CN108950613A - A kind of preparation method of tin plate and the application of thus obtained tin plate - Google Patents
A kind of preparation method of tin plate and the application of thus obtained tin plate Download PDFInfo
- Publication number
- CN108950613A CN108950613A CN201810882829.7A CN201810882829A CN108950613A CN 108950613 A CN108950613 A CN 108950613A CN 201810882829 A CN201810882829 A CN 201810882829A CN 108950613 A CN108950613 A CN 108950613A
- Authority
- CN
- China
- Prior art keywords
- tin
- tin plate
- preparation
- current density
- plate according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention provides the application of a kind of preparation method of tin plate and thus obtained tin plate, preparation method includes the following steps: to include that strip successively electroplated tin, soft heat, passivation and oiling is obtained finished product;Wherein, the first passage and most end passage current density are 10~20A/dm during the electrotinning2, pony-roughing pass current density is 5~10A/dm2;Pure induction reflow technique is used in the softening-melting process, the temperature of soft heat is 240~245 DEG C in the softening-melting process, and the time of soft heat is 0.5~1.5s;It is the sodium dichromate solution of 27~31g/L as passivating solution that concentration is used in the passivating process.The present invention be prepared coating is uniform, welding performance is good, with the good pole low tinplating steel sheet of PET film binding force, alternative chrome plating is applied to film-covered iron.
Description
Technical field
The invention belongs to iron and steel smelting technology field more particularly to the preparation methods and thus obtained plating of a kind of tin plate
The application of sheet tin.
Background technique
Film-covered iron is greatly paid close attention to as the revolutionary innovation in one, mental package field, and film-covered iron substrate is big at present
Part is chrome plating, chrome plating in manufacturing cost and with PET film binding force in terms of, but welding performance advantageous compared with tin plate
It is poor, only it is widely applied in top bottom cover and two-piece can.And tin plate is replaced chrome plating be applied to film-covered iron, at present technique
It is also immature, and conventional tin plate tin coating weight specification limit is generally in 1.1g/m2~11.2g/m2, and tin coating weight is lower than 1.1g/
m2Extremely low tin products application it is also less, and pole low tinplating steel sheet be primarily present in process of production it is tin plating uneven, soft
The problems such as alloying occurs for process of smelting section pure tin and base iron.
Summary of the invention
For the above problem in background technique, the main purpose of the present invention is to provide a kind of preparation methods of tin plate
And the application of thus obtained tin plate, obtain that coating is uniform, welding performance is good, good extremely low with PET film binding force
Tin amount tin plate, alternative chrome plating are applied to film-covered iron.
In order to achieve the above object, the present invention adopts the following technical scheme: a kind of preparation method of tin plate, including it is as follows
Step: including obtaining finished product for strip successively electroplated tin, soft heat, passivation and oiling;
Wherein, the first passage and most end passage current density are 10~20A/dm during the electrotinning2, interim orbit
Primary current density is 5~10A/dm2;
In the softening-melting process use pure induction reflow technique, in the softening-melting process temperature of soft heat be 240~
245 DEG C, the time of soft heat is 0.5~1.5s;
It is the sodium dichromate solution of 27~31g/L as passivating solution that concentration is used in the passivating process.
As a further preference, strip speed is 200~300m/min during the electrotinning.
As a further preference, the Sn during electrotinning2+Concentration is 10~25g/L.
As a further preference, the passivating solution temperature is 40~44 DEG C, and passivating solution pH is 4.2~4.6.
As a further preference, the passivation charge density is 3~5As/dm2。
As a further preference, sebacic acid dibutyl ester is used during the oiling, applies 5~7mg/m of oil mass2。
As a further preference, the strip is the primary or secondary cold-rolling plate that thickness specification is 0.14~0.55mm.
Another object of the present invention is to provide the tin plate as made from above-mentioned preparation method, the tin plate it is total tin plating
Amount is 0.5g/m2, pure tin amount 0.15-0.25g/m2, steel edge portion and middle part tin coating weight are very poor less than 0.1g/m2;The tin plate
With PET film binding force >=500N/m.
