CN109057280A - A kind of construction technology of exterior wall decorating tile - Google Patents
A kind of construction technology of exterior wall decorating tile Download PDFInfo
- Publication number
- CN109057280A CN109057280A CN201810939448.8A CN201810939448A CN109057280A CN 109057280 A CN109057280 A CN 109057280A CN 201810939448 A CN201810939448 A CN 201810939448A CN 109057280 A CN109057280 A CN 109057280A
- Authority
- CN
- China
- Prior art keywords
- parts
- decorative brick
- mortar
- thermal insulation
- laid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of construction technology of exterior wall decorating tile, mainly comprise the steps that 1) External Wall surface is handled, External Wall surface is repaired；2) watering is carried out to metope to moisten, pop up absolute altitude control line in outer wall body surrounding；3) it is laid with and selects waterproof thermal insulation mortar, decorative brick is laid on mortar by mortar thickness 20-30mm as requested, with rubber hammer tapping decorative brick until closely knit smooth reach requirement；4) after decorative brick has been spread, 24-36h is stood, cleaning jointing is carried out, should first be rejected impurity in decorative brick gap before jointing, then with dedicated gap filler jointing.The defects of present invention is cleared up and repaired, avoid hollowing, cracking and dusting by shifting to an earlier date External Wall surface is conducive to the laying of decorative brick；Decorative brick be laid with before by clear water immersion, the decorative brick back side is moistened before paving, so that decorative brick and mortar are bonded that ability is stronger, and sticking effect is more preferable.
Description
Technical field
The present invention relates to technical field of building construction, the construction technology of specifically a kind of exterior wall decorating tile.
Background technique
Exterior wall decorating tile is mainly used for decoration and the protection of external wall.Exterior wall decorating tile not only decorates whole building,
Simultaneously as its acid and alkali-resistance, physical and chemical performance is stablized, and plays an important role to protection wall, moreover it is possible to cold-proof heat insulation；It is outer to meet
Wall decoration is personalized to be developed with rich requirement, outer wall decoration technique and gimmick towards high-grade, top grade.
For the construction technology of existing exterior wall decorating tile there are certain defect, decorative brick is easy to appear the shape to fall off after putting up
Condition, not only follow-up maintenance trouble, can also cause to damage to personal safety；The construction technology of existing exterior wall decorating tile is using common
Mortar is constructed, and ordinary mortar viscosity not enough, is easy to appear decorative brick and exterior wall faced deorative after exterior wall decorating tile construction
Leakage, and the waterproof thermal-insulated performance of ordinary mortar is general, and cold-proof heat insulation effect is difficult to reach higher level.
Summary of the invention
The purpose of the present invention is to provide a kind of construction technologies of exterior wall decorating tile, to solve to propose in above-mentioned background technique
The problem of.
To achieve the above object, the invention provides the following technical scheme:
A kind of construction technology of exterior wall decorating tile, comprising the following steps:
1) External Wall surface is handled, and dust, sundries are cleaned out, and External Wall surface is repaired, avoid hollowing,
The defects of cracking and dusting；
2) watering is carried out to metope to moisten, wait 24-36h, pop up absolute altitude control line in outer wall body surrounding；
3) it is laid with and selects waterproof thermal insulation mortar, mortar thickness 20-30mm moistens the decorative brick back side before paving, protects
Positive drying is held, decorative brick is laid on mortar as requested, with rubber hammer tapping decorative brick until closely knit smooth reach
It is required that；
4) after decorative brick has been spread, 24-36h is stood, cleaning jointing is carried out, should first be picked impurity in decorative brick gap before jointing
It removes, then with dedicated gap filler jointing；
5) tile surface is managed with objects such as cotton yarns again after completion for 24 hours；
The waterproof thermal insulation mortar includes the following raw material according to parts by weight: 60-80 parts of portland cement, quartz sand 150-
180 parts, 20-30 parts of Phenolic resin powder, 15-20 parts of alumina silicate, 15-25 parts of sodium carboxymethylcellulose, acrylate
5-10 parts of ethyl ester, 20-30 parts of glass bead, 10-20 parts of porous ceramic grain, 6-10 parts of glass fibre, 5-10 parts of sawdust, additive 8-
12 parts, 160-200 parts of water.
