CN108903595A - A kind of clad steel pot and its manufacturing process - Google Patents
A kind of clad steel pot and its manufacturing process Download PDFInfo
- Publication number
- CN108903595A CN108903595A CN201810845383.0A CN201810845383A CN108903595A CN 108903595 A CN108903595 A CN 108903595A CN 201810845383 A CN201810845383 A CN 201810845383A CN 108903595 A CN108903595 A CN 108903595A
- Authority
- CN
- China
- Prior art keywords
- layer
- thermosphere
- boss
- internal layer
- pot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to steel pot and its manufacturing process, disclose a kind of clad steel pot and its manufacturing process, including pot body (1), pot body (1) includes internal layer work layer (11) and outer layer by thermosphere (12), outer layer is wrapped up internal layer work layer (11) by thermosphere (12), and the bottom and pot mouth outer of pot body (1) are equipped with the boss for reinforcement structure intensity;Molded again imitate multilayered structure is first imitated multilayered structure sheet stock oiling when manufacture respectively again to force together.The present invention passes through makes each layer hold tightly together under high tonnage presses, the material of pot body is flowed in the case where freezing off state or under heated condition by the effect of high tonnage presses, density is finer and close, the finer and closely woven arrangement of molecular structure, increases the adhesive force of aluminium alloy and stainless steel or magnetic conduction layer material;In addition pot body MULTILAYER COMPOSITE Steel material is integrally formed, and oral area is unlikely to deform under toasting pot body spraying high temperature with bottom stage formula booster action.
Description
Technical field
The present invention relates to steel pot and its manufacturing process, more particularly to a kind of clad steel pot and its manufacturing process.
Background technique
Currently, common clad steel pot in the prior art is as shown in Figs. 1-2 comprising internal layer (4), middle layer (5) and outer
Layer (6), internal layer (4) are work layer, and middle layer (5) is heat-conducting layer made of permeability magnetic material, and outer layer (6) is by thermosphere, outer layer (6)
The bottom of internal layer (4) is respectively positioned on middle layer (5), the outer edge in joint forms gap and brings easy to fall off, easy infiltration, bottom
It is recessed to test the defect that is easily detected by, in addition the common punch forming of MULTILAYER COMPOSITE steel pot as stretched, rotary press modelling, pot body can because
Spraying high temperature is toasted and is deformed, and influences product appearance quality, bottom plate high temperature deformation causes the recessed test in bottom that cannot pass through.
Summary of the invention
The present invention can be deformed for pot body in the prior art because spraying high temperature toasts, and influence product appearance quality, bottom
Plate high temperature deformation leads to the intransitable problem of the recessed test in bottom, provides a kind of clad steel pot and its manufacturing process.
In order to solve the above-mentioned technical problem, the present invention is addressed by following technical proposals:
A kind of clad steel pot and its manufacturing process, including pot body, pot body include internal layer work layer and are made of permeability magnetic material
Outer layer by thermosphere, the downwardly convex formation the bottom of a pan boss in the bottom of internal layer work layer, bottom downwardly convex shape of the outer layer by thermosphere
At pedestal, pedestal is equipped with the first groove;The lateral wall of internal layer work layer is equipped with annular boss close to boiler port, and outer layer is heated
The lateral wall of layer is equipped with outer ring boss close to boiler port, and the inside of outer ring boss is equipped with the second groove;Outer layer is by thermosphere packet
It is rolled on the outside of internal layer work layer, boss is accommodated in the first groove, and annular boss is accommodated in the second groove.Wherein annular
Reinforcing respectively the pot mouth of mutability and the bottom of a pan for boss and pedestal, greatly improves the intensity of entire pot body, reduces pot
The heated deformation probability of body spraying, improves the acceptance rate of product.In addition, outer layer made of permeability magnetic material is made by the internal layer of thermosphere
Industry layer outer surface package, active area increases when use, and heat conduction efficiency improves.
Preferably, the material of internal layer work layer is stainless steel internal layer work layer or aluminium internal layer work layer.
