CN108997901A - It is a kind of paint and its preparation method and application - Google Patents
It is a kind of paint and its preparation method and application Download PDFInfo
- Publication number
- CN108997901A CN108997901A CN201810890452.XA CN201810890452A CN108997901A CN 108997901 A CN108997901 A CN 108997901A CN 201810890452 A CN201810890452 A CN 201810890452A CN 108997901 A CN108997901 A CN 108997901A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- resin
- weight
- preferred
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of paint and its preparation method and application, the paint comprises the following components in parts by weight: 45-53 parts of resin, 30-35 parts of pigment, 1-3 parts of auxiliary agent, 4-6 parts of dumb light powder, with 10-15 parts of solvent, wherein, the auxiliary agent includes levelling agent, defoaming agent and acid catalyst, the preparation method of the paint includes the production of (1) mill base and the addition of (2) acid catalyst, to obtain the paint, the paint its coating with high diffusing reflection function can be provided for Indoor decorative plate, improve the utilization rate of indoor natural light, while increasing decorative effect, reduce room light thermal losses.
Description
Technical field
The present invention relates to paint fields, especially with regard to a kind of paint and its preparation method and application.
Background technique
Paint is a kind of mixture for decorating and protecting article with organic or inorganic material.In terms of decoration functions,
The effects of anti-corrosion and waterproof, grease proofing, chemicals-resistant, fast light, heatproof can be played, since object is exposed among atmosphere, by oxygen
The erosion of gas and water point etc., causes the breakoff phenomenons such as corrosion of metal, foxiness, cement weathering, is coated with coating in object surface,
Layer protecting film is formed, can prevent or postpone the occurrence and development of these breakoff phenomenons, prolong the service life of a variety of materials
It is long.In terms of decoration functions: the object painting of unlike material is coated, and multicoloured, bright and colourful appearance can be obtained, play beautification
The effect of human habitat, material life and cultural life to the mankind, which are made, cannot be neglected contribution.
The paint for having diffusing reflection function at present is only limitted to small-sized place (such as: laboratory and manual spray room) production small-sized zero
Component (such as: A3 billboard, lamp shade) can not be applied to high-volume industrial production and heavy construction body decorative board；Meanwhile
Has the non-painting product of diffusing reflection function, there are obvious shortcomings in terms of high temperature resistant, color-change resistant, chemicals-resistant, especially
When it is used for indoor spaces, security risk is maximum insufficient.
The information disclosed in the background technology section is intended only to increase the understanding to general background of the invention, without answering
When being considered as recognizing or imply that the information constitutes the prior art already known to those of ordinary skill in the art in any form.
Summary of the invention
The purpose of the present invention is to provide a kind of paint and its preparation method and application, can provide for Indoor decorative plate
Coating with high diffusing reflection function, improves the utilization rate of indoor natural light, while increasing decorative effect, reduces room light
Thermal losses.
To achieve the above object, the present invention provides a kind of paint, which is comprised the following components in parts by weight: resin
45-53 parts, 30-35 parts of pigment, 1-3 parts of auxiliary agent, 4-6 parts of dumb light powder and 10-15 parts of solvent, wherein the auxiliary agent includes levelling
Agent, defoaming agent and acid catalyst；The resin play the role of function, film forming and auxiliary it is cured, the pigment play colour generation and
The effect of covering power is provided, the auxiliary agent plays the role of film-forming state adjustment, and the dumb light powder plays range adjustment,
The solvent plays the role of being easy to construct.
In a preferred embodiment, which comprises the following components in parts by weight: 49 parts of resin, 32 parts of pigment, helping
1.8 parts of agent, 5 parts of dumb light powder and 13 parts of solvent, wherein the auxiliary agent includes levelling agent, defoaming agent and acid catalyst.
In a preferred embodiment, the resin includes matrix resin and assisted resin, it is preferred that the main body tree
The mass ratio of rouge and assisted resin is (5-7): 1, it is further preferred that the mass ratio of the matrix resin and assisted resin is 6:
1, it is further preferred that the matrix resin is saturated polyester resin, the assisted resin is full Amino resin, the master
Body resin plays function and filming function, which plays auxiliary solidification.
In a preferred embodiment, the mass ratio of the levelling agent, defoaming agent and acid catalyst is followed successively by 1:1:1.
In a preferred embodiment, the pigment is white pigment powder, it is preferred that the pigment is titanium dioxide；Institute
Stating dumb light powder is fumed silica, and the solvent is 150# solvent.
In a preferred embodiment, total reflectivity of the paint at visible wavelength 550nm is 95-97%,
Preferably, total reflectivity of the paint at visible wavelength 550nm is 96%；The paint is in visible wavelength 550nm
The scattered reflection rate at place is 94-96%, it is preferred that the scattered reflection rate of the paint at visible wavelength 550nm be
95.5%；Positive reflection rate of the paint at visible wavelength 550nm is 0.4-0.6%, it is preferred that the paint is in visible
Positive reflection rate at optical wavelength 550nm is 0.5%.