As a further solution of the present invention: the waterproof thermal insulation mortar includes the following raw material according to parts by weight: silicic acid
65-75 parts of salt cement, 160-170 parts of quartz sand, 22-28 parts of Phenolic resin powder, 16-19 parts of alumina silicate, carboxymethyl cellulose
18-22 parts of sodium, 6-9 parts of dimethylaminoethyl acrylate, 22-28 parts of glass bead, 12-18 parts of porous ceramic grain, glass fibre 7-9
Part, 6-8 parts of sawdust, 9-11 parts of additive, 170-190 parts of water.
As further scheme of the invention: the waterproof thermal insulation mortar includes the following raw material according to parts by weight: silicon
70 parts of acid salt cement, 165 parts of quartz sand, 25 parts of Phenolic resin powder, 18 parts of alumina silicate, 20 parts of sodium carboxymethylcellulose, propylene
7 parts of sour dimethylaminoethyl, 25 parts of glass bead, 15 parts of porous ceramic grain, 8 parts of glass fibre, 7 parts of sawdust, 10 parts of additive, water
180 parts.
As further scheme of the invention: decorative brick needs to impregnate 2h or more in clear water before being laid with, not to brick body
Bubbling, taking-up are dried stand-by.
As the present invention further scheme: the preparation method of the waterproof thermal insulation mortar the following steps are included:
1) portland cement, quartz sand, water are mixed, under 600-800r/min speed conditions, stirs 10-15min, obtain
Obtain slurry I；
2) Phenolic resin powder, sodium carboxymethylcellulose, acrylate is added in the slurry I obtained to step 1)
Ethyl ester, additive, are warming up to 60-80 DEG C, under the revolving speed of 800-1000r/min, stir 30-50min, obtain slurry II；
3) alumina silicate, glass bead, porous ceramic grain, glass fibre, sawdust is added in the slurry II obtained to step 2),
Under the revolving speed of 300-500r/min, 30-50min, discharging are stirred.
Compared with prior art, the beneficial effects of the present invention are:
The defects of present invention is cleared up and is repaired, avoid hollowing, cracking and dusting by shifting to an earlier date External Wall surface, favorably
In the laying of decorative brick；Decorative brick is impregnated before being laid with by clear water, is moistened before paving to the decorative brick back side, so that decorative brick
It is bonded that ability is stronger, and sticking effect is more preferable with mortar；Using special waterproof thermal insulation mortar, not only viscosity is higher, decorative brick
It is laid with that intensity is higher, and waterproof thermal-insulated effect is more preferable, improves service life, reduces ambient temperature to indoor influence,
It is energy saving.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described,
Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based in the present invention
Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts, all
Belong to the scope of protection of the invention.
Embodiment 1
A kind of construction technology of exterior wall decorating tile, which comprises the following steps:
1) External Wall surface is handled, and dust, sundries are cleaned out, and External Wall surface is repaired, avoid hollowing,
The defects of cracking and dusting；
2) watering is carried out to metope to moisten, be waited for 24 hours, pop up absolute altitude control line in outer wall body surrounding；
3) it is laid with and selects waterproof thermal insulation mortar, mortar thickness 20mm moistens the decorative brick back side before paving, keeps just
Face is dry, and decorative brick is laid on mortar as requested, with rubber hammer tapping decorative brick until closely knit smooth reach requirement；
4) it after decorative brick has been spread, stands for 24 hours, carries out cleaning jointing, should first be rejected impurity in decorative brick gap before jointing,
Again with dedicated gap filler jointing；
5) tile surface is managed with objects such as cotton yarns again after completion for 24 hours；
The waterproof thermal insulation mortar includes the following raw material according to parts by weight: 60 parts of portland cement, 150 parts of quartz sand,
20 parts of Phenolic resin powder, 15 parts of alumina silicate, 15 parts of sodium carboxymethylcellulose, 5 parts of dimethylaminoethyl acrylate, glass bead
20 parts, 10 parts of porous ceramic grain, 6 parts of glass fibre, 5 parts of sawdust, 8 parts of additive, 160 parts of water.
Wherein, decorative brick needs to impregnate 2h or more in clear water before being laid with, and to brick body not bubbling, taking-up is dried stand-by.
