CN108980525A - 气凝胶绝热、防护一体化产品及利用其包管的施工方法 - Google Patents
气凝胶绝热、防护一体化产品及利用其包管的施工方法 Download PDFInfo
- Publication number
- CN108980525A CN108980525A CN201810844314.8A CN201810844314A CN108980525A CN 108980525 A CN108980525 A CN 108980525A CN 201810844314 A CN201810844314 A CN 201810844314A CN 108980525 A CN108980525 A CN 108980525A
- Authority
- CN
- China
- Prior art keywords
- piece
- layer
- insulating
- integrated product
- protection integrated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及气凝胶绝热、防护一体化产品及包管的施工方法。气凝胶绝热、防护一体化产品包括由内向外依次粘合的内衬层、气凝胶层和可弯折的保护层。施工方法包括：步骤一、制作包管片；步骤二、包管；步骤三、制作遮缝片；步骤四、包缝。优点：该一体化产品结构简单，隔热及防护效果好，施工方便、快捷，施工效率高，成本低。
Description
技术领域
本发明涉及气凝胶绝热、防护一体化产品及包管的施工方法。
背景技术
随着工业的迅猛发展和人们生活水平的提高，能源问题已经变得日益突出。节约能源、降低能耗已成为新材料领域的一个研究重点。气凝胶被誉为21世纪最有前途的新材料，具有高比表面积、高空隙率、低密度和低导热系数等特点。目前，气凝胶材料已经替代了部分绝热材料而被应用于对空间、使用寿命、节能效果要求较高领域。其中气凝胶毡已被应用于工业领域管道、设备的保温及保冷。
目前，绝大多数气凝胶毡均采用在施工地根据图纸现场进行剪裁，然后再按施工规范一层层进行缠绕、粘结、捆扎、填缝，最后再安装上最外层的金属或非金属防护层。这样一来，现场施工过程繁琐、耗时长且增加了施工成本。
发明内容
本发明所要解决的技术问题是提供一种气凝胶绝热、防护一体化产品及包管的施工方法，有效的克服了现有技术的缺陷。
本发明解决上述技术问题的技术方案如下：
一种气凝胶绝热、防护一体化产品，用以包裹在管道外部并对管道隔热，包括由内向外依次粘合的内衬层、气凝胶层和可弯折的保护层。
本发明的有益效果是：该一体化产品结构简单，隔热及防护效果好，生产简单。
在上述技术方案的基础上，本发明还可以做如下改进。
进一步，上述内衬层为玻纤布。
采用上述进一步方案的有益效果是内衬层能够防止气凝胶层含有的气凝胶粉掉落，采用玻纤布使其具有较好的抗拉性能及隔热性能。
进一步，上述气凝胶层为气凝胶毡。
采用上述进一步方案的有益效果是抗拉性能好，隔热效果佳。
进一步，上述保护层为铝皮层、不锈钢片或彩钢片。
采用上述进一步方案的有益效果是韧性好，强度高，防护效果佳。
进一步，上述气凝胶层由内向外依次设有多层，且相邻两层之间连接固定。
采用上述进一步方案的有益效果是多层设计能显著提升整个产品的隔热保温性能。
进一步，相邻两层上述气凝胶层之间通过胶体粘合，或叠合后通过铆钉连接固定。
采用上述进一步方案的有益效果是气凝胶层之间连接方式多样化，连接牢固度高。
