CN109024997A - 一种播音室用隔音墙 - Google Patents
一种播音室用隔音墙 Download PDFInfo
- Publication number
- CN109024997A CN109024997A CN201810858694.0A CN201810858694A CN109024997A CN 109024997 A CN109024997 A CN 109024997A CN 201810858694 A CN201810858694 A CN 201810858694A CN 109024997 A CN109024997 A CN 109024997A
- Authority
- CN
- China
- Prior art keywords
- wall
- parts
- cotton layer
- acoustical cotton
- sound insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了一种播音室用隔音墙，属于声音污染治理技术领域，包括第一墙体和第二墙体，所述第一墙体和第二墙体之间设有隔音模块，所述隔音模块包括第一吸音棉层、第二吸音棉层和设置在所述第一吸音棉层和第二吸音棉层之间的阻尼板，所述第一吸音棉层和第二吸音棉层的两面均涂设粘结剂，所述第一墙体和第二墙体远离所述隔音模块的一侧均喷设涂料。本发明隔音效果好，解决了以往密封隔音装置可拆卸连接，固定不牢固，相邻部件之间的接触不紧密，造成声音泄露的难题，另外提供用于该隔音墙各组件之间粘连的粘结剂，具有优异的粘结强度和隔音效果。
Description
技术领域
本发明涉及声音污染治理技术领域，具体涉及一种播音室用隔音墙。
背景技术
新闻传播作为现代信息化技术信息传播的重要方式，在社会个体成员全面发展和提升的进程中扮演着至关重要的角色。新闻传播承载着向读者传递政法理念、经济思想、科学思想、先进文化知识以及伦理道德价值取向的使命，使广大读者能够清楚地认识到身处的社会政治、经济、科技、文化、制度环境，熟谙社会的风俗习惯和社会伦理道德风尚，并以此来指导调适自己的行为活动，促进社会的发展。
播音室是广播电台用来广播节目的专用工作场所，结构上需满足隔音、吸音、无回音等良好音响效果。因此，播音室的墙体对密闭性能和声学特性的要求比较高。目前常用的隔音墙一般由多个隔音墙体模块组装而成，并在相邻两个隔音墙体模块之间设置密封装置以防止声音泄露。为了安装方便，密封装置通常是可拆卸安装在隔音墙体模块上，但是这类安装方式不牢固，而且会使相邻部件之间的接触不紧密，造成声音泄露，达不到隔音的效果。为了增强各部件之间的接触的紧密度，在部件表面涂一层粘结剂粘连，但是现有的粘结剂粘接强度不够，易老化脱落，而且不能增强隔音效果，不适用于隔音墙体各部件之间的粘连。
公告号为CN103787626B的专利公开了一种隔音粘结剂，按照质量份数，包括：无机凝胶25~30；改性剂1~5；抗裂增强纤维0.3~0.5；吸音材料5~8；填充料40~60；保水剂0.3~0.6；活性激活剂0.1~0.5；减水剂0.2~0.8；疏水粉0.1~0.3；分散剂0.1~0.6。该隔音粘结剂对高频和中频的声音具有一定的吸引效果，但是，该粘结剂稳定性较差，不耐腐蚀，粘结强度较差，表面容易褶皱，起皮，吸音系数较低，不能满足播音室隔音墙体的性能要求。
