CN108913048A - A kind of antistatic Anti-skid adhesive tape - Google Patents
A kind of antistatic Anti-skid adhesive tape Download PDFInfo
- Publication number
- CN108913048A CN108913048A CN201710256081.5A CN201710256081A CN108913048A CN 108913048 A CN108913048 A CN 108913048A CN 201710256081 A CN201710256081 A CN 201710256081A CN 108913048 A CN108913048 A CN 108913048A
- Authority
- CN
- China
- Prior art keywords
- substrate
- layer
- salient point
- adhesive tape
- specially
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of antistatic Anti-skid adhesive tapes, it includes the substrate layer, adhesive layer and release film layer for stacking gradually arrangement from top to bottom, substrate layer is PE film layer, the upper surface of PE film layer is provided with the substrate salient point towards protruding above and in being evenly spaced on, each substrate salient point and PE film layer are integrally formed, and the diameter value that each substrate salient point distinguishes in rounded shape and each substrate salient point is respectively 0.25mm-0.5mm;Substrate layer includes the material of following parts by weight, specially:PE masterbatch 80%-85%, binder 5%-10%, fluorescent powder 3%-5%, short fiber of plant 5%-10%;Adhesive layer includes the material of following parts by weight, specially:Acrylate 30%-40%, epoxy resin 10%-20%, ethyl acetate 40%-50%, antistatic agent 5%-10%.Adhesive tape of the invention has the advantages that simple structure, good antiskid effect and anti-static effect are good.
Description
Technical field
The present invention relates to tape technology field more particularly to a kind of antistatic Anti-skid adhesive tapes.
Background technique
Adhesive tape is one of commonly fixed and tool covered in daily life and work, can be divided into high-temp glue by effect
Band, double faced adhesive tape, Anti-skid adhesive tape, specialty tape, pressure sensitive adhesive tape, cross cutting adhesive tape etc., are suitable for different according to different effects
Place and field.
As a kind of common adhesive tape product, Anti-skid adhesive tape is widely used in daily life;Wherein, right
For Anti-skid adhesive tape, mainly increase anti-skidding frictional force in such a way that surface is bonded particulate matter.For above-mentioned skid-proof rubber
For band, structure is complicated, at high cost and function is more single.
Summary of the invention
The purpose of the present invention is to provide a kind of antistatic Anti-skid adhesive tape, the antistatic Anti-skid adhesive tape structure is simple, anti-skidding
Effect is good and anti-static effect is good.
In order to achieve the above objectives, the present invention is achieved through the following technical solutions.
A kind of antistatic Anti-skid adhesive tape includes the substrate layer for stacking gradually arrangement from top to bottom, adhesive layer and release
Film layer, substrate layer are PE film layer, and the upper surface of PE film layer is provided with the substrate salient point towards protruding above and in being evenly spaced on, respectively
Substrate salient point and PE film layer are integrally formed, and the diameter value that each substrate salient point distinguishes in rounded shape and each substrate salient point is respectively
The height value of 0.25mm-0.5mm, each substrate salient point are respectively 0.1mm-0.5mm;
Substrate layer includes the material of following parts by weight, specially:
PE masterbatch 80%-85%
Binder 5%-10%
Fluorescent powder 3%-5%
Short fiber of plant 5%-10%;
Adhesive layer includes the material of following parts by weight, specially:
Acrylate 40%-50%
Epoxy resin 5%-15%
Ethyl acetate 30%-40%
Antistatic agent 10%-15%.
Wherein, the adhesive layer includes the material of following parts by weight, specially:
Acrylate 45%-50%
Epoxy resin 10%-15%
Ethyl acetate 30%-35%
Antistatic agent 10%-15%.
Wherein, the adhesive layer includes the material of following parts by weight, specially:
Acrylate 45%
Epoxy resin 10%
Ethyl acetate 35%
Antistatic agent 10%.
Wherein, the antistatic agent is monopalmitin.
Wherein, the substrate layer includes the material of following parts by weight, specially:
PE masterbatch 80%-83%
Binder 5%-8%
Fluorescent powder 3%-4%
Short fiber of plant 6%-10%.
Wherein, the substrate layer includes the material of following parts by weight, specially:
PE masterbatch 80%
Binder 6%
Fluorescent powder 4%
Short fiber of plant 10%.
Beneficial effects of the present invention are:A kind of antistatic Anti-skid adhesive tape of the present invention comprising have from top to bottom according to
Substrate layer, adhesive layer and the release film layer of secondary arranged stacked, substrate layer are PE film layer, and the upper surface of PE film layer is provided with upward
It protrudes and is integrally formed in the substrate salient point being evenly spaced on, each substrate salient point and PE film layer, each substrate salient point is in round respectively
The diameter value of shape and each substrate salient point is respectively 0.25mm-0.5mm, and the height value of each substrate salient point is respectively 0.1mm-
0.5mm;Substrate layer includes the material of following parts by weight, specially:PE masterbatch 80%-85%, binder 5%-10%, fluorescent powder
3%-5%, short fiber of plant 5%-10%;Adhesive layer includes the material of following parts by weight, specially:Acrylate 30%-40%, ring
Oxygen resin 10%-20%, ethyl acetate 40%-50%, antistatic agent 5%-10%.Adhesive tape of the invention simple, the anti-skidding effect with structure
The advantage that fruit is good and anti-static effect is good.
Detailed description of the invention
The present invention is further detailed below with attached drawing, but the embodiment in attached drawing is not constituted to this hair
Bright any restrictions.
Fig. 1 is the structural diagram of the present invention.
Include in Fig. 1:
1 --- substrate layer 11 --- substrate salient point
2 --- adhesive layer 3 --- release film layers.
