CN107880766A - A kind of single-component water-based finish paint and preparation method applied to drag pump car - Google Patents
A kind of single-component water-based finish paint and preparation method applied to drag pump car Download PDFInfo
- Publication number
- CN107880766A CN107880766A CN201711194918.4A CN201711194918A CN107880766A CN 107880766 A CN107880766 A CN 107880766A CN 201711194918 A CN201711194918 A CN 201711194918A CN 107880766 A CN107880766 A CN 107880766A
- Authority
- CN
- China
- Prior art keywords
- parts
- finish paint
- based finish
- agent
- component water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of single-component water-based finish paint and preparation method applied to drag pump car.The component of single-component water-based finish paint includes according to composition by weight：5 15 parts of 30 50 parts of Acrylate Modified Aqueous Polyurethane, 10 15 parts of deionized water, 0.1 2 parts of coalescents, 0.1 2 parts of rheological agent, 13 parts of thickener, 2 10 parts of wearability filler, 0.5 1.5 parts of aqueous dispersion, 0.1 1 parts of defoamer, 0.2 2 parts of mould inhibitor, 0.1 1 parts of surfactant, 0.2 1.5 parts of anti-flash rusting agent, 0.1 0.5 parts of pH adjusting agent and pigment.The single-component water-based finish paint prepared by mentioned reagent has the advantages that higher wearability, water resistance and weatherability, and it is sprayed on the anti-corruption that drag pump car can be significantly improved when on drag pump car, water resistance, alkali resistance, and then cause the vehicle body of drag pump car is not perishable to degenerate, extend the service life of drag pump car.
Description
Technical field
The present invention relates to technical field of coatings, more particularly to a kind of single-component water-based finish paint and preparation applied to drag pump car
Method.
Background technology
Drag pump car is also known as concrete ground pump, is a kind of construction equipment that pressure delivering concrete is relied on by pipeline.Drag pump
Car in use, ready-mixed concrete production is combined with pumping construction, using concrete mixing and transporting car carry out among operating,
So as to realize the uninterrupted pumping of concrete and pour.
Drag pump car can all coat coast of paint material when manufacturing inside and outside vehicle body.The brushing of paint vehicle enables to drag pump
Car has preferable outward appearance, and then is easy to distinguish the purposes of a variety of drag pump cars.In addition, the brushing of paint vehicle can also be to drag pump car
Vehicle body play a protective role, to extend the service life of drag pump car.The brushing of paint vehicle is generally divided into layered coating, wherein, bottom
The first layer for paint vehicle is painted, is in contact with the vehicle body of metal material；And finish paint is one layer of painting of last application in multiple coating
Material, it is in contact with water, rubbish and dust etc..The brushing of priming paint can improve the adhesive force of finish paint, increase the richness of finish paint
Deng.Due to last coating that finish paint is application, then finish paint just shows the whole structure after finishing, thus finish paint will
Ask with good colourity and brightness.Further, since finish paint and water, rubbish and dust etc. are in contact, thus should also have very
Good anti-pollution, ageing-resistant, the characteristic such as moistureproof, mould proof, alkali resistant, anti-corruption.
Finish paint species is various, generallys include polyester furniture finish paint, prevents outside line finish paint, polyester-urethane resin finish paint, gathers
Urethane plastics finish paint, acrylic acid top-coat and Lacquer finish enamel paint etc..In the finish paint applied to drag pump car, the bright degree of finish paint
And adhesive force is preferable, but the anti-poor-performing such as rotten, water-fast, alkaline-resisting so that easily corrosion degenerates the vehicle body of drag pump car, enters
And influence the service life of drag pump car.
The content of the invention
The present invention provides a kind of single-component water-based finish paint and preparation method applied to drag pump car, to solve existing be applied to
The problem of finish paint of drag pump car anti-poor-performing such as rotten, water-fast, alkaline-resisting.