Preferably, the outer bottom of pot body is plane, the thickness in the bottom of a pan is by center progressive additive outward.
Preferably, the outer surface rounding off of the bottom of a pan boss and internal layer work layer.
Preferably, outer layer by thermosphere be iron outer layer by thermosphere or stainless steel outer layer by thermosphere.The outer layer of this kind of magnetic conduction by
Thermosphere substantially increases heat transfer efficiency of the outer layer by thermosphere.
Preferably, the top surface of annular boss is concordant with pot mouth, side is arcwall face, the radian and internal layer of arcwall face
Radian at the identical height of work layer inner surface is identical, bottom surface and internal layer work layer outer surface rounding off.Annular boss
The intensity for substantially increasing boiler port effectively reduces its temperature distortion probability
A kind of manufacturing process of clad steel pot comprising following steps:
A. sheet stock oiling:Oiling is carried out using two sides of the oiler to sheet stock;
B. it once imitates molded:The sheet stock after oiling is carried out using press machine to be stamped and formed out internal layer work layer, by internal layer
The bottom of work layer is stamped and formed out the bottom of a pan boss, and it is convex that the lateral wall of internal layer work layer close to boiler port is stamped and formed out annular
Platform;The sheet stock of the magnetic conduction after oiling is stamped and formed out outer layer by thermosphere again, outer layer is stamped and formed out downwards by the bottom of thermosphere and is had
The pedestal of first groove, and it is convex that outer layer by the lateral wall of thermosphere close to boiler port is stamped and formed out the outer ring with the second groove
Platform;
C. it imitates for two times molded:Outer layer is wrapped on the outside of internal layer work layer by thermosphere, so as to be accommodated in first recessed for boss
In slot, annular boss is accommodated in the second groove, then internal layer work layer and outer layer are struck out one by thermosphere using press machine
Body formula pot body.
Present invention employs above scheme to have the advantages that:The present invention pass through high tonnage presses under enable aluminum alloy to or
Stainless steel holds tightly together again with magnetic conduction layer material, by high tonnage presses act on aluminum alloy materials in the case where freezing off state or
Flowed under person's heated condition, multilayered structure made to connect finer and close, the finer and closely woven arrangement of molecular structure, increase aluminium alloy or stainless steel and
The adhesive force of magnetic conduction layer material;In addition pot body MULTILAYER COMPOSITE Steel material is integrally formed, bottom stage and pot the mouth setting of pot body
Step has carried out structural strengthening to entire pot body, so that greatly reducing in the temperature distortion for reinforcing position, solves common inserted
Multiple bottom, full bottom again be easy to fall off, easy infiltration, bottom is recessed tests the problem being easily detected by.
Detailed description of the invention
Fig. 1 is common composite bottom boiler body cross-sectional view in the prior art described in background technique.
Fig. 2 is the explosive view of pot body in Fig. 1.
Fig. 3 is pan structure schematic diagram of the invention.
Fig. 4 is the explosive view of the pot body of multilayered structure in the present invention.
Fig. 5 is the enlarged drawing in Fig. 4 at A.
Fig. 6 is the enlarged drawing in Fig. 4 at B.
The toponym that each number designation is referred in attached drawing is as follows:1-pot body, 11-internal layer work layers, 12-outer layers
By thermosphere, 121-pedestals, the 1211-the first groove, 122-outer ring boss, the 1221-the second groove, 3-boss, 4-interior
Annular convex platform, 41-annular boss top surfaces, the side of 42-annular boss, 43-annular boss bottom surface.
Specific embodiment
Present invention is further described in detail with embodiment with reference to the accompanying drawing.