The present invention also provides a kind of preparation methods of paint, comprising the following steps: (1) production of mill base: part is set
Rouge and solvent mix at normal temperature, with or without uniform stirring under pressure condition, while agitating, pigment are at the uniform velocity added, adds
Continue to stir after the completion of entering, mixing speed is set according to mixing quantity, cylinder body size, power of motor, it is ensured that in 1-2 hour
Between, reach the fineness of mixture in 20 microns；(2) addition of acid catalyst: add in the mill base prepared by step (1)
Enter remaining resin and solvent, and then levelling agent, defoaming agent and dumb light powder is added, quickly stirring 30 minutes or more, makes mixture
It is uniformly dispersed, sufficiently infiltrates, acid catalyst is then at the uniform velocity added, there are a large amount of foams to generate in a mixing bowl at this time, continue stirring extremely
The foam for floating on mixture surface can quickly vanish, and stop stirring, stand 2 hours, be filtered packaging to get above-mentioned oil
Paint.
In a preferred embodiment, the resin amount in step (1) is 18-22 parts by weight, it is preferred that step
(1) resin amount in is 20 parts by weight, and the resin amount in step (2) is 27-31 parts by weight, it is preferred that step (2)
In resin amount be 29 parts by weight, it is preferred that resin described in step (1) and step (2) include matrix resin with
Assisted resin, it is further preferred that the mass ratio of the matrix resin and assisted resin is (5-7): 1, it is further preferred that institute
The mass ratio for stating matrix resin and assisted resin is 6:1, it is further preferred that the matrix resin is saturated polyester resin, institute
Stating assisted resin is full Amino resin.
In a preferred embodiment, the solvent adding amount in step (1) is 4-7 parts by weight, it is preferred that step (1)
In solvent adding amount be 6 parts by weight, the solvent adding amount in step (2) is 6-8 parts by weight, it is preferred that molten in step (2)
Agent additional amount is 7 parts by weight, it is further preferred that solvent described in step (1) and step (2) is 150# solvent；Step (2)
The additional amount of middle dumb light powder is 4-6 parts by weight, it is preferred that the additional amount of dumb light powder is 5 parts by weight in step (2), further excellent
Choosing, the dumb light powder in step (2) is fumed silica；Levelling agent, defoaming agent and the total of acid catalyst add in step (2)
Entering amount is 1-3 parts by weight, it is preferred that total additional amount of levelling agent, defoaming agent and acid catalyst is 1.8 weight in step (2)
Part, it is further preferred that the mass ratio of the levelling agent, defoaming agent and acid catalyst is followed successively by 1:1:1.
The application that the present invention also provides the preparation methods of above-mentioned paint or above-mentioned paint on decorative panel.
Compared with prior art, the invention has the following beneficial effects:
(1) present invention is produced a kind of with height using the raw material with specific function using orderly operating procedure
The paint of diffusing reflection function, process is to grind, uniformly based on mixing, and each material component and content do not change, without new
Substance generates；
(2) present invention changes the curing system of conventional paint using acid catalyst, it is made to keep certain at room temperature
Stability is finally reached high irreflexive function once in hot setting, forming special film forming process；
(3) paint of the invention is most suitable for being applied to making to apply with a thickness of the coating material on 0.1mm-2.5mm steel and aluminium sheet
Laminate is while with high diffusing reflection rate, it may have excellent chemical resistance, moisture-resistant be hot, corrosion resistance and permanent steady
Qualitative and workability, is widely used in Indoor decorative plate, enables decorative panel: a. improves colour developing efficiency, muchly reduces light
It can be lost, reduce light source and use；B. point light source is become into area source, equalizing light rays eliminate dazzle or hot spot, reduce light pollution；
C. guarantee that good photochromic consistency is presented in finished product and moulding on the whole；D. surface strength is high, and scratch resistance is easy to construct；e.
Chemical resistance is excellent, and burn into is not non-discolouring for a long time, environmental；
(4) paint of the invention is used on the metal bases such as the higher steel of intensity, aluminium, is easy to be mass produced, coating
High-efficient, coated plate is able to maintain the flexibility of metal, easily processed into type, in addition to the diffusing reflection that itself has the function of, also has
There are excellent weatherability, chemical resistance, resistance to combustion, radiationless etc. to be conducive to the unique function of safety and environmental protection, is other non-paintings
Product is irreplaceable.
Detailed description of the invention
Fig. 1 is paint process flow chart according to an embodiment of the present invention；Wherein additive shown in figure includes helping
Agent and dumb light powder.