The present invention provides a kind of single-component water-based finish paint applied to drag pump car, the component of the single-component water-based finish paint according to
Composition by weight includes：
Acrylate Modified Aqueous Polyurethane 30-50 parts, deionized water 10-15 parts, coalescents 0.1-2 parts, rheological agent
It is 0.1-2 parts, thickener 1-3 parts, wearability filler 2-10 parts, aqueous dispersion 0.5-1.5 parts, defoamer 0.1-1 parts, mould proof
Agent 0.2-2 parts, surfactant 0.1-1 parts, anti-flash rusting agent 0.2-1.5 parts, pH adjusting agent 0.1-0.5 parts and pigment 5-15
Part.
Specifically, aqueous polyurethane (English full name：Water Polyurethane) it is referred to as water-based PU.Water-based PU has
Good physical and mechanical properties, excellent cold resistance, alkali resistance, elasticity and soft durometer varies with temperature the advantages that little, however,
Its resistance to elevated temperatures is bad, poor water resistance.Acrylic acid ester emulsion (English full name：polyacrylate；English abbreviation：PA) have
Have good water resistance, weatherability, hardness big and not solvent resistant the characteristics of.Propylene is enabled to by PA modified water-solubles PU
Sour modified aqueous polyurethane has the advantages that high-wearing feature, good mechanical performance, water resistance and weatherability, and then has
More preferable using effect.
The preparation technology of Acrylate Modified Aqueous Polyurethane is：By polyether Glycols under the conditions of vacuum, temperature are 120 DEG C
It is standby to be dehydrated 24h.80 DEG C will be slowly ramped into good polyether Glycols, disposably add IPDI
And catalyst, react 2h after being warming up to 100 DEG C.After reaction terminates, 60 DEG C are cooled to, and add dihydromethyl propionic acid and N- first
Base pyrrole network alkanone, reacts 6h after being slowly ramped to 85 DEG C.Acetone is continuously added in course of reaction, to reduce the viscosity of reactant.
When nco value reaches theoretical value in system, performed polymer is transferred in high velocity dispersators, is scattered under high velocity agitation molten
In the distilled water for having chain extender and nertralizer, self-emulsifying polyether type aqueous polyurethane is obtained.In load weighted self-emulsifying polyether-type
PH adjusting agent is added in aqueous polyurethane, is warming up to dropwise addition has emulsified after 80 DEG C mix monomer and initiator, rate of addition control
System drips off in 2-3h.Acrylate Modified Aqueous Polyurethane is obtained after 80 DEG C of insulation 3h.
Coalescents are also known as coalescing aid, can promote high-molecular compound Plastic Flow and elastic deformation, and then improve
Performance is coalesced, helps film forming.In embodiments of the present invention, coalescents include ethylene glycol monobutyl ether, Lauryl Alcohol ester and the third two
At least one of alcohol butyl ether.
Rheological agent can adjust the mobility of paint, reduce the drippage occurred during roller coat or brushing and splashing, and
The viscosity increase of paint, so as to improve sag resistance.In addition, during coating transports or stores, rheological agent can be when value face
Material sedimentation, it is ensured that the uniformity and durability of final products.In embodiments of the present invention, rheological agent includes cellulose, propylene
At least one of sour, special clay and hydrophobically modified polyethers.
Thickener can improve the viscosity of single-component water-based finish paint, and then increase single-component water-based finish paint and priming paint or drag
The adhesion strength of pump truck.In embodiments of the present invention, thickener includes diatomite, Silica hydrogel, cellulose ether, natural polymer
At least one of with modified natural polymer.
Wearability filler can improve the wearability of single-component water-based finish paint, when extending the use of single-component water-based finish paint
Between.In embodiments of the present invention, wearability filler includes at least one in polytetrafluoroethylene (PTFE), graphite, polysiloxanes and carbon fiber
Kind.
