CN108855844A - A kind of fluorine carbon heat insulation decoration integrated plate production technology - Google Patents
A kind of fluorine carbon heat insulation decoration integrated plate production technology Download PDFInfo
- Publication number
- CN108855844A CN108855844A CN201810794336.8A CN201810794336A CN108855844A CN 108855844 A CN108855844 A CN 108855844A CN 201810794336 A CN201810794336 A CN 201810794336A CN 108855844 A CN108855844 A CN 108855844A
- Authority
- CN
- China
- Prior art keywords
- plate
- detect
- paint
- detection
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fluorine carbon heat insulation decoration integrated plate production technology, the fluorine carbon heat insulation decoration integrated plate production craft step is as follows：The first step：Substrate inspection, the detection of length and width：Bullet board ends 10 centimetres of left-right positions, midline positions, are respectively measured at 1 with steel tape, are accurate to 1 millimeter, take the average value of this 3 measured values as plate face length (width) value；The detection of thickness：With bow compass and vernier caliper conjunction measuring, each 10 centimetres away from plate both sides, both ends, plotted point respectively surveys a value (at 4), 10 centimetres away from plate both sides, 1 value (at 2) is respectively surveyed with cross central line plotted point, totally 6 measured values, are accurate to 1 millimeter.The fluorine carbon heat insulation decoration integrated plate production technology can carry out effective coating to fluorine carbon insulation and decoration, guarantee the quality stability of plate coating surface.
Description
Technical field
The present invention relates to fluorine carbon heat insulating decorative board production technical field more particularly to a kind of fluorine carbon heat insulation decoration integrated plate are raw
Production. art.
Background technique
Fluorocarbon coating refers to the coating using fluororesin as main film forming substance, also known as F-C paint, fluoro coatings, fluorine resin coating
Deng among various coating, for fluorine resin coating since the fluorine element electronegativity of introducing is big, carbon-fluorine bond can be strong, has especially advantageous
Properties, fire resistance, heat resistance, lower temperature resistance, chemical resistance, and have unique non-stick and low friction
Property.
Existing plate also can be in coated with fluoro carbon coating, to improve the permanence of plate in actual use, still
Existing coating process is easy to lead to the problem of a variety of production technologies such as bubble, color difference, greatly reduces the quality of finished product.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and the one kind proposed has mosquito repellent and distributes
The coating of fragrance effect.
To achieve the goals above, present invention employs following technical solutions：
A kind of fluorine carbon heat insulation decoration integrated plate production technology, the fluorine carbon heat insulation decoration integrated plate production craft step is such as
Under：
The first step：Substrate inspection, the detection of length and width：Bullet board ends 10 centimetres of left-right positions, midline positions are used
Steel tape respectively measures at 1, is accurate to 1 millimeter, takes the average value of this 3 measured values as plate face length (width) value；
The detection of thickness：With bow compass and vernier caliper conjunction measuring, each 10 centimetres away from plate both sides, both ends, plotted point is each
A value (at 4) is surveyed, 10 centimetres away from plate both sides, respectively surveys 1 value (at 2) with cross central line plotted point, totally 6 measured values, essence
Really to 1 millimeter；
The detection of edge nonstraightness：Plate is lain against on horizontal platform, is mutually leaned on the side of 2 meters of long guiding rulers with edges of boards, then use
Maximal clearance between the edge and guiding ruler side of the clearance gauge measurement plate that minimum thickness is 0.01 millimeter；
The detection of warped degree：It lies against plate is concave upright on horizontal platform, it is edge-on above plate with 2 meters of long guiding rulers, then
The maximum chinky altitude between guiding ruler and plate is measured with the clearance gauge that minimum thickness is 0.01 millimeter.
Second step：Hair plates sanding detects hair plates sanding finished plate thickness deviation：Extract 10% measurement therein.If there is
Rejected product continues checking next block of plate, if any continuous two pieces of rejected products, to expand measurement range to 50%；
The selection in abrasive band：Select the abrasive band of 40 mesh or 80 mesh.