Another object of the present invention, which also resides in, provides the application of above-mentioned tin plate, using the tin plate as film-covered iron base
Plate.
The beneficial effects of the present invention are: the preparation method of tin plate of the present invention, the first passage and most during electrotinning
Extreme trace primary current density is 10~20A/dm2, pony-roughing pass current density is 5~10A/dm2;I.e. by first of primary current density
It is limited to 10~20A/dm2, biggish current density can make forming core rate be greater than nuclei growth rate, make obtain crystal grain more
It is careful, therefore last a time that plating is come into operation still uses high current density to guarantee that surface layer grain is fine and close, last
Passage current density is limited to 10~20A/dm2, pony-roughing pass should reduce cathodic polarization with limit forming core promote crystal grain grow up, electricity
Current density is limited to 5~10A/dm2;By the design in above-mentioned plating process of tin, the uniformity of tin coating is improved.In addition,
The present invention uses pure induction reflow technique in the softening-melting process, and the temperature of soft heat is 240~245 in the softening-melting process
DEG C, the time of soft heat is 0.5~1.5s;In order to improve the problem of low tin coating weight welding performance difference, imitated by using above-mentioned heating
Rate is fast and controls induction reflow heating method with high accuracy, and cooperates suitable reflowing temperature and Reflowing Time, both ensure that plating
The corrosion resisting property of sheet tin makes low tin coating weight tin plate meet welding requirements again;Moreover, being chemically combined to improve with PET film, this hair
It is bright that electrochemical passivation is carried out as passivating solution using the high concentration sodium dichromate of 27~31g/L after soft heat, so that of the invention
Tin plate and PET film binding force are good.
Specific embodiment
The present invention solves existing by providing a kind of preparation method of tin plate and the application of thus obtained tin plate
It the production technology of pole low tinplating steel sheet and its applies in the defects of film-covered iron.
To solve the above-mentioned problems, the main thought of the embodiment of the present invention is:
The preparation method of tin plate of the embodiment of the present invention includes the following steps: to include by strip successively electroplated tin, soft
Molten, passivation and oiling, obtain finished product;
Wherein, the first passage and most end passage current density are 10~20A/dm during the electrotinning2, interim orbit
Primary current density is 5~10A/dm2;
In the softening-melting process use pure induction reflow technique, in the softening-melting process temperature of soft heat be 240~
245 DEG C, the time of soft heat is 0.5~1.5s;
It is the sodium dichromate solution of 27~31g/L as passivating solution that concentration is used in the passivating process.
Above-mentioned strip can also be used conventional cleaning treatment technique removal surface Residual oil and oxide layer and restore before electrotinning
Surface-active state, such as lye hydro-peening, electrolytic alkaline cleaning.
Since tin plate sheet surface is microcosmic uneven with certain roughness, it will lead to local current densities during electrotinning
Unevenly, it needs first passage to come into operation in electroplating bath to increase cathodic polarization and improves nucleation rate, reduction current unevenness is even
Problem increases crystal grain coverage rate, while being considered as avoiding the generation of evolving hydrogen reaction, first of primary current density limitations 10~
20A/dm2, biggish current density can make forming core rate be greater than nuclei growth rate, make obtain crystal grain it is more careful, because
Last a time that this plating is come into operation still uses high current density to guarantee that surface layer grain is fine and close, and last a time electric current is close
Degree is limited to 10~20A/dm2, pony-roughing pass should reduce cathodic polarization with limit forming core promote crystal grain grow up, current density limit
In 5~10A/dm2.To guarantee that electroplating efficiency is stablized 85% or more, and guarantee that electro-deposition matches with current density, strip fortune
Scanning frequency degree should be set in 200~300m/min, Sn in electroplate liquid2+Concentration is set in 10~25g/L.
Softening-melting process should eliminate the pin hole after electrotinning in tin layers, formed between tin layers and iron substrate have it is certain resistance to
The alloy-layer of corrosion keeps pure tin amount in 0.15~0.25g/m again2, good surface brightness and welding performance are obtained, therefore
High, the fast induction reflow heating method of heating speed using control temperature accuracy, limits 240~245 DEG C of reflowing temperature, when soft heat
Between 0.5~1.5s.
