CN109022877A - Foamed alloy and its preparation method and application for air conditioner sound-deadening and noise-reducing - Google Patents
Foamed alloy and its preparation method and application for air conditioner sound-deadening and noise-reducing Download PDFInfo
- Publication number
- CN109022877A CN109022877A CN201811058708.7A CN201811058708A CN109022877A CN 109022877 A CN109022877 A CN 109022877A CN 201811058708 A CN201811058708 A CN 201811058708A CN 109022877 A CN109022877 A CN 109022877A
- Authority
- CN
- China
- Prior art keywords
- alloy
- foamed alloy
- foamed
- salt particle
- mold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses the foamed alloys and its preparation method and application for air conditioner sound-deadening and noise-reducing.Wherein, foamed alloy includes: the copper of 100 parts by weight and the aluminium of 0.1-10 parts by weight.By using copper as basis material in the present invention, and the fine copper of a part is replaced using the aluminium of said components, can significantly drop cost of material.In addition, the tensile strength of foamed alloy can be improved to not less than 330MPa by adding mechanical property that aluminium can significantly improve foamed alloy specifically, yield strength is improved to not less than 175MPa, elongation percentage is improved to not less than 21.5%.Therefore the foamed alloy of the above embodiment of the present invention can effectively overcome the defect of foam copper low strength.
Description
Technical field
The present invention relates to field of air conditioning, in particular to for air conditioner sound-deadening and noise-reducing foamed alloy and its preparation
Methods and applications.
Background technique
In the related technology, air conditioning pipe system generally includes various terminal, muffler and filter etc., and refrigerant is in air-conditioner pipe
It is recycled in the system of road, air conditioning pipe system can generate noise during operation of air conditioner, these noises are by refrigerant by outdoor
Machine is transmitted to interior, influences the usage experience of user, and there is also some impurity in these refrigerants, these impurity are long in air-conditioning
In the case that phase runs, pipeline inner wall can be caused to damage；It in addition, air compressor is as power source, while being also a kind of strong
Noise device brings very big influence to the production and living of people, brings high risks to the health of people.Therefore, to sky
Row sound-deadening and noise-reducing is transferred in have a very important significance.
Summary of the invention
The present invention is directed to solve at least some of the technical problems in related technologies.For this purpose, of the invention
One purpose is the foamed alloy and its preparation method and application for proposing to be used for air conditioner sound-deadening and noise-reducing.The foamed alloy is with copper
Aluminium alloy replaces fine copper, and not only sound-deadening and noise-reducing effect is good, but also can significantly improve the mechanical property of foamed alloy.
According to the first aspect of the invention, the invention proposes a kind of foamed alloys for air conditioner sound-deadening and noise-reducing.
According to an embodiment of the invention, the foamed alloy includes: the aluminium of the copper of 100 parts by weight, 0.1-10 parts by weight.
Therefore, the foamed alloy for air conditioner sound-deadening and noise-reducing of the above embodiment of the present invention is using copper as main base material
Material, is added to the aluminium of 0.1-10wt%.Thus, it is possible to significantly reduce cost of material.Importantly, inventors have found that passing through
The mechanical property of foamed alloy can be significantly improved by adding suitable aluminium, specifically, the tensile strength of foamed alloy can be mentioned
Up to it is not less than 330MPa, yield strength is improved to not less than 175MPa, elongation percentage is improved to not less than 21.5%.Therefore
The foamed alloy of the above embodiment of the present invention can effectively overcome the defect of foam copper low strength.
In addition, foamed alloy according to the above embodiment of the present invention can also have the following additional technical features:
In some embodiments of the invention, the tensile strength of the foamed alloy is not less than 330MPa.
In some embodiments of the invention, the yield strength of the foamed alloy is not less than 175MPa.
In some embodiments of the invention, the elongation percentage of the foamed alloy is not less than 21.5%.
In some embodiments of the invention, the hole of the foamed alloy is through-hole.
According to the second aspect of the invention, the above-mentioned foam for air-conditioning sound-deadening and noise-reducing is prepared the invention proposes a kind of
The method of alloy.According to an embodiment of the invention, this method comprises:
(1) salt particle is filled into mold to be compacted and heated, kept the temperature；
(2) fine copper is heated and melts and obtains fine copper molten liquid, the pure of predetermined ratio is added into the fine copper molten liquid
Aluminium, to obtain alloy melt；
(3) alloy melt is poured into the mold in step (1) filled with the salt particle, the closed mold is simultaneously
It is passed through inert gas into the mold, to make the alloy melt rapid osmotic into the gap of the salt particle, and it is cold
But foamed alloy presoma is obtained；
(4) water-washing desalting is carried out to the foamed alloy presoma, to obtain foamed alloy.
The method and process for preparing foamed alloy of the above embodiment of the present invention is simple and at low cost, and the foam being prepared closes
Jin Yitong is major matrix material, is added to the aluminium of 0.1-10wt%.Thus, it is possible to significantly reduce cost of material.It is prior
It is, inventors have found that the mechanical property that can significantly improve foamed alloy by adding suitable aluminium can will specifically steep
The tensile strength of foam alloy is improved to not less than 330MPa, and yield strength is improved to not less than 175MPa, elongation percentage is improved
To not less than 21.5%.Therefore the foamed alloy of the above embodiment of the present invention can effectively overcome lacking for foam copper low strength
It falls into.
In some embodiments of the invention, in step (1), the partial size of the salt particle is 0.55-1.7mm, described to add
The temperature of heat is 800-1200 DEG C, and the soaking time is 0.5-3 hours.
