CN108976958A - A kind of graphene heat radiation coating and preparation method thereof - Google Patents
A kind of graphene heat radiation coating and preparation method thereof Download PDFInfo
- Publication number
- CN108976958A CN108976958A CN201810526246.0A CN201810526246A CN108976958A CN 108976958 A CN108976958 A CN 108976958A CN 201810526246 A CN201810526246 A CN 201810526246A CN 108976958 A CN108976958 A CN 108976958A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- heat radiation
- graphene
- radiation coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of graphene heat radiation coatings and preparation method thereof.The graphene heat radiation coating includes the raw material of following parts by weight: 10-20 parts of graphene, 5-10 parts of acetylene black, 4-8 parts of carbonyl diamide, water-soluble 5-10 parts of benzotriazole, 40-60 parts of water-based acrylic resin, 10-20 parts of polyethylene glycol, 30-90 parts of water.Graphene heat radiation coating of the invention is prepared using graphene, acetylene black, carbonyl diamide, water-soluble benzotriazole, water-based acrylic resin and polyethylene glycol as primary raw material, with preferable heating conduction, and curing time is short, can meet using needs, market popularization value is high.
Description
Technical field
The present invention relates to heat radiation coating technical field, specifically a kind of graphene heat radiation coating and preparation method thereof.
Background technique
With the general advance of scientific and technological level, electronic apparatus, mechanical equipment are more and more exquisite, multi-functional towards miniaturization
Change development.But a following caused problem is increasingly taken seriously: heat dissipation.Electronic radiation problem has become restriction electricity
The bottleneck of sub- industrial development, and efficient electronic radiation technology has become a research hotspot.
Heat radiation coating is a kind of radiating efficiency for improving body surface, reduces the sapecial coating of system temperature.Heat radiation coating
It can be divided into according to solvent difference: organic solvent type heat radiation coating, water-based cooling coating, (solvent-free) powder heat radiation coating.It is organic
Solvent type heat radiation coating is unfriendly to environment.Water-based cooling coating and no-solvent type heat radiation coating are environmentally friendly.Existing water
Property the disadvantages of heat radiation coating still remains poor radiation, curing time is long.
Summary of the invention
The purpose of the present invention is to provide a kind of graphene heat radiation coatings and preparation method thereof, to solve above-mentioned background technique
The problem of middle proposition.
To achieve the above object, the invention provides the following technical scheme:
A kind of graphene heat radiation coating, the graphene heat radiation coating include the raw material of following parts by weight: graphene 10-
20 parts, 5-10 parts of acetylene black, 4-8 parts of carbonyl diamide, water-soluble 5-10 part of benzotriazole, 40-60 parts of water-based acrylic resin, gather
10-20 parts of ethylene glycol, 30-90 parts of water.
As a further solution of the present invention: the graphene heat radiation coating includes the raw material of following parts by weight: graphite
12-17 parts of alkene, 6-8 parts of acetylene black, 5-7 parts of carbonyl diamide, water-soluble 6-8 parts of benzotriazole, water-based acrylic resin 45-52
Part, 12-18 parts of polyethylene glycol, 40-80 parts of water.
As a further solution of the present invention: the graphene heat radiation coating includes the raw material of following parts by weight: graphite
15 parts of alkene, 7 parts of acetylene black, 6 parts of carbonyl diamide, water-soluble 7 parts of benzotriazole, 48 parts of water-based acrylic resin, polyethylene glycol 16
Part, 50 parts of water.
A kind of preparation method of graphene heat radiation coating, step are as follows: (1) mix graphene, acetylene black and water, through magnetic force
5-15min is stirred, suspension is made into;(2) carbonyl diamide and water-soluble benzotriazole are added in suspension, and adjusting pH is 3-
5, then magnetic agitation 10-20min;(3) water-based acrylic resin and polyethylene glycol is added in the suspension obtained by step (2),
Magnetic agitation 20-40min;Then disperse 10-30min, last re-ultrasonic dispersion 20-30min under high speed shear dispersion machine, i.e.,
?.
As a further solution of the present invention: step (1) mixes graphene, acetylene black and water, through magnetic agitation
10min is made into suspension.
As a further solution of the present invention: carbonyl diamide and water-soluble benzotriazole is added in step (2) in suspension,
And adjusting pH is 4.5, then magnetic agitation 15min.
As a further solution of the present invention: water-based acrylic resin is added in the suspension obtained by step (2) in step (3)
And polyethylene glycol, magnetic agitation 30min;Then disperse 20min, last re-ultrasonic dispersion 24min under high speed shear dispersion machine,
To obtain the final product.
Compared with prior art, the beneficial effects of the present invention are:
Graphene heat radiation coating of the invention is with graphene, acetylene black, carbonyl diamide, water-soluble benzotriazole, aqueous third
Olefin(e) acid resin and polyethylene glycol are prepared for primary raw material, have preferable heating conduction, and curing time is short, can meet makes
With needs, market popularization value height.
