CN108891188A - Maize leaves picture and preparation method thereof - Google Patents
Maize leaves picture and preparation method thereof Download PDFInfo
- Publication number
- CN108891188A CN108891188A CN201810622110.XA CN201810622110A CN108891188A CN 108891188 A CN108891188 A CN 108891188A CN 201810622110 A CN201810622110 A CN 201810622110A CN 108891188 A CN108891188 A CN 108891188A
- Authority
- CN
- China
- Prior art keywords
- maize leaves
- powder
- coating
- drawn
- maize
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Maize leaves picture and preparation method thereof, maize leaves picture are sequentially overlapped and are formed by base, adhesive-layer, maize leaves layer, protective coating；The coating for forming protective coating is mixed to prepare by 100 parts of water, 0.1~1 part of rubber powder and appropriate decoration powder by weight; wherein rubber powder is mixed to prepare by glutinous rice powder and air bladder powder in 1.5~2.5: 0.5~1.5 ratio; make the method that maize leaves are drawn; there is the step of processing maize leaves, coating processed and picture processed; maize leaves of the invention are drawn rich in color; it is easy to save; maize leaves can also be retained and draw unique natural effects; decoration powder in coating can enhance the gradation of maize leaves picture, improve the reserve value that maize leaves are drawn.
Description
Technical field
Drawn the present invention relates to a kind of maize leaves and preparation method thereof.
Background technique
Maize leaves draw modern design, texture uniqueness, are made by specific process, have unique artistic value, by
To pursuing for numerous collectors.Since maize leaves are inbred crops, existing maize leaves draw color is more single, so to jade
Rice leaf dyes to enrich the color hierarchy of maize leaves picture, and maize leaves surface texture is complicated, and part dyeing needs to remove
Grease in maize leaves picture, the maize leaves picture color dimness after leading to dyeing is unnatural, the easily dry embrittlement of the finished product that maize leaves are drawn,
It needs to draw maize leaves and be stored in in the environment of certain humidity, increase collection cost, also there is the corn drawn in maize leaves
Blade surface sprays transparent wax or varnish, it is therefore an objective to and the gloss for increasing maize leaves picture can solidify maize leaf again and be conducive to save,
But wax and varnish are only capable of being attached to the outer surface of maize leaf, and the tiny texture on maize leaf has been filled and led up during spary,
Wax or varnish is caused to form glossy surface on maize leaf after hardening, glossy surface has the reflection characteristic of light, causes
The cross-color that maize leaves are drawn, the performance of lines is also more stiff, loses its unique natural effects.
Summary of the invention
Drawn the object of the present invention is to provide a kind of maize leaves and preparation method thereof, maize leaves can be made to draw rich in color, easily
In preservation, moreover it is possible to retain maize leaves and draw unique natural effects.
The technical scheme is that：Maize leaves are drawn, it is characterised in that：Maize leaves are drawn by base, adhesive-layer, maize leaves
Layer, protective coating are sequentially overlapped composition；Formed protective coating coating by weight by 100 parts of water, 0.1~1 part of rubber powder and
Appropriate decoration powder is mixed to prepare, and wherein rubber powder is mixed to prepare by glutinous rice powder and air bladder powder in 1.5~2.5: 0.5~1.5 ratio.
The decoration powder be bronze or silver powder or one of pearl powder or pearl powder or in which at least two mixing
Powder.
The base is velveteen layer of cloth.
The glutinous rice powder is glutinous corn flour or glutinous rice meal or one of glutinous glutinous millet powder or glutinous rice flour or in which extremely
It is two kinds few.
Make the method that maize leaves are drawn, which is characterized in that have follow steps：
1) maize leaves are handled：After maize leaves are carried out the mothproof processing of anti-corrosion, maize leaves heat is dried and is formed, then needs are cultrated
Maize leaves cultrate, for use；
2) coating processed：Glutinous rice powder and air bladder powder are put into suitable 85~95 DEG C of water by the mixed proportion, kept the temperature
Stirring and dissolving is uniform, places and is cooled to room temperature naturally, obtains mixed liquor；Remaining water and suitable is added by the weight part ratio
It decorates powder and is uniformly mixed obtained coating, or, adding after being crushed after mixed liquor is dried by the weight part ratio and suitable decoration powder
Enter and be uniformly mixed obtained coating in water, for use；
3) picture processed：According to a conventional method will treated maize leaves glue sticking in base, to be formed in base viscous
Glue-line, maize leaves layer, then by coating material in maize leaves, coating is dried with 50~120 DEG C of temperature, coating is dry
Protective coating is formed on maize leaves layer afterwards, obtains the finished product that maize leaves are drawn.