In some embodiments of the invention, further comprise before step (1):
Crude salt particle is warming up to 600-800 DEG C with the heating speed of 10-15 DEG C/min to roast；
Crude salt particle after the roasting is subjected to cooling and crushing and screening, to obtain the salt particle.
In some embodiments of the invention, in step (2), it is based on the fine copper molten liquid, is added 0.1-10wt%'s
Aluminium, to obtain the alloy melt.
According to the third aspect of the present invention, the invention proposes a kind of mufflers for air-conditioning.It is according to the present invention
Embodiment, the muffler have foamed alloy described in the above embodiment of the present invention or make using described in the above embodiment of the present invention
The foamed alloy that the method for standby foamed alloy obtains.It can not only make to disappear by using the foamed alloy of the above embodiment of the present invention
Sound device has preferable sound-deadening and noise-reducing effect, the production cost of muffler can also be further decreased, simultaneously because foamed alloy
With preferable mechanical property, it can also further extend the service life of muffler.
According to the fourth aspect of the present invention, the invention proposes a kind of blimps for compressor of air conditioner.According to this
The embodiment of invention, the blimp have foamed alloy described in the above embodiment of the present invention or use the above embodiment of the present invention
The foamed alloy that the method for preparing foamed alloy obtains.Not only may be used by using the foamed alloy of the above embodiment of the present invention
So that blimp has preferable soundproof effect, the production cost of blimp can also be further decreased, simultaneously because foam closes
Fitting has preferable mechanical property, can also further extend the service life of blimp.
According to the fifth aspect of the present invention, the invention proposes a kind of air-conditionings.According to an embodiment of the invention, the air-conditioning
With described in the above embodiment of the present invention be used for air-conditioning muffler and/or the above embodiment of the present invention described in be used for air-conditioning
The blimp of compressor.Generated noise when operation of air conditioner not only can be effectively reduced as a result, promote user experience, moreover it is possible to
It further decreases the production cost of air-conditioning and extends the service life of air-conditioning.
Additional aspect and advantage of the invention will be set forth in part in the description, and will partially become from the following description
Obviously, or practice through the invention is recognized.
Detailed description of the invention
Fig. 1 is the flow chart of the method according to an embodiment of the invention for preparing foamed alloy.
Fig. 2 is the structural schematic diagram of the muffler according to an embodiment of the invention for air-conditioning.
Fig. 3 is the structural schematic diagram of the muffler for air-conditioning of another embodiment according to the present invention.
Fig. 4 is the structural schematic diagram of the blimp according to an embodiment of the invention for compressor of air conditioner.
Fig. 5 is the schematic cross-section of the blimp according to an embodiment of the invention for compressor of air conditioner.
Specific embodiment
The embodiment of the present invention is described below in detail, examples of the embodiments are shown in the accompanying drawings, wherein from beginning to end
Same or similar label indicates same or similar element or element with the same or similar functions.Below with reference to attached
The embodiment of figure description is exemplary, it is intended to is used to explain the present invention, and is not considered as limiting the invention.
The present invention is that inventor is completed based on following discovery:
With the development of science and technology with the extensive use of material, inventor is based on current existing foam copper product, finds it
With preferable sound-deadening and noise-reducing effect, it can be used for air-conditioning sound-deadening and noise-reducing.But for foam copper using fine copper as raw material, cost of material is higher, and
And the defect of the generally existing low strength of foam copper is led so that there are hardness is low for some products being prepared using it
Cause service life is unqualified to obtain defect.
For this purpose, according to the first aspect of the invention, the invention proposes a kind of foams for air conditioner sound-deadening and noise-reducing
Alloy.According to an embodiment of the invention, the foamed alloy includes the copper of 100 parts by weight and the aluminium of 0.1-10 parts by weight.Therefore, originally
The foamed alloy for air conditioner sound-deadening and noise-reducing of invention above-described embodiment is added to using copper as major matrix material based on copper
Quality 0.1-10wt% aluminium.Thus, it is possible to significantly reduce cost of material.Importantly, inventors have found that by adding
After adding suitable aluminium, aluminium can form binary compound with copper, and the compound can effectively hinder the fortune of deformation process Dislocations
It is dynamic, and then be obviously improved the mechanical property of foamed alloy, specifically, the tensile strength of foamed alloy can be improved to being not less than
Yield strength is improved to not less than 175MPa, elongation percentage is improved to not less than 21.5% by 330MPa.Therefore the present invention is above-mentioned
The foamed alloy of embodiment can effectively overcome the defect of foam copper low strength.
A specific embodiment according to the present invention, foamed alloy is only by the aluminium of 100 parts by weight copper and 0.1-10 parts by weight
Composition.Wherein after suitable aluminium, aluminium can form binary compound with copper, and the compound can effectively hinder position in deformation process
Wrong movement, and then it is obviously improved the mechanical property of foamed alloy.
Another specific embodiment according to the present invention, above-mentioned foamed alloy can be by 100 parts by weight copper and 0.2 weight
The aluminium of part, 0.5 parts by weight, 1 parts by weight, 1.5 parts by weight, 2 parts by weight, 3 parts by weight, 5 parts by weight or 8 parts by weight forms.By
This, can according to actual needs be adjusted the aluminium content in foamed alloy, and foamed alloy is made to have both preferable noise reduction drop
Effect of making an uproar and stronger mechanical property.Specific example according to the present invention, aluminium content is preferably 1 weight in above-mentioned foamed alloy
Part, 1.5 parts by weight, 2 parts by weight, it is possible thereby to significantly improve the mechanical property of foamed alloy, that improves foamed alloy uses the longevity
Life.