Wherein, the waterproof thermal insulation mortar preparation method the following steps are included:
1) portland cement, quartz sand, water are mixed, under 600r/min speed conditions, stirs 10min, obtains slurry
Ⅰ；
2) Phenolic resin powder, sodium carboxymethylcellulose, acrylate is added in the slurry I obtained to step 1)
Ethyl ester, additive are warming up to 60 DEG C, under the revolving speed of 800r/min, stir 30min, obtain slurry II；
3) alumina silicate, glass bead, porous ceramic grain, glass fibre, sawdust is added in the slurry II obtained to step 2),
Under the revolving speed of 300r/min, 30min, discharging are stirred.
Embodiment 2
A kind of construction technology of exterior wall decorating tile, which comprises the following steps:
1) External Wall surface is handled, and dust, sundries are cleaned out, and External Wall surface is repaired, avoid hollowing,
The defects of cracking and dusting；
2) watering is carried out to metope to moisten, wait 27h, pop up absolute altitude control line in outer wall body surrounding；
3) it is laid with and selects waterproof thermal insulation mortar, mortar thickness 22mm moistens the decorative brick back side before paving, keeps just
Face is dry, and decorative brick is laid on mortar as requested, with rubber hammer tapping decorative brick until closely knit smooth reach requirement；
4) after decorative brick has been spread, 27h is stood, cleaning jointing is carried out, should first be rejected impurity in decorative brick gap before jointing,
Again with dedicated gap filler jointing；
5) tile surface is managed with objects such as cotton yarns again after completion for 24 hours；
The waterproof thermal insulation mortar includes the following raw material according to parts by weight: 65 parts of portland cement, 160 parts of quartz sand,
22 parts of Phenolic resin powder, 16 parts of alumina silicate, 18 parts of sodium carboxymethylcellulose, 6 parts of dimethylaminoethyl acrylate, glass bead
28 parts, 18 parts of porous ceramic grain, 9 parts of glass fibre, 8 parts of sawdust, 11 parts of additive, 190 parts of water.
Wherein, decorative brick needs to impregnate 2h or more in clear water before being laid with, and to brick body not bubbling, taking-up is dried stand-by.
Wherein, the waterproof thermal insulation mortar preparation method the following steps are included:
1) portland cement, quartz sand, water are mixed, under 700r/min speed conditions, stirs 12min, obtains slurry
Ⅰ；
2) Phenolic resin powder, sodium carboxymethylcellulose, acrylate is added in the slurry I obtained to step 1)
Ethyl ester, additive are warming up to 70 DEG C, under the revolving speed of 900r/min, stir 40min, obtain slurry II；
3) alumina silicate, glass bead, porous ceramic grain, glass fibre, sawdust is added in the slurry II obtained to step 2),
Under the revolving speed of 400r/min, 40min, discharging are stirred.
Embodiment 3
A kind of construction technology of exterior wall decorating tile, which comprises the following steps:
1) External Wall surface is handled, and dust, sundries are cleaned out, and External Wall surface is repaired, avoid hollowing,
The defects of cracking and dusting；
2) watering is carried out to metope to moisten, wait 30h, pop up absolute altitude control line in outer wall body surrounding；
3) it is laid with and selects waterproof thermal insulation mortar, mortar thickness 24mm moistens the decorative brick back side before paving, keeps just
Face is dry, and decorative brick is laid on mortar as requested, with rubber hammer tapping decorative brick until closely knit smooth reach requirement；
4) after decorative brick has been spread, 30h is stood, cleaning jointing is carried out, should first be rejected impurity in decorative brick gap before jointing,
Again with dedicated gap filler jointing；
5) tile surface is managed with objects such as cotton yarns again after completion for 24 hours；
The waterproof thermal insulation mortar includes the following raw material according to parts by weight: 70 parts of portland cement, 165 parts of quartz sand,
25 parts of Phenolic resin powder, 18 parts of alumina silicate, 20 parts of sodium carboxymethylcellulose, 7 parts of dimethylaminoethyl acrylate, glass bead
25 parts, 15 parts of porous ceramic grain, 8 parts of glass fibre, 7 parts of sawdust, 10 parts of additive, 180 parts of water.
Wherein, decorative brick needs to impregnate 2h or more in clear water before being laid with, and to brick body not bubbling, taking-up is dried stand-by.