Suitable food preservative is added in the mixed liquor or coating.
The beneficial effects of the invention are as follows：The glutinous rice powder is rich in amylopectin, and air bladder powder is rich in micromolecular collagen,
Glutinous rice powder and air bladder powder are natural bonding agent, and after mixing with water, maize leaf can quickly be penetrated by being applied to maize leaf surface
Epidermis, will also be decorated while combining closely with maize leaf powder be detained be solidificated in the surface of maize leaf to surface layer into
Row coloring, during infiltration, relatively thin on maize leaf and train of thought it is tiny it is abundant place penetrate into it is more and fast, on maize leaf
The coarse sparse place of thicker and stem network is penetrated into slow less, deposits decoration powder by infiltration process to show maize leaves
The distinctive texture of piece can not only be such that maize leaves draw rich in color, additionally it is possible to the clear tiny texture for retaining maize leaf, no matter
It is remote to see or closely see that show maize leaves draws unique natural effects；The animal oil in amylopectin combination air bladder in glutinous rice
Rouge can form the protective layer of the combination of inner and outside, moreover it is possible to the fat content in maize leaf is increased, so that band on maize leaf
The maize leaf flexibility of protective layer enhances, and maize leaves is made to be drawn as the resistance to drying of product humidity, is easy to the preservation of maize leaves picture.With height
Temperature dries coating, can control the curing time of coating, to control pair between coating color and maize leaf texture
Compare effect.Bronze or silver powder or pearl powder or pearl powder can make maize leaf surface form the special visual effect of mottled glittering,
The gradation of maize leaves picture is further enhanced, the reserve value that maize leaves are drawn is improved.Panne velvet cloth has fuzzy surface layer, increases
The surface area of viscose glue, can make that maize leaf is bonded especially securely so that the maize leaves enhanced by toughness after coating treatment
Piece is able to carry out retracting and saves, and reduces collection cost.Preferably glutinous corn flour or glutinous rice meal or glutinous glutinous millet powder or glutinous rice flour with
The molten and property of air bladder powder is good, and the stability of coating obtained is good, nontoxic free from extraneous odour.Remaining water is added after mixing evenly in mixed liquor
It can be used directly, crushed after mixed liquor is dried, it can be easy to use with with converting.
Specific embodiment
Maize leaves are drawn, and maize leaves picture is sequentially overlapped and is formed by base, adhesive-layer, maize leaves layer, protective coating；Form protection
The coating of coating is mixed to prepare by 100 parts of water, 0.1~1 part of rubber powder and appropriate decoration powder by weight, and wherein rubber powder is by glutinous rice
Powder and air bladder powder are mixed to prepare in 1.5~2.5: 0.5~1.5 ratio.The decoration powder is bronze or silver powder or pearl powder
Or one of pearl powder or in which at least two mixed powders.The base is velveteen layer of cloth.The glutinous rice powder is glutinous
Corn flour or glutinous rice meal or one of glutinous glutinous millet powder or glutinous rice flour or in which at least two.
The air bladder powder is commercial product, or, air bladder is made by dries pulverizing is carried out after commercially available air bladder impurity elimination cleaning
Powder uses, and the air bladder is derived from ocean fish class or freshwater fish；The glutinous corn flour or glutinous rice meal or glutinous glutinous millet powder
Or the glutinous rices powder such as glutinous rice flour is commercial goods.In the art, the link base layer refer to dry goods (including plain cloth, painting canvas etc.) and
Stationery (including cambric paper, paper jam, cardboard etc.) in the application, especially uses panne velvet cloth, it is to use that velveteen, which is commercial goods,
Suede weaves the flannelette arranged again through cut pile, feature be its surface have it is dense, concordant, tower and rich glossiness villus.It is described
Decoration powder it is logical refer to watersoluble pigment powder or dyestuff powder, in the application, the commercially available bronze of Special use or silver powder or pearl powder or
Pearl powder, wherein pearl powder is also referred to as pearlescent pigment, and color category is numerous；The food preservative is commercial goods, is pressed
The amount of its specification mark takes the circumstances into consideration to add.