Foamed alloy according to the above embodiment of the present invention since aluminium therein can form binary compound with copper, and is somebody's turn to do
Compound can effectively hinder the movement of deformation process Dislocations, and then be obviously improved the mechanical property of foamed alloy.Specifically,
The tensile strength of its foamed alloy can achieve not less than 330MPa；Yield strength can achieve not less than 175MP；Elongation percentage can
It is not less than 21.5% to reach.
Another specific embodiment according to the present invention, the hole of foamed alloy are through-hole.It is possible thereby to make foamed alloy
With better aeration and bigger specific surface area, so as to further increase the sound-deadening and noise-reducing effect of foamed alloy.
According to the second aspect of the invention, the above-mentioned foam for air-conditioning sound-deadening and noise-reducing is prepared the invention proposes a kind of
The method of alloy.According to an embodiment of the invention, with reference to Fig. 1, this method comprises:
S100: salt particle is filled into mold and is compacted and heated, kept the temperature
According to an embodiment of the invention, in the present invention by with salt particle fill mold and it is compacted, heat and
Heat preservation not only can make alloy melt form foaming structure, can also pass through the partial size of control salt particle by medium of salt particle
Under big, the pore structure for the foamed alloy that the conditions control such as heating condition and soaking time is finally prepared, porosity, aperture it is big
Small and specific surface area etc., and then there is the foamed alloy for ensuring finally to be prepared preferable mechanical property and sound-deadening and noise-reducing to imitate
Fruit.
A specific embodiment according to the present invention, the partial size of salt particle can be 0.55-1.7mm, such as 0.55mm,
0.7mm, 0.9mm, 1mm, 1.3mm or 1.65mm, the temperature of heating can be 800-1200 DEG C, such as 800 DEG C, 900 DEG C, 950
DEG C or 1100 DEG C, soaking time can be 0.5-3 hours, such as 1h, 1.5h, 2h, 2.5h or 3h.Inventors have found that if salt
The partial size of grain is too small, subsequent when pouring into alloy melt in the mold filled with salt particle, will increase alloy melt in salt particle
In flow resistance, and then influence the difficulty that penetration depth and increase of the alloy melt in salt particle form through-hole alloy；And
If the partial size of salt particle is excessive, and is easy to cause alloy melt to seep salt particle and assembles in mold bottom and form, same unfavorable
In formation foamed alloy.It, can be in addition, by the way that salt particle to be compacted to and controlled above-mentioned heating temperature and soaking time in the present invention
It effectively avoids larger with alloy melt temperature difference due to salt particle and causes alloy melt thermal loss too fast, cannot effectively permeate
Salt particle, and then pore structure and the porosity etc. for influencing alloy.As a result, the present invention in by control salt particle be above-mentioned partial size simultaneously
Above-mentioned heating and heat-retaining condition are controlled, mobility and penetration depth of the alloy melt in salt particle can be not only significantly improved,
And then so that alloy melt is effectively penetrated into salt particle and form through-hole foam structure, moreover it is possible to further increase the equal of foamed alloy
Evenness simultaneously makes foamed alloy have suitable porosity, pore size and specific surface area, closes so as to further increase foam
The mechanical property and sound-deadening and noise-reducing effect of gold.
Another specific embodiment according to the present invention, into mold fill salt particle before further comprise: will be thick
Salt particle is warming up to 600-800 DEG C with the heating speed of 10-15 DEG C/min and is roasted；By by roasting after crude salt particle into
Row cooling and crushing and screening, to obtain salt particle.Thus, it is possible to effectively control the particle size range of salt particle, and then further
Mobility and penetration depth of the alloy melt in salt particle are controlled, alloy melt is enable to penetrate into salt particle and forms through-hole bubble
Foam structure, while improving the uniformity of foamed alloy and making foamed alloy that there is suitable porosity, pore size and specific surface
Product, to further increase the mechanical property and sound-deadening and noise-reducing effect of foamed alloy.
Another specific embodiment according to the present invention, the density of the salt block formed after overcompaction, heating and heat preservation can
Think 1-2g/cm3.Inventors have found that being above-mentioned density by salt block in control mold, it can be further improved alloy melt and exist
Osmotic effect in salt particle, and the through-hole foam alloy with uniform porosity and pore size is obtained, it is possible thereby into one
Step improves the mechanical property and sound-deadening and noise-reducing effect of foamed alloy.
Crude salt particle can be put into crucible by another specific embodiment according to the present invention, and 10- is used in electric furnace
The heating speed of 15 DEG C/min is warming up to 600-800 DEG C, furnace cooling after heat preservation 2 hours.By crude salt particle after cooling in earthenware
It is carried out in crucible after being crushed, carries out classification processing with sub-sieve 10-30 mesh, obtain the salt particle of the particle size range；By salt particle
It is put into mold, then salt particle is compacted, then mold is put into high temperature furnace and is heated to 800-1200 DEG C of heat preservation 0.5-3 hours
It is spare.
S200: fine copper being heated and melts and obtains fine copper molten liquid, the fine aluminium of predetermined ratio is added into fine copper molten liquid,
To obtain alloy melt
A specific embodiment according to the present invention, fine copper block can be put into crucible, be melted fine copper using resistance furnace
Change, keeps the temperature 30 minutes after fusing；Fine aluminium block is added in crucible, is sufficiently stirred after aluminium block fusing, keeps alloy uniform, kept the temperature
30 minutes, so that albronze melt be made.Thus, it is possible to be sufficiently mixed copper and aluminium.
