CN108864888A - A kind of fire-retardant furniture environmental protection coating material of ordor removing - Google Patents
A kind of fire-retardant furniture environmental protection coating material of ordor removing Download PDFInfo
- Publication number
- CN108864888A CN108864888A CN201810497056.0A CN201810497056A CN108864888A CN 108864888 A CN108864888 A CN 108864888A CN 201810497056 A CN201810497056 A CN 201810497056A CN 108864888 A CN108864888 A CN 108864888A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire
- resin
- environmental protection
- protection coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of fire-retardant furniture environmental protection coating materials of ordor removing, consist of the following compositions according to parts by weight：Change 40-64 parts of surname epoxy resin, 10-25 parts of natural resin, 32-46 parts of rosin resin, 8-17 parts of inorganic filler, 10-25 parts of carbon fiber powder, 12-15 parts of talcum powder, 14-18 parts of polyethylene glycol, 12-15 parts of nano-bentonite, 8-13 parts of calcium superphosphate, 4-11 parts of glacial acetic acid, 4-12 parts of magnesium sulfate, 4-10 parts of calcium hydroxide, 7-10 parts of mandarin oil, 1-5 parts of auxiliary agent and 3-8 parts of trbasic zinc phosphate.The present invention is low in cost, raw material is easy to get, each component cooperates, and paint solidification effect obtained is good, anticorrosive, wear-resistant, and it is strong to resist corrosive nature, paint film smooth finish, plentiful light, good airproof performance have good physicochemical property, and there is environmental-protecting performance, harmful substance in the air that can purify, adsorbs and degrade.
Description
Technical field
The present invention relates to household paint field, especially a kind of fire-retardant furniture environmental protection coating material of ordor removing.
Background technique
Household environment-friendlywater coating be it is a kind of can securely be covered on body surface, rise protection, decoration, mark and other specific uses
Chemical mixture coating.Coating is because of the moisture-proof defencive function of its anti-corrosion and decoration function, and by the favor of finishing person,
But existing coating adds harmful organic solvent, although the production of most of coating is simple, cheap, mostly with toxic secondary work
With, such as release formaldehyde harm to the human body is larger, can also affect to environment, resistance to oxidation is not strong, fire protection flame retarding
Performance is poor, and wear-resistance and oil-resistance ability is poor.With people to environmental protection consciousness it is more and more stronger, to health and environmental issue increasingly close
Note, this just needs a kind of reliable performance, high-durability, to the environment protection oil paint of human body and environmental nonpollution.
Summary of the invention
The purpose of the present invention is to provide a kind of fire-retardant furniture environmental protection coating materials of ordor removing, solve above-mentioned technological deficiency.
To achieve the above object, the present invention provides the following technical solutions：
A kind of fire-retardant furniture environmental protection coating material of ordor removing, consists of the following compositions according to parts by weight：Change 40-64 parts of surname epoxy resin, day
Right 10-25 parts of resin, 32-46 parts of rosin resin, 8-17 parts of inorganic filler, 10-25 parts of carbon fiber powder, 12-15 parts of talcum powder,
14-18 parts of polyethylene glycol, 12-15 parts of nano-bentonite, 8-13 parts of calcium superphosphate, 4-11 parts of glacial acetic acid, 4-12 parts of magnesium sulfate, hydrogen
4-10 parts of calcium oxide, 7-10 parts of mandarin oil, 1-5 parts of auxiliary agent and 3-8 parts of trbasic zinc phosphate.
Further, the fire-retardant furniture environmental protection coating material of above-mentioned a kind of ordor removing, consists of the following compositions according to parts by weight：Change surname ring
55-64 parts of oxygen resin, 18-25 parts of natural resin, 40-46 parts of rosin resin, 12-17 parts of inorganic filler, carbon fiber powder 16-25
Part, 13-15 parts of talcum powder, 17-18 parts of polyethylene glycol, 14-15 parts of nano-bentonite, 10-13 parts of calcium superphosphate, glacial acetic acid 7-11
Part, 8-12 parts of magnesium sulfate, 7-10 parts of calcium hydroxide, 8-10 parts of mandarin oil, 3-5 parts of auxiliary agent and 5-8 parts of trbasic zinc phosphate.
Further, the fire-retardant furniture environmental protection coating material of above-mentioned a kind of ordor removing, consists of the following compositions according to parts by weight：Asphalt mixtures modified by epoxy resin
62 parts of rouge, 4 parts of auxiliary agent, 20 parts of carbon fiber powder, 17 parts of nano graphite powder, 12 parts of attapulgite, crosses phosphorus at 40 parts of acrylic resin
12 parts of sour calcium, 8 parts of mandarin oil, 9 parts of titanium dioxide, 7 parts of magnesium sulfate, 10 parts of potassium breeze, 3 parts of microelement and 7 parts of silica.
