CN109053015A - A kind of corrosion protection cement grinding aid and preparation method thereof - Google Patents
A kind of corrosion protection cement grinding aid and preparation method thereof Download PDFInfo
- Publication number
- CN109053015A CN109053015A CN201810979607.7A CN201810979607A CN109053015A CN 109053015 A CN109053015 A CN 109053015A CN 201810979607 A CN201810979607 A CN 201810979607A CN 109053015 A CN109053015 A CN 109053015A
- Authority
- CN
- China
- Prior art keywords
- grinding aid
- corrosion protection
- cement grinding
- triethanolamine
- protection cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of corrosion protection cement grinding aid and preparation method thereof, it is characterized in that, it is mixed by following components in percentage by weight: the water of 34.5%-45.5%, the Nacl of 6.5%-7.5%, the anhydrous sodium sulphate of 5.5%-6.5%, the sodium lignin sulfonate of 2.8%-3.2%, the triethanolamine of 14%-18%, the molasses of 1.8%-2.2%, remaining is additive.The present invention is free of sodium nitrite, and toxicity is faint and has good corrosion resistance.
Description
Technical field
The present invention relates to the field of building materials, in particular to a kind of corrosion protection cement grinding aid and preparation method thereof.
Background technique
Cement grinding aid is a kind of chemical addition agent for improving cement grinding effect and performance, can significantly improve cement platform
When yield, each age strength of cement, improve its mobility, prevent steel reinforced concrete erosion.Anti-erosion anti-corrosion is added in cement
Agent can make cement concrete have the superperformances such as salt resistance class ion erosion, the destruction of freeze thawing resistance circulation and highly resistance infiltration, and mixed
Solidifying soil aseptic applications are easy, do not need special construction technique.
Sodium nitrite is usually added into conventional cement grinding aid, people are because sodium nitrite is in cement using sodium nitrite
It can play the role of in grinding aid certain against corrosion.Although sodium nitrite itself is not carcinogen, sodium nitrite connects
The explosion of organic matter easy firing is touched, if generation sodium nitrate can react with oxygen by being exposed in air accidentally, with oxidisability, and is had
The friction of machine object or impact energy cause to burn or explode, and have toxicity.And sodium nitrite can also generate nitrous under certain condition
Amine has carcinogenicity.It can be seen that sodium nitrite has more virulent property, when serious can also threat to life, to cause security risk.
Summary of the invention
Technical problem to be solved by the invention is to provide a kind of, and the anticorrosive and toxicity without sodium nitrite is significantly faint
Corrosion protection cement grinding aid and preparation method thereof.
It is as follows that the present invention solves technical solution used by above-mentioned technical problem:
A kind of corrosion protection cement grinding aid of the present invention, it is mixed by following components in percentage by weight: 35%-
45% water, the Nacl of 6.5%-7.5%, the anhydrous sodium sulphate of 5.5%-6.5%, the sodium lignin sulfonate of 2.8%-3.2%,
The triethanolamine of 14%-18%, the molasses of 1.8%-2.2%, remaining is additive.The triethanolamine that the present invention is added is more traditional
Sodium nitrite toxicity significantly reduces, and is easier to store, and triethanolamine has corrosion resistance, moreover it is possible to prevent the poly- of crushing process powder
Collection and positice ground effect, improve the mobility and loading density of cement, reach preferable cement milling effect, and can reduce powder
The power consumption of broken machine.
Further, the additive is the dodium thiosulfate that the additive is 2.8%-3.2%, the urine of 3.8%-4.2%
Element, the compound hydramine of 14%-18%, the glycerol of 2.5%-3.5% can interact with triethanolamine and help each component in water
It gradually and is slowly discharged in mud grinding process, cement is effectively prevent to corrode, to improve cement grinding effect.
Further, water 40%, Nacl 7%, anhydrous sodium sulphate 6%, dodium thiosulfate 3%, urea 4% are wooden
Plain sodium sulphate is 3%, triethanolamine 16%, and compound hydramine is 16%, and glycerol 3%, molasses 2% effectively prevent cement
Corrosion, preferably raising cement milling effect.
A kind of preparation method of corrosion protection cement grinding aid of the present invention, which comprises the following steps:
In 16-32 degrees Celsius of environment, water, Nacl, anhydrous sodium sulphate, dodium thiosulfate, urea, sulfomethylated lignin are sequentially added according to sequencing
Sour sodium, triethanolamine, compound hydramine, glycerol, molasses, one component of every addition make to next component after completely dissolution, is added
Each component preferably plays a role, and cement is effectively prevent to corrode, preferably raising cement milling effect.
