preparation process of glass fiber reinforcement bonded fabric according to claim 3, it is characterised in that: the step
Mixing temperature setting in rapid one is 160 DEG C -180 DEG C.
5. a kind of preparation process of glass fiber reinforcement bonded fabric according to claim 3, it is characterised in that: the step
In rapid two after the completion of added material, 30min is first stirred, after static 10min, then 1h is stirred to it.
6. a kind of preparation process of glass fiber reinforcement bonded fabric according to claim 3, it is characterised in that: the step
The temperature setting of preliminarily dried is 120-150 DEG C in rapid three.
7. a kind of preparation process of glass fiber reinforcement bonded fabric according to claim 3, it is characterised in that: the step
The temperature setting of vacuum drum drying equipment drying is 160-180 DEG C in rapid three.