Fig. 2 is according to an embodiment of the present invention using the coating plate face diffusing reflection effect picture after present invention paint.
Specific embodiment
With reference to the accompanying drawing, specific embodiments of the present invention will be described in detail, it is to be understood that guarantor of the invention
Shield range is not limited by the specific implementation.
Unless otherwise explicitly stated, otherwise in entire disclosure and claims, term " includes " or its change
Changing such as "comprising" or " including " etc. will be understood to comprise stated element or component, and not exclude other members
Part or other component parts.
The manufacturer of saturated polyester resin involved in following embodiments is Royal DSM 8880, full Amino resin
Manufacturer be Zhejiang Aoshi Chemical Co., Ltd, model OS 303-98, titanium white production producer be Du Pont 960, gas phase
Silica manufacturer is Degussa R972, and the manufacturer of levelling agent is Germany Bi Ke, model BYK354, defoaming agent life
Production producer is Germany Bi Ke, model BYK052, and the manufacturer of acid catalyst is U.S. Jin Shi, model Nacure1051,
The manufacturer of 150# solvent is hundred specialization work goods and materials Co., Ltd of Jiangyin City, model S-150.
Paint of embodiment 1 and preparation method thereof
1, paint component (in parts by weight):
42 parts of saturated polyester resin, 7 parts of full Amino resin, 32 parts of titanium dioxide, 0.6 part of levelling agent, defoaming agent 0.6
Part, 0.6 part of acid catalyst, 5 parts of fumed silica, 13 parts of solvent.
2, the preparation method of above-mentioned paint is following (also can refer to Fig. 1):
(1) production of mill base: the 150# solvent of the resin of 20 parts by weight and 6 parts by weight is mixed at normal temperature, in no pressure
Pigment is at the uniform velocity added while agitating in uniform stirring under the conditions of power, continues to stir after the completion of being added, between 1-2 hours,
Reach the fineness of mixture in 20 microns；
(2) resin of remaining 29 parts by weight the addition of acid catalyst: is added in the mill base prepared by step (1)
With the 150# solvent of 7 parts by weight, and then be added 0.6 parts by weight of levelling agent, 5 parts by weight of 0.6 parts by weight of defoaming agent and dumb light powder, fastly
Speed stirring 30 minutes or more, so that mixture is uniformly dispersed, sufficiently infiltrated, 0.6 parts by weight of acid catalyst are then at the uniform velocity added, at this time
There are a large amount of foams to generate in a mixing bowl, continuing stirring to the foam for floating on mixture surface can quickly vanish, and stop stirring, quiet
It sets 2 hours, is filtered packaging to get above-mentioned paint.
2 performance parameter of embodiment
By the paint application in embodiment 1 on aluminum honeycomb panel, and the light diffusing reflection aluminum honeycomb panel is sent to country and is built
(test center's number: WT2018B01B00300 mid-term -2) is detected at testing of materials center, and monitoring result is as follows: decorative cover
Thickness degree are as follows: 68 μm of average value, 65 μm of minimum value, it is seen that light reflectivity (including mirror-reflection) is 96%, it is seen that light reflectivity
(removal mirror-reflection) is that 95%, 550nm reflectivity (removal mirror-reflection) is 95%, other indexs: presentation quality, size permit
Perhaps deviation, aluminium plate thickness, film flexibility, coating adhesion, coating salt tolerant acidity, coating oil resistivity, coating alkali resistance, coating
Resistance to nitric acid, climbing drum peel strength, flatwise tensile strength, flat crushing strength, concora crush elasticity modulus, plane shear intensity, plane shear bullet
Property modulus, bending stiffness, shearing rigidity, impact resistance energy, hot water resistance, coating stain resistance, temperature difference resistance, resistance to artificial time are old
The testing result of change meets the technical requirements in JG/T334-2012.
By the paint application in embodiment 1 on aluminium sheet, which is sent to Shanghai Silicate Inst., Chinese Academy of Sciences
Detected (research institute's examining report number: (2018) word the 0527th, test sample number: 0518100L), testing result
As follows: the total reflectivity at visible wavelength 550nm is 96%, and the scattered reflection rate at visible wavelength 550nm is
95.5%, the positive reflection rate at visible wavelength 550nm is 0.5%, to further confirm paint according to the present invention
It can be finally reached high irreflexive function, point light source is become into area source, equalizing light rays eliminate dazzle or hot spot, and it is dirty to reduce light
Dye, it is specifically as shown in Figure 2 using the coating plate face diffusing reflection effect picture of the paint.
The aforementioned description to specific exemplary embodiment of the invention is in order to illustrate and illustration purpose.These descriptions
It is not wishing to limit the invention to disclosed precise forms, and it will be apparent that according to the above instruction, can much be changed
And variation.The purpose of selecting and describing the exemplary embodiment is that explaining specific principle of the invention and its actually answering
With so that those skilled in the art can be realized and utilize a variety of different exemplary implementation schemes of the invention and
Various chooses and changes.The scope of the present invention is intended to be limited by claims and its equivalents.
