CN109036635A - 高分散导电银浆 - Google Patents
高分散导电银浆 Download PDFInfo
- Publication number
- CN109036635A CN109036635A CN201811057602.5A CN201811057602A CN109036635A CN 109036635 A CN109036635 A CN 109036635A CN 201811057602 A CN201811057602 A CN 201811057602A CN 109036635 A CN109036635 A CN 109036635A
- Authority
- CN
- China
- Prior art keywords
- parts
- conductive
- silver paste
- high dispersive
- triethanolamine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明涉及银浆的技术领域，尤其涉及一种高分散导电银浆。这种高分散导电银浆包括以下质量份的组分：片状银粉60‑72份、导电石墨烯1‑1.5份、硝酸纤维素0.3‑0.5份、三乙醇胺1‑2份、异丙醇铝0.1‑0.2份、聚乙二醇1‑2份。本发明设计独特，组成合理，制备方便，具有优异的导电性能，并且与基材附着力好，在提高涂料导电、机械性能的同时，保证了涂料的粘接性、易加工性、硬度、扩散性，同时对环境污染小。
Description
技术领域
本发明涉及一种银浆，尤其涉及一种高分散导电银浆。
背景技术
导电浆料作为一种功能性印料因其良好的物理性能在电子信息产品中得到广泛的应用，随着电子产品向更轻、更薄、功能性更强大和更环保的方向发展，对其性能也提出更高的要求。其中低温无卤导电银浆因其优异的导电性、导热性和实用性，广泛应用于薄膜开关、电容电极、触摸屏等方面。低温导电银浆是以导电银粉作为导电填料，与高聚物树脂、溶剂、固化剂、助剂等经搅拌、分散而制成的均匀浆料。导电银浆涂覆在基材上后，在低温环境下烘干(一般低于160℃)，待溶剂释放后，树脂与固化剂逐步反应、固化，最终形成致密的导电膜层。
在电子行业中，为了满足产品的高强度、高机械性能需求，低温导电银浆固化后的导电膜层一般有机械性的要求(膜层硬度、膜层与基材附着力等)。导电银粉为金属粉体，硬度相对较高，但树脂等高聚物的硬度则一般较差。而当以提高银粉填充量方式来满 足高硬度需求时，相对少量的树脂不能充分、有效包覆银粉，导致表层银粉吸附不牢而出现脱落现象。
发明内容
本发明旨在解决上述缺陷，提供一种高分散导电银浆。
为了克服背景技术中存在的缺陷，本发明解决其技术问题所采用的技术方案是：这种高分散导电银浆包括以下质量份的组分：片状银粉60-72份、导电石墨烯1-1.5份、硝酸纤维素0.3-0.5份、三乙醇胺1-2份、异丙醇铝0.1-0.2份、聚乙二醇1-2份。
根据本发明的另一个实施例，进一步包括片状银粉72份、导电石墨烯1.5份、硝酸纤维素0.5份、三乙醇胺2份、异丙醇铝0.2份、聚乙二醇2份。
根据本发明的另一个实施例，进一步包括片状银粉60份、导电石墨烯1份、硝酸纤维素0.3份、三乙醇胺1份、异丙醇铝0.1份、聚乙二醇1份。
根据本发明的另一个实施例，进一步包括片状银粉68份、导电石墨烯1.3份、硝酸纤维素0.4份、三乙醇胺1份、异丙醇铝0.15份、聚乙二醇1份。
本发明的有益效果是：本发明设计独特，组成合理，制备方便，具有优异的导电性能，并且与基材附着力好，在提高涂料导电、机械性能的同时，保证了涂料的粘 接性、易加工性、硬度、扩散性，同时对环境污染小。
具体实施方式
为了克服背景技术中存在的缺陷，本发明解决其技术问题所采用的技术方案是：这种高分散导电银浆包括以下质量份的组分：片状银粉60-72份、导电石墨烯1-1.5份、硝酸纤维素0.3-0.5份、三乙醇胺1-2份、异丙醇铝0.1-0.2份、聚乙二醇1-2份。
实施例
片状银粉72份、导电石墨烯1.5份、硝酸纤维素0.5份、三乙醇胺2份、异丙醇铝0.2份、聚乙二醇2份。
实施例
片状银粉60份、导电石墨烯1份、硝酸纤维素0.3份、三乙醇胺1份、异丙醇铝0.1份、聚乙二醇1份。
实施例
片状银粉68份、导电石墨烯1.3份、硝酸纤维素0.4份、三乙醇胺1份、异丙醇铝0.15份、聚乙二醇1份。
本发明的有益效果是：本发明设计独特，组成合理，制备方便，具有优异的导电性能，并且与基材附着力好，在提高涂料导电、机械性能的同时，保证了涂料的粘 接性、易加工性、硬度、扩散性，同时对环境污染小。
Claims (4)
1.一种高分散导电银浆，其特征在于：包括以下质量份的组分：片状银粉60-72份、导电石墨烯1-1.5份、硝酸纤维素0.3-0.5份、三乙醇胺1-2份、异丙醇铝0.1-0.2份、聚乙二醇1-2份。
2.如权利要求1所述的高分散导电银浆，其特征在于：片状银粉72份、导电石墨烯1.5份、硝酸纤维素0.5份、三乙醇胺2份、异丙醇铝0.2份、聚乙二醇2份。
3.如权利要求1所述的高分散导电银浆，其特征在于：片状银粉60份、导电石墨烯1份、硝酸纤维素0.3份、三乙醇胺1份、异丙醇铝0.1份、聚乙二醇1份。
4.如权利要求1所述的高分散导电银浆，其特征在于：片状银粉68份、导电石墨烯1.3份、硝酸纤维素0.4份、三乙醇胺1份、异丙醇铝0.15份、聚乙二醇1份。