Embodiment one：The maize leaves being collected into are subjected to the mothproof processing of anti-corrosion, after cleaning, maize leaves heat is dried and is formed, then
The maize leaves cultrated will be needed to cultrate, for use；150 mesh of requirement are sticked into glutinous millet powder and 150 mesh air bladder powder by 1.5: 0.5 ratio
Example is mixed and made into rubber powder, takes 1 gram of rubber powder to be put into 500 grams of water that temperature is 95 DEG C, insulated and stirred 5 minutes, visually stirs molten
It after solution is uniform, places and is cooled to room temperature naturally, obtain mixed liquor；It adds 500 grams of water and 1 gram of bronze is uniformly mixed to be made and apply
Material, according to a conventional method will treated maize leaves glue sticking in panne velvet cloth, to form adhesive-layer, corn in panne velvet cloth
Leaf layer, then by coating material in maize leaves, coating is dried with 120 DEG C of temperature, in maize leaves layer after coating is dry
Upper formation protective coating obtains the finished product that maize leaves are drawn.
Embodiment two：Maize leaves are handled by the method for embodiment one, for use；By 300 mesh glutinous rice flours of requirement and 300 mesh
Air bladder powder is mixed and made into rubber powder in 2.5: 1.5 ratio, takes 50 grams of rubber powder to be put into 300 grams of water that temperature is 85 DEG C, uses
Electric blender insulated and stirred 10 minutes, after visual stirring and dissolving is uniform, is placed naturally and is cooled to room temperature, obtain mixed liquor；It will
300 mesh powder, which are ground into, after mixed liquor drying and are taken in the 10 grams therein water that 1 kilogram is added together with 10 grams of silver powder mixes
Uniformly obtained coating；According to a conventional method will treated maize leaves glue sticking in panne velvet cloth, to be formed in panne velvet cloth
Adhesive-layer, maize leaves layer, then by coating material in maize leaves, coating is dried with 50 DEG C of temperature, after coating is dry
Protective coating is formed on maize leaves layer, obtains the finished product that maize leaves are drawn.
Embodiment three：Maize leaves are handled by the method for embodiment one, for use；200 mesh of requirement are sticked into rice meal and 200
Mesh air bladder powder is mixed and made into rubber powder in 1: 1 ratio, takes 5 grams of rubber powder to be put into 1000 grams of water at a temperature of 90 °C, heat preservation is stirred
It mixes 5 minutes, after visual stirring and dissolving is uniform, places and be cooled to room temperature naturally, obtain mixed liquor；Mixed liquor net weight is referred to as 1001
Gram, it adds 4 grams of water and 1 gram of pearl powder is uniformly mixed obtained coating, appropriate food preservative is entered in coating, routinely
Method will treated maize leaves glue sticking on cambric paper, to form adhesive-layer, maize leaves layer on cambric paper, then will
Coating material dries coating with 85 DEG C of temperature in maize leaves, and protection is formed on maize leaves layer after coating is dry
Coating obtains the finished product that maize leaves are drawn.
Example IV：Maize leaves are handled by the method for embodiment one, for use；250 mesh of requirement are sticked into corn flour and 250
Mesh air bladder powder is mixed and made into rubber powder in 2.5: 0.5 ratio, takes 100 grams of rubber powder to be put into 500 grams of water that temperature is 85 DEG C, makes
With electric blender, insulated and stirred 10 minutes, after visual stirring and dissolving is uniform, places and is cooled to room temperature naturally, obtain mixed liquor,
Suitable food preservative is mixed into mixed liquor；250 mesh powder are ground into after mixed liquor is dried and take 8 grams therein together with 5
Gram pearl powder be added in 1 kilogram of water together and be uniformly mixed obtained coating；It according to a conventional method will treated maize leaves glue
It is bonded on plain cloth, so that adhesive-layer, maize leaves layer are formed on plain cloth, then by coating material in maize leaves, with 65
DEG C temperature coating is dried, protective coating is formed after coating is dry on maize leaves layer, obtains the finished product that maize leaves are drawn.