Embodiment 1
A kind of clad steel pot and, as in Figure 3-5 comprising pot body 1, pot body 1 include internal layer work layer 11 and by magnetic conduction
Outer layer made of material is by thermosphere 12, and the downwardly convex formation the bottom of a pan boss 3 in the bottom of internal layer work layer 11, outer layer is by thermosphere 12
The downwardly convex formation pedestal 121 in bottom, pedestal 121 are equipped with the first groove 1211;The lateral wall of internal layer work layer 11 is close to pot
Annular boss 4 is equipped at mouthful, outer layer is equipped with outer ring boss 122 close to boiler port by the lateral wall of thermosphere 12, and outer ring is convex
The inside of platform 122 is equipped with the second groove 1221;Outer layer is wrapped in the outside of internal layer work layer 11 by thermosphere 12, and boss 3 is accommodated in the
In one groove 1211, annular boss 4 is accommodated in the second groove 1221.
The material of internal layer work layer 11 is stainless steel internal layer work layer or aluminium internal layer work layer.
The outer bottom of pot body 1 is plane, and the thickness in the bottom of a pan is by center progressive additive outward.
The outer surface rounding off of the bottom of a pan boss 3 and internal layer work layer 11.
Outer layer by thermosphere 12 be iron outer layer by thermosphere or stainless steel outer layer by thermosphere.
The top surface 41 of annular boss 4 is concordant with pot mouth, and side 42 is arcwall face, the radian of arcwall face and internal layer operation
Radian at the identical height of 11 inner surface of layer is identical, bottom surface 43 and 11 outer surface rounding off of internal layer work layer.
A kind of manufacturing process of clad steel pot comprising following steps:
A. sheet stock oiling:Oiling is carried out using two sides of the oiler to sheet stock;
B. it once imitates molded:The sheet stock after oiling is carried out using press machine to be stamped and formed out internal layer work layer 11, it will be interior
The bottom of layer work layer 11 is stamped and formed out the bottom of a pan boss 3, and the lateral wall of internal layer work layer 11 is stamped and formed out close to boiler port
Annular boss 4;The sheet stock of the magnetic conduction after oiling is stamped and formed out outer layer by thermosphere 12 again, outer layer is downward by the bottom of thermosphere 12
It is stamped and formed out the pedestal 121 with the first groove 1211, and outer layer is stamped and formed out by the lateral wall of thermosphere 12 close to boiler port
Outer ring boss 122 with the second groove 1221;
C. it imitates for two times molded:Outer layer is wrapped in the outside of internal layer work layer 11 by thermosphere 12, so that boss 3 is accommodated in the
In one groove 1211, annular boss 4 is accommodated in the second groove 1221, then uses press machine by internal layer work layer 11 and outer layer
By the integrated pot body of 12 punching press of thermosphere.
When imitating molded, using high tonnage presses, so that multilayered structure holds tightly together.
Concave bottom test in the bottom of a pan is carried out to finished product clad steel pot:1. measuring bottom of pot body diameter;2. being drawn with angle board in the bottom of a pan
Eight lines out, each line both pass through the center in the bottom of a pan, and every two lines line angle degree differs 45 °, it is recessed to measure a bottom on each line
Measure the recessed size in bottom of 8 points of maximum point and record;3. pot body is heated to 200 DEG C, the recessed size in bottom of above-mentioned eight points is measured,
And calculate changing value;4. base diameter indent exists in 0.3%-0.6%* diameter, cold conditions room temperature state lower bottom part diameter indent
It is qualified products within 0.6%* diameter.
Embodiment 2
It is common to answer bottom (non-porous multiple bottom) test result entirely:
LGA- test specimens bottom valley
Embodiment 3
The imitative pressure pot test result of composite steel:
LGA- test specimens bottom valley
Wherein, embodiment 2 and embodiment 3 are respectively common full bottom again (non-porous multiple bottom) pot and the imitative pressure pot test number of composite steel
According to.
