CN109096900A - A kind of environment-friendly water-based woodcare paint - Google Patents
A kind of environment-friendly water-based woodcare paint Download PDFInfo
- Publication number
- CN109096900A CN109096900A CN201810802180.3A CN201810802180A CN109096900A CN 109096900 A CN109096900 A CN 109096900A CN 201810802180 A CN201810802180 A CN 201810802180A CN 109096900 A CN109096900 A CN 109096900A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- water
- carbon nano
- woodcare paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to water paint fields, more particularly to a kind of environment-friendly water-based woodcare paint, the raw material including following parts by weight: 45-55 parts of aqueous polyurethane dispersion, 25-35 parts of pure water, 35-45 parts of acrylic acid ester emulsion, 5-8 parts of thickener, 0.5-1 parts of defoaming agent, 1-2 parts of dispersing agent, 1-2 parts of levelling agent, 10-15 parts of modified carbon nano tube fiber, modified 2-4 parts of tea seed cake powder, 15-20 parts of mixed plant slurry.The present invention improves the wearability of water paint by adding modified carbon nano tube fiber in the feed；The addition of tea seed cake powder is conducive to the adhesive force for promoting water paint；Mixed plant slurry makes water paint play the role of mosquito proof and promotes air freshness.
Description
Technical field
The present invention relates to water paint fields, and in particular to a kind of environment-friendly water-based woodcare paint.
Background technique
Currently, pollution situation of the countries in the world pay attention to day by day volatile organic matter (VOC) to air, and formulated various phases
Stringent limitation has been done in the regulation answered, the requirement to solvent volatile quantity in coating, and the Chinese government also increasingly payes attention in coating
The problem of VOC, has issued " 10 indoor decorating and refurnishing materials close to home substances limitations State General Administration for Quality Supervision's on December 10th, 2001
Mandatory standard ", State Environmental Protection Administration in 2005 has promulgated that HJ/T201-2005 " want by environmental labelling product technology
Seek-water paint " VOC content of clear stipulaties water-based industrial paint product is less than 250g/L.On June 1st, 2010 is issued strong
Property standard GB/T 24409-2009 " limits of harmful substances in car paint " processed limits VOC content in car paint
System.Under such overall situation, various Environmentally friendly coatings just come into being, such as high-solid-content paint, powdery paints, aqueous painting
Material etc., wherein water paint almost can reach the level of Diamond Search, therefore become coating because having very low volatile organic content
An important development direction.
Water paint refers to water as solvent or makees the coating of decentralized medium, there is environment-friendly tasteless, easy to clean, fire hazard
Low feature is mainly used in four big fields: steel construction industry, auto parts and components and mechanical equipment industry, automobile at present
Paint industry, rail traffic paint industry.Wood furniture industry is in great demand to coating, but water paint is in wood furniture
Industry is difficult to be received always, this is because wood furniture is often subject to wear, lacquer painting needs to have comparable wearability, aqueous
Paint has certain gap compared with traditional oil paint in wearability, greatly limits it and leads in wood furniture
The application in domain.
For example, Chinese invention CN102432815B discloses a kind of waterborne polyurethane resin, one kind of water paint is also belonged to,
Its waterborne polyurethane resin prepared is completed under unrestricted environmentally friendly solvent dilution, and preparation process and gained produce
Object has all reached the standard of environmental protection, but it is demonstrated experimentally that its wearability has certain gap compared to traditional paint.
Therefore, the good aqueous woodware paint of exploitation wearability has become an urgent demand of water paint industry development.
Summary of the invention
In view of the drawbacks of the prior art, the present invention provides a kind of environment-friendly water-based woodcare paints, are added to modified tea seed cake powder, change
Property carbon nano-fiber and plant slurry, not only environment-friendly tasteless, also has stronger wearability, while having mosquito repellent and to promote air clear
The effect newly spent.
To achieve the above object, the present invention adopts the following technical scheme:
A kind of environment-friendly water-based woodcare paint, the raw material including following parts by weight: 45-55 parts of aqueous polyurethane dispersion, pure water 25-35
Part, it is 35-45 parts of acrylic acid ester emulsion, 5-8 parts of thickener, 0.5-1 parts of defoaming agent, 1-2 parts of dispersing agent, 1-2 parts of levelling agent, modified
10-15 parts of carbon nano-fiber, modified 2-4 parts of tea seed cake powder, 15-20 parts of mixed plant slurry.
Preferably, a kind of environment-friendly water-based woodcare paint includes the raw material of following parts by weight: aqueous polyurethane dispersion 50
Part, 30 parts of pure water, 40 parts of acrylic acid ester emulsion, 6 parts of thickener, 0.8 part of defoaming agent, 1.5 parts of dispersing agent, 1.5 parts of levelling agent, change
Property 12 parts of carbon nano-fiber, modified 3 parts of tea seed cake powder, 18 parts of mixed plant slurry.