Embodiment five：Maize leaves are handled by the method for embodiment one, for use；By requirement by glutinous corn flour, glutinous rice
Powder, glutinous glutinous millet powder, glutinous rice flour press 1:1:1:The glutinous rice powder and air bladder powder of 1 ratio mixing are mixed and made into rubber powder in 2: 1 ratio, take
10 grams of rubber powder is put into 800 grams of water at a temperature of 90 °C, insulated and stirred 7 minutes, after visual stirring and dissolving is uniform, is placed naturally
It is cooled to room temperature, obtains mixed liquor；It adds 200 grams of water and 5 grams of watersoluble pigment is uniformly mixed obtained coating, routinely
Method will treated maize leaves glue sticking on painting canvas, to form adhesive-layer, maize leaves layer on painting canvas, then by coating
It is applied in maize leaves, coating is dried with 100 DEG C of temperature, form protection after coating is dry on maize leaves layer and apply
Layer obtains the finished product that maize leaves are drawn.
Embodiment six：Maize leaves are handled by the method for embodiment one, for use；The commercially available glutinous rice of requirement and air bladder powder are pressed
2: 1.5 ratio is mixed and made into rubber powder, and 60 grams of rubber powder is taken to be put into 300 grams of water at a temperature of 90 °C, using electric blender,
It insulated and stirred 10 minutes, after visual stirring and dissolving is uniform, places and is cooled to room temperature naturally, obtain mixed liquor；Mixed liquor is dried
It is crushed into powder afterwards and takes to be uniformly mixed to be made in the 3 grams therein water that 1 kilogram is added together with 0.5 gram of water-soluble dye and apply
Material；According to a conventional method will treated maize leaves glue sticking on drawing paper, to form adhesive-layer, maize leaves on drawing paper
Layer, then by coating material in maize leaves, dries coating with 70 DEG C of temperature, after coating is dry on maize leaves layer shape
At protective coating, the finished product that maize leaves are drawn is obtained.
Claims (6)
1. maize leaves are drawn, it is characterised in that：Maize leaves, which are drawn, is sequentially overlapped group by base, adhesive-layer, maize leaves layer, protective coating
At；The coating for forming protective coating is mixed to prepare by 100 parts of water, 0.1~1 part of rubber powder and appropriate decoration powder by weight,
Middle rubber powder is mixed to prepare by glutinous rice powder and air bladder powder in 1.5~2.5: 0.5~1.5 ratio.
2. maize leaves according to claim 1 are drawn, it is characterised in that：The decoration powder is bronze or silver powder or pearl powder
Or one of pearl powder or in which at least two mixed powders.
3. maize leaves according to claim 1 are drawn, it is characterised in that：The base is velveteen layer of cloth.
4. maize leaves according to claim 1 are drawn, it is characterised in that：The glutinous rice powder is glutinous corn flour or glutinous rice meal
Or one of glutinous glutinous millet powder or glutinous rice flour or in which at least two.
5. making the method that any maize leaves are drawn described in Claims 1-4, which is characterized in that have follow steps：
1) maize leaves are handled：After maize leaves are carried out the mothproof processing of anti-corrosion, maize leaves heat is dried and is formed, then the jade that needs are cultrated
Meter Ye cultrates, for use；
2) coating processed：Glutinous rice powder and air bladder powder are put into suitable 85~95 DEG C of water by the mixed proportion, insulated and stirred
It is uniformly dissolved, places and be cooled to room temperature naturally, obtain mixed liquor；Remaining water and suitable decoration is added by the weight part ratio
Powder is uniformly mixed obtained coating, or, water is added by the weight part ratio and suitable decoration powder after crushing after mixed liquor is dried
In be uniformly mixed obtained coating, for use；
3) picture processed：According to a conventional method will treated maize leaves glue sticking in base, thus formed in base adhesive-layer,
Maize leaves layer, then by coating material in maize leaves, coating is dried with 50~120 DEG C of temperature, after coating is dry
Protective coating is formed on maize leaves layer, obtains the finished product that maize leaves are drawn.
6. the method that production maize leaves according to claim 5 are drawn, it is characterised in that：In the mixed liquor or coating
Suitable food preservative is added.