CN108858570A - A kind of preparation method for office furniture work top - Google Patents
A kind of preparation method for office furniture work top Download PDFInfo
- Publication number
- CN108858570A CN108858570A CN201810847067.7A CN201810847067A CN108858570A CN 108858570 A CN108858570 A CN 108858570A CN 201810847067 A CN201810847067 A CN 201810847067A CN 108858570 A CN108858570 A CN 108858570A
- Authority
- CN
- China
- Prior art keywords
- substrate
- office furniture
- work top
- preparation
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods for office furniture work top, include the following steps：A, substrate is selected；B, substrate is finished；C, edge sealing and bound edge decorative cover；D, cooling and air-dry；E, quality inspection and inventory.This is used for the preparation method of office furniture work top, can produce the plate used convenient for office furniture, and with the characteristic that anti-mildew, expeling moth well and appearance are smooth, process flow is simple, and can be improved the performance of plate.
Description
Technical field
The present invention relates to technical field of office furniture, specially a kind of preparation method for office furniture work top.
Background technique
With the raising of people's working environment, plate used by more and more office furniture uses environment-friendly type substantially
Plate, but comparatively, price will be expensive.Currently, the commonly used office furniture of people is exactly desk, it is mostly
It is supported using synthetic plate, price is more relatively cheap, but the work top of these desks is in the most contact in routine work
Face, put computer, file and other office accommodations, and in office process, cup, the work of desk may be knocked over
Make table top because of adsorption moisture, and cannot thoroughly blot, plate is caused to go mouldy, noxious material, the health of crisis office worker, separately
Outside, it since work top is all made of wood materials, uses for a long time, might have moth, not only work top is damaged,
It is also possible to the file to storage destroys, so design produces a kind of preparation side for office furniture work top here
Method, in order to solve the above problems.
Summary of the invention
The purpose of the present invention is to provide a kind of preparation methods for office furniture work top, to solve above-mentioned background
The problem of being proposed in technology.
To achieve the above object, the present invention provides the following technical solutions：A kind of preparation for office furniture work top
Method includes the following steps：
A, substrate is selected：It selects wood fibre or other plant fiber is substrate；
B, substrate is finished：(1) wood fibre or other plant fiber are smashed and is immersed in BAAPE solution；(2)
Crushing substrate after immersion is pulled out and carries out fiber separation；(3) the crushing substrate for carrying out fiber separation is dried, and added
Add Lauxite；(4) fiber after drying is realized to the thick molding of fiber first with vacuum pneumatic, then passes through sweeping through the material roller and hot pressing
Machine is formed；
C, edge sealing and bound edge decorative cover：Plate after will be hot-forming is placed on gluing table top, using sizer at
Substrate after type carries out brushing PVC glue, repaves dress natural veneer as facing；
D, cooling and air-dry：Substrate after edge sealing is carried out using air-cooler cooling and air-dried；
E, quality inspection and inventory：By product after cooling by quality inspection personnel inspection, rupture or folding line are checked whether
Substandard products screen out if having, if without encapsulation inventory.
Preferably, it finishes in substrate, BAAPR solution is dimethyl phthalate solution.
Preferably, it finishes in substrate, the time for impregnating substrate is 5-10h, and the time of dry substrate is 3-5h.
Preferably, temperature when hot press works is between 100-200 DEG C.
Compared with prior art, the beneficial effects of the invention are as follows：
1, the preparation method for being used for office furniture work top, can produce for office furniture workbench
Face, process flow is simple, and can be improved the performance of plate.
2, the present invention enables substrate to have good anti-mildew, passes through by carrying out edge sealing to substrate using PVC glue
Substrate is immersed in dimethyl phthalate solution, has and drives away moth effect well, by using natural veneer as facing, so that
The appearance on work top surface layer is smooth, and more beautiful.
Specific embodiment
It is clearly and completely described below in conjunction with the technical solution in the embodiment of the present invention, it is clear that described reality
Applying example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is general
Logical technical staff every other embodiment obtained without making creative work belongs to what the present invention protected
Range.
The present invention provides a kind of technical solution：A kind of preparation method for office furniture work top, including following step
Suddenly：
A, substrate is selected：It selects wood fibre or other plant fiber is substrate；
B, substrate is finished：(1) wood fibre or other plant fiber are smashed and is immersed in BAAPE solution；(2)
Crushing substrate after immersion is pulled out and carries out fiber separation；(3) the crushing substrate for carrying out fiber separation is dried, and added
Add Lauxite；(4) fiber after drying is realized to the thick molding of fiber first with vacuum pneumatic, then passes through sweeping through the material roller and hot pressing
Machine is formed；
C, edge sealing and bound edge decorative cover：Plate after will be hot-forming is placed on gluing table top, using sizer at
Substrate after type carries out brushing PVC glue, and PVC glue has good leakproofness, so carrying out edge sealing using PVC glue, ensure that base
Material ontology not will cause mildew not by the dipping of steam, repave dress natural veneer as facing, using natural veneer as decorations
Face, it is not only beautiful but also smooth, comfortable work top is provided and is used for office worker；
D, cooling and air-dry：Substrate after edge sealing is carried out using air-cooler cooling and air-dried, the substrate after air-drying can
It prevents from breeding bacterium；
E, quality inspection and inventory：By product after cooling by quality inspection personnel inspection, rupture or folding line are checked whether
Substandard products screen out if having, if without encapsulation inventory.