To promote the hydrated chromium oxide that can be firmly combined with polar group on PET film to be formed in passivating process, passivating solution is dense
Degree is set in 27~31g/L, and passivating solution temperature is set in 40~44 DEG C, and passivating solution pH value is set in 4.2~4.6, is passivated charge
Density is set in 3~5As/dm2。
In addition, in order to guarantee to avoid a generation for rust that from should carrying out at oiling in inventory and transportational process after low tin coating weight output
Reason, oiling type use sebacic acid dibutyl ester, apply oil mass and are set in 5~7mg/m2。
In conclusion the embodiment of the present invention passes through in such a way that electroplating technology section is using high current forming core, low current crystallization
And strip speed and Sn that matching is certain2+Concentration ensure that the uniformity that tin layers are distributed under low tin amount, while soft using incuding
Molten heating method quickly accurately reaches set temperature, and coating pure tin amount is in 0.15~0.25g/m after ensure that alloying2, make
The tin plate has excellent welding performance and corrosion resisting property, and passivation guarantees passivation using high sodium dichromate solution and current density
The amount and structure of film are obtained the adhesion performance excellent with PET film, and can both be protected before strip coiling using appropriate DOS oil
Card surface quality in turn avoids coating bad problem in coating process.
It is 0.5g/m that total tin coating weight, which can be obtained, in the embodiment of the present invention2Pole low tinplating steel sheet, the present invention in for save life
It produces cost consideration and replaces chrome plating to be applied to film-covered iron with pole low tinplating steel sheet,
Conventional tin plate tin coating weight specification limit is generally in 1.1g/m2~11.2g/m2, tin coating weight is low in currently available technology
In 1.1g/m2Extremely low tin products application it is also less, pole low tinplating steel sheet is primarily present tin plating unevenness in process of production
Alloying, which occurs, for even, soft-melting process section pure tin and base iron causes coating pure tin amount too low, and alloy-layer and substrate exposed area increase,
In subsequent tank welding process processed contact resistance it is excessive cause bad welding performance, rust spot incidence in inventory and transportational process
The problems such as high, in conjunction with the development trend of tin plate market coating thinnedization, the embodiment of the present invention devises above-mentioned tin coating weight 0.5g/
m2Extremely low tin tin plate, welding performance uniform with coating is good, is greater than the advantage of 500N/m with PET film binding force, can
It substitutes chrome plating and is applied to film-covered iron.
In order to which above and other purpose, feature and the advantage of the present invention can be clearer and more comprehensible, several implementations are cited below particularly
Example, to illustrate the preparation method of tin plate of the present invention and the application of thus obtained tin plate.Making following explanation is
In order to enable anyone skilled in the art can manufacture and using the present invention.For specific embodiment and purposes explanation only
It is provided as example.To those skilled in the art, the embodiments described herein can be variously changed and is combined, and
And general principles defined herein can be applied and other embodiments and purposes without departing from the scope of the invention.
Therefore, the present invention be not intended to by it is described and show embodiment limit, but should according to herein disclosed principles and spy
Levy consistent widest range.
Embodiment 1
Using once cold rolling cover annealing plate T-3BA, thickness specification 0.35mm, width specifications 980mm, successively sprayed by lye
Wash, electrolytic alkaline cleaning, plating process of tin, rinsing extract, soft heat, water quenching, passivation, rinsing, drying, oiling, batch to obtain finished product;Its
Middle electroplating technology section strip steel speed of service 280m/min, 3 passages that come into operation, 6 pieces of soluble anodes, upper and lower surface consistent each 3
A rectifier control, current density use 10A/dm2+8A/dm2+10A/dm2Mode, Sn2+Concentration 20g/L, actual measurement plating effect
Rate 87%;240 DEG C of reflowing temperature, Reflowing Time 1s, 85 DEG C of water-quenched slag are used in soft heat section, then passivation technology section passivation electricity
Lotus density sets 3As/dm2, sodium dichromate concentration survey 28g/L, pH4.3,42.4 DEG C of passivating solution temperature, oiler setting value
6mg/m2, it is batched by coiling machine, it is final to obtain the film-covered iron total tin coating weight 0.51g/m in tin plate upper surface2, upper surface alloy
Tin amount 0.31g/m2, the total tin coating weight 0.58g/m in lower surface2, lower surface alloy tin amount 0.36g/m2, total tin coating weight pole in strip edge
Difference is less than 0.1g/m2, upper surface chromium content 5.5mg/m2, lower surface chromium content 5.8mg/m2, when user uses in conjunction with PET film
Peel strength 600N/m.