Specific embodiment
The technical solution of the patent is explained in further detail With reference to embodiment.
Embodiment 1
A kind of graphene heat radiation coating, the graphene heat radiation coating include the raw material of following parts by weight: graphene 10
Part, 5 parts of acetylene black, 4 parts of carbonyl diamide, water-soluble 5 parts of benzotriazole, 40 parts of water-based acrylic resin, 10 parts of polyethylene glycol, water
30 parts.
A kind of preparation method of graphene heat radiation coating, step are as follows: (1) mix graphene, acetylene black and water, through magnetic force
5min is stirred, suspension is made into;(2) carbonyl diamide and water-soluble benzotriazole are added in suspension, and adjusting pH is 3, so
Magnetic agitation 10min afterwards;(3) water-based acrylic resin and polyethylene glycol, magnetic agitation is added in the suspension obtained by step (2)
20min;Then disperse 10min under high speed shear dispersion machine, last re-ultrasonic dispersion 20min to get.
Embodiment 2
A kind of graphene heat radiation coating, the graphene heat radiation coating include the raw material of following parts by weight: graphene 20
Part, 10 parts of acetylene black, 8 parts of carbonyl diamide, water-soluble 10 parts of benzotriazole, 60 parts of water-based acrylic resin, 20 parts of polyethylene glycol,
90 parts of water.
A kind of preparation method of graphene heat radiation coating, step are as follows: (1) mix graphene, acetylene black and water, through magnetic force
15min is stirred, suspension is made into;(2) carbonyl diamide and water-soluble benzotriazole are added in suspension, and adjusting pH is 5, so
Magnetic agitation 20min afterwards;(3) water-based acrylic resin and polyethylene glycol, magnetic agitation is added in the suspension obtained by step (2)
40min;Then disperse 30min under high speed shear dispersion machine, last re-ultrasonic dispersion 30min to get.
Embodiment 3
A kind of graphene heat radiation coating, the graphene heat radiation coating include the raw material of following parts by weight: graphene 15
Part, 7 parts of acetylene black, 6 parts of carbonyl diamide, water-soluble 7 parts of benzotriazole, 48 parts of water-based acrylic resin, 16 parts of polyethylene glycol, water
50 parts.
A kind of preparation method of graphene heat radiation coating, step are as follows: (1) mix graphene, acetylene black and water, through magnetic force
10min is stirred, suspension is made into.(2) carbonyl diamide and water-soluble benzotriazole are added in suspension, and adjusting pH is 4.5,
Then magnetic agitation 15min.(3) water-based acrylic resin is added in the suspension obtained by step (2) and polyethylene glycol, magnetic force stirs
Mix 30min;Then disperse 20min under high speed shear dispersion machine, last re-ultrasonic dispersion 24min to get.
Embodiment 4
A kind of graphene heat radiation coating, the graphene heat radiation coating include the raw material of following parts by weight: graphene 12
Part, 6 parts of acetylene black, 5 parts of carbonyl diamide, water-soluble 6 parts of benzotriazole, 45 parts of water-based acrylic resin, 12 parts of polyethylene glycol, water
40 parts.
A kind of preparation method of graphene heat radiation coating, step are as follows: (1) mix graphene, acetylene black and water, through magnetic force
8min is stirred, suspension is made into;(2) carbonyl diamide and water-soluble benzotriazole are added in suspension, and adjusting pH is 3.6,
Then magnetic agitation 13min;(3) water-based acrylic resin is added in the suspension obtained by step (2) and polyethylene glycol, magnetic force stirs
Mix 25min;Then disperse 16min under high speed shear dispersion machine, last re-ultrasonic dispersion 22min to get.
Embodiment 5
A kind of graphene heat radiation coating, the graphene heat radiation coating include the raw material of following parts by weight: graphene 17
Part, 8 parts of acetylene black, 7 parts of carbonyl diamide, water-soluble 8 parts of benzotriazole, 52 parts of water-based acrylic resin, 18 parts of polyethylene glycol, water
80 parts.
A kind of preparation method of graphene heat radiation coating, step are as follows: (1) mix graphene, acetylene black and water, through magnetic force
12min is stirred, suspension is made into;(2) carbonyl diamide and water-soluble benzotriazole are added in suspension, and adjusting pH is 4.5,
Then magnetic agitation 17min;(3) water-based acrylic resin is added in the suspension obtained by step (2) and polyethylene glycol, magnetic force stirs
Mix 35min;Then disperse 24min under high speed shear dispersion machine, last re-ultrasonic dispersion 26min to get.
Comparative example 1
A kind of graphene heat radiation coating, the graphene heat radiation coating include the raw material of following parts by weight: graphene 15
Part, 7 parts of acetylene black, water-soluble 7 parts of benzotriazole, 48 parts of water-based acrylic resin, 16 parts of polyethylene glycol, 50 parts of water.
