CN109021733A - A kind of aqueous, environmental protective automobile coating and preparation method thereof - Google Patents
A kind of aqueous, environmental protective automobile coating and preparation method thereof Download PDFInfo
- Publication number
- CN109021733A CN109021733A CN201810573336.5A CN201810573336A CN109021733A CN 109021733 A CN109021733 A CN 109021733A CN 201810573336 A CN201810573336 A CN 201810573336A CN 109021733 A CN109021733 A CN 109021733A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- aqueous
- agent
- automobile coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of aqueous, environmental protective automobile coating and preparation method thereof, belongs to automobile coating technical field.Automobile coating of the invention, by 60-70 parts by weight water-based acrylic resin, 20-30 parts by weight water-soluble methyl ether amino resins, 10-15 parts by weight aqueous epoxy resins, 5-8 parts by weight aqueous levelling agent, 4-6 parts by weight aqueous defoamer, 3-6 parts by weight anti-settling agent, 2-4 parts by weight nano-titanium dioxide, 1-3 parts by weight di-iron trioxide, 2-2.5 parts by weight conch meal, 5-10 parts by weight wetting agent, 3-6 parts per weight dispersing agent, 5-8 parts by weight of thickening agent, 4-7 parts by weight polytetrafluorethylepowder powder, the more ethylene oxidic esters of 4-5 parts by weight of glycerin, 8-12 parts by weight curing agent, 1-3 parts by weight ultraviolet absorbing agent and 30-60 parts by weight of deionized water composition.The automobile coating glossiness is high, and impact resistance, resistance to acid and alkali, wearability, durability, weatherability, stain resistant are excellent, and environment friendly and pollution-free.
Description
Technical field
The invention belongs to automobile coating technical fields, and in particular to a kind of aqueous, environmental protective automobile coating and preparation method thereof.
Background technique
Automobile coating is a kind of protective film being sprayed on automobile, plays protection and decorative effect.Different automobile coating effects
Difference, there are three types of currently used automobile coatings: common paint, metallic paint and opalescent lacquers.The main component commonly painted is resin, pigment
And additive, spraying process is fairly simple, and it is at low cost, but be easy to fade, unsightly.Metallic paint is on the basis of common paint
It is added to metallic particles, to spray one layer of varnish above also after having sprayed to protect metallic particles not to be damaged, and keep light
Brightness, lacquer spraying technique are complicated.Opalescent lacquers is added to very thin mica grain on the basis of common paint, and color is more bright-colored, still
The somewhat expensive complex procedures of emerylite.
During use, vehicle body Chang Huiyu hard objects contact-impact causes vehicle paint to scratch to automobile, reduces aesthetics, example
Such as, in the process of moving, shock of the vehicle body by road blinding;In carwash, impurities in water washes away vehicle body.In addition,
Automobile is chronically exposed in various rugged environments, and vehicle body is easy aging, burn into full of bacterium, causes the reduction of vehicle paint glossiness.
Also, existing automobile coating, based on solvent type, a large amount of volatile organic compounds cause ecological environment in coating process
Serious pollution, while also great harm is brought to human health.Pursuit with people to higher quality of the life
With the raising of the ecological awareness, automobile coating needs more comprehensively to meet the complicated adverse circumstances that automobile uses and the spy for having safety and environmental protection
Point, therefore, developing, there is the environment-friendly water-based car paint of high gloss, scratch-resistant, impact resistance, durability to become automobile coating section
Grind the important topic of personnel.
Water paint is free of benzene,toluene,xylene, formaldehyde, free TDI toxic heavy metal using water as diluent, nontoxic stingless
Swash smell, it is harmless, it is free from environmental pollution, paint film is plentiful, it is sparkling and crystal-clear it is bright, flexibility is good and have it is water-fast, wear-resisting, resistance to always
Change, color inhibition, fast drying, it is easy to use the features such as.Therefore it is well suited as the research direction of new automobile paint.The prior art
In, it is more existing with water-based automobile paint, but there are some problems, as additive is easy to reunite, it is difficult to dispersion steady in a long-term
Or levelability is poor, the final apparent mass and mechanical property for influencing automobile.