公开号为CN106381000A的专利文献公开了公开了一种隔音防水涂料，按照重量份计，由以下原料组成：酚醛树脂70-100份、滑石粉5-10份、灰钙粉1-5份、二氧化硅1-5份、聚氧乙烯聚氧丙醇胺醚1-5份、吸声功能材料1-10份、防水剂1-10份、成膜助剂1.5-5份和乙酸丁酯10-30份。该涂料强度高、机械性能优越，同时具有隔音、防水、防污染、易洗涤及耐擦洗的特点。但是，经验证该涂料粘结性能较差，浸水后的拉伸胶粘强度、热老化后的拉伸胶粘强度较低，涂料的收缩率较大，影响隔音效果。
发明内容
有鉴于此，本发明提供了一种播音室用隔音墙，隔音效果好，解决了以往密封隔音装置可拆卸连接，固定不牢固，相邻部件之间的接触不紧密，造成声音泄露的难题，另外提供用于该隔音墙各组件之间粘连的粘结剂，具有优异的粘结强度和隔音效果。
为解决上述技术问题，本发明所采取的技术方案是：
一种播音室用隔音墙，包括第一墙体和第二墙体，所述第一墙体和第二墙体之间设有隔音模块，所述隔音模块包括第一吸音棉层、第二吸音棉层和设置在所述第一吸音棉层和第二吸音棉层之间的阻尼板，所述第一吸音棉层和第二吸音棉层的两面均涂设粘结剂，所述第一墙体和第二墙体远离所述隔音模块的一侧均喷设涂料。
优选的，所述粘结剂由以下重量份的成分制备：聚丙烯酰胺25-30份，硅酸钠15-22份，填料5-8份，助剂6-8份，隔音剂3-6份，表面活性剂2.5-4份，丙酮23-28份，水40-45份。
优选的，所述填料为高岭土、碳化硅和二氧化钛的混合物，重量比高岭土：碳化硅：二氧化钛为1:2-4:4-6。
优选的，所述填料的粒度为200-300目。
优选的，所述助剂为铬酸钠、壬基酚聚氧乙烯醚、对甲苯磺酸的混合物，重量比铬酸钠：壬基酚聚氧乙烯醚：对甲苯磺酸为1:5-7:3.5-5。
优选的，所述助剂为铬酸钠、壬基酚聚氧乙烯醚、对甲苯磺酸的混合物，重量比铬酸钠：壬基酚聚氧乙烯醚：对甲苯磺酸为1:5-6:4-5。
优选的，所述表面活性剂为琥珀酸二辛酯磺酸钠、十二烷基氨基丙酸钠中的一种或两种。
优选的，所述表面活性剂为琥珀酸二辛酯磺酸钠、十二烷基氨基丙酸钠中的混合物，重量比琥珀酸二辛酯磺酸钠：十二烷基氨基丙酸钠为1:0.4-0.8。
本发明的有益效果是：
本发明包括第一墙体和第二墙体，二者之间形成有空腔，空腔内填充有隔音模块。隔音模块包括第一吸音棉层、第二吸音棉层和设置在第一吸音棉层和第二吸音棉层之间的阻尼板，隔音消除噪音效果较好。为了增强第一吸音棉层、第二吸音棉层的支撑固定效果，可在第一吸音棉层、第二吸音棉层内均设置龙骨。第一吸音棉层和第二吸音棉层的两面均涂设粘结剂，第一墙体和第一吸音棉层之间，第一吸音棉层和阻尼板之间，阻尼板和第二吸音棉层之间，第二吸音棉层和第二墙体之间均通过粘结剂粘连。第一墙体和第二墙体远离隔音模块的一侧均喷设涂料，该涂料优选防水，耐腐蚀，有消音效果的涂料。本发明针对播音室墙体的要求制备的涂料，防水，隔音，综合性能优异。
本发明所用的粘结剂以聚丙烯酰胺和硅酸钠为主料，具有较好的机械性能和粘结性能，填料为高岭土、碳化硅和二氧化钛的混合物，能够减小有机基体热解失重带来的体积收缩、粘接层结构疏松、粘接界面结合强度弱等不利影响，提升粘结剂的性能。助剂为铬酸钠、壬基酚聚氧乙烯醚、对甲苯磺酸的混合物，与聚丙烯酰胺和硅酸钠结合并对其进行改性，其中，铬酸钠耐酸碱腐蚀，增强粘结剂的耐老化能力，使其晶相结构不易被破坏；壬基酚聚氧乙烯醚提高表面活性，改善粘结剂的润湿性，对甲苯磺酸起固化作用，进一步缩短粘结剂的表干时间。表面活性剂可显著降低表面张力，更容易生成胶团，润湿能力和增溶能力更强。隔音剂优选Terotex-218隔音剂，具有较强的吸收能力，减少结构噪音。丙酮为有机溶剂。