The present invention compared with the existing technology has the following advantages that and effect: the more traditional nitrous of the triethanolamine that the present invention is added
Sour sodium toxicity significantly reduces, and is easier to store, and triethanolamine has corrosion resistance, moreover it is possible to prevent crushing process powder aggregation and
Positice ground effect improves the mobility and loading density of cement, reaches preferable cement milling effect, and can reduce pulverizer
Power consumption;Each component interaction effectively prevent cement to corrode, to improve cement grinding effect.
Specific embodiment
The present invention will be further described in detail below with reference to the embodiments, following embodiment be explanation of the invention and
The invention is not limited to following embodiments.
Embodiment 1: under 16 degrees Celsius of environment, it is bright successively to take and dissolve 34.5kg water, 7.5kg Nacl, 6.5kg member
Powder, 2.8kg dodium thiosulfate, 3.8kg urea, 3.2kg sodium lignin sulfonate, 18kg triethanolamine, the compound hydramine of 18kg, 3.5kg are sweet
Corrosion protection cement grinding aid is made to whole dissolutions in oil, 2.2kg molasses, stirring after standing.
Embodiment 2: under 25 degrees Celsius of environment, successively take and dissolve 40kg water, 7kg Nacl, 6kg anhydrous sodium sulphate, 3kg
Dodium thiosulfate, 4kg urea, 3kg sodium lignin sulfonate, 16kg triethanolamine, the compound hydramine of 16kg, 3kg glycerol, 2kg molasses, stirring
To whole dissolutions, corrosion protection cement grinding aid is made after standing.
Embodiment 3: under 32 degrees Celsius of environment, it is bright successively to take and dissolve 45.5kg water, 6.5kg Nacl, 5.5kg member
Powder, 3.2kg dodium thiosulfate, 4.2kg urea, 2.8kg sodium lignin sulfonate, 14kg triethanolamine, the compound hydramine of 14kg, 2.5kg are sweet
Corrosion protection cement grinding aid is made to whole dissolutions in oil, 1.8kg molasses, stirring after standing.
Test against corrosion:
By MgSO4And Na2SO4Being added in distilled water and being configured to sulfuric acid content is 7000mg/L, 20250mg/L and 3000mg/
The etchant of L, to the corrosion protection cement grinding aid and traditional cement containing sodium nitrite of above-described embodiment 1, embodiment 2, embodiment 3
Grinding aid is added in cement with 0.05% blending ratio, is pressed into 10mm × 10mm × 60mm size, is then carried out
Demould within 24 hours, and product be placed in 50 DEG C waters and is conserved 7 days, then be respectively put into etchant and impregnate 28 days, then into
The detection of row flexural strength, coefficient against corrosion are followed successively by embodiment 2, embodiment 3, embodiment 1 and tradition containing sodium nitrite from big to small
Cement grinding aid.As it can be seen that also having for the more traditional cement grinding aid containing sodium nitrite of corrosion protection cement grinding aid of the invention
There is same or better corrosion resistance.
In addition, it should be noted that, embodiment of the present invention is only to carry out to the preferred embodiment of the present invention
Description, not present inventive concept and range are defined, under the premise of not departing from design philosophy of the present invention, in this field
The all variations and modifications that engineers and technicians make technical solution of the present invention should all fall into protection scope of the present invention,
The claimed technology contents of the present invention, are all described in the claims.
Claims (4)
1. a kind of corrosion protection cement grinding aid, which is characterized in that it is mixed by following components in percentage by weight:
The water of 34.5%-45.5%, the Nacl of 6.5%-7.5%, the anhydrous sodium sulphate of 5.5%-6.5%, the wood of 2.8%-3.2%
Quality sodium sulfonate, the triethanolamine of 14%-18%, the molasses of 1.8%-2.2%, remaining is additive.
2. a kind of corrosion protection cement grinding aid as described in claim 1, which is characterized in that the additive is 2.8%-3.2%
Dodium thiosulfate, the urea of 3.8%-4.2%, the compound hydramine of 14%-18%, the glycerol of 2.5%-3.5%.
3. a kind of corrosion protection cement grinding aid as claimed in claim 2, which is characterized in that water 40%, Nacl 7%, member
Bright powder is 6%, dodium thiosulfate 3%, urea 4%, sodium lignin sulphate 3%, triethanolamine 16%, and compound hydramine is
16%, glycerol 3%, molasses 2%.
4. a kind of preparation method of corrosion protection cement grinding aid as claimed in claim 2 or claim 3, which is characterized in that including following step
It is rapid:
In 16-32 degrees Celsius of environment, water, Nacl, anhydrous sodium sulphate, dodium thiosulfate, urea, wood are sequentially added according to sequencing
Quality sodium sulfonate, triethanolamine, compound hydramine, glycerol, molasses, one component of every addition are added next to after completely dissolution
Component.