Summary of the invention
In view of this, the purpose of the present invention is how to provide a kind of aqueous, environmental protective automobile coating and preparation method thereof, the automobile
Paint glossiness height, good weatherability, resistance to acid and alkali is good, wearability is good, impact resistance is good, durability is good, thermal insulation is good, environmentally friendly nothing
Pollution.
A kind of aqueous, environmental protective automobile coating, composition and parts by weight are as follows:
Preferably, the aqueous levelling agent is BYK-333.
Preferably, the aqueous defoamer is BYK-093.
Preferably, the anti-settling agent is BYK-E420.
Preferably, the thickener is association type polyurethane thickener.
Preferably, the wetting agent is BYK-307 or BYK-377.
Preferably, the dispersing agent is BYK-190 or BYK-182.
Preferably, the ultraviolet absorbing agent UV326.
Preferably, the curing agent is benzene dimethylamine or triethylamine.
The preparation method of above-mentioned aqueous, environmental protective automobile coating, which is characterized in that steps are as follows: first that 60-70 parts by weight are aqueous
Acrylic resin, 10-15 parts by weight aqueous epoxy resins, 5-8 parts by weight aqueous levelling agent, 4-6 parts by weight aqueous defoamer, 3-
6 parts by weight anti-settling agents, 2-4 parts by weight nano-titanium dioxide, 1-3 parts by weight di-iron trioxide, 2-2.5 parts by weight conch meal, 5-
10 parts by weight wetting agents, 3-6 parts per weight dispersing agent, 5-8 parts by weight of thickening agent, 4-7 parts by weight polytetrafluorethylepowder powder, 4-5 weight
Amount part glycerin multiple glycidyl ester, 1-3 parts by weight ultraviolet absorbing agent and 30-60 parts by weight of deionized water are uniformly mixed,
Then 8-12 parts by weight curing agent is added and 20-30 parts by weight water-soluble methyl ether amino resins continues to be uniformly mixed, obtain
Aqueous, environmental protective automobile coating.
Compared with prior art, the beneficial effects of the present invention are:
Aqueous, environmental protective automobile coating glossiness height of the invention, good impact resistance, resistance to acid and alkali is good, wearability is good, durability
Good, good weatherability, stain resistant are good and environment friendly and pollution-free;Through experimental tests;Impact strength is in 62-69kg/cm, ageing-resistant reality
Test that 1000h is not blistering, does not peel off, acidproof 100h is not blistering, does not peel off, and alkaline-resisting 50h is not blistering, does not peel off, UV resistant 500h
It is not blistering, do not peel off, gloss retention is in 95-97% after scraping, static adhesive force≤1, -35 DEG C to 80 DEG C without dusting, nothing
Fission;20 ° of gloss reach 98% or more, and washability 15000 times or more, stain resistant≤10%.
The preparation process of aqueous, environmental protective automobile coating of the invention is simple, and process is environmentally protective.
Specific embodiment
For a further understanding of the present invention, the preferred embodiment of the invention is described below with reference to embodiment, still
It should be appreciated that these descriptions are only further explanation the features and advantages of the present invention, rather than to the claims in the present invention
Limitation.
A kind of aqueous, environmental protective automobile coating, by 60-70 parts by weight water-based acrylic resin, 20-30 parts by weight water-soluble methyl ether
Amino resins, 10-15 parts by weight aqueous epoxy resins, 5-8 parts by weight aqueous levelling agent, 4-6 parts by weight aqueous defoamer, 3-6
Parts by weight anti-settling agent, 2-4 parts by weight nano-titanium dioxide, 1-3 parts by weight di-iron trioxide, 2-2.5 parts by weight conch meal, 5-10
Parts by weight wetting agent, 3-6 parts per weight dispersing agent, 5-8 parts by weight of thickening agent, 4-7 parts by weight polytetrafluorethylepowder powder, 4-5 weight
Part glycerin multiple glycidyl ester, 8-12 parts by weight curing agent, 1-3 parts by weight ultraviolet absorbing agent and 30-60 parts by weight deionization
Water composition.
