CN108893748A - A kind of preparation method and its application method of Silver Jewelry detergent - Google Patents
A kind of preparation method and its application method of Silver Jewelry detergent Download PDFInfo
- Publication number
- CN108893748A CN108893748A CN201810458931.4A CN201810458931A CN108893748A CN 108893748 A CN108893748 A CN 108893748A CN 201810458931 A CN201810458931 A CN 201810458931A CN 108893748 A CN108893748 A CN 108893748A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- detergent
- ultramicro
- silver jewelry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the preparation methods and its application method of a kind of Silver Jewelry detergent, are related to silver jeweleries auxiliary material technical field.The detergent is by diatomite, talcum powder, calcium pyrophosphate, gypsum, chitosan, graphite, zinc oxide, copper powder are stand-by, ethyl alcohol, silicic acid, hydrogen peroxide, ultrapure water, sldium lauryl sulfate, sodium sulfate of polyethenoxy ether of fatty alcohol；The application method of Silver Jewelry detergent of the present invention is that ornaments are immersed into detergent, is washed using ultrasonic oscillation, and preparation of reagents of the present invention is convenient, is easy to save, has good removal effect to foreign matters such as oxide, the sulfide on Silver Jewelry surface.
Description
Technical field
The present invention relates to silver jeweleries auxiliary material technical field, in particular to a kind of the preparation method and its use of Silver Jewelry detergent
Method.
Background technique
Jewelry, jadeware, gold-silver ornaments, can not only generate dirt using its surface over time also will form surface oxidation
Object makes ornaments tarnish, and general cleaning supplies have certain damage to ornaments, and not environmentally, and cannot repeat benefit
With.Therefore it is badly in need of developing not damaged, environmentally friendly, the reusable cleaning powder of a kind of pair of jewelry, jadeware, gold-silver ornaments.
Summary of the invention
For the defect for overcoming the above-mentioned prior art, the present invention provides a kind of processing method of high-intensitive Silver Jewelry, also provides
The application method of the detergent, in order to high-efficiency washing Silver Jewelry.
It is achieved particular by following technical scheme：
A kind of preparation method of Silver Jewelry detergent, including：
（1）In terms of mass parts, take 23-35 parts of diatomite, 18-22 parts of talcum powder, 10-18 parts of calcium pyrophosphates, 8-15 parts of gypsum,
20-30 parts of chitosans, 12-18 parts of graphite, 20-25 parts of zinc oxide, 15-23 parts of copper powders are stand-by, 15-30 parts of ethyl alcohol, 3-5 parts of silicon
Acid, 5-8 parts of hydrogen peroxide, 100-120 parts of ultrapure waters, 3-5 parts of sldium lauryl sulfates, 3-5 parts of fatty alcohol polyoxyethylene ether sulfuric acid
Sodium；
（2）Copper powder, diatomite, talcum powder, gypsum, zinc oxide are heated to 200-300 DEG C, 20-30min is kept the temperature, adds after cooling
Enter to be mixed evenly, vibrating screen ultra micro milling, it is spare to obtain Ultramicro-powder a, by calcium pyrophosphate, chitosan, graphite air-flow Ultramicro-powder
It is spare that Ultramicro-powder b is obtained after broken；
（3）By ultrapure water, silicic acid, sldium lauryl sulfate, sodium sulfate of polyethenoxy ether of fatty alcohol Hybrid Heating to 60-80 DEG C, stir
5-8min is mixed, Ultramicro-powder a is added and boils 10min, Ultramicro-powder b mixing is then added, 40-50 DEG C is down to temperature, second is added
Alcohol, hydrogen peroxide, which stir evenly, to be sealed.
The application method of Silver Jewelry detergent of the invention, which is characterized in that the ultrasonic wave for being first 30-50KHz with frequency
Cleaning agent 10min is handled, then jewellery are immersed in cleaning agent, with the ultrasonic cleaning 20-30min of 80-130KHz, is taken out
Jewellery, with clear water shower 30s.
Further, the power of the ultrasonication cleaning agent is 200-400W；Power is when the ultrasonic cleaning
600-800W, cleaning temperature are 40-45 DEG C.