Another specific embodiment according to the present invention is based on fine copper molten liquid, the aluminium of 0.1-10wt% is added, so as to
To alloy melt.Inventors have found that the additive amount of aluminium has a great impact to the mechanical property of foamed alloy, such as make aluminium and copper
It is capable of forming binary compound, and the compound can effectively hinder the movement of deformation process Dislocations, and then be obviously improved bubble
The mechanical property of foam alloy.Passing through copper and aluminium in control foamed alloy in invention is above-mentioned composition, and bubble not only can be significantly reduced
The cost of material of foam alloy can also make the microstructure for promoting copper, so that foamed alloy be made to imitate with preferable sound-deadening and noise-reducing
Fruit and with the comparable mechanical property of foam copper, it is ensured that the tensile strength of foamed alloy is not low not less than 330MPa, yield strength
It is not less than 21.5% in 175MPa, elongation percentage.
A specific embodiment according to the present invention, be based on fine copper molten liquid, can be added 0.2wt%, 0.5wt%,
The aluminium of 1wt%, 1.5wt%, 2wt%, 3wt%, 5wt%, 8wt%, to obtain alloy melt.Thus, it is possible to according to reality
It needs to be adjusted the aluminium content in foamed alloy, and foamed alloy is made to have both preferable sound-deadening and noise-reducing effect and stronger power
Learn performance.Specific example according to the present invention, in above-mentioned foamed alloy aluminium content be preferably copper mass 1wt%, 1.5wt%,
2wt% improves product service life it is possible thereby to significantly improve the mechanical property of foamed alloy.
S300: alloy melt is poured into the mold in step S100 filled with salt particle, closed mold and into mold
It is passed through inert gas, to make alloy melt rapid osmotic into the gap of salt particle, and cooling obtains foamed alloy presoma
A specific embodiment according to the present invention, after the completion of step S100 heat preservation, adjustable argon pressure table will
Alloy melt pours into mold, then that mold is closed, then argon gas conduit mouth is extend into mold, opens argon gas bottle valve,
Under atmospheric pressure, alloy melt rapid osmotic is into salt particle gap.Close argon gas, melt takes out with after the mold is cooled to obtain the final product
To foamed alloy presoma.
S400: water-washing desalting is carried out to foamed alloy presoma, to obtain foamed alloy
The method and process for preparing foamed alloy of the above embodiment of the present invention is simple and at low cost, and relative to fine copper
For the foam copper of raw material, by using copper as basis material in the present invention, and a part of fine copper is replaced using the aluminium of certain component, no
Cost of material only can be significantly reduced, it is also possible that aluminium and copper form compound, and the microstructure of copper is promoted, to make to steep
Foam alloy has preferable sound-deadening and noise-reducing effect and stronger mechanical property.Wherein, the tensile strength of foamed alloy is not less than
330MPa, yield strength are not less than 21.5% not less than 175MPa, elongation percentage.
According to the third aspect of the present invention, the invention proposes a kind of mufflers for air-conditioning.It is according to the present invention
Embodiment, the muffler have foamed alloy described in the above embodiment of the present invention or make using described in the above embodiment of the present invention
The foamed alloy that the method for standby foamed alloy obtains.Air-conditioning can generate noise at work, and noise is using refrigerant as propagation medium
It is passed to interior, room noise is caused to generate.Therefore, it needs to be dropped by muffler before refrigerant enters air conditioner indoor unit
It makes an uproar processing, by using the foamed alloy of the above embodiment of the present invention muffler can not only imitated with preferable sound-deadening and noise-reducing
Fruit can also further decrease the production cost of muffler, simultaneously because foamed alloy has preferable mechanical property, it can be with
Further extend the service life of muffler.
A specific embodiment according to the present invention, foamed alloy can be used for muffler in the following manner.Specifically:
As Figure 2-3, muffler may include shell 110, the first foamed alloy 120 and the second foamed alloy 130, in shell 110
It is formed with refrigerant passage, the first foamed alloy 120 and the second foamed alloy 130 are arranged in refrigerant passage, and the second foam
The thickness of alloy is different from the thickness of the first foamed alloy.Wherein, the first foamed alloy 120 can be used for reducing making an uproar in refrigerant
Sound, the second foamed alloy 130 can be used for reducing the impurity in noise and filtering refrigerant in refrigerant, and then reduce impurity pair
The damage of air-conditioner hose extends the service life of air-conditioning；And the thickness of the first foamed alloy 120 and the second foamed alloy 130
Thickness it is different, can make refrigerant and noise that can receive more barriers during traveling, to multiple frequencies of noise
Duan Jinhang noise reduction, and then can effectively promote muffler noise reduction effect.
Further, the first foamed alloy 120 and the second foamed alloy 130 can be configured to annular, at this time the first bubble
The thickness of foam alloy 120 and the second foamed alloy 130 is the distance between respective inner sidewall and lateral wall；When the first foam closes
When having a complete closure refrigerant passage in gold 120 and the second foamed alloy 130, the thickness of the foamed alloy of refrigerant passage is blocked
The as radius of refrigerant passage；The thickness of second foamed alloy 130 can be greater than the thickness of the first foamed alloy 120, and second
At least part of cross-sectional area of foamed alloy 130 is identical as the cross-sectional area of refrigerant passage.Wherein, the first foamed alloy 120
It can be set on the internal perisporium of shell 110, so that refrigerant when flowing through the shell 110 of muffler, reduces sound pollution；Second
Being at least partly filled up completely radially in refrigerant passage and by refrigerant passage, refrigerant stream can be set in foamed alloy 130
When through refrigerant passage, the sound wave in refrigerant is entered with refrigerant in the hole of the second foamed alloy 130, and sound wave causes hole
Vibration, so as to cause the vibration that the second foamed alloy 130 is whole, in the inside of the second foamed alloy 130, phase between hole
It is intercommunicated to form the alloy fiber network to check and balance and the second foamed alloy 130 is made to generate the damping for preventing sound wave from spreading, sound
Wave is converted into thermal energy after being damped, and then has haved the function that noise.Simultaneously as constantly with second in refrigerant flow process
Hole in foamed alloy 130 and the first foamed alloy 120 rubs, and can convert thermal energy for the kinetic energy in refrigerant, heat
Heat transfer can be led to and be discharged into air the sound energy that can further consume in refrigerant；In addition, based on the theory that aperture is eliminated the noise,
When refrigerant flows through the second foamed alloy 130 or the first foamed alloy 120, refrigerant is closed by the first foamed alloy 120 and the second foam
Micropore in gold 130 shunts, and can also further decrease the noise in refrigerant.