本发明的涂料以酚醛树脂为主料，高岭土具有较好的耐火性、悬浮性和粘性，聚乙烯醇树脂，具有很好的粘接性和成膜性，松香具有较好的粘结性，与聚乙烯醇树脂相结合，提高涂料的悬浮性。碳酸锆铵作为防水剂，防水防污染，JS-RMA耐腐蚀剂与酚醛树脂协同作用，提高涂料的耐老化、耐腐蚀性能，隔音剂吸音，能使声能衰减，使涂料具备较好的隔音功效。本发明针对播音室墙体的要求制备的涂料，防水，隔音，综合性能优异。
本发明通过在第一墙体和第二墙体之间设置隔音模块，墙体各个组件之间均通过粘结剂牢固粘接，隔音效果好，解决了以往密封隔音装置可拆卸连接，固定不牢固，相邻部件之间的接触不紧密，造成声音泄露的难题。本发明隔音模块具有较好的消音、隔音效果，满足播音室高质量的隔音要求，阻止声音的泄露。本发明的粘结剂，通过助剂对聚丙烯酰胺和硅酸钠改性，并与填料、表面活性剂、隔音剂等有机结合，发挥各组分的协同效应，制得用于播音室隔音墙体的粘结剂，具有良好的机械性能和耐老化性能，综合性能优异，满墙体组件的粘接要求，粘接性好。
附图说明
下面结合附图对本发明作进一步的详细说明。
图1是本发明实施例1的隔音墙的结构示意图。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚，下面将结合本发明实施例的附图1，对本发明实施例的技术方案进行清楚、完整地描述。显然，所描述的实施例是本发明的一部分实施例，而不是全部的实施例。基于所描述的本发明的实施例，本领域普通技术人员所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
参阅图1，该实施例提供了一种播音室用隔音墙，包括第一墙体1和第二墙体5，所述第一墙体1和第二墙体5之间设有隔音模块，所述隔音模块包括第一吸音棉层2、第二吸音棉层4和设置在所述第一吸音棉层2和第二吸音棉层4之间的阻尼板3，所述第一吸音棉层2和第二吸音棉层4的两面均涂设粘结剂，所述第一墙体1和第二墙体5远离所述隔音模块的一侧均喷设涂料。
其中，为了增强第一吸音棉层2、第二吸音棉层4的支撑固定效果，在第一吸音棉层2、第二吸音棉层4内均设置龙骨，优选轻钢龙骨。第一吸音棉层2和第二吸音棉层4的两面均涂设粘结剂，第一墙体1和第一吸音棉层2之间，第一吸音棉层2和阻尼板3之间，阻尼板3和第二吸音棉层4之间，第二吸音棉层4和第二墙体5之间均通过粘结剂粘连。为了更加牢固，隔音模块粘连牢固后，用“工”字型密封件固定。第一墙体1和第二墙体5远离隔音模块的一侧均喷设涂料，该涂料优选防水，耐腐蚀，有消音效果的涂料。
第一吸音棉层2、第二吸音棉层4采用石英砂、石灰石、白云石为主要原料，并掺杂有硼砂和聚酯纤维，混合制备而成，具有较好的隔音、消噪效果。阻尼板3选用阻尼隔音板，是由两块建筑板材，如石膏板，玻镁板，水泥压力纤维板等材料两两中间夹着一层高分子阻尼材料而形成，具有在阻尼层较大的声能转化消耗原理而使透射量大减，透声系数低，隔声量大大提升。同时，带高分子阻尼材料的复合结构起到解耦消振的作用，使板材和系统的吻合效应大大削弱，隔声量提升明显。
实施例2
本实施例的提供一种播音室用隔音墙是在实施例1的基础上进行的改进，区别在于：所述粘结剂由以下重量份的成分制备：聚丙烯酰胺25份，硅酸钠15份，填料5份，助剂6份，Terotex-218隔音剂3份，表面活性剂2.5份，丙酮23份，水40份。
所述填料为高岭土、碳化硅和二氧化钛的混合物，重量比高岭土：碳化硅：二氧化钛为1:2:4，粒度为200目。
所述助剂为铬酸钠、壬基酚聚氧乙烯醚、对甲苯磺酸的混合物，重量比铬酸钠：壬基酚聚氧乙烯醚：对甲苯磺酸为1:5:3.5。
所述表面活性剂为琥珀酸二辛酯磺酸钠。
实施例3