A kind of preparation method of graphene heat radiation coating, step are as follows: (1) mix graphene, acetylene black and water, through magnetic force
10min is stirred, suspension is made into.(2) water-soluble benzotriazole is added in suspension, and adjusting pH is 4.5, then magnetic force stirs
Mix 15min.(3) water-based acrylic resin and polyethylene glycol, magnetic agitation 30min is added in the suspension obtained by step (2);It connects
Disperse 20min under high speed shear dispersion machine, last re-ultrasonic dispersion 24min to get.
Comparative example 2
A kind of graphene heat radiation coating, the graphene heat radiation coating include the raw material of following parts by weight: graphene 15
Part, 7 parts of acetylene black, 6 parts of carbonyl diamide, 48 parts of water-based acrylic resin, 16 parts of polyethylene glycol, 50 parts of water.
A kind of preparation method of graphene heat radiation coating, step are as follows: (1) mix graphene, acetylene black and water, through magnetic force
10min is stirred, suspension is made into.(2) carbonyl diamide is added in suspension, and adjusting pH is 4.5, then magnetic agitation
15min.(3) water-based acrylic resin and polyethylene glycol, magnetic agitation 30min is added in the suspension obtained by step (2);Then
Disperse 20min under high speed shear dispersion machine, last re-ultrasonic dispersion 24min to get.
Comparative example 3
A kind of graphene heat radiation coating, the graphene heat radiation coating include the raw material of following parts by weight: graphene 15
Part, 7 parts of acetylene black, 48 parts of water-based acrylic resin, 16 parts of polyethylene glycol, 50 parts of water.
A kind of preparation method of graphene heat radiation coating, step are as follows: (1) mix graphene, acetylene black and water, through magnetic force
10min is stirred, suspension is made into.(2) adjusting pH of suspension is 4.5, then magnetic agitation 15min.(3) in step (2) gained
Water-based acrylic resin and polyethylene glycol, magnetic agitation 30min are added in suspension;Then disperse under high speed shear dispersion machine
20min, last re-ultrasonic dispersion 24min to get.
Experimental example
The embodiment 1-5 and comparative example 1-3 heat radiation coating prepared is tested for the property, as a result see the table below.
Table the performance test results
The preferred embodiment of the patent is described in detail above, but this patent is not limited to above-mentioned embodiment party
Formula within the knowledge of one of ordinary skill in the art can also be under the premise of not departing from this patent objective
It makes a variety of changes.
Claims (7)
1. a kind of graphene heat radiation coating, which is characterized in that the graphene heat radiation coating includes the raw material of following parts by weight:
10-20 parts of graphene, 5-10 parts of acetylene black, 4-8 parts of carbonyl diamide, water-soluble 5-10 parts of benzotriazole, water-based acrylic resin
40-60 parts, 10-20 parts of polyethylene glycol, 30-90 parts of water.
2. graphene heat radiation coating according to claim 1, which is characterized in that the graphene heat radiation coating includes following
The raw material of parts by weight: 12-17 parts of graphene, 6-8 parts of acetylene black, 5-7 parts of carbonyl diamide, water-soluble 6-8 parts of benzotriazole, water
Property 45-52 parts of acrylic resin, 12-18 parts of polyethylene glycol, 40-80 parts of water.
3. graphene heat radiation coating according to claim 1, which is characterized in that the graphene heat radiation coating includes following
The raw material of parts by weight: 15 parts of graphene, 7 parts of acetylene black, 6 parts of carbonyl diamide, water-soluble 7 parts of benzotriazole, water soluble acrylic acid
48 parts of resin, 16 parts of polyethylene glycol, 50 parts of water.
4. a kind of preparation method of graphene heat radiation coating a method according to any one of claims 1-3, which is characterized in that step are as follows:
(1) graphene, acetylene black and water are mixed, through magnetic agitation 5-15min, is made into suspension;(2) phosphinylidyne is added in suspension
Diamines and water-soluble benzotriazole, and adjusting pH is 3-5, then magnetic agitation 10-20min;(3) suspension obtained by step (2)
Water-based acrylic resin and polyethylene glycol, magnetic agitation 20-40min are added in liquid;Then disperse under high speed shear dispersion machine
10-30min, last re-ultrasonic dispersion 20-30min to get.
5. the preparation method of graphene heat radiation coating as claimed in claim 4, which is characterized in that step (1) is by graphene, second
Acetylene black and water mixing, through magnetic agitation 10min, are made into suspension.
6. the preparation method of graphene heat radiation coating as claimed in claim 4, which is characterized in that step (2) is in suspension
Carbonyl diamide and water-soluble benzotriazole is added, and adjusting pH is 4.5, then magnetic agitation 15min.
7. the preparation method of graphene heat radiation coating as claimed in claim 4, which is characterized in that step (3) is in step (2) institute
It obtains and water-based acrylic resin and polyethylene glycol, magnetic agitation 30min is added in suspension;Then divide under high speed shear dispersion machine
Dissipate 20min, last re-ultrasonic dispersion 24min to get.