Further, the second foamed alloy 130 can be set in the middle section of refrigerant passage, and the first foamed alloy
120 are separately positioned on the front side of the second foamed alloy 130 and rear side.As a result, the first foamed alloy 120 can not only filled
The heat dissipation area of foot, after the acoustic wave energy in refrigerant is converted into thermal energy, the first foamed alloy 120 can be more quickly by refrigerant
Heat is dispersed into air, and refrigerant can also be made to come into full contact with the second foamed alloy 130, and refrigerant is passing through the second foamed alloy
The acoustic wave energy that can preferably decay in refrigerant when 130, to reduce noise.Wherein, the thickness distribution of the first foamed alloy 120
It is not particularly restricted, for example, the thickness of the first foamed alloy 120 can be uniformly distributed (as shown in Figure 2) or close to refrigerant
(as shown in Figure 3) is gradually increased on the direction in channel middle position.It should be noted that " preceding " for towards refrigerant in the present invention
The direction of outlet 111, " rear " is towards the direction of refrigerant inlet 112.
It should be noted that above-mentioned be directed to foamed alloy or prepare technical characteristic and effect described in the method for foamed alloy
Fruit is equally applicable to the muffler, and details are not described herein again.
According to the fourth aspect of the present invention, the invention proposes a kind of blimps for compressor of air conditioner.According to this
The embodiment of invention, the blimp have foamed alloy described in the above embodiment of the present invention or use the above embodiment of the present invention
The foamed alloy that the method for preparing foamed alloy obtains.The blimp is located at the outside of compressor, with for absorb by
Noise caused by compressor hinders the noise transmission of compressor, by using the above embodiment of the present invention foamed alloy not
It can only make blimp that there is preferable soundproof effect and reduce production cost, and since foamed alloy has both preferable mechanics
Performance can also further extend the service life of blimp.
A specific embodiment according to the present invention, foamed alloy can be used for blimp in the following manner.Specifically,
As illustrated in figures 4-5, blimp may include sound insulation cover body 210, and sound insulation cover body 210 limits the receiving sky for accommodating compressor
Between, sound insulation cover body 210 includes foamed alloy layer 220.Wherein, foamed alloy layer 220 has high porosity and high through-hole rate
Feature, and high porosity and high through-hole rate are conducive to the absorption and decaying of sound wave, sound wave can convert in foamed alloy layer 220
For thermal energy, sound wave will lead to alloy fiber in foamed alloy layer 220 and vibrate, and alloy fiber forms network between each other and mutually leads
System can form the damping for hindering sound wave transmitting, and sound wave converts kinetic energy into thermal energy in foamed alloy layer 220, and then makes to press
Sound attenuation caused by contracting machine dissipates, and improves the sound-deadening and noise-reducing effect of blimp.
Further, blimp can be all made of foamed alloy layer 220, and then the noise for generating compressor can be with
Directly is absorbed and decayed by foamed alloy layer.Of course, it should be understood that blimp can also include other parts, such as
The support plate 230 of foamed alloy layer 220 is supported, the inner sidewall or lateral wall that foam metal layer 220 is arranged in support plate 230 are extremely
On few one, i.e. support plate 230 can be inner support plate 231 and/or external support board 232, with for foam metal layer 220 into
Row support and limit, wherein sound-absorbing hole (not shown) is also provided in support plate 230.As long as it should be noted that sound insulation
Cover includes that the technical solution of foamed alloy layer belongs to protection scope of the present invention.
It should be noted that above-mentioned be directed to foamed alloy or prepare technical characteristic and effect described in the method for foamed alloy
Fruit is equally applicable to the blimp, and details are not described herein again.
According to the fifth aspect of the present invention, the invention proposes a kind of air-conditionings.According to an embodiment of the invention, the air-conditioning
With described in the above embodiment of the present invention be used for air-conditioning muffler and/or the above embodiment of the present invention described in be used for air-conditioning
The blimp compressor of compressor.Generated noise when operation of air conditioner not only can be effectively reduced as a result, promote user's body
It tests, moreover it is possible to further decrease the production cost of air-conditioning and extend the service life of air-conditioning.
It should be noted that above-mentioned be equally applicable to this for technical characteristic described in muffler or compressor and effect
Air-conditioning, details are not described herein again.
Embodiment 1
(1) 5kg sodium chloride salt particle is put into crucible, is warming up to 600 using the heating speed of 5 DEG C/min in electric furnace
DEG C, furnace cooling after heat preservation 2 hours.Salt after cooling is roasted, carries out in crucible after being crushed, is handled with 5 mesh sub-sieves,
Obtain the salt particle of 5 mesh partial sizes.The salt of 5 mesh partial sizes is put into mold, is then pressed on salt particle and is compacted using wire netting.It will
Mold, which is put into high temperature furnace, is heated to 900 DEG C of heat preservations 1 hour.
