CN108997836A - A kind of printing ink of high-solid lower-viscosity degree and preparation method thereof - Google Patents
A kind of printing ink of high-solid lower-viscosity degree and preparation method thereof Download PDFInfo
- Publication number
- CN108997836A CN108997836A CN201811127501.0A CN201811127501A CN108997836A CN 108997836 A CN108997836 A CN 108997836A CN 201811127501 A CN201811127501 A CN 201811127501A CN 108997836 A CN108997836 A CN 108997836A
- Authority
- CN
- China
- Prior art keywords
- agent
- printing ink
- solid lower
- viscosity degree
- ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to printing ink of a kind of high-solid lower-viscosity degree and preparation method thereof.The printing ink of the high-solid lower-viscosity degree includes following components: water-based acrylic resin: 40-50%;Pigment: 10-20%;Plasticiser: 2-5%;Levelling agent: 0.5%;Antistatic agent: 1-5%;Trifunctional urethane acrylate: 20-30%;Coupling agent: 1%;Defoaming agent: 0.5%;Crosslinking agent: 1%.The present invention has the characteristics that apparent high solids content, and viscosity is relatively low, it can be realized the high speed continuous printing of intaglio printing, good rapid-curing cutback performance, high adhesive ability, it is ensured that printing quality, it is less prone to printing quality, printing effect is good, and is free of volatile organic matter, meets ecological requirements, ink manufacture and printing environment can be improved, guarantee the health of worker.
Description
Technical field
The present invention relates to a kind of printing ink, and in particular to a kind of printing ink of high-solid lower-viscosity degree and preparation method thereof.
Background technique
Ink is important materials used for printing packaging materials, it is expressed the pattern and text on stock by printing.
It is chlorinated polypropylene ink, polyurethane ink, polyacrylic acid ester oil that in China, usage amount is maximum at this stage, in printing packaging
Ink, containing organic solvents such as a large amount of benzene, toluene, butanone, ethyl acetate in this kind of solvent-based ink, in solvent-based ink
In use process, the solvent contamination air of volatilization endangers the health of operator, the residual solvent meeting in packing articles
Food in serious pollution packaging, therefore the research and development for carrying out environment-friendlyink ink are imperative.
China generally acknowledges that more environmentally friendly ink is water-based ink at this stage at present, low volatilization, high-environmental, less harmful,
The advantage of high-quality is increasingly favored by people, but domestic current water-based ink development and incomplete, almost without true
The water-based ink of positive compound intaglio printing, there are problems for existing water-based ink, such as solid content is low, viscosity is high, solid
Change the disadvantages of speed is slow.
Summary of the invention
In order to overcome the part of background technique insufficient, the present invention provides printing ink and its preparation of a kind of high-solid lower-viscosity degree
Method.
The technical scheme adopted by the invention is that: a kind of printing ink of high-solid lower-viscosity degree, by weight percentage, the height
Gu the printing ink of low viscosity includes following components:
Water-based acrylic resin: 40-50%,
Pigment: 10-20%,
Plasticiser: 2-5%,
Levelling agent: 0.5%,
Antistatic agent: 1-5%,
Trifunctional urethane acrylate: 20-30%,
Coupling agent: 1%,
Defoaming agent: 0.5%,
Crosslinking agent: 1%.
Further, the pigment passes through modification, the method being modified are as follows: water is added first in pigment and carries out
Stirring, then adds molybdenum disulfide powder and ethyl alcohol, pours into stirring container and be sufficiently stirred 30-40 minutes together, add
Between carboxyl benzene sulfonate, continue stirring 15-20 minutes, obtain mixed emulsion;Lotion is finally poured into vacuum ball grinder and is placed in ball
Grinding machine carries out planetary vacuum ball milling;Finally, the pigment after drying materials are modified is taken out in pressure release.
Further, wherein the ratio of pigment, water, molybdenum disulfide powder and ethyl alcohol is 100:5~20:5:60~70.
It is handled by the above pigment modification, improves the viscosity of ink, accelerate the drying of ink, guaranteed equal when printing
Even densification improves the comprehensive performance of the ink of ink, it is opposite with there is higher solid content, lower dense for common ink
Degree, wherein solid content is higher by 20-30% for common water-based ink, while viscosity is lower.Wherein molybdenum disulphide powder
End, water and ethyl alcohol, improve the mixed uniformity of pigment, reduce the viscosity of ink, and molybdenum disulfide powder therein can add
The grinding of fast pigment improves ink adhesion so that fine pigment partial size, increases the contact area of ink and substrate.
Further, the trifunctional urethane acrylate is made of following methods: first will be by six methylenes
Group diisocyanate tripolymer, hydroxypropyl acrylate, dibutyl tin dilaurate, hydroquinone are uniformly mixed to get mixture,
Then mixture is put into reaction kettle and keeps being heated to 60 DEG C, continue 2 hours.
Urethane acrylate is that light consolidates the important basic resin in field, and the urethane bond energy contained forms a variety of hydrogen bonds,
It can be improved wear-resisting property, flexibility, temperature tolerance and the adhesive ability to substrate of solidfied material, the present invention is by being added trifunctional
Urethane acrylic can be modified ink, improve ink comprehensive performance, especially adhesive ability and solidification rate.