Preferably, it finishes in substrate, BAAPR solution is dimethyl phthalate solution, and dimethyl phthalate solution is imitated with good expelling parasite
Fruit can be used for a long time by being impregnated into material main body, be volatilized slower, and to no damage to human body.
Preferably, it finishes in substrate, the time for impregnating substrate is 5-10h, and the time of dry substrate is 3-5h.
Preferably, temperature when hot press works is between 100-200 DEG C.
Embodiment one
A kind of preparation method for office furniture work top, includes the following steps：
A, substrate is selected：It selects wood fibre or other plant fiber is substrate；
B, substrate is finished：(1) wood fibre or other plant fiber are smashed and is immersed in BAAPE solution；(2)
Crushing substrate after immersion is pulled out and carries out fiber separation；(3) the crushing substrate for carrying out fiber separation is dried, and added
Add Lauxite；(4) fiber after drying is realized to the thick molding of fiber first with vacuum pneumatic, then passes through sweeping through the material roller and hot pressing
Machine is formed；
C, edge sealing and bound edge decorative cover：Plate after will be hot-forming is placed on gluing table top, using sizer at
Substrate after type carries out brushing PVC glue, repaves dress natural veneer as facing；
D, cooling and air-dry：Substrate after edge sealing is carried out using air-cooler cooling and air-dried；
E, quality inspection and inventory：By product after cooling by quality inspection personnel inspection, rupture or folding line are checked whether
Substandard products screen out if having, if without encapsulation inventory.
Preferably, it finishes in substrate, BAAPR solution is dimethyl phthalate solution.
Preferably, it finishes in substrate, the time for impregnating substrate is 5h, and the time of dry substrate is 3h.
Preferably, temperature when hot press works is between 100 DEG C.
Embodiment two
A kind of preparation method for office furniture work top, includes the following steps：
A, substrate is selected：It selects wood fibre or other plant fiber is substrate；
B, substrate is finished：(1) wood fibre or other plant fiber are smashed and is immersed in BAAPE solution；(2)
Crushing substrate after immersion is pulled out and carries out fiber separation；(3) the crushing substrate for carrying out fiber separation is dried, and added
Add Lauxite；(4) fiber after drying is realized to the thick molding of fiber first with vacuum pneumatic, then passes through sweeping through the material roller and hot pressing
Machine is formed；
C, edge sealing and bound edge decorative cover：Plate after will be hot-forming is placed on gluing table top, using sizer at
Substrate after type carries out brushing PVC glue, repaves dress natural veneer as facing；
D, cooling and air-dry：Substrate after edge sealing is carried out using air-cooler cooling and air-dried；
E, quality inspection and inventory：By product after cooling by quality inspection personnel inspection, rupture or folding line are checked whether
Substandard products screen out if having, if without encapsulation inventory.
Preferably, it finishes in substrate, BAAPR solution is dimethyl phthalate solution.
Preferably, it finishes in substrate, the time for impregnating substrate is 10h, and the time of dry substrate is 5h.
Preferably, temperature when hot press works is between 200 DEG C.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (4)
1. a kind of preparation method for office furniture work top, includes the following steps：
A, substrate is selected：It selects wood fibre or other plant fiber is substrate；
B, substrate is finished：(1) wood fibre or other plant fiber are smashed and is immersed in BAAPE solution；It (2) will leaching
Crushing substrate after bubble is pulled out and carries out fiber separation；(3) the crushing substrate for carrying out fiber separation is dried, and adds urea
Urea formaldehyde；(4) fiber after drying realized to the thick molding of fiber first with vacuum pneumatic, then by sweeping through the material roller and hot press into
Row molding；
C, edge sealing and bound edge decorative cover：Plate after will be hot-forming is placed on gluing table top, using sizer to molding after
Substrate carry out brush PVC glue, repave dress natural veneer as facing；
D, cooling and air-dry：Substrate after edge sealing is carried out using air-cooler cooling and air-dried；
E, quality inspection and inventory：By product after cooling by quality inspection personnel inspection, the substandard products of rupture or folding line are checked whether,
It is screened out if having, if without encapsulation inventory.
2. a kind of preparation method for office furniture work top according to claim 1, it is characterised in that：Finishing
In substrate, BAAPR solution is dimethyl phthalate solution.
3. a kind of preparation method for office furniture work top according to claim 1, it is characterised in that：Finishing
In substrate, the time for impregnating substrate is 5-10h, and the time of dry substrate is 3-5h.
4. a kind of preparation method for office furniture work top according to claim 1, it is characterised in that：Hot press
Temperature when work is between 100-200 DEG C.