还提供一种利用气凝胶绝热、防护一体化产品包管的施工方法，包括以下步骤：
步骤一、制作包管片，具体为，取气凝胶绝热、防护一体化产品，裁切成多片规格一致的长方形片，将每片长方形的气凝胶绝热、防护一体化产品的所有功能层由外向内逐层沿每层功能层两端的边沿线分别裁切掉N×L的宽度，得到多片包管片；
其中，N为所有功能层由内向外每层功能层的层数，2cm≤L≤3cm；
步骤二、包管，具体为，将多片包管片依次顺序卷绕包裹在管道外，并通过箍紧件固定在管道外，并使相邻两片包管片的内衬层相互靠近的一端端部相抵，且相邻两片包管片的连接处形成环状的包管缝；
其中，包管片的长度方向与管道的长度方向一致，相邻两片包管片的保护层相互靠近一端端部之间的间距为M；
步骤三、制作遮缝片，具体为，取气凝胶绝热、防护一体化产品，裁切成多片宽度为S且规格一致的长方形片，对每片长方形的气凝胶绝热、防护一体化产品所有功能层的由内向外逐层沿每层功能层两端的边沿线分别裁切掉N′×L的宽度，得到多片遮缝片；
其中，S＝M+2L，N′为所有功能层由外向内每层功能层的层数；
步骤四、包缝，具体为，预先在相邻两片包管片相抵的一端每层功能层的表面涂覆粘合剂，之后将遮缝片环绕嵌合在包管缝处，并卷绕粘合在相邻两片包管片相抵的一端外部，且通过箍紧件固定在包管缝处。
有益效果是：施工工艺简单、快捷，施工周期短，成本低。
进一步，上述粘合剂为白乳胶、环氧树脂、有机硅粘结剂、无机粘结剂的一种。
采用上述进一步方案的有益效果是粘合效果佳，可选材料多，利于施工。
进一步，上述箍紧件为不锈钢扎带、自攻螺丝、扎丝的一种。
采用上述进一步方案的有益效果是箍紧件方便施工，确保包管片和遮缝片包管牢固、稳定。
附图说明
图1为本发明的气凝胶绝热、防护一体化产品的结构剖视图；
图2为本发明的气凝胶绝热、防护一体化产品的其他一些实施例的结构剖视图；
图3为包管的施工方法中包管片在管道外卷绕后的截面结构示意图；
图4为包管的施工方法中在管道外包管完毕后的截面结构示意图；
图5为图4中沿A-A面的截面结构示意图；
图6为图4中沿B-B面的截面结构示意图。
附图中，各标号所代表的部件列表如下：
1、内衬层，2、气凝胶层，3、保护层，4、反射层，5、包管片，6、管道，7、包管缝，8、遮缝片。
具体实施方式
以下结合附图对本发明的原理和特征进行描述，所举实例只用于解释本发明，并非用于限定本发明的范围。
实施例一：如图1所示，本实施例的气凝胶绝热、防护一体化产品，用以包裹在管道外部并对管道隔热，包括由内向外依次粘合的内衬层1、气凝胶层2和可弯折的保护层3。
整个气凝胶绝热、防护一体化产品结构强度较好，在作为管道或其他物件表面防护及绝热层使用时，具有较佳的防护效果和隔热效果，能有效降低管道及其他物件的热量损耗。
较佳的，上述内衬层1为玻纤布，内衬层1的设计能够防止气凝胶层2含有的气凝胶粉掉落，并且内衬层1采用玻纤布其本身就具备一定隔热性能，同时其具有较好的抗拉性能，并能起到一定降噪的作用，绿色环保。
较佳的，上述气凝胶层2为气凝胶毡，导热系数低，有一定的抗拉及抗压强度，便于保温施工应用，隔热效果较佳。
较佳的，上述保护层3为铝皮层、不锈钢片或彩钢片，其韧性较好，强度高，作为防护外层其防护效果佳，也可以采用其他强度及韧性较好的非金属材料。
较佳的，上述气凝胶层2由内向外依次设有多层，且相邻两层之间连接固定，多层气凝胶层2的设计使得整个气凝胶绝热、防护一体化产品的隔热效果进一步得到提升。