Wherein, the waterproof thermal insulation mortar preparation method the following steps are included:
1) portland cement, quartz sand, water are mixed, under 700r/min speed conditions, stirs 12min, obtains slurry
Ⅰ；
2) Phenolic resin powder, sodium carboxymethylcellulose, acrylate is added in the slurry I obtained to step 1)
Ethyl ester, additive are warming up to 70 DEG C, under the revolving speed of 900r/min, stir 40min, obtain slurry II；
3) alumina silicate, glass bead, porous ceramic grain, glass fibre, sawdust is added in the slurry II obtained to step 2),
Under the revolving speed of 400r/min, 40min, discharging are stirred.
Embodiment 4
A kind of construction technology of exterior wall decorating tile, which comprises the following steps:
1) External Wall surface is handled, and dust, sundries are cleaned out, and External Wall surface is repaired, avoid hollowing,
The defects of cracking and dusting；
2) watering is carried out to metope to moisten, wait 32h, pop up absolute altitude control line in outer wall body surrounding；
3) it is laid with and selects waterproof thermal insulation mortar, mortar thickness 28mm moistens the decorative brick back side before paving, keeps just
Face is dry, and decorative brick is laid on mortar as requested, with rubber hammer tapping decorative brick until closely knit smooth reach requirement；
4) after decorative brick has been spread, 32h is stood, cleaning jointing is carried out, should first be rejected impurity in decorative brick gap before jointing,
Again with dedicated gap filler jointing；
5) tile surface is managed with objects such as cotton yarns again after completion for 24 hours；
The waterproof thermal insulation mortar includes the following raw material according to parts by weight: 75 parts of portland cement, 170 parts of quartz sand,
28 parts of Phenolic resin powder, 19 parts of alumina silicate, 22 parts of sodium carboxymethylcellulose, 9 parts of dimethylaminoethyl acrylate, glass bead
22 parts, 12 parts of porous ceramic grain, 7 parts of glass fibre, 6 parts of sawdust, 9 parts of additive, 170 parts of water.
Wherein, decorative brick needs to impregnate 2h or more in clear water before being laid with, and to brick body not bubbling, taking-up is dried stand-by.
Wherein, the waterproof thermal insulation mortar preparation method the following steps are included:
1) portland cement, quartz sand, water are mixed, under 700r/min speed conditions, stirs 12min, obtains slurry
Ⅰ；
2) Phenolic resin powder, sodium carboxymethylcellulose, acrylate is added in the slurry I obtained to step 1)
Ethyl ester, additive are warming up to 70 DEG C, under the revolving speed of 900r/min, stir 40min, obtain slurry II；
3) alumina silicate, glass bead, porous ceramic grain, glass fibre, sawdust is added in the slurry II obtained to step 2),
Under the revolving speed of 400r/min, 40min, discharging are stirred.
Embodiment 5
A kind of construction technology of exterior wall decorating tile, which comprises the following steps:
1) External Wall surface is handled, and dust, sundries are cleaned out, and External Wall surface is repaired, avoid hollowing,
The defects of cracking and dusting；
2) watering is carried out to metope to moisten, wait 36h, pop up absolute altitude control line in outer wall body surrounding；
3) it is laid with and selects waterproof thermal insulation mortar, mortar thickness 30mm moistens the decorative brick back side before paving, keeps just
Face is dry, and decorative brick is laid on mortar as requested, with rubber hammer tapping decorative brick until closely knit smooth reach requirement；
4) after decorative brick has been spread, 36h is stood, cleaning jointing is carried out, should first be rejected impurity in decorative brick gap before jointing,
Again with dedicated gap filler jointing；
5) tile surface is managed with objects such as cotton yarns again after completion for 24 hours；
The waterproof thermal insulation mortar includes the following raw material according to parts by weight: 80 parts of portland cement, 180 parts of quartz sand,
30 parts of Phenolic resin powder, 20 parts of alumina silicate, 25 parts of sodium carboxymethylcellulose, 10 parts of dimethylaminoethyl acrylate, vitreous are micro-
30 parts of pearl, 20 parts of porous ceramic grain, 10 parts of glass fibre, 10 parts of sawdust, 12 parts of additive, 200 parts of water.
Wherein, decorative brick needs to impregnate 2h or more in clear water before being laid with, and to brick body not bubbling, taking-up is dried stand-by.
Wherein, the waterproof thermal insulation mortar preparation method the following steps are included:
1) portland cement, quartz sand, water are mixed, under 800r/min speed conditions, stirs 15min, obtains slurry
Ⅰ；
2) Phenolic resin powder, sodium carboxymethylcellulose, acrylate is added in the slurry I obtained to step 1)
Ethyl ester, additive are warming up to 80 DEG C, under the revolving speed of 1000r/min, stir 50min, obtain slurry II；
3) alumina silicate, glass bead, porous ceramic grain, glass fibre, sawdust is added in the slurry II obtained to step 2),
Under the revolving speed of 500r/min, 50min, discharging are stirred.