Specific embodiment
Below with reference to specific embodiment, the present invention will be described.
Embodiment one, as shown in Figure 1, a kind of antistatic Anti-skid adhesive tape, includes the base for stacking gradually arrangement from top to bottom
Material layer 1, adhesive layer 2 and release film layer 3, substrate layer 1 are PE film layer, and the upper surface of PE film layer is provided with court and protrudes above and in equal
The even substrate salient point 11 being spaced apart, each substrate salient point 11 are integrally formed with PE film layer, and each substrate salient point 11 is distinguished in rounded shape
And the diameter value of each substrate salient point 11 is respectively 0.25mm-0.5mm, the height value of each substrate salient point 11 is respectively 0.1mm-
0.5mm。
It should further be noted that adhesive layer 2 includes the material of following parts by weight, specially:
Acrylate 35%
Epoxy resin 15%
Ethyl acetate 45%
Antistatic agent 5%;Wherein, antistatic agent is monopalmitin.
In addition, substrate layer includes the material of following parts by weight, specially:
PE masterbatch 80%
Binder 6%
Fluorescent powder 4%
Short fiber of plant 10%.
For the substrate layer 1 of the present embodiment one, PE material is used to be prepared, i.e. the substrate layer of the present embodiment one
1 is PE film layer;Wherein, the upper surface of PE film layer is integrally formed in the substrate salient point 11 being evenly spaced on.For this implementation
It for the substrate salient point 11 of example one, can effectively increase the contact friction force of PE film layer upper surface, and then play well
Antiskid effect.For the short fiber of plant of substrate layer 1, can effectively enhancing base materials layer 1 intensity and and enhance table
The contact friction force in face;For the fluorescent powder of substrate layer 1, fluorescent effect can be effectively acted as.
In addition, the adhesive layer 2 of the present embodiment one is made of acrylate, epoxy resin, ethyl acetate, antistatic agent, third
The material of main part of olefin(e) acid ester, epoxy resin, ethyl acetate as adhesive layer 2;Due to being mixed into antistatic agent in adhesive layer 2,
In one use process of the present embodiment, being mixed into the antistatic agent of adhesive layer 2 can be very good anti-static effect.
Based on the above situation, it may be appreciated that the adhesive tape of the present embodiment one has simple structure, good antiskid effect and anti-static effect
Good advantage.
Embodiment two, the present embodiment two and the difference of embodiment one are:Adhesive layer 2 includes the material of following parts by weight, tool
Body is:
Acrylate 50%
Epoxy resin 10%
Ethyl acetate 30%
Antistatic agent 10%.
In addition, substrate layer includes the material of following parts by weight, specially:
PE masterbatch 82%
Binder 10%
Fluorescent powder 3%
Short fiber of plant 5%.
Embodiment three, the present embodiment three and the difference of embodiment one are:Adhesive layer 2 includes the material of following parts by weight, tool
Body is:
Acrylate 40%
Epoxy resin 15%
Ethyl acetate 30%
Antistatic agent 15%.
In addition, substrate layer includes the material of following parts by weight, specially:
PE masterbatch 85%
Binder 5%
Fluorescent powder 5%
Short fiber of plant 5%.
The above is only a preferred embodiment of the present invention, for those of ordinary skill in the art, according to the present invention
Thought, there will be changes in the specific implementation manner and application range, and the content of the present specification should not be construed as to the present invention
Limitation.
Claims (6)
1. a kind of antistatic Anti-skid adhesive tape, it is characterised in that:It include the substrate layer for stacking gradually arrangement from top to bottom(1), glue
Adhesion coating(2)And release film layer(3), substrate layer(1)For PE film layer, the upper surface of PE film layer is provided with court and protrudes above and in uniform
The substrate salient point being spaced apart(11), each substrate salient point(11)It is integrally formed with PE film layer, each substrate salient point(11)Respectively in circle
Shape and each substrate salient point(11)Diameter value be respectively 0.25mm-0.5mm, each substrate salient point(11)Height value be respectively
0.1mm-0.5mm;
Substrate layer(1)It include the material of following parts by weight, specially:
PE masterbatch 80%-85%
Binder 5%-10%
Fluorescent powder 3%-5%
Short fiber of plant 5%-10%;
Adhesive layer(2)It include the material of following parts by weight, specially:
Acrylate 40%-50%
Epoxy resin 5%-15%
Ethyl acetate 30%-40%
Antistatic agent 10%-15%.
2. a kind of antistatic Anti-skid adhesive tape according to claim 1, it is characterised in that:The adhesive layer(2)Include with
The material of lower parts by weight, specially:
Acrylate 45%-50%
Epoxy resin 10%-15%
Ethyl acetate 30%-35%
Antistatic agent 10%-15%.
3. a kind of antistatic Anti-skid adhesive tape according to claim 2, it is characterised in that:The adhesive layer(2)Include with
The material of lower parts by weight, specially:
Acrylate 45%
Epoxy resin 10%
Ethyl acetate 35%
Antistatic agent 10%.
4. according to claim 1 to a kind of antistatic Anti-skid adhesive tape described in 3 any one, it is characterised in that:The antistatic
Agent is monopalmitin.
5. a kind of antistatic Anti-skid adhesive tape according to claim 1, it is characterised in that:The substrate layer(1)Include with
The material of lower parts by weight, specially:
PE masterbatch 80%-83%
Binder 5%-8%
Fluorescent powder 3%-4%
Short fiber of plant 6%-10%.
6. a kind of antistatic Anti-skid adhesive tape according to claim 5, it is characterised in that:The substrate layer(1)Include with
The material of lower parts by weight, specially:
PE masterbatch 80%
Binder 6%
Fluorescent powder 4%
Short fiber of plant 10%.