CN108926504A - A kind of environmental protection face mask substrate material and its preparation method and application - Google Patents

A kind of environmental protection face mask substrate material and its preparation method and application Download PDF

Info

Publication number
CN108926504A
CN108926504A CN201810852048.3A CN201810852048A CN108926504A CN 108926504 A CN108926504 A CN 108926504A CN 201810852048 A CN201810852048 A CN 201810852048A CN 108926504 A CN108926504 A CN 108926504A
Authority
CN
China
Prior art keywords
parts
face mask
mask substrate
substrate material
mixed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810852048.3A
Other languages
Chinese (zh)
Inventor
黄志优
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201810852048.3A priority Critical patent/CN108926504A/en
Publication of CN108926504A publication Critical patent/CN108926504A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of environmentally friendly face mask substrate materials and its preparation method and application.The environmental protection face mask substrate material includes the component of following parts by weight: 20-30 parts of polylactic acid, 20-30 parts of jackfruit shell, 20-30 parts of diatomite, 10-15 parts of perilla leaf powder, 3-8 parts of limonin, 10-17 parts of raspberry seed oil.Environmentally friendly face mask substrate material raw material of the invention is that polylactic acid, jackfruit shell, diatomite, perilla leaf powder, limonin and raspberry seed oil, raw material are easy to get, and reduces preparation cost；The face mask substrate material being prepared not only has preferable fungistatic effect；And after facial mask use, face mask substrate material can be used for preparing feed addictive, reduces snakehead skin-ulcer morbidity and mortality, realizes the secondary use of face mask substrate material, avoid a large amount of wasting of resources, very environmentally friendly.

Description

A kind of environmental protection face mask substrate material and its preparation method and application
Technical field
The present invention relates to a kind of face mask substrate material, specifically a kind of environmental protection face mask substrate material and its preparation method and application.
Background technique
Facial mask is a kind of skin-protection product.The form of facial mask mainly have mud paste type facial mask, tear-pull facial mask, gel-type facial mask, Four kinds of hygenic towelette type facial mask.It is currently on the market since hygenic towelette type facial mask has many advantages, such as that easy to carry, deposited rear face cleaning is convenient Main product, obtained the generally approval of consumer.Hygenic towelette type facial mask includes facial mask liquid and the facial mask for infiltrating facial mask liquid Substrate, face mask substrate material are the carriers for adsorbing facial mask liquid.Currently on the market widely used face mask substrate material mostly use non-woven fabrics, Silk, tencel, biological fiber, nonwoven fabric material.The market potential of pursuit with people to skin care, facial mask is constantly mined, People also increasingly increase the consumption of facial mask.But due to facial mask use after, face paper is dropped, and causes a large amount of rubbish Rubbish, while a large amount of natural resources is consumed, it is not environmentally friendly enough.Therefore, it is necessary to provide a kind of environmentally friendly face mask substrate material and its preparation Methods and applications.
Summary of the invention
The purpose of the present invention is to provide a kind of environmentally friendly face mask substrate materials and its preparation method and application, to solve above-mentioned background The problem of being proposed in technology.
To achieve the above object, the invention provides the following technical scheme:
A kind of environmental protection face mask substrate material, the component including following parts by weight: 20-30 parts of polylactic acid, jackfruit shell 20-30 Part, 20-30 parts of diatomite, 10-15 parts of perilla leaf powder, 3-8 parts of limonin, 10-17 parts of raspberry seed oil.
As a further solution of the present invention: the component including following parts by weight: 22-26 parts of polylactic acid, jackfruit shell 22-25 parts, 23-27 parts of diatomite, 11-13 parts of perilla leaf powder, 4-7 parts of limonin, 12-15 parts of raspberry seed oil.
As a further solution of the present invention: the component including following parts by weight: 24 parts of polylactic acid, jackfruit shell 23 Part, 13 parts of 25 parts of diatomite, 12 parts of perilla leaf powder, 6 parts of limonin, raspberry seed oil.