Aqueous dispersion has a relatively low surface tension, and can be quickly wetting pigment, and then disperse aqueous polyurethane
Other compositions in coating.In embodiments of the present invention, aqueous dispersion includes polycarboxylate sodium or ammonium polyacrylate salt.
Defoamer suppresses foam and produces or eliminate caused foam to reduce surface tension.In embodiments of the present invention,
Defoamer includes polyethers defoamer or polyether-modified silicon.Such as GPE types defoamer, GPES type defoamers.
Mould inhibitor refers to there is killing or inhibiting effect to mould, and the preparation for preventing application from going mouldy.In the present invention
In embodiment, mould inhibitor includes at least one of quaternary ammonium salt derivative, sodium fluoride and organic tin salt.
The surface of surfactant has fixed hydrophilic lipophilic group, can be aligned on the surface of solution, thus
The addition of surfactant enables to the interface of single-component water-based finish paint that obvious change occurs, and then causes one-component water
Property finish paint has hydrophilicity.In embodiments of the present invention, surfactant includes sodium n-alkylbenzenesulfonate, laruyl alcohol sulphur
Sour sodium, glycerol stearate monoesters etc..
Anti- flash rusting agent can prevent the surface of ferrous metal ground that cathodization reaction occurs.In addition, anti-flash rusting agent can also
Iron ion is prevented, and then avoids iron by the dioxygen oxidation in air, and then prevents drag pump car from flash rusting occur.Of the invention real
Apply in example, it is a variety of that anti-flash rusting agent includes CH 07A, FSX-J150 or SER-AD FA179 etc..
PH adjusting agent can adjust the pH value of single-component water-based finish paint, and then cause single-component water-based finish paint to avoid producing sudden strain of a muscle
Rust problem.In embodiments of the present invention, pH adjusting agent includes dimethylethanolamine, ammoniacal liquor etc..
Pigment enables to drag pump car to have different colors, in order to distinguish different application environments, thus pigment
Using can be set according to practical application.
More preferable, the component of finish paint includes according to composition by weight：45 parts of Acrylate Modified Aqueous Polyurethane, deionization
15 parts of water, 1.5 parts of coalescents, 1.5 parts of rheological agent, 3 parts of thickener, 6 parts of wearability filler, 1.5 parts of aqueous dispersion, disappear
15 parts of 1 part of infusion, 1 part of mould inhibitor, 0.5 part of surfactant, 1.5 parts of anti-flash rusting agent, 0.3 part of pH adjusting agent and pigment.
The present invention also provides a kind of preparation method of the single-component water-based finish paint applied to drag pump car, and methods described includes：
Deionized water is slowly added to wearability filler, aqueous dispersion, defoamer, mould proof successively in the state of stirring
Agent, preservative, surfactant, anti-flash rusting agent and pigment, and 20-30 points are stirred under 200-250 revs/min of rotating speed
Clock；
After the completion of stirring, mixing speed is brought up to 500-600 revs/min, and be slowly added to acrylic acid modified water successively
Property polyurethane, coalescents, rheological agent and thickener, stir 60-80 minutes after obtain single-component water-based finish paint.
The technical scheme that embodiments of the invention provide can include the following benefits：
The present invention provides a kind of single-component water-based finish paint and preparation method applied to drag pump car.Wherein, it is single-component water-based
Finish paint includes according to composition by weight：Acrylate Modified Aqueous Polyurethane 30-50 parts, deionized water 10-15 parts, coalescents
0.1-2 parts, rheological agent 0.1-2 parts, thickener 1-3 parts, wearability filler 2-10 parts, aqueous dispersion 0.5-1.5 parts, defoaming
Agent 0.1-1 parts, mould inhibitor 0.2-2 parts, surfactant 0.1-1 parts, anti-flash rusting agent 0.2-1.5 parts, pH adjusting agent 0.1-0.5
Part and pigment 5-15 parts.By mentioned reagent prepare single-component water-based finish paint have higher wearability, water resistance and
The advantages that weatherability, and the anti-corruption that drag pump car can be significantly improved when on drag pump car, water resistance, alkali resistance are sprayed on, and then
Degenerated so that the vehicle body of drag pump car is not perishable, extend the service life of drag pump car.