Aqueous, environmental protective automobile coating of the invention further includes the color filters of 4-7 parts by weight.
Various raw materials of the invention are the prior art, can be commercially available, in which: water-soluble methyl ether amino resins
Model can be XY-B-800-80;Aqueous epoxy resins are purchased from Dow Chemical;Aqueous levelling agent be organosilicon levelling agent,
Acrylic type levelling agent etc. commonly uses BYK-333;Aqueous defoamer is organic silicon defoaming agent, polyacrylic defoaming agent, phosphoric acid
Vinegar class defoaming agent, silylated polyether class defoaming agent, acetylenic diols defoaming agent etc. commonly use BYK-093;Anti-settling agent is commonly used for BYK-
E420;Nano-titanium dioxide, titanium sesquioxide, the partial size of conch meal and polytetrafluorethylepowder powder are the smaller the better, and at least 500
Mesh;Wetting agent is commonly used for BYK-307 or BYK-377;Dispersing agent is commonly used for BYK-190 or BYK-182;Thickener is commonly used for associating
Type polyurethane thickener;Curing agent is benzene dimethylamine or triethylamine;Ultraviolet absorbing agent is UV326.
The preparation method of above-mentioned aqueous, environmental protective automobile coating, by formula, first by 60-70 parts by weight water-based acrylic resin, 10-
15 parts by weight aqueous epoxy resins, 5-8 parts by weight aqueous levelling agent, 4-6 parts by weight aqueous defoamer, 3-6 parts by weight anti-settling agent,
2-4 parts by weight nano-titanium dioxide, 1-3 parts by weight di-iron trioxide, 2-2.5 parts by weight conch meal, 5-10 parts by weight wetting agent,
3-6 parts per weight dispersing agent, 5-8 parts by weight of thickening agent, 4-7 parts by weight polytetrafluorethylepowder powder, 4-5 parts by weight of glycerin shrink sweet more
Grease, 1-3 parts by weight ultraviolet absorbing agent and 30-60 parts by weight of deionized water are uniformly mixed, and 8-12 weight is then added
Part curing agent and 20-30 parts by weight water-soluble methyl ether amino resins continue to be uniformly mixed, and obtain aqueous, environmental protective automobile coating.
The present invention is further illustrated with reference to embodiments.
Embodiment 1
Aqueous, environmental protective automobile coating, by 60 parts by weight water-based acrylic resins, 20 parts by weight water-soluble methyl ether amino resins, 10
Parts by weight aqueous epoxy resins, 5 parts by weight aqueous levelling agent BYK-333,4 parts by weight aqueous defoamer BYK-093,3 parts by weight
Anti-settling agent BYK-E420,2 parts by weight nano-titanium dioxides, 1 parts by weight di-iron trioxide, 2 parts by weight conch meals, 5 parts by weight profit
Humectant BYK-377,3 parts per weight dispersing agent BYK-182,5 parts by weight association type polyurethane thickeners, 4 parts by weight polytetrafluoroethylene (PTFE)
Powder, the more ethylene oxidic esters of 4 parts by weight of glycerin, 8 parts by weight curing agent triethylamines, 1 parts by weight ultraviolet absorbing agent UV326 and 30
Parts by weight of deionized water composition.