Embodiment 2
Using the secondary cold-rolling plate DR-7M BA of thin gauge, thickness specification 0.23mm, width specifications 950mm successively pass through
Lye hydro-peening, electrolytic alkaline cleaning, plating process of tin, rinsing extract, soft heat, water quenching, passivation, rinsing, drying, oiling, wherein being electroplated
Process section strip speed 300m/min, 3 passages that come into operation, 6 pieces of soluble anodes, consistent each 3 rectifications of upper and lower surface
Device control, current density use 13A/dm2+5A/dm2+13A/dm2Mode, Sn2+Concentration 22g/L surveys electroplating efficiency 90%;
245 DEG C, Reflowing Time 0.84s of soft-melting process section reflowing temperature, 90 DEG C of water-quenched slag;Then passivation technology section is passivated charge density
Set 4As/dm2, sodium dichromate concentration survey 28g/L, pH4.2,44.3 DEG C of passivating solution temperature, oiler setting value 6mg/m2, warp
Coiling machine is crossed to batch, it is final to obtain the film-covered iron total tin coating weight 0.51g/m in tin plate upper surface2, upper surface alloy tin amount
0.34g/m2, the total tin coating weight 0.56g/m in lower surface2, lower surface alloy tin amount 0.35g/m2, total tin coating weight is very poor small in strip edge
In 0.1g/m2, upper surface chromium content 6.2mg/m2, lower surface chromium content 6.5mg/m2, removed in conjunction with PET film when user uses
Intensity 550N/m, spark is small when tubbing is welded, even weld, no rosin joint dry joint phenomenon.
Embodiment 3
Using once cold rolling plate T-4CA, thickness specification 0.2mm, width specifications 858mm, successively by lye hydro-peening, electrolysis
Alkali cleaning, plating process of tin, rinsing extract, soft heat, water quenching, passivation, rinsing, drying, oiling, wherein electroplating technology section strip steel run
Speed 300m/min, 3 passages that come into operation, 6 pieces of soluble anodes, the consistent each 3 rectifiers control of upper and lower surface, electric current are close
Degree uses 12A/dm2+8A/dm2+12A/dm2Mode, Sn2+Concentration 23g/L surveys electroplating efficiency 85%;Soft-melting process section is soft
240 DEG C of melting temperatur, Reflowing Time 0.84s, 90 DEG C of water-quenched slag, then passivation technology section passivation charge density sets 4As/dm2,
Sodium dichromate concentration survey 26.5g/L, pH4.3,43.3 DEG C of passivating solution temperature, oiler setting value 6mg/m2, by coiling machine
It batches, it is final to obtain film-covered iron tin plate, the total tin coating weight 0.49g/m in upper surface2, upper surface alloy tin amount 0.34g/m2, following table
The total tin coating weight 0.55g/m in face2, lower surface alloy tin amount 0.35g/m2, tin coating weight is very poor in strip edge is less than 0.1g/m2, upper surface
Chromium content 6.4mg/m2, lower surface chromium content 6.2mg/m2, peel strength 570N/m, tank weldering processed in conjunction with PET film when user uses
Spark is small when connecing, even weld, no rosin joint dry joint phenomenon.