较佳的，相邻两层上述气凝胶层2之间通过胶体粘合，或叠合后通过铆钉连接固定，使得气凝胶层2之间连接方式多样化，连接牢固度较高。
在其他一些实施例中，如图2所示，实施例一中的气凝胶绝热、防护一体化产品还可以包括反射层4，上述反射层4粘合设置在相邻两层的上述气凝胶层2之间，上述反射层一般采用铝箔或玻纤布，其具有较好的隔热及热反射性能，确保整个气凝胶绝热、防护一体化产品在管道外包裹使用后能最大程度的降低管道内液体或气体的热量损耗，减少与外界的热交换。
实施例二：如图3、4、5、6所示，本实施例的利用实施例一中气凝胶绝热、防护一体化产品包管的施工方法，包括以下步骤：
步骤一、制作包管片5，具体为，取气凝胶绝热、防护一体化产品，裁切成多片规格一致的长方形片，将每片长方形的气凝胶绝热、防护一体化产品的所有功能层由外向内逐层沿每层功能层两端的边沿线分别裁切掉N×L的宽度，得到多片包管片5；
其中，N为所有功能层由内向外每层功能层的层数，2cm≤L≤3cm；
步骤二、包管，具体为，将多片包管片5依次顺序卷绕包裹在管道6外，并通过箍紧件固定在管道6外，并使相邻两片包管片5的内衬层1相互靠近的一端端部相抵，且相邻两片包管片5的连接处形成环状的包管缝7；
其中，包管片5的长度方向与管道6的长度方向一致，相邻两片包管片5的保护层3相互靠近一端端部之间的间距为M；
步骤三、制作遮缝片8，具体为，取气凝胶绝热、防护一体化产品，裁切成多片宽度为S且规格一致的长方形片，对每片长方形的气凝胶绝热、防护一体化产品所有功能层的由内向外逐层沿每层功能层两端的边沿线分别裁切掉N′×L的宽度，得到多片遮缝片8；
其中，S＝M+2L，N′为所有功能层由外向内每层功能层的层数；
步骤四、包缝，具体为，预先在相邻两片包管片5相抵的一端每层功能层的表面涂覆粘合剂，之后将遮缝片8环绕嵌合在包管缝7处，并卷绕粘合在相邻两片包管片5相抵的一端外部，且通过箍紧件固定在包管缝7处。
整个施工步骤简单，包管无缝隙，结构紧凑，质量较好，施工效率高，周期短，有效节约了施工成本，极具推广价值。
较佳的，步骤四中，上述粘合剂为白乳胶、环氧树脂、有机硅粘结剂、无机粘结剂的一种，能有效将遮缝片8与的内衬层1与相邻两个包管片5的内衬层1粘合，粘合后牢固度较高，不易分离，并且其成本低，能一定程度节约施工成本。
较佳的，上述箍紧件为不锈钢扎带、自攻螺丝、扎丝的一种，为不锈钢扎带时，将多个扎带分别环绕在包管片5及遮缝片8外，并将扎带两端紧固，以使包管片5及遮缝片8固定牢固；为自攻螺丝时，在包管片5及遮缝片8的保护层3外用多个均匀分布的自攻螺丝紧固即可；为扎丝时，将扎丝环绕在包管片5及遮缝片8外，再通过拧紧扎丝使包管片5及遮缝片8紧固在管道6外部即可，还可以采用其他具有同等作用或效果的箍紧件。
需要特别说明的是：施工过程中，若气凝胶绝热、防护一体化产品中含有反射层4，则反射层的宽度应与相邻外层的气凝胶层2的宽度一致，且两者的两端边沿处相互平齐。
以上所述仅为本发明的较佳实施例，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (10)
1.一种气凝胶绝热、防护一体化产品，用以包裹在管道外部并对管道隔热，其特征在于：包括由内向外依次粘合的内衬层(1)、气凝胶层(2)和可弯折的保护层(3)。
2.根据权利要求1所述的一种气凝胶绝热、防护一体化产品，其特征在于：所述内衬层(1)为玻纤布。
3.根据权利要求1所述的一种气凝胶绝热、防护一体化产品，其特征在于：所述气凝胶层(2)为气凝胶毡。