Preferably, the defoaming agent is the polysiloxane hydrophobic particle that non-volatile part content is greater than 98wt%.
Preferably, the dispersing agent is polyisobutene maleate.
Preferably, the levelling agent is the ionic acrylic copolymer that non-volatile part content is 40-60wt%.
Preferably, the thickener is carragheen.
Preferably, the modified tea seed cake powder is added in high-speed mixer by the tea seed cake powder that will be dried, 70 DEG C -75 DEG C
Under be stirred, be added tea seed cake powder weight 1-1.5% silane coupling agent, stir 8-10 minutes, be prepared.
Preferably, the modified carbon nano tube fiber is by the way that the cetomacrogol 1000-1500 of 0.4-0.6g is dissolved in 40-
In 50ml pure water, ultrasonic disperse 15-20 minutes, finely dispersed dispersion liquid is obtained；0.3-0.5g carbon is added in dispersion liquid to receive
Rice fiber, is stirred 12h, so that polyethylene glycol is substantially adhered to carbon nano-fiber surface, be prepared.
Preferably, the mixed plant slurry is prepared by the raw material of following parts by weight: 3 parts of Chinese Stellera Root, asarum 3
Part, 4 parts of santal, 5 parts of wheat flour, 5 parts of folium artemisiae argyi, 2 parts of rose, 2 parts of rubber powder, 2 parts of atlapulgite, 50 parts of water.
Preferably, the mixed plant slurry is prepared by following steps: by Chinese Stellera Root, asarum, santal, Chinese mugwort
After leaf, rose clean up, dry 4 hours, are then comminuted into the mixed-powder of 300-500 mesh at 60-70 DEG C；Then
Wheat flour, rubber powder are stirred evenly into the water, are heated to 60-80 DEG C；Residual components are added, at 800-1000 revs/min
It is stirred 15-20 minutes under clock, is cooled to room temperature, is eventually adding mixed-powder, be ground into 600-800 mesh slurry.
Compared with prior art, the invention has the following beneficial effects:
(1) present invention adds modified carbon nano tube fibers, improve the wear-resisting property of water paint；The addition of modified tea seed cake powder, increases
The adhesive force of water paint is added.Using the unique one-dimentional structure of carbon nano-fiber, physics and chemical property, make itself and modified tea seed cake
Powder, aqueous polyurethane dispersion and acrylic acid ester emulsion collective effect generate synergistic function.
(2) present invention adds mixed plant slurries, have the effect of mosquito proof, and wood furniture is made to have good stay
Fragrant effect promotes indoor air freshness.
Specific embodiment
Present invention will be further explained below with reference to specific examples.These embodiments are merely to illustrate the present invention and do not have to
In limiting the scope of the invention.
Embodiment 1
A kind of environment-friendly water-based woodcare paint, the raw material including following parts by weight: 45 parts of aqueous polyurethane dispersion, 25 parts of pure water, third
35 parts of olefin(e) acid ester lotion, 5 parts of thickener, 0.5 part of defoaming agent, 1 part of dispersing agent, 1 part of levelling agent, 10 parts of modified carbon nano tube fiber,
Modified 2 parts of tea seed cake powder, 15 parts of mixed plant slurry.
Defoaming agent is the polysiloxane hydrophobic particle that non-volatile part content is greater than 98wt% in the present embodiment.
Dispersing agent is polyisobutene maleate in the present embodiment.
Levelling agent is the ionic acrylic copolymer that non-volatile part content is 40wt% in the present embodiment.
Thickener is carragheen in the present embodiment.
Modified tea seed cake powder is added in high-speed mixer by the tea seed cake powder that will be dried in the present embodiment, at 70 DEG C DEG C into
Row stirring, is added the silane coupling agent of tea seed cake powder weight 1%, stirs 8 minutes, is prepared.
Modified carbon nano tube fiber is the ultrasound by the way that the cetomacrogol 1000 of 0.4g to be dissolved in 40ml pure water in the present embodiment
Dispersion 15 minutes, obtains finely dispersed dispersion liquid；0.3g carbon nano-fiber is added in dispersion liquid, is stirred 12h, makes to gather
Ethylene glycol is substantially adhered to carbon nano-fiber surface, is prepared.
Mixed plant slurry is prepared by the raw material of following parts by weight in the present embodiment: 3 parts of Chinese Stellera Root, 3 parts of asarum,
4 parts of santal, 5 parts of wheat flour, 5 parts of folium artemisiae argyi, 2 parts of rose, 2 parts of rubber powder, 2 parts of atlapulgite, 50 parts of water.