本实施例的提供一种播音室用隔音墙是在实施例1的基础上进行的改进，区别在与：所述粘结剂由以下重量份的成分制备：聚丙烯酰胺27份，硅酸钠18份，填料6份，助剂6.5份，Terotex-218隔音剂4份，表面活性剂3份，丙酮25份，水42份。
所述填料为高岭土、碳化硅和二氧化钛的混合物，重量比高岭土：碳化硅：二氧化钛为1:3:4，粒度为250目。
所述助剂为铬酸钠、壬基酚聚氧乙烯醚、对甲苯磺酸的混合物，重量比铬酸钠：壬基酚聚氧乙烯醚：对甲苯磺酸为1:5:4。
所述表面活性剂为十二烷基氨基丙酸钠。
实施例4
本实施例的提供一种播音室用隔音墙是在实施例1的基础上进行的改进，区别在于：所述粘结剂由以下重量份的成分制备：聚丙烯酰胺28份，硅酸钠20份，填料7份，助剂7份，Terotex-218隔音剂5份，表面活性剂3.5份，丙酮26份，水43份。
所述填料为高岭土、碳化硅和二氧化钛的混合物，重量比高岭土：碳化硅：二氧化钛为1:2:5，粒度为300目。
所述助剂为铬酸钠、壬基酚聚氧乙烯醚、对甲苯磺酸的混合物，重量比铬酸钠：壬基酚聚氧乙烯醚：对甲苯磺酸为1:6:5。
所述表面活性剂为琥珀酸二辛酯磺酸钠、十二烷基氨基丙酸钠中的混合物，重量比琥珀酸二辛酯磺酸钠：十二烷基氨基丙酸钠为1:0.4。
实施例5
本实施例的提供一种播音室用隔音墙是在实施例1的基础上进行的改进，区别在于：所述粘结剂由以下重量份的成分制备：聚丙烯酰胺30份，硅酸钠22份，填料8份，助剂8份，Terotex-218隔音剂6份，表面活性剂4份，丙酮28份，水45份。
所述填料为高岭土、碳化硅和二氧化钛的混合物，重量比高岭土：碳化硅：二氧化钛为1:4:6，粒度为300目。
所述助剂为铬酸钠、壬基酚聚氧乙烯醚、对甲苯磺酸的混合物，重量比铬酸钠：壬基酚聚氧乙烯醚：对甲苯磺酸为1:7:5。
所述表面活性剂为琥珀酸二辛酯磺酸钠、十二烷基氨基丙酸钠中的混合物，重量比琥珀酸二辛酯磺酸钠：十二烷基氨基丙酸钠为1:0.8。
实施例6
本实施例的提供一种播音室用隔音墙是在实施例1的基础上进行的改进，区别在于：所述粘结剂，包含的成分同实施例4，但与实施例4不同的是，本实施例中，所述表面活性剂为琥珀酸二辛酯磺酸钠、十二烷基氨基丙酸钠中的混合物，重量比琥珀酸二辛酯磺酸钠：十二烷基氨基丙酸钠为1:0.6。
实施例7
本实施例提供了实施例2-6的粘结剂的制备方法，包含以下步骤：
S1：将聚丙烯酰胺、硅酸钠和1/2重量份数的水混合，置于搅拌机中搅拌，温度为55-60℃，转速为200r/min，搅拌10min后，加入表面活性剂和助剂，保持温度不变，转速调整为300r/min，搅拌30min后，得到混合物一；
S2：将填料置于90℃真空干燥箱中干燥8h后，加入丙酮、隔音剂和余下1/2重量份数的水置于反应釜中混合，设置温度100-105℃，转速500r/min，搅拌5h，得到混合物二；
S3：待步骤S2中反应釜中温度降至55-60℃后，加入步骤S1中的混合物一，调节转速为200r/min，搅拌2h后，得到混合物三；
S4：将步骤S3得到的混合物三置于冷冻室中，-5℃冷冻4h后，在80℃水浴缸中水浴加热3h后，以200r/min的转速搅拌10min，即可。
实施例8
本实施例提供了实施例1的涂料由以下重量份的成分制备：酚醛树脂35份，高岭土7份，聚乙烯醇树脂3.5份，松香1份，碳酸锆铵9份，JS-RMA耐腐蚀剂5份，Terotex-218隔音剂2份，乙醇15份，水30份。
实施例9
本实施例提供了实施例1的涂料由以下重量份的成分制备：酚醛树脂32份，高岭土7.5份，聚乙烯醇树脂4份，松香1.2份，碳酸锆铵9份，JS-RMA耐腐蚀剂6份，Terotex-218隔音剂2.5份，乙醇16份，水32份。