It should be appreciated that the general description and following detailed description of the above are only exemplary and explanatory, not
Can the limitation present invention.
Embodiment
Embodiment 1
The embodiment of the present invention provides a kind of single-component water-based finish paint applied to drag pump car, the group of the single-component water-based finish paint
Part includes according to weight fraction：
50 parts of Acrylate Modified Aqueous Polyurethane, 15 parts of deionized water, 2 parts of coalescents, 2 parts of rheological agent, thickener 1
Part, 10 parts of wearability filler, 0.5 part of aqueous dispersion, 0.1 part of defoamer, 0.2 part of mould inhibitor, 1 part of surfactant, anti-sudden strain of a muscle
Become rusty 15 parts of 0.2 part of agent, 0.5 part of pH adjusting agent and pigment.Wherein, coalescents use ethylene glycol monobutyl ether, and rheological agent uses
Cellulose, thickener use diatomite, and wearability filler uses carbon fiber, and aqueous dispersion uses polycarboxylate sodium, defoamer
Using polyether-modified silicon, mould inhibitor uses quaternary ammonium salt derivative, and surfactant uses sldium lauryl sulfate, and anti-flash rusting agent is adopted
With anti-flash rusting agent CH 07A, pH adjusting agent uses dimethylethanolamine.
The embodiment of the present invention also provides a kind of preparation method of the single-component water-based finish paint applied to drag pump car, this method master
Including：
Deionized water is slowly added to wearability filler, aqueous dispersion, defoamer, mould proof successively in the state of stirring
Agent, preservative, surfactant, anti-flash rusting agent and pigment, and 20-30 points are stirred under 200-250 revs/min of rotating speed
Clock；
After the completion of stirring, mixing speed is brought up to 500-600 revs/min, and be slowly added to acrylic acid modified water successively
Property polyurethane, coalescents, rheological agent and thickener, stir 60-80 minutes after obtain single-component water-based finish paint.
Embodiment 2
The embodiment of the present invention provides a kind of single-component water-based finish paint applied to drag pump car, the group of the single-component water-based finish paint
Part includes according to weight fraction：
30 parts of Acrylate Modified Aqueous Polyurethane, 10 parts of deionized water, 0.1 part of coalescents, 0.1 part of rheological agent, thickening
3 parts of agent, 2 parts of wearability filler, 1.5 parts of aqueous dispersion, 1 part of defoamer, 2 parts of mould inhibitor, 0.1 part of surfactant, anti-sudden strain of a muscle
Become rusty 5 parts of 0.2 part of agent, 0.1 part of pH adjusting agent and pigment.Wherein, coalescents use Lauryl Alcohol ester, and rheological agent uses third
Olefin(e) acid, thickener use Silica hydrogel, and wearability filler uses polysiloxanes, and aqueous dispersion uses ammonium polyacrylate salt, defoaming
Agent uses polyether-modified silicon, and mould inhibitor uses sodium fluoride, and surfactant uses glycerol stearate monoesters, and anti-flash rusting agent uses
Anti- flash rusting agent FSX-J150, pH adjusting agent use dimethylethanolamine.
The embodiment of the present invention also provides a kind of preparation method of the single-component water-based finish paint applied to drag pump car, and this method is same
The step of embodiment, is identical, is only coalescents, rheological agent, thickener, wearability filler, aqueous dispersion, defoamer, anti-
Mould dose, surfactant, anti-flash rusting agent, the species of pH adjusting agent and pigment it is different.