Mixed plant slurry is prepared by following steps in the present embodiment: by Chinese Stellera Root, asarum, santal, folium artemisiae argyi,
After rose cleans up, dry 4 hours, are then comminuted into the mixed-powder of 300 mesh at 60 DEG C；Then by wheat flour
Powder, rubber powder stir evenly into the water, are heated to 60 DEG C；Residual components are added, are stirred 15 minutes under 800 revs/min, it is cold
But to room temperature, it is eventually adding mixed-powder, is ground into 600 mesh slurries.
Embodiment 2
A kind of environment-friendly water-based woodcare paint, the raw material including following parts by weight: 55 parts of aqueous polyurethane dispersion, 35 parts of pure water, third
45 parts of olefin(e) acid ester lotion, 1 part of defoaming agent, 2 parts of dispersing agent, 2 parts of levelling agent, 15 parts of modified carbon nano tube fiber, changes by 8 parts of thickener
4 parts of powder of tea seed cake, 20 parts of mixed plant slurry of property.
Defoaming agent is the polysiloxane hydrophobic particle that non-volatile part content is greater than 98wt% in the present embodiment.
Dispersing agent is polyisobutene maleate in the present embodiment.
Levelling agent is the ionic acrylic copolymer that non-volatile part content is 60wt% in the present embodiment.
Thickener is carragheen in the present embodiment.
Modified tea seed cake powder is added in high-speed mixer by the tea seed cake powder that will be dried in the present embodiment, at 75 DEG C into
Row stirring, is added the silane coupling agent of tea seed cake powder weight 1.5%, stirs 10 minutes, is prepared.
Modified carbon nano tube fiber is the ultrasound by the way that the polyethylene glycol 1500 of 0.6g to be dissolved in 50ml pure water in the present embodiment
Dispersion 20 minutes, obtains finely dispersed dispersion liquid；0.5g carbon nano-fiber is added in dispersion liquid, is stirred 12h, makes to gather
Ethylene glycol is substantially adhered to carbon nano-fiber surface, is prepared.
Mixed plant slurry is prepared by the raw material of following parts by weight in the present embodiment: 3 parts of Chinese Stellera Root, 3 parts of asarum,
4 parts of santal, 5 parts of wheat flour, 5 parts of folium artemisiae argyi, 2 parts of rose, 2 parts of rubber powder, 2 parts of atlapulgite, 50 parts of water.
Mixed plant slurry is prepared by following steps in the present embodiment: by Chinese Stellera Root, asarum, santal, folium artemisiae argyi,
After rose cleans up, dry 4 hours, are then comminuted into the mixed-powder of 500 mesh at 70 DEG C；Then by wheat flour
Powder, rubber powder stir evenly into the water, are heated to 80 DEG C；Residual components are added, are stirred 20 minutes under 1000 revs/min,
It is cooled to room temperature, is eventually adding mixed-powder, be ground into 800 mesh slurries.
Embodiment 3
A kind of environment-friendly water-based woodcare paint, the raw material including following parts by weight: 50 parts of aqueous polyurethane dispersion, 30 parts of pure water, third
40 parts of olefin(e) acid ester lotion, 6 parts of thickener, 0.8 part of defoaming agent, 1.5 parts of dispersing agent, 1.5 parts of levelling agent, modified carbon nano tube fiber 12
Part, modified 3 parts of tea seed cake powder, 18 parts of mixed plant slurry.
Defoaming agent is the polysiloxane hydrophobic particle that non-volatile part content is greater than 98wt% in the present embodiment.
Dispersing agent is polyisobutene maleate in the present embodiment.
Levelling agent is the ionic acrylic copolymer that non-volatile part content is 50wt% in the present embodiment.
Thickener is carragheen in the present embodiment.
Modified tea seed cake powder is added in high-speed mixer by the tea seed cake powder that will be dried in the present embodiment, is carried out at 72 DEG C
The silane coupling agent of tea seed cake powder weight 1.2% is added in stirring, stirs 9 minutes, is prepared.
Modified carbon nano tube fiber is the ultrasound by the way that the cetomacrogol 1000 of 0.5g to be dissolved in 45ml pure water in the present embodiment
Dispersion 18 minutes, obtains finely dispersed dispersion liquid；0.4g carbon nano-fiber is added in dispersion liquid, is stirred 12h, makes to gather
Ethylene glycol is substantially adhered to carbon nano-fiber surface, is prepared.
Mixed plant slurry is prepared by the raw material of following parts by weight in the present embodiment: 3 parts of Chinese Stellera Root, 3 parts of asarum,
4 parts of santal, 5 parts of wheat flour, 5 parts of folium artemisiae argyi, 2 parts of rose, 2 parts of rubber powder, 2 parts of atlapulgite, 50 parts of water.