The preparation of above-mentioned aqueous, environmental protective automobile coating: first by water-based acrylic resin, aqueous epoxy resins, aqueous levelling agent,
Aqueous defoamer, anti-settling agent, nano-titanium dioxide, di-iron trioxide, conch meal, wetting agent, dispersing agent, association type polyurethane
Thick dose, polytetrafluorethylepowder powder, glycerin multiple glycidyl ester, ultraviolet absorbing agent and deionized water are uniformly mixed, then
Triethylamine is added and water-soluble methyl ether amino resins continues to be uniformly mixed, obtains aqueous, environmental protective automobile coating.
Embodiment 2
Aqueous, environmental protective automobile coating, by 70 parts by weight water-based acrylic resins, 30 parts by weight water-soluble methyl ether amino resins, 15
Parts by weight aqueous epoxy resins, 8 parts by weight aqueous levelling agent BYK-333,6 parts by weight aqueous defoamer BYK-093,6 parts by weight
Anti-settling agent BYK-E420,4 parts by weight nano-titanium dioxides, 3 parts by weight di-iron trioxides, 2.5 parts by weight conch meals, 10 parts by weight
Wetting agent BYK-377,6 parts per weight dispersing agent BYK-182,8 parts by weight association type polyurethane thickeners, 7 parts by weight polytetrafluoroethyl-nes
Alkene powder, the more ethylene oxidic esters of 5 parts by weight of glycerin, 12 parts by weight curing agent triethylamines, 3 parts by weight ultraviolet absorbing agent UV326
It is formed with 60 parts by weight of deionized water.
The preparation of above-mentioned aqueous, environmental protective automobile coating: first by water-based acrylic resin, aqueous epoxy resins, aqueous levelling agent,
Aqueous defoamer, anti-settling agent, nano-titanium dioxide, di-iron trioxide, conch meal, wetting agent, dispersing agent, association type polyurethane
Thick dose, polytetrafluorethylepowder powder, glycerin multiple glycidyl ester, ultraviolet absorbing agent and deionized water are uniformly mixed, then
Triethylamine is added and water-soluble methyl ether amino resins continues to be uniformly mixed, obtains aqueous, environmental protective automobile coating.
Embodiment 3
Aqueous, environmental protective automobile coating, by 65 parts by weight water-based acrylic resins, 25 parts by weight water-soluble methyl ether amino resins, 12
Parts by weight aqueous epoxy resins, 6 parts by weight aqueous levelling agent BYK-333,5 parts by weight aqueous defoamer BYK-093,4 parts by weight
Anti-settling agent BYK-E420,3 parts by weight nano-titanium dioxides, 2 parts by weight di-iron trioxides, 2.2 parts by weight conch meals, 7 parts by weight
Wetting agent BYK-377,5 parts per weight dispersing agent BYK-182,6 parts by weight association type polyurethane thickeners, 5 parts by weight polytetrafluoroethyl-nes
Alkene powder, the more ethylene oxidic esters of 4.5 parts by weight of glycerin, 10 parts by weight curing agent triethylamines, 2 parts by weight ultraviolet absorbing agents
UV326 and 40 parts by weight of deionized water composition.
The preparation of above-mentioned aqueous, environmental protective automobile coating: first by water-based acrylic resin, aqueous epoxy resins, aqueous levelling agent,
Aqueous defoamer, anti-settling agent, nano-titanium dioxide, di-iron trioxide, conch meal, wetting agent, dispersing agent, association type polyurethane
Thick dose, polytetrafluorethylepowder powder, glycerin multiple glycidyl ester, ultraviolet absorbing agent and deionized water are uniformly mixed, then
Triethylamine is added and water-soluble methyl ether amino resins continues to be uniformly mixed, obtains aqueous, environmental protective automobile coating.