Embodiment 4
Using once cold rolling cover annealing plate T-3BA, thickness specification 0.14mm, width specifications 960mm, successively sprayed by lye
Wash, electrolytic alkaline cleaning, plating process of tin, rinsing extract, soft heat, water quenching, passivation, rinsing, drying, oiling, batch to obtain finished product;Its
Middle electroplating technology section strip steel speed of service 250m/min, 3 passages that come into operation, 6 pieces of soluble anodes, upper and lower surface consistent each 3
A rectifier control, current density use 15A/dm2+5A/dm2+15A/dm2Mode, Sn2+Concentration 10g/L, actual measurement plating effect
Rate 87%;243 DEG C of reflowing temperature, Reflowing Time 0.5s, 80 DEG C of water-quenched slag are used in soft heat section, then passivation technology section is passivated
Charge density sets 3.5As/dm2, sodium dichromate concentration survey 26g/L, pH4.4,40 DEG C of passivating solution temperature, oiler setting value
6mg/m2, it is batched by coiling machine, it is final to obtain the film-covered iron total tin coating weight 0.52g/m in tin plate upper surface2, upper surface alloy
Tin amount 0.32g/m2, the total tin coating weight 0.56g/m in lower surface2, lower surface alloy tin amount 0.34g/m2, tin coating weight is very poor in strip edge
Less than 0.1g/m2, upper surface chromium content 5.6mg/m2, lower surface chromium content 5.6mg/m2, shelled in conjunction with PET film when user uses
From intensity 630N/m.
Embodiment 5
Using the secondary cold-rolling plate DR-7M BA of thin gauge, thickness specification 0.42mm, width specifications 960mm successively pass through
Lye hydro-peening, electrolytic alkaline cleaning, plating process of tin, rinsing extract, soft heat, water quenching, passivation, rinsing, drying, oiling, wherein being electroplated
Process section strip speed 220m/min, 3 passages that come into operation, 6 pieces of soluble anodes, consistent each 3 rectifications of upper and lower surface
Device control, current density use 18A/dm2+6A/dm2+15A/dm2Mode, Sn2+Concentration 18g/L surveys electroplating efficiency 90%;
242 DEG C, Reflowing Time 1.0s of soft-melting process section reflowing temperature, 85 DEG C of water-quenched slag;Then passivation technology section charge density density
Set 3As/dm2, sodium dichromate concentration survey 27.5g/L, pH4.5,41.3 DEG C of passivating solution temperature, oiler setting value 5mg/m2,
It is batched by coiling machine, it is final to obtain the film-covered iron total tin coating weight 0.51g/m in tin plate upper surface2, upper surface alloy tin amount
0.34g/m2, the total tin coating weight 0.55g/m in lower surface2, lower surface alloy tin amount 0.35g/m2, tin coating weight is very poor in strip edge is less than
0.1g/m2, upper surface chromium content 6.2mg/m2, lower surface chromium content 6.5mg/m2, removed in conjunction with PET film when user uses strong
560N/m is spent, spark is small when tubbing is welded, even weld, no rosin joint dry joint phenomenon.
Embodiment 6
Using once cold rolling plate T-4CA, thickness specification 0.55mm, width specifications 850mm, successively pass through lye hydro-peening, electricity
Solution alkali cleaning, plating process of tin, rinsing extract, soft heat, water quenching, passivation, rinsing, drying, oiling, wherein electroplating technology section strip steel transport
Scanning frequency degree 200m/min, 3 passages that come into operation, 6 pieces of soluble anodes, the consistent each 3 rectifiers control of upper and lower surface, electric current
Density uses 20A/dm2+10A/dm2+20A/dm2Mode, Sn2+Concentration 25g/L surveys electroplating efficiency 85%;Soft-melting process section
245 DEG C of reflowing temperature, Reflowing Time 1.5s, 90 DEG C of water-quenched slag, then passivation technology section passivation charge density sets 5As/
Dm2, sodium dichromate concentration survey 31g/L, pH4.6,44 DEG C of passivating solution temperature, oiler setting value 7mg/m2, by coiling machine
It batches, it is final to obtain film-covered iron tin plate, the total tin coating weight 0.49g/m in upper surface2, upper surface alloy tin amount 0.34g/m2, following table
The total tin coating weight 0.55g/m in face2, lower surface alloy tin amount 0.35g/m2, tin coating weight is very poor in strip edge is less than 0.1g/m2, upper surface
Chromium content 6.4mg/m2, lower surface chromium content 6.2mg/m2, peel strength 580N/m, tank weldering processed in conjunction with PET film when user uses
Spark is small when connecing, even weld, no rosin joint dry joint phenomenon.