Third step：UV permeates priming paint (primary), detects plate gap and wet-film thickness：Plate gap is no more than 20 centimetres,
Wet-film thickness is 20 ± 5 microns；
Detect UV priming paint levelability；
Detect the aridity of UV priming paint：It is touched by naked hand, whether thoughts and feelings has viscous feel；
Detect the coating surface of plate：The case where having detected whether bubble, shrinkage cavity and being unevenly coated.
4th step：Whether paint film sanding (primary), detection production board base have bright spot：The bright spot of continuous three pieces of plate bases is no more than
10/square metre；
It detects whether sand occur show-through；
Select the suitable sand amount of cutting；
Moment checks plate face effect；
The selection in paint film sanding abrasive band：Abrasive band is 320 mesh.
5th step：UV putty (infiltration priming paint is secondary), the gap between detection plate and plate：No more than 20 centimetres；
Detect wet-film thickness：It should be 50 ± 5 microns.
Detect UV levelability；
Detect UV stationary state：It is touched by naked hand, whether thoughts and feelings has viscous feel；
Sampling Detection after paint film sanding：It chooses therein 1% and checks hardness, i.e., with the 3H pencil polished with 45 degree of angles edge paint
Film edge part is drawn forward, if can scratch paint film will adjust the intensity of illumination of lamp in time, until the paint film of continuous two boards is hard
Degree is qualified；
Detect curing temperature：Time interval is 30 minutes；
Detect the painting surface layer of every block of plate：The case where having detected whether bubble, shrinkage cavity and being unevenly coated.
6th step：Whether paint film sanding (secondary), detection production board base have bright spot：The bright spot of continuous three pieces of plate bases is no more than
10/square metre；
It detects whether sand occur show-through；
Select the suitable sand amount of cutting；
Moment checks plate face effect；
The selection in paint film sanding abrasive band：Abrasive band is 320 mesh.
7th step：It rolls lacquer painting to apply, detects the uniformity of former paint stirring：Precipitation status of the former paint of detection in whipping process,
Until being stirred to no precipitating；
The selection of diluent；
The addition of curing agent；
Adjust viscous viscosity：Diluent additive amount is 15% or so of former paint.Viscosity is in 40-60 seconds/painting -4,25 DEG C (or 80-
90 seconds/apply -1,25 DEG C).
Select the sieve mesh number of filtering finishing coat；
The allotment of paint amount：Finishing coat dosage is deployed according to the principle of " a small amount of multiple "；
Control roller speed：Roller speed is 7 ms/min.
Regulating roller away from；
Detect the wet-film thickness of roller coating：Wet-film thickness should be 35 ± 5 microns.
8th step：The drying of finishing coat sets baking temperature：45 to 70 DEG C；
Set baking time：240 to 300 minutes；
The random sampling of drying process：The plate or while drying in batches for randomly selecting 1% from every batch of randomly select 1 block of plate
Material examines paint film pencil hardness；
Detect the solidification situation of paint film：Whether viscous situation is occurred；
Detect hardness of paint film：Not less than 2H.
9th step：The case where examining plate coating surface.
Tenth step：Overlay film detects whether the protective film of product；
Detect the compression strength of packing case；
Product quality list is detected whether；
Whether high-visible detect mark, work certificate, operation instructions, the text of product quality list and pattern.
Preferably, the type that diluent is selected in the 7th step is lacquer thinner.
Preferably, the type that curing agent is selected in the 7th step is polyamide curing agent.
A kind of fluorine carbon heat insulation decoration integrated plate production technology provided by the invention, this process flow can keep the temperature fluorine carbon
Decoration carries out effective coating, guarantees the quality stability of plate coating surface.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.