The usual way of prior art preparation urethane acrylate is to utilize isocyanate group in polyisocyanates and more
In first alcohol hydroxyl translate, and using hydroxyl acrylate introduce activity group, prepared ink have complex process,
The disadvantages of low and rate of polymerization of photopolymerization reaction activity is slower, and often occur solidifying incomplete phenomenon in the curing process.This
The method and process that invention prepares trifunctional urethane acrylate is simple, and helps to improve rate of polymerization.
Further, the coupling agent includes methyltrimethoxysilane, dimethyl diethoxysilane, phenyl three
In Ethoxysilane, hexamethyldisilazane, 3- glycidoxypropyltrime,hoxysilane or vinyltrimethoxysilane
Any one or at least two combination.
Further, the crosslinking agent is ammonium carbonate zinc and/or ammonium carbonate pick.Ammonium carbonate zinc and ammonium carbonate pick belong to nothing
Machine crosslinking agent can be reacted with resin and carboxyl, can generate zinc ion key or pick ionic bond, these ionic bonds have very strong resistance to
Hot and alcohol resistance can greatly improve the chemical stability of ink, improve the adhesive force of ink, be not easy to be oxidized.
Further, the defoaming agent is organic silicon defoaming agent, and the defoaming agent includes that moral modest 6800 and/or moral are modest
6500。
A method of preparing the printing ink of high-solid lower-viscosity degree, comprising the following steps:
Step 1: water-based acrylic resin, pigment being mixed according to the ratio and trifunctional urethane acrylate is uniformly mixed to get
Mixed solution a.
Step 2: coupling agent, crosslinking agent, levelling agent, antistatic agent being added according to the ratio in the mixed solution a that step 1 obtains
Mixed solution b is obtained with plasticiser, mixed solution b pours into the blender with heating function to be thoroughly mixed 2-4 small
When.
Step 3: completing in step 2 and then be added to stir 1-2 hours in blender by defoaming agent to obtain solution c.
Step 4: the solution c in step 3 being poured into ball mill and is ground 5-8 hours, until last granularity reaches 0.5
~2 microns obtain the printing ink of final high-solid lower-viscosity degree.
Further, the temperature of blender controls 50-70 DEG C in the step 2, the control of the revolving speed of blender 2500~
4000 revs/min.
Further, at 25-40 DEG C, the revolving speed of blender is controlled in 1000- the control of blender temperature in the step 3
1500 revs/min.
The beneficial effects of the present invention are:
1, of the invention that processing is modified to common pigment, the viscosity of ink is improved, the drying of ink is accelerated, guarantees print
Even compact when brush improves the comprehensive performance of the ink of ink, opposite to contain admittedly with for common ink with higher
Amount, lower concentration, wherein solid content is higher by 20-30% for common water-based ink, while viscosity is lower.
2, the present invention joined molybdenum disulfide powder, water and ethyl alcohol when modified, improve the uniform of the mixing of pigment
Property, the viscosity of ink is reduced, and molybdenum disulfide powder therein can speed up the grinding of pigment, so that fine pigment partial size, increases
The contact area of big ink and substrate, improves ink adhesion.
3, the present invention is capable of providing more light reaction groups double bond by addition trifunctional urethane acrylate,
To enhance light reaction, crosslink density increases, so substantially reducing the curing time of ink.
Specific embodiment
The present invention is described in further details below with reference to embodiment.
Embodiment 1:
A kind of printing ink of high-solid lower-viscosity degree, by weight percentage, the printing ink of the high-solid lower-viscosity degree includes with the following group
Point:
Water-based acrylic resin: 50%,
Pigment: 20%,
Plasticiser: 2%,
Levelling agent: 0.5%,
Antistatic agent: 5%,
Trifunctional urethane acrylate: 20%,
Coupling agent: 1%,
Defoaming agent: 0.5%,
Crosslinking agent: 1%.
Embodiment 2:
A kind of printing ink of high-solid lower-viscosity degree, by weight percentage, the printing ink of the high-solid lower-viscosity degree includes with the following group
Point:
Water-based acrylic resin: 40%,
Pigment: 17%,
Plasticiser: 5%,
Levelling agent: 0.5%,
Antistatic agent: 5%,
Trifunctional urethane acrylate: 30%,
Coupling agent: 1%,
Defoaming agent: 0.5%,
Crosslinking agent: 1%.
Embodiment 3:
A kind of printing ink of high-solid lower-viscosity degree, by weight percentage, the printing ink of the high-solid lower-viscosity degree includes with the following group
Point:
Water-based acrylic resin: 47%,
Pigment: 10%,
Plasticiser: 5%,
Levelling agent: 0.5%,
Antistatic agent: 5%,
Trifunctional urethane acrylate: 30%,
Coupling agent: 1%,
Defoaming agent: 0.5%,
Crosslinking agent: 1%.