A kind of preparation method of environmental protection face mask substrate material, comprising the following steps:
(1) pretreatment of raw material:
A. diatomite is mixed with its 2-4 times water, is placed at 32-40 DEG C and is uniformly mixed, obtains diatomite slurry；
B. jackfruit shell is placed at 40-55 DEG C after drying, is cut into the fritter of 0.5-1cm, be placed in raspberry seed oil and fry 5-8min drains oil content after taking-up, obtains blocky jackfruit shell to black；
C, perilla leaf powder is mixed with its 4-8 times water, is placed at 80-100 DEG C and is stirred 22-30min, obtains purple perilla Leaf slurry；
(2) perilla leaf slurry is mixed with limonin, is placed at 75-85 DEG C and is stirred to react 40-55min；
(3) blocky jackfruit shell is placed at 90-100 DEG C and dries 5-10min, with mass fraction be 0.1-0.2% after taking-up Sodium bicarbonate solution elute blocky jackfruit shell, then be washed to pH with deionized water and be in neutrality；Then by blocky jackfruit shell Pulverize and sieve 100-200 mesh after drying；
(4) diatomite slurry is uniformly mixed with step (2) gains, step (3) gains, obtains mixed slurry；
(5) it after mixing polylactic acid and mixed slurry, feeds the mixture into double screw extruder and squeezes out, twin-screw extrusion Machine temperature is set as 158-182 DEG C；Later by Mask Molding Machine form to get.
As a further solution of the present invention: the pretreatment of step (1) raw material:
A. diatomite is mixed with its 3 times water, is placed at 36 DEG C and is uniformly mixed, obtains diatomite slurry；
B. jackfruit shell is placed at 48 DEG C after drying, is cut into the fritter of 0.6m, be placed in raspberry seed oil and fry 7min extremely Black drains oil content after taking-up, obtains blocky jackfruit shell；
C, perilla leaf powder is mixed with its 6 times water, is placed at 92 DEG C and is stirred 27min, obtains perilla leaf slurry.
As a further solution of the present invention: step (2) mixes perilla leaf slurry with limonin, is placed at 82 DEG C and stirs Mix reaction 46min.
As a further solution of the present invention: blocky jackfruit shell is placed at 97 DEG C by step (3) dries 6min, uses after taking-up The sodium bicarbonate solution that mass fraction is 0.12% elutes blocky jackfruit shell, then is washed to pH with deionized water and is in neutrality；So Afterwards 150 mesh will be pulverized and sieved after the drying of blocky jackfruit shell.
A kind of application of the environmental protection face mask substrate material in cosmetics, feed addictive.
Compared with prior art, the beneficial effects of the present invention are:
Environmentally friendly face mask substrate material raw material of the invention be polylactic acid, jackfruit shell, diatomite, perilla leaf powder, limonin and Raspberry seed oil, raw material are easy to get, and reduce preparation cost；The face mask substrate material being prepared not only has preferable fungistatic effect；And After facial mask use, face mask substrate material can be used for preparing feed addictive, reduce snakehead skin-ulcer morbidity and mortality, realize The secondary use of face mask substrate material, avoids a large amount of wasting of resources, very environmentally friendly.
Specific embodiment
The technical solution of the patent is explained in further detail With reference to embodiment.
Embodiment 1
A kind of environmental protection face mask substrate material, the component including following parts by weight: 20 parts of polylactic acid, 20 parts of jackfruit shell, diatom 20 parts of soil, 10 parts of perilla leaf powder, 3 parts of limonin, 10 parts of raspberry seed oil.