Mortar prepared by embodiment 1-5 is tested for the property, test result is as shown in table 1.
Table 1
As can be seen that the waterproof thermal insulation mortar that the present invention uses, not only viscosity is higher from result above, decorative brick is laid with
Intensity is higher, and waterproof thermal-insulated effect is more preferable, improves service life, and reduces ambient temperature to indoor influence, saves
The energy.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (6)
1. a kind of construction technology of exterior wall decorating tile, which comprises the following steps:
1) External Wall surface is handled, and dust, sundries are cleaned out, and External Wall surface is repaired, and avoids hollowing, cracking
And the defects of dusting；
2) watering is carried out to metope to moisten, wait 24-36h, pop up absolute altitude control line in outer wall body surrounding；
3) it is laid with and selects waterproof thermal insulation mortar, mortar thickness 20-30mm moistens the decorative brick back side before paving, keeps just
Face is dry, and decorative brick is laid on mortar as requested, with rubber hammer tapping decorative brick until closely knit smooth reach requirement；
4) after decorative brick has been spread, 24-36h is stood, cleaning jointing is carried out, should first be rejected impurity in decorative brick gap before jointing,
Again with dedicated gap filler jointing；
5) tile surface is managed with objects such as cotton yarns again after completion for 24 hours；
The waterproof thermal insulation mortar includes the following raw material according to parts by weight: 60-80 parts of portland cement, quartz sand 150-180
Part, 20-30 parts of Phenolic resin powder, 15-20 parts of alumina silicate, 15-25 parts of sodium carboxymethylcellulose, dimethylaminoethyl acrylate
5-10 parts, 20-30 parts of glass bead, 10-20 parts of porous ceramic grain, 6-10 parts of glass fibre, 5-10 parts of sawdust, additive 8-12
Part, 160-200 parts of water.
2. the construction technology of exterior wall decorating tile according to claim 1, which is characterized in that the waterproof thermal insulation mortar includes
Below according to the raw material of parts by weight: 65-75 parts of portland cement, 160-170 parts of quartz sand, 22-28 parts of Phenolic resin powder, silicon
Sour aluminium 16-19 parts, it is 18-22 parts of sodium carboxymethylcellulose, 6-9 parts of dimethylaminoethyl acrylate, 22-28 parts of glass bead, more
Haydite 12-18 parts of hole, 7-9 parts of glass fibre, 6-8 parts of sawdust, 9-11 parts of additive, 170-190 parts of water.
3. the construction technology of exterior wall decorating tile according to claim 2, which is characterized in that the waterproof thermal insulation mortar includes
Below according to the raw material of parts by weight: 70 parts of portland cement, 165 parts of quartz sand, 25 parts of Phenolic resin powder, 18 parts of alumina silicate,
20 parts of sodium carboxymethylcellulose, 7 parts of dimethylaminoethyl acrylate, 25 parts of glass bead, 15 parts of porous ceramic grain, glass fibre 8
Part, 7 parts of sawdust, 10 parts of additive, 180 parts of water.
4. the construction technology of exterior wall decorating tile according to claim 1, which is characterized in that decorative brick needs before being laid with clear
2h or more is impregnated in water, to brick body not bubbling, taking-up is dried stand-by.
5. a kind of preparation method of waterproof thermal insulation mortar a method according to any one of claims 1-3, which is characterized in that including following step
It is rapid:
1) portland cement, quartz sand, water are mixed, under 600-800r/min speed conditions, stirs 10-15min, starched
Material I；
2) Phenolic resin powder, sodium carboxymethylcellulose, acrylate second is added in the slurry I obtained to step 1)
Ester, additive, are warming up to 60-80 DEG C, under the revolving speed of 800-1000r/min, stir 30-50min, obtain slurry II；
3) alumina silicate, glass bead, porous ceramic grain, glass fibre, sawdust is added in the slurry II obtained to step 2), in 300-
Under the revolving speed of 500r/min, 30-50min, discharging are stirred.
6. a kind of waterproof thermal insulation mortar a method according to any one of claims 1-3.