对比例1
本对比例提供一种粘结剂同实施例6，但与实施例6不同的是，本对比例中，不含有填料。
对比例2
本对比例提供一种粘结剂同实施例6，但与实施例6不同的是，本对比例中，不含有助剂。
对比例3
本对比例提供一种粘结剂同实施例6，但与实施例6不同的是，本对比例中，不含有Terotex-218隔音剂。
对比例4
本对比例提供一种粘结剂同实施例6，但与实施例6不同的是，本对比例中，不含有表面活性剂。
对比例5
本对比例提供一种粘结剂同实施例6，但与实施例6不同的是，本对比例中的制备方法，缺少步骤S4。
粘结剂的检测方法
拉伸胶粘原强度、浸水后的拉伸胶粘强度、热老化后的拉伸胶粘强度和收缩率测试：参见JC/T547-2005；吸声系数的检测参见GBJ88-1985，检测结果见表1。
表1 实施例2-6及对比例1-5粘结剂的检测结果
从表1中可以看出：实施例2至6均表现出优异的拉伸胶粘强度，拉伸胶粘原强度、浸水后的拉伸胶粘强度、热老化后的拉伸胶粘强度均较好，收缩率低在2%-2.4%之间，吸声系数达到0.43以上，说明本发明配方合理，和工艺适配性好。对比例1与实施例6相比，缺少填料，粘结剂的拉伸胶粘强度最差，收缩率最大，说明填料对粘结剂的防水性能和收缩率有着重要的影响；对比例2与实施例6相比，缺少助剂，它们的拉伸胶粘强度有明显下降，尤其是热老化后的拉伸胶粘强度较差，说明助剂可以改善粘结剂的耐老化性能和粘结强度；对比例3与实施例6相比，缺少隔音剂，粘结剂的吸音系数最小，说明隔音剂能够提高粘结剂的吸音能力；对比例4和实施例6相比，缺少表面活性剂，对比例5和实施例6相比，缺少步骤S4，即没有对混合物三进行冷冻和水浴加热处理，粘结剂的综合性能均较差，说明，表面活性剂能够降低表面张力，增强各组分之间的相溶性，冷冻后加热处理，提高粘结剂的分散性，使体系更加稳定。本发明各原料之间是相辅相成的，改变任意一种成分或工艺步骤，粘结剂的性能就会明显下降，说明本发明配方合理，和工艺适配性好。
涂料的性能测试
1）机械性能测试
在实际应用过程中，涂料的机械性能是衡量其耐用性的重要考核指标。涂层因配方组分比例不同，其机械性能会有一定差别。
向模具内浇注入调配好的混合液，室温下固化后得到涂层试样。其规格为：长为30mm，宽lO mm，厚度为100μm。采用美国美特斯CMT5305万能试验机对漆层进行应力应变测试，应变率为10mm/min。
拉伸强度是试样在拉力机上被拉断时，单位截面积上承受的负荷,用N／mm2表示，计算公式如1-1所示：
P＝F/S (1-1)
式中：
P一试样的拉伸强度，N／mm2；
F－试样断裂时断裂截面上所受的力，N；
S-试样断裂面的面积，mm2。
其中，1MPa=1N／mm2
断裂伸长率是试样被拉断时的伸长与原长度的比值，用百分率表示，计算公式如1-2所示：
E=(L1-L0)/L0 （1-2）
式中：
E一断裂伸长率，％；
L0一试样原长度，mm；
L1—试样断裂时受力部分的长度，mm。
2）耐水性测试
取涂料混合液30g于玻璃培养皿中，自然干燥，制成薄膜。采用吸水率表征薄膜的耐水性，将薄膜裁剪成15mm×15mm的正方形试样，称取试样质量（精确至0.001g）。将其放入装有蒸馏水的培养皿中，蒸馏水没过薄膜的上表面，在室温下浸泡24h后取出。用滤纸轻轻擦拭掉薄膜表面的水分，并立即称重。根据公式2-1，计算薄膜的吸水率，每个试样测试3次，取平均值。
W=(m1-m0)/m0×100% （2-1）
式中，W-薄膜的吸水率，%；
m0-试样的初始质量，g；
m1-试样吸水后的质量，g。
3）耐腐蚀测试