(2) 2kg fine copper block is put into crucible, is melted fine copper using resistance furnace, kept the temperature 30 minutes after fusing, then exist
20g fine aluminium block is added in crucible, after aluminium block fusing, is sufficiently stirred, keeps alloy uniform, keep the temperature 30 minutes, to be made
Albronze melt, it is spare.
(3) after the completion of the alloy melt heat preservation in the salt particle and step (2) in step (1), argon pressure table is adjusted, it will
Albronze melt pours into mold, then by mold close, then extending into argon gas conduit mouth in mold, open argon bottle
Valve, under atmospheric pressure, albronze melt rapid osmotic is into salt particle gap.Argon gas is closed, copper aluminum melt is cold with mold
But it after, takes out and obtains foamed alloy presoma.
(4) water-washing desalting is carried out to foamed alloy presoma, obtains through-hole foam alloy.
2, compressor blimp is prepared:
As shown in figure 4, blimp includes sound insulation cover body 210, sound insulation cover body 210 limits the receiving for accommodating compressor
Space, sound insulation cover body 210 are formed by the above-mentioned through-hole foam alloy being prepared.
Embodiment 2
(1) 5kg sodium chloride salt particle is put into crucible, is warming up to 600 using the heating speed of 5 DEG C/min in electric furnace
DEG C, furnace cooling after heat preservation 2 hours.Salt after cooling is roasted, carries out in crucible after being crushed, is handled with 5 mesh sub-sieves,
Obtain the salt particle of 5 mesh partial sizes.The salt of 5 mesh partial sizes is put into mold, is pressed on salt particle and is compacted using wire netting.By mold
It is put into high temperature furnace and is heated to 900 DEG C of heat preservations 1 hour.
(2 are put into 2kg fine copper block in crucible, are melted fine copper using resistance furnace, keep the temperature 30 minutes after fusing, then exist
100g fine aluminium block is added in crucible, after aluminium block fusing, is sufficiently stirred, keeps alloy uniform, keep the temperature 30 minutes, to be made
Albronze melt, it is spare.
(3) after the completion of the alloy melt heat preservation in the salt particle and step (2) in step (1), argon pressure table is adjusted, it will
Albronze melt pours into mold, then by mold close, then extending into argon gas conduit mouth in mold, open argon bottle
Valve, under atmospheric pressure, albronze melt rapid osmotic is into salt particle gap.Argon gas is closed, copper aluminum melt is cold with mold
But it after, takes out and obtains foamed alloy presoma.
(4) water-washing desalting is carried out to foamed alloy presoma, obtains through-hole foam alloy.
2, compressor blimp is prepared:
As shown in figure 4, blimp includes sound insulation cover body 210, sound insulation cover body 210 limits the receiving for accommodating compressor
Space, sound insulation cover body 210 are formed by the above-mentioned through-hole foam alloy being prepared.
Embodiment 3
(1) 5kg sodium chloride salt particle is put into crucible, is warming up to 600 using the heating speed of 5 DEG C/min in electric furnace
DEG C, furnace cooling after heat preservation 2 hours.Salt after cooling is roasted, carries out in crucible after being crushed, is handled with 5 mesh sub-sieves,
Obtain the salt particle of 5 mesh partial sizes.The salt of 5 mesh partial sizes is put into mold, is pressed on salt particle and is compacted using wire netting.By mold
It is put into high temperature furnace and is heated to 900 DEG C of heat preservations 1 hour.
(2 are put into 2kg fine copper block in crucible, are melted fine copper using resistance furnace, keep the temperature 30 minutes after fusing, then exist
200g fine aluminium block is added in crucible, after aluminium block fusing, is sufficiently stirred, keeps alloy uniform, keep the temperature 30 minutes, to be made
Albronze melt, it is spare.
(3) after the completion of the alloy melt heat preservation in the salt particle and step (2) in step (1), argon pressure table is adjusted, it will
Albronze melt pours into mold, then by mold close, then extending into argon gas conduit mouth in mold, open argon bottle
Valve, under atmospheric pressure, albronze melt rapid osmotic is into salt particle gap.Argon gas is closed, copper aluminum melt is cold with mold
But it after, takes out and obtains foamed alloy presoma.
(4) water-washing desalting is carried out to foamed alloy presoma, obtains through-hole foam alloy.
2, compressor blimp is prepared:
As shown in figure 4, blimp includes sound insulation cover body 210, sound insulation cover body 210 limits the receiving for accommodating compressor
Space, sound insulation cover body 210 are formed by the above-mentioned through-hole foam alloy being prepared.
Embodiment 4
(1) 5kg sodium chloride salt particle is put into crucible, is warming up to 600 using the heating speed of 5 DEG C/min in electric furnace
DEG C, furnace cooling after heat preservation 2 hours.Salt after cooling is roasted, carries out in crucible after being crushed, is handled with 5 mesh sub-sieves,
Obtain the salt particle of 5 mesh partial sizes.The salt of 5 mesh partial sizes is then placed in mold, is pressed on salt particle and is compacted using wire netting.It will
Mold, which is put into high temperature furnace, is heated to 900 DEG C of heat preservations 1 hour.
(2) 2kg fine copper block is put into crucible, is melted fine copper using resistance furnace, kept the temperature 30 minutes after fusing, then exist
50g fine aluminium block is added in crucible, after aluminium block fusing, is sufficiently stirred, keeps alloy uniform, keep the temperature 30 minutes, to be made
Albronze melt, it is spare.
(3) after the completion of the alloy melt heat preservation in the salt particle and step (2) in step (1), argon pressure table is adjusted, it will
Albronze melt pours into mold, then by mold close, then extending into argon gas conduit mouth in mold, open argon bottle
Valve, under atmospheric pressure, albronze melt rapid osmotic is into salt particle gap.Argon gas is closed, copper aluminum melt is cold with mold
But it after, takes out and obtains foamed alloy presoma.