Embodiment 4
A kind of printing ink of high-solid lower-viscosity degree, by weight percentage, the printing ink of the high-solid lower-viscosity degree includes with the following group
Point:
Water-based acrylic resin: 50%,
Pigment: 16%,
Plasticiser: 5%,
Levelling agent: 0.5%,
Antistatic agent: 1%,
Trifunctional urethane acrylate: 25%,
Coupling agent: 1%,
Defoaming agent: 0.5%,
Crosslinking agent: 1%,
Wherein comparative example is the indices of common ink.
It reads 1 data of table and combines practical production experience, the ink of embodiment 1-4 has the spy of apparent high solids content
Point, and viscosity is relatively low, can be realized the high speed continuous printing of intaglio printing, good rapid-curing cutback performance, high energy of attachment
Power, it is ensured that printing quality is less prone to printing quality, and printing effect is good, and is free of volatile organic matter, meets environmentally friendly need
It asks, ink manufacture and printing environment can be improved, guarantee the health of worker.
Every technical staff's notice: of the invention although the present invention is described according to above-mentioned specific embodiment
Invention thought be not limited in the invention, any repacking with inventive concept will all be included in this patent protection of the patent right
In range.
Claims (10)
1. a kind of printing ink of high-solid lower-viscosity degree, it is characterised in that: by weight percentage, the off-set oil of the high-solid lower-viscosity degree
Ink includes following components:
Water-based acrylic resin: 40-50%,
Pigment: 10-20%,
Plasticiser: 2-5%,
Levelling agent: 0.5%,
Antistatic agent: 1-5%,
Trifunctional urethane acrylate: 20-30%,
Coupling agent: 1%,
Defoaming agent: 0.5%,
Crosslinking agent: 1%.
2. a kind of printing ink of high-solid lower-viscosity degree according to claim 1, it is characterised in that: the pigment is by changing
Property processing, be modified method are as follows: first in pigment be added water be stirred, then add molybdenum disulfide powder and second
Alcohol pours into stirring container together and is sufficiently stirred 30-40 minutes, adds a carboxyl benzene sulfonate, continues to stir 15-20 points
Clock obtains mixed emulsion;Lotion is finally poured into vacuum ball grinder and is placed in ball mill progress planetary vacuum ball milling;Finally, pressure release,
Take out the pigment after drying materials are modified.
3. a kind of printing ink of high-solid lower-viscosity degree according to claim 2, it is characterised in that: wherein pigment, water, two sulphur
The ratio for changing molybdenum powder and ethyl alcohol is 100:5~20:5:60~70.
4. a kind of printing ink of high-solid lower-viscosity degree according to claim 1, it is characterised in that: the trifunctional is reunited
Urethane acrylate is made of following methods: first will by hexamethylene diisocyanate trimer, hydroxypropyl acrylate,
Dibutyl tin dilaurate, hydroquinone are uniformly mixed to get mixture, and then mixture is put into reaction kettle and keeps adding
Heat continues 2 hours to 60 DEG C.
5. a kind of printing ink of high-solid lower-viscosity degree according to claim 1, it is characterised in that: the coupling agent includes
Methyltrimethoxysilane, dimethyl diethoxysilane, phenyl triethoxysilane, hexamethyldisilazane, 3- epoxy third
Any one in oxygroup propyl trimethoxy silicane or vinyltrimethoxysilane or at least two combination.
6. a kind of printing ink of high-solid lower-viscosity degree according to claim 1, it is characterised in that: the crosslinking agent is carbon
Sour ammonium zinc and/or ammonium carbonate pick.
7. a kind of printing ink of high-solid lower-viscosity degree according to claim 1, it is characterised in that: the defoaming agent is to have
Machine silicon class defoaming agent, the defoaming agent include moral modest 6800 and/or moral modest 6500.
8. a kind of method for the printing ink for preparing high-solid lower-viscosity degree, it is characterised in that: the following steps are included:
Step 1: water-based acrylic resin, pigment being mixed according to the ratio and trifunctional urethane acrylate is uniformly mixed to get
Mixed solution a:
Step 2: coupling agent, crosslinking agent, levelling agent, antistatic agent and modeling being added according to the ratio in the mixed solution a that step 1 obtains
Agent obtains mixed solution b, and mixed solution b is poured into the blender with heating function and is thoroughly mixed 2-4 hours:
Step 3: it completes in step 2 and then is added to stir 1-2 hours in blender by defoaming agent to obtain solution c:
Step 4: the solution c in step 3 being poured into ball mill and is ground 5-8 hours, until to reach 0.5~2 micro- for last granularity
Rice obtains the printing ink of final high-solid lower-viscosity degree.
9. a kind of printing ink of high-solid lower-viscosity degree according to claim 8, it is characterised in that: stirred in the step 2
The temperature of machine controls 50-70 DEG C, and the revolving speed of blender is controlled at 2500~4000 revs/min.
10. a kind of printing ink of high-solid lower-viscosity degree according to claim 8, it is characterised in that: stirred in the step 3
At 25-40 DEG C, the revolving speed of blender is controlled at 1000-1500 revs/min the control of device temperature.