Compared with prior art, the beneficial effects of the invention are as follows：
The present invention is low in cost, and raw material is easy to get, and each component cooperates, and paint solidification effect obtained is good, flame retardant property is good, resists
Burn into is wear-resistant, and it is strong to resist corrosive nature, paint film smooth finish, plentiful light, and good airproof performance has good physicochemical property, and
And there is environmental-protecting performance, harmful substance in the air that can purify, adsorbs and degrade.
Specific embodiment
The technical solution of the patent is explained in further detail With reference to embodiment.
Embodiment 1
A kind of fire-retardant furniture environmental protection coating material of ordor removing, consists of the following compositions according to parts by weight：Change 40 parts of surname epoxy resin, natural tree
10 parts of rouge, 32 parts of rosin resin, 8 parts of inorganic filler, 10 parts of carbon fiber powder, 12 parts of talcum powder, 14 part, nanometer of polyethylene glycol are swollen
12 parts of profit soil, 8 parts of calcium superphosphate, 4 parts of glacial acetic acid, 4 parts of magnesium sulfate, 4 parts of calcium hydroxide, 7 parts of mandarin oil, 1 part of auxiliary agent and phosphoric acid
3 parts of zinc.
Embodiment 2
A kind of fire-retardant furniture environmental protection coating material of ordor removing, consists of the following compositions according to parts by weight：Change 64 parts of surname epoxy resin, natural tree
25 parts of rouge, 46 parts of rosin resin, 17 parts of inorganic filler, 25 parts of carbon fiber powder, 15 parts of talcum powder, polyethylene glycol 18 part, nanometer
15 parts of bentonite, 13 parts of calcium superphosphate, 11 parts of glacial acetic acid, 12 parts of magnesium sulfate, 10 parts of calcium hydroxide, 10 parts of mandarin oil, 5 parts of auxiliary agent
With 8 parts of trbasic zinc phosphate.
Embodiment 3
A kind of fire-retardant furniture environmental protection coating material of ordor removing, consists of the following compositions according to parts by weight：Change 55 parts of surname epoxy resin, natural tree
18 parts of rouge, 40 parts of rosin resin, 12 parts of inorganic filler, 16 parts of carbon fiber powder, 13 parts of talcum powder, polyethylene glycol 17 part, nanometer
14 parts of bentonite, 10 parts of calcium superphosphate, 7 parts of glacial acetic acid, 8 parts of magnesium sulfate, 7 parts of calcium hydroxide, 8 parts of mandarin oil, 3 parts of auxiliary agent and phosphorus
5 parts of sour zinc.
The preferred embodiment of the patent is described in detail above, but this patent is not limited to above-mentioned embodiment party
Formula within the knowledge of one of ordinary skill in the art can also be under the premise of not departing from this patent objective
It makes a variety of changes.
Claims (3)
1. a kind of fire-retardant furniture environmental protection coating material of ordor removing, which is characterized in that consisted of the following compositions according to parts by weight：Change surname asphalt mixtures modified by epoxy resin
40-64 parts of rouge, 32-46 parts of rosin resin, 8-17 parts of inorganic filler, 10-25 parts of carbon fiber powder, is slided 10-25 parts of natural resin
12-15 parts of mountain flour, 14-18 parts of polyethylene glycol, 12-15 parts of nano-bentonite, 8-13 parts of calcium superphosphate, 4-11 parts of glacial acetic acid, sulphur
Sour magnesium 4-12 parts, 4-10 parts of calcium hydroxide, 7-10 parts of mandarin oil, 1-5 parts of auxiliary agent and 3-8 parts of trbasic zinc phosphate.
2. the fire-retardant furniture environmental protection coating material of a kind of ordor removing according to claim 1, which is characterized in that according to parts by weight by below at
It is grouped as：Change 55-64 parts of surname epoxy resin, 18-25 parts of natural resin, 40-46 parts of rosin resin, 12-17 parts of inorganic filler, carbon
16-25 parts of fiber dust, 13-15 parts of talcum powder, 17-18 parts of polyethylene glycol, 14-15 parts of nano-bentonite, calcium superphosphate 10-13
Part, 7-11 parts of glacial acetic acid, 8-12 parts of magnesium sulfate, 7-10 parts of calcium hydroxide, 8-10 parts of mandarin oil, 3-5 parts of auxiliary agent and trbasic zinc phosphate 5-8
Part.
3. the fire-retardant furniture environmental protection coating material of a kind of ordor removing according to claim 1, which is characterized in that according to parts by weight by below at
It is grouped as：Change 55 parts of surname epoxy resin, 18 parts of natural resin, 40 parts of rosin resin, 12 parts of inorganic filler, carbon fiber powder 16
Part, 13 parts of talcum powder, 17 parts of polyethylene glycol, 14 parts of nano-bentonite, 10 parts of calcium superphosphate, 7 parts of glacial acetic acid, 8 parts of magnesium sulfate, hydrogen
7 parts of calcium oxide, 8 parts of mandarin oil, 3 parts of auxiliary agent and 5 parts of trbasic zinc phosphate.