4.根据权利要求1所述的一种气凝胶绝热、防护一体化产品，其特征在于：所述保护层(3)为铝皮层、不锈钢片或彩钢片。
5.根据权利要求1至4任一项所述的一种气凝胶绝热、防护一体化产品，其特征在于：所述气凝胶层(2)由内向外依次设有多层，且相邻两层之间连接固定。
6.根据权利要求5所述的一种气凝胶绝热、防护一体化产品，其特征在于：相邻两层所述气凝胶层(2)之间通过胶体粘合，或叠合后通过铆钉连接固定。
7.一种利用如权利要求1至5任一项所述的气凝胶绝热、防护一体化产品包管的施工方法，其特征在于，包括以下步骤：
步骤一、制作包管片(5)，具体为，取气凝胶绝热、防护一体化产品，裁切成多片规格一致的长方形片，将每片长方形的气凝胶绝热、防护一体化产品的所有功能层由外向内逐层沿每层功能层两端的边沿线分别裁切掉N×L的宽度，得到多片包管片(5)；
其中，N为包管片(5)的所有功能层由内向外每层功能层的层数，2cm≤L≤3cm；
步骤二、包管，具体为，将多片包管片(5)依次顺序卷绕包裹在管道(6)外，并使每片包管片(5)的两侧侧端叠合，之后，分别通过箍紧件将每片包管片(5)箍紧在管道(6)外，并使相邻两片包管片(5)的内衬层(1)相互靠近的一端端部相抵，且相邻两片包管片(5)的连接处形成环状的包管缝(7)；
其中，包管片(5)的长度方向与管道(6)的长度方向一致，相邻两片包管片(5)的保护层(3)相互靠近一端端部之间的间距为M；
步骤三、制作遮缝片(8)，具体为，取气凝胶绝热、防护一体化产品，裁切成多片宽度为S且规格一致的长方形片，对每片长方形的气凝胶绝热、防护一体化产品所有功能层的由内向外逐层沿每层功能层两端的边沿线分别裁切掉N′×L的宽度，得到多片遮缝片(8)；
其中，S＝M+2L，N′为遮缝片(8)的所有功能层由外向内每层功能层的层数；
步骤四、包缝，具体为，预先在相邻两片包管片(5)相抵的一端每层功能层的表面涂覆粘合剂，之后将遮缝片(8)环绕嵌合在包管缝(7)处，并卷绕粘合在相邻两片包管片(5)相抵的一端外部，并使每片遮缝片(8)的两侧侧端叠合，之后，分别通过箍紧件将每片遮缝片(8)固定在包管缝(7)处。
8.根据权利要求7所述的一种气凝胶绝热、防护一体化产品包管的施工方法，其特征在于：步骤二中，每片包管片(5)的两侧侧端叠合前，将每片包管片(5)的一侧均由内向外沿其侧端边沿线分别裁切掉G×L的宽度，将每片包管片(5)的另一侧由外向内沿其侧端边沿线分别裁切掉N×L的宽度，并确保裁切后的包管片(5)的内衬层(1)的宽度与管道(6)的外周周长相等；
其中，G为包管片(5)的所有功能层由外向内每层功能层的层数；在每片包管片(5)的两侧侧端叠合后，所述包管片(5)每层功能层的两侧侧端相接触，并通过粘合剂相粘结。
9.根据权利要求7所述的一种气凝胶绝热、防护一体化产品包管的施工方法，其特征在于：步骤四中，每片遮缝片(8)的两侧侧端叠合前，将每片遮缝片(8)的一侧均由内向外沿其侧端边沿线分别裁切掉N′×L的宽度，将每片遮缝片(8)的另一侧由外向内沿其侧端边沿线分别裁切掉G′×L的宽度，并确保裁切后的遮缝片(8)的保护层(3)的长度与包管片(5)的保护层(3)的宽度相等；
其中，G′为遮缝片(8)的所有功能层由内向外每层功能层的层数；在每片遮缝片(8)的两侧侧端叠合后，所述遮缝片(8)每层功能层的两侧侧端相接触，并通过粘合剂相粘结。
10.根据权利要求8或9所述的一种气凝胶绝热、防护一体化产品包管的施工方法，其特征在于：所述粘合剂为白乳胶、环氧树脂、有机硅粘结剂、无机粘结剂的一种。