Embodiment 3
The embodiment of the present invention provides a kind of single-component water-based finish paint applied to drag pump car, the group of the single-component water-based finish paint
Part includes according to weight fraction：
45 parts of Acrylate Modified Aqueous Polyurethane, 15 parts of deionized water, 1.5 parts of coalescents, 1.5 parts of rheological agent, thickening
3 parts of agent, 6 parts of wearability filler, 1.5 parts of aqueous dispersion, 1 part of defoamer, 1 part of mould inhibitor, 0.5 part of surfactant, anti-sudden strain of a muscle
Become rusty 15 parts of 1.5 parts of agent, 0.3 part of pH adjusting agent and pigment.Wherein, coalescents use propandiol butyl ether, and rheological agent is using special
Clay processed, thickener use cellulose ether, and wearability filler uses graphite, and aqueous dispersion uses ammonium polyacrylate salt, defoaming
Agent uses polyethers defoamer, and mould inhibitor uses organic tin salt, and surfactant uses sldium lauryl sulfate, and anti-flash rusting agent is adopted
With anti-flash rusting agent SER-AD FA179, pH adjusting agent uses ammoniacal liquor.
The embodiment of the present invention also provides a kind of preparation method of the single-component water-based finish paint applied to drag pump car, and this method is same
The step of embodiment, is identical, is only coalescents, rheological agent, thickener, wearability filler, aqueous dispersion, defoamer, anti-
Mould dose, surfactant, anti-flash rusting agent, the species of pH adjusting agent and pigment it is different.
Embodiment 4
The embodiment of the present invention provides a kind of single-component water-based finish paint applied to drag pump car, the group of the single-component water-based finish paint
Part includes according to weight fraction：
40 parts of Acrylate Modified Aqueous Polyurethane, 12 parts of deionized water, 0.8 part of coalescents, 1.1 parts of rheological agent, thickening
1.5 parts of agent, 7 parts of wearability filler, 1 part of aqueous dispersion, 0.8 part of defoamer, 1.2 parts of mould inhibitor, 0.7 part of surfactant,
10 parts of anti-1.1 parts of flash rusting agent, 0.2 part of pH adjusting agent and pigment.Wherein, coalescents are using ethylene glycol monobutyl ether and the third two
Alcohol butyl ether, rheological agent use hydrophobically modified polyethers, and thickener uses natural polymer and modified natural polymer, wearability
Filler uses polytetrafluoroethylene (PTFE), and aqueous dispersion uses polycarboxylate sodium, and defoamer uses polyethers defoamer, and mould inhibitor is adopted
With sodium fluoride and organic tin salt, surfactant uses sodium n-alkylbenzenesulfonate, and anti-flash rusting agent uses anti-flash rusting agent FSX-
J150, pH adjusting agent use dimethylethanolamine.
The embodiment of the present invention also provides a kind of preparation method of the single-component water-based finish paint applied to drag pump car, and this method is same
The step of embodiment, is identical, is only coalescents, rheological agent, thickener, wearability filler, aqueous dispersion, defoamer, anti-
Mould dose, surfactant, anti-flash rusting agent, the species of pH adjusting agent and pigment it is different.
Imitated to verify that single-component water-based finish paint provided in an embodiment of the present invention is applied in drag pump car with preferably application
Fruit, the single-component water-based finish paint that the embodiment of the present invention 3 is provided and the like product progress performance inspection for applying equally to drag pump car
Contrast is surveyed, wherein, testing result is as shown in table 1.
Table 1：Test result
As shown in Table 1, single-component water-based finish paint provided in an embodiment of the present invention compared with similar products, the embodiment of the present invention
Wearability, scratch resistance, water resistance, alkali resistance and the alcohol resistance of the single-component water-based finish paint provided are better than like product.
Thus, when single-component water-based finish paint is applied to drag pump car, the wearability of drag pump car, scratch resistance, water-fast can be significantly improved
Property, alkali resistance and alcohol resistance, and then extend the service life of drag pump car.