In the various embodiments described above, total tin coating weight and pure tin amount are according to " GB/T1838-2008 ferrostan tin coating weight examination
Proved recipe method " measurement, total tin coating weight=pure tin amount+alloy tin amount.
The binding force of tin plate and PET film is surveyed according to " GB/T 2791-1995 adhesive T peeling strength test method "
Amount.
Technical solution in above-mentioned the embodiment of the present application, at least have the following technical effects or advantages:
For improve tin coating uniformity, the present invention design in electroplating technology in using head and the tail passage use high current it is close
Degree guarantees that forming core and grain size are careful, and pony-roughing pass guarantees that crystal grain is grown up using low current density, and by certain tin from
Son and strip speed guarantee higher electroplating efficiency;In order to improve the problem of low tin coating weight welding performance difference, by using heating
Efficiency is fast and controls induction reflow heating method with high accuracy, and cooperates suitable reflowing temperature and Reflowing Time, both ensure that
The corrosion resisting property of tin plate makes low tin coating weight tin plate meet welding requirements again;For improve with PET film be chemically combined, soft heat it
Afterwards in such a way that the sodium dichromate of high concentration carries out electrochemical passivation, and design the passivation to match with high concentration sodium dichromate
Technological parameter is to meet service requirement;Additionally, due to the table of low tin coating weight tin plate rust spot and scuffing in storage and transportational process
Planar defect incidence is higher, therefore the generation of surface defect can be reduced using the DOS oil of higher caliper.
Above-described specific embodiment has carried out further the purpose of the present invention, technical scheme and beneficial effects
It is described in detail, it should be understood that being not limited to this hair the foregoing is merely a specific embodiment of the invention
Bright, all within the spirits and principles of the present invention, any modification, equivalent substitution, improvement and etc. done should be included in the present invention
Protection scope within.
Claims (10)
1. a kind of preparation method of tin plate, characterized by the following steps: including by strip successively electroplated tin, soft
Molten, passivation and oiling, obtain finished product;
Wherein, the first passage and most end passage current density are 10~20A/dm during the electrotinning2, pony-roughing pass electricity
Current density is 5~10A/dm2;
Pure induction reflow technique is used in the softening-melting process, the temperature of soft heat is 240~245 in the softening-melting process
DEG C, the time of soft heat is 0.5~1.5s;
It is the sodium dichromate solution of 27~31g/L as passivating solution that concentration is used in the passivating process.
2. the preparation method of tin plate according to claim 1, it is characterised in that: strip is transported during the electrotinning
200~300m/min of scanning frequency degree.
3. the preparation method of tin plate according to claim 1, it is characterised in that: the Sn during electrotinning2+It is dense
Degree is 10~25g/L.
4. the preparation method of tin plate according to claim 1, it is characterised in that: the passivating solution temperature is 40~44
℃。
5. the preparation method of tin plate according to claim 1, it is characterised in that: the passivating solution pH is 4.2~4.6.
6. the preparation method of tin plate according to claim 1, it is characterised in that: the passivation charge density be 3~
5As/dm2。
7. the preparation method of tin plate according to claim 1, it is characterised in that: use certain herbaceous plants with big flowers two during the oiling
Sour dibutyl ester, painting oil mass are 5~7mg/m2。
8. the preparation method of tin plate according to claim 1, it is characterised in that: the strip is that thickness specification is 0.14
The primary or secondary cold-rolling plate of~0.55mm.
9. the tin plate as made from claim 1-8 described in any item preparation methods, it is characterised in that: the tin plate it is total
Tin coating weight is 0.5g/m2, pure tin amount 0.15-0.25g/m2, steel edge portion and middle part tin coating weight are very poor less than 0.1g/m2;The plating
Sheet tin and PET film binding force >=500N/m.
10. the application of the tin plate as made from claim 1-8 described in any item preparation methods, it is characterised in that: will be described
Tin plate is as film-covered iron substrate.