Mixed plant slurry is prepared by following steps in the present embodiment: by Chinese Stellera Root, asarum, santal, folium artemisiae argyi,
After rose cleans up, dry 4 hours, are then comminuted into the mixed-powder of 400 mesh at 65 DEG C；Then by wheat flour
Powder, rubber powder stir evenly into the water, are heated to 70 DEG C；Residual components are added, are stirred 18 minutes under 900 revs/min, it is cold
But to room temperature, it is eventually adding mixed-powder, is ground into 700 mesh slurries.
Water paint obtained by embodiment 1-3 and general water paint performance test the result is as follows:
| Embodiment 1 | Embodiment 2 | Embodiment 3 | Common water borne paint | |
| Adhesive force, grade | 1 | 1 | 1 | 3 |
| Solvent resistant wiping (ethyl alcohol) | It sees the bottom for 74 times | It sees the bottom for 88 times | It sees the bottom for 81 times | It sees the bottom for 32 times |
From experimental result as can be seen that water paint of the invention is all substantially better than common water borne paint on adhesive force and wearability.
Specific embodiments of the present invention are described above.It is to be appreciated that the invention is not limited to above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring substantive content of the invention.
Claims (10)
1. a kind of environment-friendly water-based woodcare paint, which is characterized in that the raw material including following parts by weight: aqueous polyurethane dispersion 45-
55 parts, 25-35 parts of pure water, 35-45 parts of acrylic acid ester emulsion, 5-8 parts of thickener, 0.5-1 parts of defoaming agent, 1-2 parts of dispersing agent, stream
Flat agent 1-2 parts, 10-15 parts of modified carbon nano tube fiber, modified 2-4 parts of tea seed cake powder, 15-20 parts of mixed plant slurry.
2. a kind of environment-friendly water-based woodcare paint according to claim 1, which is characterized in that the raw material including following parts by weight:
50 parts of aqueous polyurethane dispersion, 30 parts of pure water, 40 parts of acrylic acid ester emulsion, 6 parts of thickener, 0.8 part of defoaming agent, dispersing agent
1.5 parts, 1.5 parts of levelling agent, 12 parts of modified carbon nano tube fiber, modified 3 parts of tea seed cake powder, 18 parts of mixed plant slurry.
3. a kind of environment-friendly water-based woodcare paint according to claim 1 or 2, it is characterised in that: the defoaming agent is non-volatile
Part content is greater than the polysiloxane hydrophobic particle of 98wt%.
4. a kind of environment-friendly water-based woodcare paint according to claim 1 or 2, it is characterised in that: the dispersing agent is poly- isobutyl
Alkene maleate.
5. a kind of environment-friendly water-based woodcare paint according to claim 1 or 2, it is characterised in that: the levelling agent is non-volatile
The ionic acrylic copolymer that part content is 40-60wt%.
6. a kind of environment-friendly water-based woodcare paint according to claim 1 or 2, which is characterized in that the thickener is carragheen.
7. a kind of environment-friendly water-based woodcare paint according to claim 1 or 2, it is characterised in that: the modified tea seed cake powder is logical
It crosses and dry tea seed cake powder is added in high-speed mixer, be stirred at 70 DEG C -75 DEG C, be added tea seed cake powder weight 1-1.5%'s
Silane coupling agent is stirred 8-10 minutes, is prepared.
8. a kind of environment-friendly water-based woodcare paint according to claim 1 or 2, it is characterised in that: the modified carbon nano tube fiber
It is ultrasonic disperse 15-20 minutes, to be divided by the way that the cetomacrogol 1000-1500 of 0.4-0.6g to be dissolved in 40-50ml pure water
Dissipate uniform dispersion liquid；0.3-0.5g carbon nano-fiber is added in dispersion liquid, is stirred 12h, keeps polyethylene glycol sufficiently attached
On carbon nano-fiber surface, be prepared.
9. a kind of environment-friendly water-based woodcare paint according to claim 1 or 2, which is characterized in that the mixed plant slurry by
The raw material of following parts by weight is prepared: 3 parts of Chinese Stellera Root, 3 parts of asarum, and 4 parts of santal, 5 parts of wheat flour, 5 parts of folium artemisiae argyi, rose
Spend 2 parts, 2 parts of rubber powder, 2 parts of atlapulgite, 50 parts of water.
10. mixed plant slurry according to claim 9, which is characterized in that be prepared by following steps: by winter daphne
After radix euphorbiae lantu, asarum, santal, folium artemisiae argyi, rose clean up, dry 4 hours, are then comminuted into 300-500 at 60-70 DEG C
Purpose mixed-powder；Then wheat flour, rubber powder are stirred evenly into the water, is heated to 60-80 DEG C；Add it is remaining at
Point, it is stirred 15-20 minutes under 800-1000 revs/min, is cooled to room temperature, is eventually adding mixed-powder, be ground into 600-800
Mesh slurry.