Those skilled in the art will readily occur to the present invention its after considering specification and putting into practice the disclosure invented here
Its embodiment.The application be intended to the present invention any modification, purposes or adaptations, these modifications, purposes or
Person's adaptations follow the general principle of the present invention and including undocumented common knowledges in the art of the invention
Or conventional techniques.Description and embodiments are considered only as exemplary, and true scope and spirit of the invention are by following
Claim is pointed out.
It should be appreciated that the relational terms of such as " first " and " second " or the like be used merely to an entity or
Operation makes a distinction with another entity or operation, and not necessarily requires or imply to exist between these entities or operation and appoint
What this actual relation or order.The invention is not limited in the precision architecture being described above, and can be not
Depart from its scope and carry out various modifications and changes.The scope of the present invention is only limited by appended claim.
Claims (10)
1. a kind of single-component water-based finish paint applied to drag pump car, it is characterised in that the component of the finish paint is according to composition by weight
Including：
Acrylate Modified Aqueous Polyurethane 30-50 parts, deionized water 10-15 parts, coalescents 0.1-2 parts, rheological agent 0.1-2
Part, thickener 1-3 parts, wearability filler 2-10 parts, aqueous dispersion 0.5-1.5 parts, defoamer 0.1-1 parts, mould inhibitor 0.2-2
Part, surfactant 0.1-1 parts, anti-flash rusting agent 0.2-1.5 parts, pH adjusting agent 0.1-0.5 parts and pigment 5-15 parts.
2. single-component water-based finish paint according to claim 1, it is characterised in that the component of the finish paint is according to composition by weight
Including：
45 parts of Acrylate Modified Aqueous Polyurethane, 15 parts of deionized water, 1.5 parts of coalescents, 1.5 parts of rheological agent, thickener 3
Part, 6 parts of wearability filler, 1.5 parts of aqueous dispersion, 1 part of defoamer, 1 part of mould inhibitor, 0.5 part of surfactant, anti-flash rusting agent
15 parts of 1.5 parts, 0.3 part of pH adjusting agent and pigment.
3. single-component water-based finish paint according to claim 1 or 2, it is characterised in that the coalescents include ethylene glycol
At least one of monobutyl ether, Lauryl Alcohol ester and propandiol butyl ether.
4. single-component water-based finish paint according to claim 1 or 2, it is characterised in that the wearability filler includes poly- four
At least one of PVF, graphite, polysiloxanes and carbon fiber.
5. single-component water-based finish paint according to claim 1 or 2, it is characterised in that the rheological agent includes cellulose, third
At least one of olefin(e) acid, special clay and hydrophobically modified polyethers.
6. single-component water-based finish paint according to claim 1 or 2, it is characterised in that the aqueous dispersion includes poly- carboxylic
Acid sodium-salt or ammonium polyacrylate salt.
7. single-component water-based finish paint according to claim 1 or 2, it is characterised in that the mould inhibitor spreads out including quaternary ammonium salt
At least one of biology, sodium fluoride and organic tin salt.
8. single-component water-based finish paint according to claim 1 or 2, it is characterised in that the defoamer disappears including polyethers
Infusion or polyether-modified silicon.
9. single-component water-based finish paint according to claim 1 or 2, it is characterised in that the thickener includes diatomite, silicon
At least one of gel, cellulose ether, natural polymer and modified natural polymer.
10. the preparation method of a kind of single-component water-based finish paint applied to drag pump car, it is characterised in that methods described includes：
Deionized water is slowly added to wearability filler, aqueous dispersion, defoamer, mould inhibitor, anti-successively in the state of stirring
Rotten agent, surfactant, anti-flash rusting agent and pigment, and 20-30 minutes are stirred under 200-250 revs/min of rotating speed；
After the completion of stirring, mixing speed is brought up to 500-600 revs/min, and is slowly added to acrylic modified waterborne successively and gathers
Urethane, coalescents, rheological agent and thickener, single-component water-based finish paint is obtained after stirring 60-80 minutes.