(4) water-washing desalting is carried out to foamed alloy presoma, obtains through-hole foam alloy.
2, compressor blimp is prepared:
As shown in figure 4, blimp includes sound insulation cover body 210, sound insulation cover body 210 limits the receiving for accommodating compressor
Space, sound insulation cover body 210 are formed by the above-mentioned through-hole foam alloy being prepared.
Embodiment 5
(1) 5kg sodium chloride salt particle is put into crucible, is warming up to 600 using the heating speed of 5 DEG C/min in electric furnace
DEG C, furnace cooling after heat preservation 2 hours.Salt after cooling is roasted, carries out in crucible after being crushed, is handled with 5 mesh sub-sieves,
Obtain the salt particle of 5 mesh partial sizes.The salt of 5 mesh partial sizes is then placed in mold, is pressed on salt particle and is compacted using wire netting.It will
Mold, which is put into high temperature furnace, is heated to 900 DEG C of heat preservations 1 hour.
(2) 2kg fine copper block is put into crucible, is melted fine copper using resistance furnace, kept the temperature 30 minutes after fusing, then exist
150g fine aluminium block is added in crucible, after aluminium block fusing, is sufficiently stirred, keeps alloy uniform, keep the temperature 30 minutes, to be made
Albronze melt, it is spare.
(3) after the completion of the alloy melt heat preservation in the salt particle and step (2) in step (1), argon pressure table is adjusted, it will
Albronze melt pours into mold, then by mold close, then extending into argon gas conduit mouth in mold, open argon bottle
Valve, under atmospheric pressure, albronze melt rapid osmotic is into salt particle gap.Argon gas is closed, copper aluminum melt is cold with mold
But it after, takes out and obtains foamed alloy presoma.
(4) water-washing desalting is carried out to foamed alloy presoma, obtains through-hole foam alloy.
2, compressor blimp is prepared:
As shown in figure 4, blimp includes sound insulation cover body 210, sound insulation cover body 210 limits the receiving for accommodating compressor
Space, sound insulation cover body 210 are formed by the above-mentioned through-hole foam alloy being prepared.
Comparative example 1
1, foam copper is prepared:
(1) 5Kg crude salt particle is put into crucible, is warming up to 600 DEG C using the heating speed of 5 DEG C/min in electric furnace,
Furnace cooling after heat preservation 2 hours.It roasts salt after cooling to carry out in crucible after being crushed, carries out classification processing with 5 mesh sub-sieves,
Obtain the salt particle of 5 mesh partial sizes；The salt particle of 5 mesh partial sizes is put into mold, is then pressed on salt particle and is pressed using wire netting
It is real, then mold is put into high temperature furnace and is heated to 900 DEG C of heat preservations 1 hour.
(2) 2kg fine copper block is put into crucible, is melted fine copper using resistance furnace, keep the temperature 30 minutes after fusing.
(3) after the completion of the fine copper molten liquid heat preservation in the salt particle and step (2) in step (1), argon pressure table is adjusted,
Fine copper molten liquid is poured into mold, it is then that mold is closed, then argon gas conduit mouth is extend into mold, open argon gas cylinder valve
Door, under gas pressure, fine copper molten liquid rapid osmotic is into salt particle gap.Argon gas is closed, melt takes with after the mold is cooled
Foam copper presoma is obtained out.
(4) water-washing desalting is carried out to foam copper presoma, obtains through-hole foam copper.
2, compressor blimp is prepared:
As shown in figure 4, blimp includes sound insulation cover body 210, sound insulation cover body 210 limits the receiving for accommodating compressor
Space, sound insulation cover body 210 are formed by the above-mentioned through-hole foam copper being prepared.
Comparative example 2
1, foam copper is prepared:
(1) 5Kg crude salt particle is put into crucible, is warming up to 600 DEG C using the heating speed of 5 DEG C/min in electric furnace,
Furnace cooling after heat preservation 2 hours.It roasts salt after cooling to carry out in crucible after being crushed, be carried out at classification with 10 mesh sub-sieves
Reason obtains the salt particle of 10 mesh partial sizes；The salt particle of 10 mesh partial sizes is put into mold, is then pressed in salt particle using wire netting
Then mold is put into high temperature furnace and is heated to 900 DEG C of heat preservations 1 hour by upper compacting.
(2) 2kg fine copper block is put into crucible, is melted fine copper using resistance furnace, keep the temperature 30 minutes after fusing.
(3) after the completion of the fine copper molten liquid heat preservation in the salt particle and step (2) in step (1), argon pressure table is adjusted,
Fine copper molten liquid is poured into mold, it is then that mold is closed, then argon gas conduit mouth is extend into mold, open argon gas cylinder valve
Door, under gas pressure, fine copper molten liquid rapid osmotic is into salt particle gap.Argon gas is closed, melt takes with after the mold is cooled
Foam copper presoma is obtained out.
(4) water-washing desalting is carried out to foam copper presoma, obtains through-hole foam copper.
2, compressor blimp is prepared:
As shown in figure 4, blimp includes sound insulation cover body 210, sound insulation cover body 210 limits the receiving for accommodating compressor
Space, sound insulation cover body 210 are formed by the above-mentioned through-hole foam copper being prepared.
Comparative example 3
1, foam copper is prepared:
(1) 5Kg crude salt particle is put into crucible, is warming up to 600 DEG C using the heating speed of 5 DEG C/min in electric furnace,
Furnace cooling after heat preservation 3 hours.It roasts salt after cooling to carry out in crucible after being crushed, be carried out at classification with 15 mesh sub-sieves
Reason obtains the salt particle of 15 mesh partial sizes；The salt particle of 15 mesh partial sizes is put into mold, is then pressed in salt particle using wire netting
Then mold is put into high temperature furnace and is heated to 900 DEG C of heat preservations 1 hour by upper compacting.