A kind of preparation method of environmental protection face mask substrate material, comprising the following steps:
(1) pretreatment of raw material:
A. diatomite is mixed with its 2 times water, is placed at 32 DEG C and is uniformly mixed, obtains diatomite slurry；
B. jackfruit shell is placed at 40 DEG C after drying, is cut into the fritter of 0.5cm, be placed in raspberry seed oil and fry 5min extremely Black drains oil content after taking-up, obtains blocky jackfruit shell；
C, perilla leaf powder is mixed with its 4 times water, is placed at 80 DEG C and is stirred 22min, obtains perilla leaf slurry；
(2) perilla leaf slurry is mixed with limonin, is placed at 75 DEG C and is stirred to react 40min；
(3) blocky jackfruit shell is placed at 90 DEG C and dries 5min, the sodium bicarbonate for being 0.1% with mass fraction after taking-up is molten Liquid elutes blocky jackfruit shell, then is washed to pH with deionized water and is in neutrality；Then it will crushed after the drying of blocky jackfruit shell Sieve 100 mesh；
(4) diatomite slurry is uniformly mixed with step (2) gains, step (3) gains, obtains mixed slurry；
(5) it after mixing polylactic acid and mixed slurry, feeds the mixture into double screw extruder and squeezes out, twin-screw extrusion Machine temperature is set as 158-182 DEG C；Later by Mask Molding Machine form to get.
Embodiment 2
A kind of environmental protection face mask substrate material, the component including following parts by weight: 30 parts of polylactic acid, 30 parts of jackfruit shell, diatom 30 parts of soil, 15 parts of perilla leaf powder, 8 parts of limonin, 17 parts of raspberry seed oil.
A kind of preparation method of environmental protection face mask substrate material, comprising the following steps:
(1) pretreatment of raw material:
A. diatomite is mixed with its 4 times water, is placed at 40 DEG C and is uniformly mixed, obtains diatomite slurry；
B. jackfruit shell is placed at 55 DEG C after drying, is cut into the fritter of 1cm, be placed in raspberry seed oil and fry 8min to black Color drains oil content after taking-up, obtains blocky jackfruit shell；
C, perilla leaf powder is mixed with its 8 times water, is placed at 100 DEG C and is stirred 30min, obtains perilla leaf slurry；
(2) perilla leaf slurry is mixed with limonin, is placed at 85 DEG C and is stirred to react 55min；
(3) blocky jackfruit shell is placed at 100 DEG C and dries 10min, the sodium bicarbonate for being 0.2% with mass fraction after taking-up Solution elutes blocky jackfruit shell, then is washed to pH with deionized water and is in neutrality；Then it will be crushed after the drying of blocky jackfruit shell Be sieved 200 mesh；
(4) diatomite slurry is uniformly mixed with step (2) gains, step (3) gains, obtains mixed slurry；
(5) it after mixing polylactic acid and mixed slurry, feeds the mixture into double screw extruder and squeezes out, twin-screw extrusion Machine temperature is set as 158-182 DEG C；Later by Mask Molding Machine form to get.
Embodiment 3
A kind of environmental protection face mask substrate material, the component including following parts by weight: 24 parts of polylactic acid, 23 parts of jackfruit shell, diatom 25 parts of soil, 12 parts of perilla leaf powder, 6 parts of limonin, 13 parts of raspberry seed oil.
A kind of preparation method of environmental protection face mask substrate material, comprising the following steps:
(1) pretreatment of raw material:
A. diatomite is mixed with its 3 times water, is placed at 36 DEG C and is uniformly mixed, obtains diatomite slurry；
B. jackfruit shell is placed at 48 DEG C after drying, is cut into the fritter of 0.6m, be placed in raspberry seed oil and fry 7min extremely Black drains oil content after taking-up, obtains blocky jackfruit shell；
C, perilla leaf powder is mixed with its 6 times water, is placed at 92 DEG C and is stirred 27min, obtains perilla leaf slurry.
(2) perilla leaf slurry is mixed with limonin, is placed at 82 DEG C and is stirred to react 46min.
(3) blocky jackfruit shell is placed at 97 DEG C and dries 6min, the sodium bicarbonate for being 0.12% with mass fraction after taking-up Solution elutes blocky jackfruit shell, then is washed to pH with deionized water and is in neutrality；Then it will be crushed after the drying of blocky jackfruit shell Be sieved 150 mesh.
