CN109014021A - 一种树脂砂型铸造用耐高温涂料 - Google Patents
一种树脂砂型铸造用耐高温涂料 Download PDFInfo
- Publication number
- CN109014021A CN109014021A CN201810841982.5A CN201810841982A CN109014021A CN 109014021 A CN109014021 A CN 109014021A CN 201810841982 A CN201810841982 A CN 201810841982A CN 109014021 A CN109014021 A CN 109014021A
- Authority
- CN
- China
- Prior art keywords
- parts
- sand mould
- bonded sand
- temperature resistant
- resin bonded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种树脂砂型铸造用耐高温涂料，其按照以下原料的重量份数组成：水溶性环氧树脂32‑53份、聚酯多元醇2‑5份、二乙醇胺7‑10份、甲苯8‑11份、聚丙烯酰胺0.3‑1份、苯磺酸钠6‑10份、氧化铝2‑8份、纳米二氧化钛1‑4份、硅胶3‑7份、小苏打5‑8份、石蜡12‑19份、蓝晶石粉3‑7份、煅烧钾长石1‑5份、漆黄素0.5‑2份、鱼油3‑10份、高岭土2‑6份、去离子水26‑47份。本发明的用于树脂砂型铸造的涂料配方组分合理，涂料粘结优良，易涂刷，抗高温，冷却后，浇铸时防止了粘砂、夹砂等缺陷，表面光洁度高。
Description
技术领域
本发明涉及铸件涂料技术领域，尤其涉及一种树脂砂型铸造用耐高温涂料。
背景技术
目前，传统树脂砂作为砂型在铸件和铸型中间起到阻挡隔离作用，达到防粘砂目的。在浇铸过程中，由于附着力差、强度低、耐火差、发气量大等原因，在沙粒之间起固化用的树脂被烧灼分解，砂粒之间的连接被破坏，高温金属液就会渗透到砂型中，造成粘砂。同时烧灼分解后形成大量气体，留着铸件表面形成气孔缺陷，容易造成铸件产生粘砂，砂眼，气孔、碳渣等缺陷。然而，目前树脂砂涂料普遍具有悬浮性低，使用时经常搅拌否则难以涂刷均匀，涂刷后，烘干过程中，涂层也容易脱落，造成铸件粘砂，铸件表面质量差。
发明内容
本发明的目的就在于为了解决上述问题而提供一种树脂砂型铸造用耐高温涂料。
为了实现上述目的，本发明是通过以下技术方案实现的：一种树脂砂型铸造用耐高温涂料，按照以下原料的重量份数组成：水溶性环氧树脂32-53份、聚酯多元醇2-5份、二乙醇胺7-10份、甲苯8-11份、聚丙烯酰胺0.3-1份、苯磺酸钠6-10份、氧化铝2-8份、纳米二氧化钛1-4份、硅胶3-7份、小苏打5-8份、石蜡12-19份、蓝晶石粉3-7份、煅烧钾长石1-5份、漆黄素0.5-2份、鱼油3-10份、高岭土2-6份、去离子水26-47份。
上述的一种树脂砂型铸造用耐高温涂料，按照以下原料的重量份数组成：水溶性环氧树脂32-50份、聚酯多元醇2-4份、二乙醇胺7-9份、甲苯8-10份、聚丙烯酰胺0.3-0.7份、苯磺酸钠6-8份、氧化铝2-6份、纳米二氧化钛1-3份、硅胶3-5份、小苏打5-7份、石蜡12-17份、蓝晶石粉3-6份、煅烧钾长石1-4份、漆黄素0.5-1.5份、鱼油3-8份、高岭土2-5份、去离子水26-42份。