(2) 2kg fine copper block is put into crucible, is melted fine copper using resistance furnace, keep the temperature 30 minutes after fusing.
(3) after the completion of the fine copper molten liquid heat preservation in the salt particle and step (2) in step (1), argon pressure table is adjusted,
Fine copper molten liquid is poured into mold, it is then that mold is closed, then argon gas conduit mouth is extend into mold, open argon gas cylinder valve
Door, under gas pressure, fine copper molten liquid rapid osmotic is into salt particle gap.Argon gas is closed, melt takes with after the mold is cooled
Foam copper presoma is obtained out.
(4) water-washing desalting is carried out to foam copper presoma, obtains through-hole foam copper.
2, compressor blimp is prepared:
As shown in figure 4, blimp includes sound insulation cover body 210, sound insulation cover body 210 limits the receiving for accommodating compressor
Space, sound insulation cover body 210 are formed by the above-mentioned through-hole foam copper being prepared.
Test analysis:
Respectively to the mechanical property of the foam copper obtained in the foamed alloy and comparative example 1-3 obtained in embodiment 1-5 into
Row test analysis surveys the sound-deadening and noise-reducing effect of compressor blimp obtained in embodiment 1-5 and comparative example 1-3
Examination, wherein mechanics properties testing is carried out using cupping machine, tensile speed 50mm/min.Test result is shown in Table 1.
1 mechanical property of table and sound-deadening and noise-reducing test result
Conclusion:
From table 1 it follows that being compared with raw material is prepared into the foam copper beaten, to pass through in the embodiment of the present invention with independent copper
Using copper as basis material, and the aluminium of certain component is added, the foamed alloy being prepared can be made to have with foam copper quite very
Extremely it is better than the mechanical property of foam copper, and the level of noise detected after the air-conditioning sound cover prepared with foamed alloy is used to be less than
The level of noise detected after the air-conditioning sound cover prepared with foam copper is used, i.e. the sound-deadening and noise-reducing effect of foamed alloy is better than foam
Copper.
In the description of this specification, reference term " one embodiment ", " some embodiments ", " example ", " specifically show
The description of example " or " some examples " etc. means specific features, structure, material or spy described in conjunction with this embodiment or example
Point is included at least one embodiment or example of the invention.In the present specification, schematic expression of the above terms are not
It must be directed to identical embodiment or example.Moreover, particular features, structures, materials, or characteristics described can be any
It can be combined in any suitable manner in a or multiple embodiment or examples.In addition, without conflicting with each other, the technology of this field
The feature of different embodiments or examples described in this specification and different embodiments or examples can be combined by personnel
And combination.
Although the embodiments of the present invention has been shown and described above, it is to be understood that above-described embodiment is example
Property, it is not considered as limiting the invention, those skilled in the art within the scope of the invention can be to above-mentioned
Embodiment is changed, modifies, replacement and variant.
Claims (12)
1. a kind of foamed alloy for air conditioner sound-deadening and noise-reducing characterized by comprising copper, the 0.1-10 weight of 100 parts by weight
Measure the aluminium of part.
2. foamed alloy according to claim 1, which is characterized in that the tensile strength of the foamed alloy is not less than
330MPa。
3. foamed alloy according to claim 1, which is characterized in that the yield strength of the foamed alloy is not less than
175MPa。
4. foamed alloy according to claim 1, which is characterized in that the elongation percentage of the foamed alloy is not less than
21.5%.
5. foamed alloy according to claim 1, which is characterized in that the hole of the foamed alloy is through-hole.
6. a kind of method for preparing any one of claim 1-5 foamed alloy characterized by comprising
(1) salt particle is filled into mold to be compacted and heated, kept the temperature；
(2) fine copper is heated and melts and obtains fine copper molten liquid, the fine aluminium of predetermined ratio is added into the fine copper molten liquid, with
Just alloy melt is obtained；
(3) alloy melt is poured into the mold in step (1) filled with the salt particle, the closed mold and to institute
It states and is passed through inert gas in mold, to make the alloy melt rapid osmotic into the gap of the salt particle, and cooling
To foamed alloy presoma；
(4) water-washing desalting is carried out to the foamed alloy presoma, to obtain foamed alloy.
7. according to the method described in claim 6, it is characterized in that, the partial size of the salt particle is 0.55- in step (1)
1.7mm, the temperature of the heating are 800-1200 DEG C, and the soaking time is 0.5-3 hours.
8. according to the method described in claim 6, it is characterized in that, further comprising before step (1):
Crude salt particle is warming up to 600-800 DEG C with the heating speed of 10-15 DEG C/min to roast；
Crude salt particle after the roasting is subjected to cooling and crushing and screening, to obtain the salt particle.
9. according to the method described in claim 6, it is characterized in that, being based on the fine copper molten liquid, addition in step (2)
The aluminium of 0.1-10wt%, to obtain the alloy melt.
10. a kind of muffler for air-conditioning, which is characterized in that the muffler has claim 1-5 described in any item
Foamed alloy or the foamed alloy being prepared using the described in any item methods of claim 6-9.
11. a kind of blimp for compressor of air conditioner, which is characterized in that the blimp has any one of claim 1-5
The foamed alloy or the foamed alloy being prepared using the described in any item methods of claim 6-9.
12. a kind of air-conditioning, which is characterized in that the air-conditioning has muffler described in any one of claim 10 and/or claim 11
The blimp.