Embodiment 4
Aqueous, environmental protective automobile coating, by 67 parts by weight water-based acrylic resins, 28 parts by weight water-soluble methyl ether amino resins, 14
Parts by weight aqueous epoxy resins, 7 parts by weight aqueous levelling agent BYK-333,5.5 parts by weight aqueous defoamer BYK-093,5 weight
Part anti-settling agent BYK-E420,3.5 parts by weight nano-titanium dioxides, 2.5 parts by weight di-iron trioxides, 2.5 parts by weight conch meals, 8
Parts by weight wetting agent BYK-377,5 parts per weight dispersing agent BYK-182,6.5 parts by weight association type polyurethane thickeners, 6.5 weight
Part polytetrafluorethylepowder powder, the more ethylene oxidic esters of 4.6 parts by weight of glycerin, 11 parts by weight curing agent triethylamines, 2.5 parts by weight are ultraviolet
Light absorbers UV326 and 50 parts by weight of deionized water composition.
The preparation of above-mentioned aqueous, environmental protective automobile coating: first by water-based acrylic resin, aqueous epoxy resins, aqueous levelling agent,
Aqueous defoamer, anti-settling agent, nano-titanium dioxide, di-iron trioxide, conch meal, wetting agent, dispersing agent, association type polyurethane
Thick dose, polytetrafluorethylepowder powder, glycerin multiple glycidyl ester, ultraviolet absorbing agent and deionized water are uniformly mixed, then
Triethylamine is added and water-soluble methyl ether amino resins continues to be uniformly mixed, obtains aqueous, environmental protective automobile coating.
Comparative example 1
Automobile coating, by 60 parts by weight water-based acrylic resins, 20 parts by weight water-soluble methyl ether amino resins, 5 parts by weight water
Property levelling agent BYK-333,4 parts by weight aqueous defoamer BYK-093,3 parts by weight anti-settling agent BYK-E420,2 parts by weight nanometers two
Titanium oxide, 1 parts by weight di-iron trioxide, 2 parts by weight conch meals, 5 parts by weight wetting agent BYK-377,3 parts per weight dispersing agent BYK-
182,5 parts by weight association type polyurethane thickeners, 4 parts by weight polytetrafluorethylepowder powders, the more ethylene oxidic esters of 4 parts by weight of glycerin, 8
Parts by weight curing agent triethylamine, 1 parts by weight ultraviolet absorbing agent UV326 and 20 parts by weight of deionized water composition.
The preparation of above-mentioned automobile coating: first by water-based acrylic resin, aqueous levelling agent, aqueous defoamer, anti-settling agent, nanometer
It is titanium dioxide, di-iron trioxide, conch meal, wetting agent, dispersing agent, association type polyurethane thickener, polytetrafluorethylepowder powder, sweet
The more ethylene oxidic esters of oil, ultraviolet absorbing agent and deionized water are uniformly mixed, and triethylamine and water-soluble methyl ether is then added
Amino resins continues to be uniformly mixed, and obtains automobile coating.
Comparative example 2
Automobile coating, by 60 parts by weight water-based acrylic resins, 20 parts by weight water-soluble methyl ether amino resins, 10 parts by weight water
Property epoxy resin, 5 parts by weight aqueous levelling agent BYK-333,4 parts by weight aqueous defoamer BYK-093,3 parts by weight anti-settling agents
BYK-E420,2 parts by weight nano-titanium dioxides, 2 parts by weight conch meals, 5 parts by weight wetting agent BYK-377,3 parts per weight dispersing agents
BYK-182,5 parts by weight association type polyurethane thickeners, the more ethylene oxidic esters of 4 parts by weight of glycerin, 8 parts by weight curing agent, three second
Amine, 1 parts by weight ultraviolet absorbing agent UV326 and 20 parts by weight of deionized water composition.
The preparation of above-mentioned automobile coating: first by water-based acrylic resin, aqueous epoxy resins, aqueous levelling agent, aqueous defoaming
Agent, anti-settling agent, nano-titanium dioxide, conch meal, wetting agent, dispersing agent, association type polyurethane thickener, the more glycidols of glycerol
Ester, ultraviolet absorbing agent and deionized water are uniformly mixed, and triethylamine is then added and water-soluble methyl ether amino resins continues
It is uniformly mixed, obtains automobile coating.