取混合液30g于玻璃培养皿中，在烘箱中干燥，制成薄膜试样。取干净的烧杯，配制3.5%浓度的NaCl溶液，将试样分别浸入配制好的溶液中，保持密封环境45天后，取出试样观察薄膜表面的腐蚀情况。
4）附着力测试
附着力测试利用划格法，依据ISO2409和GB/19286-98标准，对底材为镀锌铁片上涂覆厚度为121-250μm的测试涂料，对涂料试样进行井字划格，之后轻轻扫去表面杂质，以胶带中间与划线格平行放置，用手抹平胶带，随后以接近60°角揭开胶带，检查切割部位状态。
吸声系数的检测参见GBJ88-1985，实施例8和9涂料的性能检测结果如表2所示。
表2 实施例8和9涂料的检测结果
| 拉伸强度MPa | 断裂伸长率% | 耐水性 | 耐腐蚀性 | 附着力 | 吸音系数 | |
| 实施例8 | 22.8 | 121.5 | 42 | 无皱皮、气泡、剥落现象 | 光滑，无脱落 | 0.44 |
| 实施例9 | 23.1 | 126.4 | 42 | 无皱皮、气泡、剥落现象 | 光滑，无脱落 | 0.45 |
表2给出了本发明实施例8和9的涂料的测试结果，可以看出，本发明实施例8和9的涂料的机械性能好，以酚醛树脂为主料，高岭土具有较好的耐火性、悬浮性和粘性，聚乙烯醇树脂，具有很好的粘接性和成膜性，松香具有较好的粘结性，与聚乙烯醇树脂相结合，提高涂料的悬浮性。碳酸锆铵作为防水剂，防水防污染，JS-RMA耐腐蚀剂与酚醛树脂协同作用，提高涂料的耐老化、耐腐蚀性能，隔音剂吸音，能使声能衰减，使涂料具备较好的隔音功效。本发明针对播音室墙体的要求制备的涂料，防水，隔音，综合性能优异。
以上所述是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明所述原理的前提下，还可以作出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (8)
1.一种播音室用隔音墙，包括第一墙体和第二墙体，其特征在于：所述第一墙体和第二墙体之间设有隔音模块，所述隔音模块包括第一吸音棉层、第二吸音棉层和设置在所述第一吸音棉层和第二吸音棉层之间的阻尼板，所述第一吸音棉层和第二吸音棉层的两面均涂设粘结剂，所述第一墙体和第二墙体远离所述隔音模块的一侧均喷设涂料。
2.如权利要求1所述的一种播音室用隔音墙，其特征在于：所述粘结剂由以下重量份的成分制备：聚丙烯酰胺25-30份，硅酸钠15-22份，填料5-8份，助剂6-8份，隔音剂3-6份，表面活性剂2.5-4份，丙酮23-28份，水40-45份。
3.如权利要求2所述的一种播音室用隔音墙，其特征在于：所述填料为高岭土、碳化硅和二氧化钛的混合物，重量比高岭土：碳化硅：二氧化钛为1:2-4:4-6。
4.如权利要求3所述的一种播音室用隔音墙，其特征在于：所述填料的粒度为200-300目。
5.如权利要求2所述的一种播音室用隔音墙，其特征在于：所述助剂为铬酸钠、壬基酚聚氧乙烯醚、对甲苯磺酸的混合物，重量比铬酸钠：壬基酚聚氧乙烯醚：对甲苯磺酸为1:5-7:3.5-5。
6.如权利要求5所述的一种播音室用隔音墙，其特征在于：所述助剂为铬酸钠、壬基酚聚氧乙烯醚、对甲苯磺酸的混合物，重量比铬酸钠：壬基酚聚氧乙烯醚：对甲苯磺酸为1:5-6:4-5。
7.如权利要求2所述的一种播音室用隔音墙，其特征在于：所述表面活性剂为琥珀酸二辛酯磺酸钠、十二烷基氨基丙酸钠中的一种或两种。
8.如权利要求7所述的一种播音室用隔音墙，其特征在于：所述表面活性剂为琥珀酸二辛酯磺酸钠、十二烷基氨基丙酸钠中的混合物，重量比琥珀酸二辛酯磺酸钠：十二烷基氨基丙酸钠为1:0.4-0.8。