(4) diatomite slurry is uniformly mixed with step (2) gains, step (3) gains, obtains mixed slurry；
(5) it after mixing polylactic acid and mixed slurry, feeds the mixture into double screw extruder and squeezes out, twin-screw extrusion Machine temperature is set as 158-182 DEG C；Later by Mask Molding Machine form to get.
Embodiment 4
A kind of environmental protection face mask substrate material, the component including following parts by weight: 22 parts of polylactic acid, 22 parts of jackfruit shell, diatom 23 parts of soil, 11 parts of perilla leaf powder, 4 parts of limonin, 12 parts of raspberry seed oil.
Embodiment 5
A kind of environmental protection face mask substrate material, the component including following parts by weight: 26 parts of polylactic acid, 25 parts of jackfruit shell, diatom 27 parts of soil, 13 parts of perilla leaf powder, 7 parts of limonin, 15 parts of raspberry seed oil.
Comparative example 1
Except jackfruit shell is not contained in raw material, other preparation processes and embodiment 3 are consistent.
Comparative example 2
Only contain jackfruit shell in raw material.
Comparative example 3
Raw material and embodiment 3 are consistent, the preparation method comprises the following steps: together after mixing by all raw materials, twin-screw extrusion is added It is squeezed out in machine, double screw extruder temperature is set as 158-182 DEG C；Later by Mask Molding Machine form to get.
Experimental example 1
Fungistatic effect experiment is carried out to the facial mask of embodiment 1-3 and comparative example 1-3, the results are shown in Table 1.
Table 1
Project Embodiment 1 Embodiment 2 Embodiment 3 Comparative example 1 Comparative example 2 Comparative example 3
Escherichia coli bacteriostasis rate % 99.8 100 100 62.1 29.8 74.2
Staphylococcus aureus bacteriostasis rate % 98.9 99.1 99.5 59.8 26.5 68.3
Embodiment 2
The face mask substrate material can be used for adsorbing the facial mask liquid of pure plant Traditional-Chinese-medicine-type.Face mask substrate material is placed at 55-65 DEG C and is dried, It is then comminuted into end, obtains feed addictive.After actually using facial mask, first facial mask liquid can be squeezed out, then by face mask substrate material into Row drying.
It is basic feed with commercially available common Snakeheaded fish feeding stuff, test 1-3 group continuously feeds 20 days facial masks of 1-3 containing embodiment respectively The Snakeheaded fish feeding stuff of the feed addictive of substrate preparation, then moves on to and feeds 10 days common Snakeheaded fish feeding stuffs, is treated with 30 days for a prevention Journey.Feeding method according to this continuously feeds the 2-3 course for the treatment of to test group snakehead.Control group 1-3 group continuously feeds 20 days containing comparison respectively The Snakeheaded fish feeding stuff of the feed addictive of example 1-3 face mask substrate material preparation, then moves on to and feeds 10 days common Snakeheaded fish feeding stuffs, with 30 days for one A prevention course for the treatment of.Feeding method according to this continuously feeds the 2-3 course for the treatment of to control group snakehead.During test, blank control group snakehead is held It is continuous to feed commercially available common Snakeheaded fish feeding stuff.Test group, control group and blank control group snakehead skin-ulcer morbidity number are recorded simultaneously Amount and The dead quantity.10 days after the prevention course for the treatment of, comparative analysis test group, control group and blank control group snakehead body surface fester Disease morbidity and mortality, the results are shown in Table 2.
Table 2
Project Disease incidence % Death rate %
Test 1 group 3.1 0
Test 2 groups 3.6 1
Test 3 groups 2.8 0
Compare 1 group 10.3 4.2
Compare 2 groups 12.6 5.7
Compare 3 groups 7.2 3.3
Blank control group 12.5 5.8
The preferred embodiment of the patent is described in detail above, but this patent is not limited to above-mentioned embodiment party Formula within the knowledge of one of ordinary skill in the art can also be under the premise of not departing from this patent objective It makes a variety of changes.