Beneficial effects of the present invention：
Preparation of reagents of the present invention is convenient, is easy to save, and by coordinating each component ratio, allows in detergent there are suitable acid and oxygen
Compound, the oxide and sulfide for Silver Jewelry surface use ultrasonic wave by good removal effect, and in cleaning, make
Detergent is obtained efficiently to rub with Silver Jewelry, it is fabulous for the foreign matter removal effect on Silver Jewelry surface.
Specific embodiment
Embodiment 1
A kind of preparation method of Silver Jewelry detergent, including：
（1）Take 23 parts of diatomite, 18 parts of talcum powder, 10 parts of calcium pyrophosphates, 8 parts of gypsum, 20 parts of chitosans, 12 parts of graphite, 20 parts
Zinc oxide, 15 parts of copper powders are stand-by, 15 parts of ethyl alcohol, 3 parts of silicic acid, 5 parts of hydrogen peroxide, 100 parts of ultrapure waters, 3 parts of sldium lauryl sulfates,
3 parts of sodium sulfate of polyethenoxy ether of fatty alcohol；
（2）Copper powder, diatomite, talcum powder, gypsum, zinc oxide are heated to 200 DEG C, 20min is kept the temperature, mixing is added after cooling and stirs
It mixes uniformly, vibrating screen ultra micro milling, it is spare to obtain Ultramicro-powder a, and calcium pyrophosphate, chitosan, graphite air-flow must be surpassed after pulverizing
Micro mist b is spare；
（3）By ultrapure water, silicic acid, sldium lauryl sulfate, sodium sulfate of polyethenoxy ether of fatty alcohol Hybrid Heating to 60 DEG C, stirring
5min adds Ultramicro-powder a and boils 10min, and Ultramicro-powder b mixing is then added, and is down to 40 DEG C to temperature, ethyl alcohol, peroxide is added
Change hydrogen, which stirs evenly, to be sealed.
The application method of Silver Jewelry detergent of the invention, which is characterized in that the ultrasonication for being first 30KHz with frequency
Jewellery, are then immersed in cleaning agent by cleaning agent 10min, with the ultrasonic cleaning 20min of 80KHz, take out jewellery, use clear water
Shower 30s.The power of the ultrasonication cleaning agent is 200W；Power is 600W, cleaning when the ultrasonic cleaning
Temperature is 40 DEG C.
Claims (3)
1. a kind of preparation method of Silver Jewelry detergent, which is characterized in that including：
（1）In terms of mass parts, take 23-35 parts of diatomite, 18-22 parts of talcum powder, 10-18 parts of calcium pyrophosphates, 8-15 parts of gypsum,
20-30 parts of chitosans, 12-18 parts of graphite, 20-25 parts of zinc oxide, 15-23 parts of copper powders are stand-by, 15-30 parts of ethyl alcohol, 3-5 parts of silicon
Acid, 5-8 parts of hydrogen peroxide, 100-120 parts of ultrapure waters, 3-5 parts of sldium lauryl sulfates, 3-5 parts of fatty alcohol polyoxyethylene ether sulfuric acid
Sodium；
（2）Copper powder, diatomite, talcum powder, gypsum, zinc oxide are heated to 200-300 DEG C, 20-30min is kept the temperature, adds after cooling
Enter to be mixed evenly, vibrating screen ultra micro milling, it is spare to obtain Ultramicro-powder a, by calcium pyrophosphate, chitosan, graphite air-flow Ultramicro-powder
It is spare that Ultramicro-powder b is obtained after broken；
（3）By ultrapure water, silicic acid, sldium lauryl sulfate, sodium sulfate of polyethenoxy ether of fatty alcohol Hybrid Heating to 60-80 DEG C, stir
5-8min is mixed, Ultramicro-powder a is added and boils 10min, Ultramicro-powder b mixing is then added, 40-50 DEG C is down to temperature, second is added
Alcohol, hydrogen peroxide, which stir evenly, to be sealed.
2. the application method of Silver Jewelry detergent according to claim 1, which is characterized in that be first 30-50KHz with frequency
Ultrasonication cleaning agent 10min, then jewellery are immersed in cleaning agent, with the ultrasonic cleaning 20- of 80-130KHz
30min takes out jewellery, with clear water shower 30s.
3. the application method of Silver Jewelry detergent according to claim 2, which is characterized in that the ultrasonication cleaning
The power of agent is 200-400W；Power is 600-800W when the ultrasonic cleaning, and cleaning temperature is 40-45 DEG C.