Claims (10)
1. a kind of paint, which is characterized in that comprise the following components in parts by weight: 45-53 parts of resin, 30-35 parts of pigment, auxiliary agent 1-
3 parts, 4-6 parts of dumb light powder and 10-15 parts of solvent, wherein the auxiliary agent includes levelling agent, defoaming agent and acid catalyst.
2. paint as described in claim 1, which is characterized in that comprise the following components in parts by weight: 49 parts of resin, pigment 32
Part, 1.8 parts of auxiliary agent, 5 parts of dumb light powder and 13 parts of solvent, wherein the auxiliary agent includes levelling agent, defoaming agent and acid catalyst.
3. paint as described in claim 1, which is characterized in that the resin includes matrix resin and assisted resin, it is preferred that
The mass ratio of the matrix resin and assisted resin is (5-7): 1, it is further preferred that the matrix resin and assisted resin
Mass ratio is 6:1, it is further preferred that the matrix resin is saturated polyester resin, the assisted resin is full methyl-etherified ammonia
Base resin.
4. paint as described in claim 1, which is characterized in that the mass ratio of the levelling agent, defoaming agent and acid catalyst according to
Secondary is 1:1:1.
5. paint as described in claim 1, which is characterized in that the pigment is white pigment powder, it is preferred that the pigment is
Titanium dioxide；The dumb light powder is fumed silica, and the solvent is 150# solvent.
6. paint as described in claim 1, which is characterized in that total reflectivity of the paint at visible wavelength 550nm
For 95-97%, it is preferred that total reflectivity of the paint at visible wavelength 550nm is 96%；The paint is in visible light
Scattered reflection rate at wavelength 550nm is 94-96%, it is preferred that scattered reflection of the paint at visible wavelength 550nm
Rate is 95.5%；The positive reflection rate of the paint in visible wavelength 550nm at is 0.4-0.6%, it is preferred that it is described paint in
Positive reflection rate at visible wavelength 550nm is 0.5%.
7. a kind of preparation method of paint, which comprises the following steps:
(1) production of mill base: part resin and solvent being mixed at normal temperature, uniform stirring, while agitating, are at the uniform velocity added
Pigment continues to stir, guarantees to reach the fineness of mixture in 20 microns after the completion of being added；
(2) remaining resin and solvent, Jin Erjia the addition of acid catalyst: is added in the mill base prepared by step (1)
Enter levelling agent, defoaming agent and dumb light powder, quickly stirring 30 minutes or more, so that mixture is uniformly dispersed, sufficiently infiltrated, then at the uniform velocity
Acid catalyst is added, stirring to the foam for floating on mixture surface can quickly vanish, and stop stirring, stand 2 hours, carried out
Filter packaging is to get paint described in claim 1.
8. the preparation method of paint according to claim 7, which is characterized in that the resin amount in step (1) is 18-
22 parts by weight, it is preferred that the resin amount in step (1) is 20 parts by weight, and the resin amount in step (2) is 27-31
Parts by weight, it is preferred that the resin amount in step (2) is 29 parts by weight, it is preferred that described in step (1) and step (2)
Resin includes matrix resin and assisted resin, it is further preferred that the mass ratio of the matrix resin and assisted resin is (5-
7): 1, it is further preferred that the mass ratio of the matrix resin and assisted resin is 6:1, it is further preferred that the main body tree
Rouge is saturated polyester resin, and the assisted resin is full Amino resin.
9. the preparation method of paint according to claim 7, which is characterized in that the solvent adding amount in step (1) is 4-7
Parts by weight, it is preferred that the solvent adding amount in step (1) is 6 parts by weight, and the solvent adding amount in step (2) is 6-8 weight
Part, it is preferred that the solvent adding amount in step (2) is 7 parts by weight, it is further preferred that described in step (1) and step (2)
Solvent be 150# solvent；The additional amount of dumb light powder is 4-6 parts by weight in step (2), it is preferred that dumb light powder in step (2)
Additional amount is 5 parts by weight, it is further preferred that the dumb light powder in step (2) is fumed silica；Levelling agent in step (2),
Total additional amount of defoaming agent and acid catalyst is 1-3 parts by weight, it is preferred that levelling agent, defoaming agent and acid catalysis in step (2)
Total additional amount of agent be 1.8 parts by weight, it is further preferred that the mass ratio of the levelling agent, defoaming agent and acid catalyst according to
Secondary is 1:1:1.
10. the preparation method of paint described in any one of claims 1-6 or the described in any item paint of claim 7-9 is filling
Application on plaque.