上述的一种树脂砂型铸造用耐高温涂料，按照以下原料的重量份数组成：水溶性环氧树脂44份、聚酯多元醇3份、二乙醇胺8份、甲苯9份、聚丙烯酰胺0.5份、苯磺酸钠7份、氧化铝4份、纳米二氧化钛2份、硅胶4份、小苏打6份、石蜡14份、蓝晶石粉5份、煅烧钾长石3份、漆黄素1份、鱼油5份、高岭土4份、去离子水36份。
综上所述本发明具有以下有益效果：本发明的用于树脂砂型铸造的涂料配方组分合理，涂料粘结优良，易涂刷，抗高温，冷却后，浇铸时防止了粘砂、夹砂等缺陷，表面光洁度高。
具体实施方式
具体实施例1：
一种树脂砂型铸造用耐高温涂料，其按照以下原料的重量份数组成：水溶性环氧树脂50份、聚酯多元醇4份、二乙醇胺9份、甲苯10份、聚丙烯酰胺0.7份、苯磺酸钠8份、氧化铝6份、纳米二氧化钛3份、硅胶5份、小苏打7份、石蜡17份、蓝晶石粉6份、煅烧钾长石4份、漆黄素1.5份、鱼油8份、高岭土5份、去离子水42份。
具体实施例2：
一种树脂砂型铸造用耐高温涂料，其按照以下原料的重量份数组成：水溶性环氧树脂44份、聚酯多元醇3份、二乙醇胺8份、甲苯9份、聚丙烯酰胺0.5份、苯磺酸钠7份、氧化铝4份、纳米二氧化钛2份、硅胶4份、小苏打6份、石蜡14份、蓝晶石粉5份、煅烧钾长石3份、漆黄素1份、鱼油5份、高岭土4份、去离子水36份。
具体实施例3：
一种树脂砂型铸造用耐高温涂料，其按照以下原料的重量份数组成：水溶性环氧树脂32份、聚酯多元醇2份、二乙醇胺7份、甲苯8份、聚丙烯酰胺0.3份、苯磺酸钠6份、氧化铝3份、纳米二氧化钛1份、硅胶3份、小苏打5份、石蜡12份、蓝晶石粉3份、煅烧钾长石1份、漆黄素0.5份、鱼油3份、高岭土2份、去离子水26份。
以上所举实施例为本发明的较佳实施方式，仅用来方便说明本发明，并非对本发明作任何形式上的限制，任何所属技术领域中具有通常知识者，若在不脱离本发明所提技术特征的范围内，利用本发明所揭示技术内容所作出局部更动或修饰的等效实施例，并且未脱离本发明的技术特征内容，均仍属于本发明技术特征的范围内。
Claims (3)
1.一种树脂砂型铸造用耐高温涂料，其特征在于，按照以下原料的重量份数组成：水溶性环氧树脂32-53份、聚酯多元醇2-5份、二乙醇胺7-10份、甲苯8-11份、聚丙烯酰胺0.3-1份、苯磺酸钠6-10份、氧化铝2-8份、纳米二氧化钛1-4份、硅胶3-7份、小苏打5-8份、石蜡12-19份、蓝晶石粉3-7份、煅烧钾长石1-5份、漆黄素0.5-2份、鱼油3-10份、高岭土2-6份、去离子水26-47份。
2.根据权利要求1所述的一种树脂砂型铸造用耐高温涂料，其特征在于，按照以下原料的重量份数组成：水溶性环氧树脂32-50份、聚酯多元醇2-4份、二乙醇胺7-9份、甲苯8-10份、聚丙烯酰胺0.3-0.7份、苯磺酸钠6-8份、氧化铝2-6份、纳米二氧化钛1-3份、硅胶3-5份、小苏打5-7份、石蜡12-17份、蓝晶石粉3-6份、煅烧钾长石1-4份、漆黄素0.5-1.5份、鱼油3-8份、高岭土2-5份、去离子水26-42份。
3.根据权利要求1所述的一种树脂砂型铸造用耐高温涂料，其特征在于，按照以下原料的重量份数组成：水溶性环氧树脂44份、聚酯多元醇3份、二乙醇胺8份、甲苯9份、聚丙烯酰胺0.5份、苯磺酸钠7份、氧化铝4份、纳米二氧化钛2份、硅胶4份、小苏打6份、石蜡14份、蓝晶石粉5份、煅烧钾长石3份、漆黄素1份、鱼油5份、高岭土4份、去离子水36份。