CN109082022A - A kind of Wood-plastic material and preparation method thereof for flowerpot - Google Patents
A kind of Wood-plastic material and preparation method thereof for flowerpot Download PDFInfo
- Publication number
- CN109082022A CN109082022A CN201710449231.4A CN201710449231A CN109082022A CN 109082022 A CN109082022 A CN 109082022A CN 201710449231 A CN201710449231 A CN 201710449231A CN 109082022 A CN109082022 A CN 109082022A
- Authority
- CN
- China
- Prior art keywords
- parts
- wood
- plastic material
- flowerpot
- mold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The Wood-plastic material and preparation method thereof that the invention discloses a kind of for flowerpot, it is characterized in that, by weight, it is made of following component: 19-25 parts of polyvinyl chloride, 60-80 parts of glass fibre, 5-10 parts of dimethylethanolamine, 5-10 parts of ammonium polyphosphate (APP), 5-8 parts of sodium methyl silicate, 2-3 parts of aluminium oxide, 0.5-1 parts of polytetrahydrofuran, Ultraviolet Absorber UV-P 0.2-0.5,1 part of phytosterol, 8-10 parts of hardening agent.The present invention also provides the preparation methods of the flowerpot Wood-plastic material.The problems such as above-mentioned formula combination preparation method is able to solve existing Wood-plastic material as flowerpot materials'use, and that there are aerations is insufficient, easy to aging, cracking.
Description
Technical field
The present invention relates to Wood-plastic material fields, and in particular to a kind of Wood-plastic material for flowerpot.
Background technique
Flowerpot plants a kind of vessel of flower, for the small inverted round stage in the big bottom end of mouth or terrace edge shape.Plant the flowerpot of flowers
It is various informative, it is not of uniform size.The characteristics of production of flowers and plants person or the personage that raises flowers can be according to the characteristics and needs and flowerpot of flowers
Flowerpot is selected, according to making material difference, can be divided into many types.It is mud, porcelain, plastics, Shi Jimu that usual flowerpot, which is with quality,
The basin of the materials such as product production describes device, is mainly used in afforestation, landscape planting, private garden, subdistrict greening.Wood moulding material
Material, it is few in the field application study as a kind of green material, so existing Wood-plastic material makes as flowerpot material
With the problems such as that there are hydrophobic aerations is insufficient, easy to aging, cracking.
Summary of the invention
Technical problem to be solved by the present invention lies in a kind of flowerpot Wood-plastic material and preparation method thereof is provided, can solve
Certainly existing Wood-plastic material as flowerpot materials'use, existing aeration is insufficient, it is easy to aging, cracking the problems such as.
In order to solve the above-mentioned prior art problems, the present invention uses following scheme:
A kind of Wood-plastic material and preparation method thereof for flowerpot, which is characterized in that by weight, be made of following component:
19-25 parts of polyvinyl chloride, 60-80 parts of glass fibre, 5-10 parts of dimethylethanolamine, 5-10 parts of ammonium polyphosphate (APP), methyl silicon
Sour sodium 5-8 parts, 2-3 parts of aluminium oxide, 0.5-1 parts of polytetrahydrofuran, Ultraviolet Absorber UV-P 0.2-0.5,1 part of phytosterol,
8-10 parts of hardening agent.
The preparation method of the flowerpot Wood-plastic material, comprising the following steps:
(1) it stocks up: after glass fibre is impregnated 2 hours in water, using single screw extrusion machine, squeezing out remove in an extruder
The plant fiber arrived is placed into fiber crusher and is crushed, broken plant fiber is crossed 80 meshes, is dried for standby, aqueous
Measure < 2wt%；
(2) mixing: step (1) is obtained into glass fibre and above-mentioned raw materials by formula, by high-speed mixer, is mixed under room temperature equal
It is even；
(3) mat formation: after molding garden furniture mold will be needed to be uniformly coated with release agent, by step (2) uniformly mixed raw material
Mat formation into the former of mold；
(4) precompressed: apply pressure 5-6MPa pressure to the raw material after mating formation in step (3) mold；
(5) hot pressing: while to pressure 10-15MPa pressure is applied to raw material after step (4) precompressed, temperature is promoted to 180-200
DEG C, it maintains 5 minutes；
(6) it demoulds: maintaining mold pressure in hot pressing, after Wood-plastic material temperature is down to 60 DEG C or less in mold, pressure release demoulding,
Obtain flowerpot Wood-plastic material manufactured goods.
Preferably, the Ultraviolet Absorber UV-P, main component is 2-(2 ˊ--5 ˊ of hydroxyl-aminomethyl phenyl) benzo three
Nitrogen azoles.
Preferably, the hardening agent is by 9-15 parts of magnesia, 9-15 parts of calcium carbonate, 5-9 parts of molybdenum trioxides, 5-9 parts
The powder mixing of melamine cyanurate is obtained by being granulated, granule size 0.5-1mm.
The invention has the beneficial effects that: the present invention provide by adopting the above technical scheme a kind of flowerpot Wood-plastic material and its
Preparation method is able to solve existing Wood-plastic material as flowerpot materials'use, there are aerations insufficient, easy to aging, cracking etc.