Through the present invention known to above data compared with ordinary electromagnetic furnace is applicable in composite bottom boiler:After this MULTILAYER COMPOSITE steel pot is heated
Bottom is unlikely to deform, magnetic conductive area is big, it is thermally conductive more evenly.It will not be because of the heated raised magnetic conduction in bottom compared with common full composite bottom boiler
Area reduces, and loses the thermal efficiency.Present invention process covers simultaneously:Make other materials, aluminium alloy and stainless steel under high tonnage presses
Or magnetic conduction layer material holds tightly together again.Make other materials, aluminum alloy materials cold by the effect of high tonnage presses
It is flowed under solid-state or under heated condition, keeps other materials, aluminium alloy density finer and close, the finer and closely woven arrangement of molecular structure, simultaneously
Increase the adhesive force of aluminium alloy and stainless steel or magnetic conduction layer material.Increase composite layer in the bottom of a pan in compared with the prior art, this
The bottom of clad steel pot in application be it is complete surround, considerably increase radiating efficiency, solve heat dissipation between different materials not
Equalization problem, to reduce the recessed probability in bottom.
In short, the foregoing is merely a prefered embodiment of the invention, it is all according to equivalent change made by scope of the present invention patent
With modification, shall all be covered by the patent of the invention.
Claims (7)
1. a kind of clad steel pot, including pot body (1), it is characterised in that:Pot body (1) includes internal layer work layer (11) and by magnetic conduction material
Outer layer made of expecting is by thermosphere (12), and the downwardly convex formation the bottom of a pan boss (3) in the bottom of internal layer work layer (11), outer layer is by thermosphere
(12) the downwardly convex formation pedestal (121) in bottom, pedestal (121) are equipped with the first groove (1211);Internal layer work layer (11)
Lateral wall close to boiler port be equipped with annular boss (4), outer layer by thermosphere (12) lateral wall close to boiler port be equipped with outer ring
The inside of shape boss (122), outer ring boss (122) is equipped with the second groove (1221);Outer layer is wrapped in internal layer by thermosphere (12)
On the outside of work layer (11), boss (3) is accommodated in the first groove (1211), and annular boss (4) is accommodated in the second groove
(1221) in.
2. a kind of clad steel pot according to claim 1, it is characterised in that:The material of internal layer work layer (11) is stainless steel
Internal layer work layer or aluminium internal layer work layer.
3. a kind of clad steel pot according to claim 1, it is characterised in that:The outer bottom of pot body (1) is plane, the bottom of a pan
Thickness is by center progressive additive outward.
4. a kind of clad steel pot according to claim 1, it is characterised in that:The outer surface of the bottom of a pan boss (3) and internal layer are made
The outer surface connection of industry layer (11) is arcwall face.
5. a kind of clad steel pot according to claim 1, it is characterised in that:Outer layer is heated for iron outer layer by thermosphere (12)
Layer or stainless steel outer layer are by thermosphere.
6. a kind of clad steel pot according to claim 1, it is characterised in that:The top surface (41) of annular boss (4) is pot
The top surface of mouth, the side (42) of annular boss (4) are arcwall face, the bottom surface (43) of annular boss (4) and internal layer work layer
(11) outer surface connection is arcwall face.
7. a kind of clad steel pot manufacturing process, is used for the described in any item clad steel pots of manufacturing claims 1-6, feature exists
In including the following steps:
A. sheet stock oiling:Oiling is carried out using two sides of the oiler to sheet stock;
B. it once imitates molded:The sheet stock after oiling is carried out using press machine to be stamped and formed out internal layer work layer (11), by internal layer
The bottom of work layer (11) is stamped and formed out the bottom of a pan boss (3), and by the lateral wall of internal layer work layer (11) close to boiler port punching press
It is formed annular boss (4);The sheet stock of the magnetic conduction after oiling is stamped and formed out outer layer by thermosphere (12) again, outer layer is by thermosphere (12)
Bottom be stamped and formed out the pedestal (121) with the first groove (1211) downwards, and outer layer is leaned on by the lateral wall of thermosphere (12)
Nearly boiler port is stamped and formed out the outer ring boss (122) with the second groove (1221);
It is secondary imitate it is molded:Outer layer is wrapped on the outside of internal layer work layer (11) by thermosphere (12), so that boss (3) is accommodated in the
In one groove (1211), annular boss (4) is accommodated in the second groove (1221), then uses press machine by internal layer work layer
(11) and outer layer is by the integrated pot body of thermosphere (12) punching press.