The comprehensive performance of the automobile coating of embodiment 1-4 and comparative example 1-2 is detected, impact resistance uses national standard GB/
T1732-1993 detection, resistance to ag(e)ing are detected using GB/T1865-1997, and dry Scratch Resistance uses AS/NZS1580.403.1-
1999 detections, static adhesive force are detected using GB/T9286-1998, and 20 ° of gloss are detected using GB/T9754-2007.Weatherability
Detection be placed in subzero 35 DEG C of environment seven days first is that automobile coating iron plate will be coated with, apparently changed using automobile coating as characterization
As a result, detection second is that place temperature sensor in sealing iron case, and outer surface is applied into automobile coating in iron case, is subsequently placed in 30
DEG C environment in, and be warming up to 50 DEG C with 5 DEG C/min, the maximum temperature detected using temperature sensor is characterization result.As a result
As shown in table 1.
The performance characterization of the automobile coating of table 1 embodiment 1-4 and comparative example 1-2
As it can be seen from table 1 automobile coating glossiness height of the invention, good impact resistance, resistance to acid and alkali is good, wearability is good,
Durability is good, good weatherability, stain resistant are good, environment friendly and pollution-free.
The foregoing description of the disclosed embodiments enables those skilled in the art to implement or use the present invention.
Various modifications to these embodiments will be readily apparent to those skilled in the art, as defined herein
General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, of the invention
It is not intended to be limited to the embodiments shown herein, and is to fit to and the principles and novel features disclosed herein phase one
The widest scope of cause.
Claims (10)
1. a kind of aqueous, environmental protective automobile coating, which is characterized in that composition and parts by weight are as follows:
2. aqueous, environmental protective automobile coating according to claim 1, which is characterized in that the aqueous levelling agent is BYK-333.
3. aqueous, environmental protective automobile coating according to claim 1, which is characterized in that the aqueous defoamer is BYK-093.
4. aqueous, environmental protective automobile coating according to claim 1, which is characterized in that the anti-settling agent is BYK-E420.
5. aqueous, environmental protective automobile coating according to claim 1, which is characterized in that the thickener is association type polyurethane
Thick dose.
6. aqueous, environmental protective automobile coating according to claim 1, which is characterized in that the wetting agent be BYK-307 or
BYK-377。
7. aqueous, environmental protective automobile coating according to claim 1, which is characterized in that the dispersing agent is BYK-190 or BYK-
182。
8. aqueous, environmental protective automobile coating according to claim 1, which is characterized in that the ultraviolet absorbing agent UV326.
9. aqueous, environmental protective automobile coating according to claim 1, which is characterized in that the curing agent is benzene dimethylamine or three second
Amine.
10. the preparation method of aqueous, environmental protective automobile coating described in claim 1-9 any one, which is characterized in that steps are as follows:
First by 60-70 parts by weight water-based acrylic resin, 10-15 parts by weight aqueous epoxy resins, the aqueous levelling of 5-8 parts by weight
Agent, 4-6 parts by weight aqueous defoamer, 3-6 parts by weight anti-settling agent, 2-4 parts by weight nano-titanium dioxide, 1-3 parts by weight three aoxidize
Two iron, 2-2.5 parts by weight conch meal, 5-10 parts by weight wetting agent, 3-6 parts per weight dispersing agent, 5-8 parts by weight of thickening agent, 4-7 weight
Measure part polytetrafluorethylepowder powder, the more ethylene oxidic esters of 4-5 parts by weight of glycerin, 1-3 parts by weight ultraviolet absorbing agent and 30-60 weight
Part deionized water is uniformly mixed, and 8-12 parts by weight curing agent and 20-30 parts by weight water-soluble methyl ether amino tree is then added
Rouge continues to be uniformly mixed, and obtains aqueous, environmental protective automobile coating.