Problem.
Specific embodiment
Below in conjunction with specific embodiment, the present invention will be described in detail, herein illustrative examples and explanation of the invention
For explaining the present invention, but it is not as a limitation of the invention.
Embodiment
A kind of Wood-plastic material and preparation method thereof for flowerpot, which is characterized in that by weight, by following component system
At: 19-25 parts of polyvinyl chloride, 60-80 parts of glass fibre, 5-10 parts of dimethylethanolamine, 5-10 parts of ammonium polyphosphate (APP), first
5-8 parts of base sodium metasilicate, 2-3 parts of aluminium oxide, 0.5-1 parts of polytetrahydrofuran, Ultraviolet Absorber UV-P 0.2-0.5, phytosterol 1
Part, 8-10 parts of hardening agent.
The preparation method of the flowerpot Wood-plastic material, comprising the following steps:
(1) it stocks up: after glass fibre is impregnated 2 hours in water, using single screw extrusion machine, squeezing out remove in an extruder
The plant fiber arrived is placed into fiber crusher and is crushed, broken plant fiber is crossed 80 meshes, is dried for standby, aqueous
Measure < 2wt%；
(2) mixing: step (1) is obtained into glass fibre and above-mentioned raw materials by formula, by high-speed mixer, is mixed under room temperature equal
It is even；
(3) mat formation: after molding garden furniture mold will be needed to be uniformly coated with release agent, by step (2) uniformly mixed raw material
Mat formation into the former of mold；
(4) precompressed: apply pressure 5-6MPa pressure to the raw material after mating formation in step (3) mold；
(5) hot pressing: while to pressure 10-15MPa pressure is applied to raw material after step (4) precompressed, temperature is promoted to 180-200
DEG C, it maintains 5 minutes；
(6) it demoulds: maintaining mold pressure in hot pressing, after Wood-plastic material temperature is down to 60 DEG C or less in mold, pressure release demoulding,
Obtain flowerpot Wood-plastic material manufactured goods.
In the present embodiment, the Ultraviolet Absorber UV-P, main component is 2-(2 ˊ--5 ˊ of hydroxyl-aminomethyl phenyl) benzo
Triazole；
In the present embodiment, the hardening agent is by 9-15 parts of magnesia, 9-15 parts of calcium carbonate, 5-9 parts of molybdenum trioxides, 5-9 part three
The powder mixing of poly cyanamid cyanurate is obtained by being granulated, granule size 0.5-1mm.
The technical principle of the invention is described above in combination with a specific embodiment.These descriptions are intended merely to explain of the invention
Principle, and shall not be construed in any way as a limitation of the scope of protection of the invention.Based on the explanation herein, the technology of this field
Personnel can associate with other specific embodiments of the invention without creative labor, these modes are fallen within
Within protection scope of the present invention.
Claims (3)
1. a kind of Wood-plastic material and preparation method thereof for flowerpot, which is characterized in that by weight, by following component system
At: 19-25 parts of polyvinyl chloride, 60-80 parts of glass fibre, 5-10 parts of dimethylethanolamine, 5-10 parts of ammonium polyphosphate (APP), first
5-8 parts of base sodium metasilicate, 2-3 parts of aluminium oxide, 0.5-1 parts of polytetrahydrofuran, Ultraviolet Absorber UV-P 0.2-0.5, phytosterol 1
Part, 8-10 parts of hardening agent.
2. the Wood-plastic material and preparation method thereof according to claim 1 for flowerpot, which is characterized in that including following step
It is rapid:
(1) it stocks up: after glass fibre is impregnated 2 hours in water, using single screw extrusion machine, squeezing out remove in an extruder
The plant fiber arrived is placed into fiber crusher and is crushed, broken plant fiber is crossed 80 meshes, is dried for standby, aqueous
Measure < 2wt%；
(2) mixing: step (1) is obtained into glass fibre and above-mentioned raw materials by formula, by high-speed mixer, is mixed under room temperature equal
It is even；
(3) mat formation: after molding garden furniture mold will be needed to be uniformly coated with release agent, by step (2) uniformly mixed raw material
Mat formation into the former of mold；
(4) precompressed: apply pressure 5-6MPa pressure to the raw material after mating formation in step (3) mold；
(5) hot pressing: while to pressure 10-15MPa pressure is applied to raw material after step (4) precompressed, temperature is promoted to 180-200
DEG C, it maintains 5 minutes；
(6) it demoulds: maintaining mold pressure in hot pressing, after Wood-plastic material temperature is down to 60 DEG C or less in mold, pressure release demoulding,
Obtain flowerpot Wood-plastic material manufactured goods.
3. the Wood-plastic material and preparation method thereof according to claim 1 for flowerpot, which is characterized in that the ultraviolet light
Absorbent UV-P, main component are 2-(2 ˊ--5 ˊ of hydroxyl-aminomethyl phenyls) benzotriazole；The hardening agent is by 9-15 parts of oxygen
The powder mixing for changing magnesium, 9-15 parts of calcium carbonate, 5-9 parts of molybdenum trioxides, 5-9 parts of melamine cyanurates is obtained by being granulated,
Granule size is 0.5-1mm.