CN109012230A - 一种带衬中空纤维膜 - Google Patents
一种带衬中空纤维膜 Download PDFInfo
- Publication number
- CN109012230A CN109012230A CN201811030714.1A CN201811030714A CN109012230A CN 109012230 A CN109012230 A CN 109012230A CN 201811030714 A CN201811030714 A CN 201811030714A CN 109012230 A CN109012230 A CN 109012230A
- Authority
- CN
- China
- Prior art keywords
- fibre membrane
- parts
- solvent
- hollow
- belt material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种带衬中空纤维膜,由包括以下重量份的组分制成:10‑30份的溶剂材料、30‑50份的非溶剂材料和40‑60份的聚偏氟乙烯。本发明设计合理,节约成本,使膜的表层与内衬管的结合强度大幅提升,同时能提高中空纤维过滤膜的内压破坏水压将改善过滤膜的整体性能和使用寿命,从而降低污水处理企业的使用成本,是一种理想的过滤材料。
Description
技术领域
本发明属于中空纤维膜领域,更具体地说,涉及一种带衬中空纤维膜。
背景技术
随着我国经济的不断发展,水资源的消耗和污染问题日益突出。我国水资源分布不均,北方水资源比较缺乏,除鼓励节约用水外,也应该对水资源进行回收再利用,提高水资源的利用效率。在水污染防治方面,由于多年的工业化进程中对环境水体保护的不够,目前国水体污染相当严重,数据显示我国河流长度有70%左右被污染,污染源主要来自工业生产排放的污水以及各种生活污水。
在水污染防治以及水资源的回收再利用方面,和传统AO法相比,膜生物反应器(MBR)是一种高效的水资源回用与污水处理的方法。膜生物反应器中的核心原件为污水处理用过滤膜,主要包括帘式膜、平板膜、管式膜、卷式膜等。其中帘式膜主要采用中空纤维过滤膜作为过滤材料。
鉴于此,制备一种带衬中空纤维膜,使膜的表层与内衬管的结合强度大幅提升,同时能提高中空纤维过滤膜的内压破坏水压将改善过滤膜的整体性能和使用寿命,从而降低污水处理企业的使用成本。
发明内容
针对现有技术存在的不足,本发明的目的在于提供了一种带衬中空纤维膜,设计合理,节约成本,使膜的表层与内衬管的结合强度大幅提升,同时能提高中空纤维过滤膜的内压破坏水压将改善过滤膜的整体性能和使用寿命,从而降低污水处理企业的使用成本,是一种理想的过滤材料。
为实现上述目的,本发明提供了如下技术方案:
一种带衬中空纤维膜,其特征在于:由包括以下重量份的组分制成:10-30份的溶剂材料、30-50份的非溶剂材料和40-60份的聚偏氟乙烯。
作为一种优化的技术方案,所述溶剂材料包括二甲基乙酰胺或者甲基二吡烷酮或者二甲基甲酰胺或者三醋酸甘油酯或者二乙酸甘油酯或者碳酸丙烯酸中的其中几种或者一种。
作为一种优化的技术方案,所述非溶剂材料包括甘油或者聚乙二醇或者四乙二醇或者二甘醇的其中几种或者一种。
作为一种优化的技术方案,所述带衬中空纤维膜还包括1-2份的氯化锂。
作为一种优化的技术方案,所述带衬中空纤维膜还包括1-2份的偶联剂。
本发明中还提供了一种带衬中空纤维膜的制备方法,其特征在于:步骤如下:
1)、按重量份配制聚偏氟乙烯、氯化锂、偶联剂、溶剂和非溶剂;
2)、混合溶剂和非溶剂,加入反应釜中,加热搅拌均匀,再加入氯化锂和偶联剂,真空脱泡后制得过滤层原料;
3)、将过滤层原料注入模具中,从模具的上侧穿进模具,从下侧拉出模具,制得;
4)、将半成品的中空纤维膜加入到涂覆设备上进行涂覆,冷却定型,经过收卷装置收卷得到带衬中空纤维膜。
由于采用了上述技术方案,与现有技术相比,本发明设计合理,节约成本,使膜的表层与内衬管的结合强度大幅提升,同时能提高中空纤维过滤膜的内压破坏水压将改善过滤膜的整体性能和使用寿命,从而降低污水处理企业的使用成本,是一种理想的过滤材料。
具体实施方式
实施例
一种带衬中空纤维膜,由包括以下重量份的组分制成:10-30份的溶剂材料、30-50份的非溶剂材料和40-60份的聚偏氟乙烯。所述溶剂材料包括二甲基乙酰胺或者甲基二吡烷酮或者二甲基甲酰胺或者三醋酸甘油酯或者二乙酸甘油酯或者碳酸丙烯酸中的其中几种或者一种。所述非溶剂材料包括甘油或者聚乙二醇或者四乙二醇或者二甘醇的其中几种或者一种。所述带衬中空纤维膜还包括1-2份的氯化锂。所述带衬中空纤维膜还包括1-2份的偶联剂。
一种带衬中空纤维膜的制备方法,其特征在于:步骤如下:
1)、按重量份配制聚偏氟乙烯、氯化锂、偶联剂、溶剂和非溶剂;
2)、混合溶剂和非溶剂,加入反应釜中,加热搅拌均匀,再加入氯化锂和偶联剂,真空脱泡后制得过滤层原料;
3)、将过滤层原料注入模具中,从模具的上侧穿进模具,从下侧拉出模具,制得;
4)、将半成品的中空纤维膜加入到涂覆设备上进行涂覆,冷却定型,经过收卷装置收卷得到带衬中空纤维膜。
本发明设计合理,节约成本,使膜的表层与内衬管的结合强度大幅提升,同时能提高中空纤维过滤膜的内压破坏水压将改善过滤膜的整体性能和使用寿命,从而降低污水处理企业的使用成本,是一种理想的过滤材料。
本发明的保护范围并不仅局限于上述实施例,凡属于本发明思路下的技术方案均属于本发明的保护范围。应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理前提下的若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (6)
1.一种带衬中空纤维膜,其特征在于:由包括以下重量份的组分制成:
10-30份的溶剂材料、30-50份的非溶剂材料和40-60份的聚偏氟乙烯。
2.根据权利要求1所述的一种带衬中空纤维膜,其特征在于:所述溶剂材料包括二甲基乙酰胺或者甲基二吡烷酮或者二甲基甲酰胺或者三醋酸甘油酯或者二乙酸甘油酯或者碳酸丙烯酸中的其中几种或者一种。
3.根据权利要求2所述的一种带衬中空纤维膜,其特征在于:所述非溶剂材料包括甘油或者聚乙二醇或者四乙二醇或者二甘醇的其中几种或者一种。
4.根据权利要求3所述的一种带衬中空纤维膜,其特征在于:所述带衬中空纤维膜还包括1-2份的氯化锂。
5.根据权利要求4所述的一种带衬中空纤维膜,其特征在于:所述带衬中空纤维膜还包括1-2份的偶联剂。
6.根据权利要求5所述的一种带衬中空纤维膜的制备方法,其特征在于:步骤如下:
1)、按重量份配制聚偏氟乙烯、氯化锂、偶联剂、溶剂和非溶剂;
2)、混合溶剂和非溶剂,加入反应釜中,加热搅拌均匀,再加入氯化锂和偶联剂,真空脱泡后制得过滤层原料;
3)、将过滤层原料注入模具中,从模具的上侧穿进模具,从下侧拉出模具,制得;
4)、将半成品的中空纤维膜加入到涂覆设备上进行涂覆,冷却定型,经过收卷装置收卷得到带衬中空纤维膜。