Claims (8)

1. a kind of environmental protection face mask substrate material, which is characterized in that the component including following parts by weight: 20-30 parts of polylactic acid, jackfruit 20-30 parts of shell, 20-30 parts of diatomite, 10-15 parts of perilla leaf powder, 3-8 parts of limonin, 10-17 parts of raspberry seed oil.
2. environmental protection face mask substrate material according to claim 1, which is characterized in that the component including following parts by weight: poly- cream 22-26 parts sour, 22-25 parts of jackfruit shell, 23-27 parts of diatomite, 11-13 parts of perilla leaf powder, 4-7 parts of limonin, raspberry seed It is 12-15 parts oily.
3. environmental protection face mask substrate material according to claim 1, which is characterized in that the component including following parts by weight: poly- cream 24 parts of acid, 23 parts of jackfruit shell, 25 parts of diatomite, 12 parts of perilla leaf powder, 6 parts of limonin, 13 parts of raspberry seed oil.
4. a kind of preparation method of environmentally friendly face mask substrate material a method according to any one of claims 1-3, which is characterized in that including following step It is rapid:
(1) pretreatment of raw material:
A. diatomite is mixed with its 2-4 times water, is placed at 32-40 DEG C and is uniformly mixed, obtains diatomite slurry；
B. jackfruit shell is placed at 40-55 DEG C after drying, is cut into the fritter of 0.5-1cm, be placed in raspberry seed oil and fry 5- 8min drains oil content after taking-up, obtains blocky jackfruit shell to black；
C, perilla leaf powder is mixed with its 4-8 times water, is placed at 80-100 DEG C and is stirred 22-30min, obtain perilla leaf slurry Material；
(2) perilla leaf slurry is mixed with limonin, is placed at 75-85 DEG C and is stirred to react 40-55min；
(3) blocky jackfruit shell is placed at 90-100 DEG C and dries 5-10min, the carbon for being 0.1-0.2% with mass fraction after taking-up Sour hydrogen sodium solution elutes blocky jackfruit shell, then is washed to pH with deionized water and is in neutrality；Then blocky jackfruit shell is dried After pulverize and sieve 100-200 mesh；
(4) diatomite slurry is uniformly mixed with step (2) gains, step (3) gains, obtains mixed slurry；
(5) it after mixing polylactic acid and mixed slurry, feeds the mixture into double screw extruder and squeezes out, double screw extruder temperature Degree is set as 158-182 DEG C；Later by Mask Molding Machine form to get.
5. the preparation method of environmental protection face mask substrate material as claimed in claim 4, which is characterized in that the pretreatment of step (1) raw material:
A. diatomite is mixed with its 3 times water, is placed at 36 DEG C and is uniformly mixed, obtains diatomite slurry；
B. jackfruit shell is placed at 48 DEG C after drying, is cut into the fritter of 0.6m, be placed in raspberry seed oil and fry 7min to black, Oil content is drained after taking-up, obtains blocky jackfruit shell；
C, perilla leaf powder is mixed with its 6 times water, is placed at 92 DEG C and is stirred 27min, obtains perilla leaf slurry.
6. the preparation method of environmental protection face mask substrate material as claimed in claim 4, which is characterized in that step (2) is by perilla leaf slurry It is mixed with limonin, is placed at 82 DEG C and is stirred to react 46min.
7. the preparation method of environmental protection face mask substrate material as claimed in claim 4, which is characterized in that step (3) is by blocky jackfruit Shell, which is placed at 97 DEG C, dries 6min, elutes blocky jackfruit shell with the sodium bicarbonate solution that mass fraction is 0.12% after taking-up, then PH is washed to deionized water to be in neutrality；Then 150 mesh will be pulverized and sieved after the drying of blocky jackfruit shell.
8. a kind of application of environmentally friendly face mask substrate material a method according to any one of claims 1-3 in cosmetics, feed addictive.
CN201810852048.3A 2018-07-30 2018-07-30 A kind of environmental protection face mask substrate material and its preparation method and application Pending CN108926504A (en)