A kind of fluorine carbon heat insulation decoration integrated plate production technology, fluorine carbon heat insulation decoration integrated plate production craft step are as follows：
The first step：Substrate inspection, the detection of length and width：Bullet board ends 10 centimetres of left-right positions, midline positions are used
Steel tape respectively measures at 1, is accurate to 1 millimeter, takes the average value of this 3 measured values as plate face length (width) value；
The detection of thickness：With bow compass and vernier caliper conjunction measuring, each 10 centimetres away from plate both sides, both ends, plotted point is each
A value (at 4) is surveyed, 10 centimetres away from plate both sides, respectively surveys 1 value (at 2) with cross central line plotted point, totally 6 measured values, essence
Really to 1 millimeter；
The detection of edge nonstraightness：Plate is lain against on horizontal platform, is mutually leaned on the side of 2 meters of long guiding rulers with edges of boards, then use
Maximal clearance between the edge and guiding ruler side of the clearance gauge measurement plate that minimum thickness is 0.01 millimeter；
The detection of warped degree：It lies against plate is concave upright on horizontal platform, it is edge-on above plate with 2 meters of long guiding rulers, then
The maximum chinky altitude between guiding ruler and plate is measured with the clearance gauge that minimum thickness is 0.01 millimeter.
Second step：Hair plates sanding detects hair plates sanding finished plate thickness deviation：Extract 10% measurement therein.If there is
Rejected product continues checking next block of plate, if any continuous two pieces of rejected products, to expand measurement range to 50%；
The selection in abrasive band：Select the abrasive band of 40 mesh or 80 mesh.
Third step：UV permeates priming paint (primary), detects plate gap and wet-film thickness：Plate gap is no more than 20 centimetres,
Wet-film thickness is 20 ± 5 microns；
Detect UV priming paint levelability；
Detect the aridity of UV priming paint：It is touched by naked hand, whether thoughts and feelings has viscous feel；
Detect the coating surface of plate：The case where having detected whether bubble, shrinkage cavity and being unevenly coated.
4th step：Whether paint film sanding (primary), detection production board base have bright spot：The bright spot of continuous three pieces of plate bases is no more than
10/square metre；
It detects whether sand occur show-through；
Select the suitable sand amount of cutting；
Moment checks plate face effect；
The selection in paint film sanding abrasive band：Abrasive band is 320 mesh.
5th step：UV putty (infiltration priming paint is secondary), the gap between detection plate and plate：No more than 20 centimetres；
Detect wet-film thickness：It should be 50 ± 5 microns.
Detect UV levelability；
Detect UV stationary state：It is touched by naked hand, whether thoughts and feelings has viscous feel；
Sampling Detection after paint film sanding：It chooses therein 1% and checks hardness, i.e., with the 3H pencil polished with 45 degree of angles edge paint
Film edge part is drawn forward, if can scratch paint film will adjust the intensity of illumination of lamp in time, until the paint film of continuous two boards is hard
Degree is qualified；
Detect curing temperature：Time interval is 30 minutes；
Detect the painting surface layer of every block of plate：The case where having detected whether bubble, shrinkage cavity and being unevenly coated.
6th step：Whether paint film sanding (secondary), detection production board base have bright spot：The bright spot of continuous three pieces of plate bases is no more than
10/square metre；
It detects whether sand occur show-through；
Select the suitable sand amount of cutting；
Moment checks plate face effect；
The selection in paint film sanding abrasive band：Abrasive band is 320 mesh.
7th step：It rolls lacquer painting to apply, detects the uniformity of former paint stirring：Precipitation status of the former paint of detection in whipping process,
Until being stirred to no precipitating；
The selection of diluent：The type of diluent is lacquer thinner；
The addition of curing agent：The type of curing agent is polyamide curing agent；
Adjust viscous viscosity：Diluent additive amount is 15% or so of former paint.Viscosity is in 40-60 seconds/painting -4,25 DEG C (or 80-
90 seconds/apply -1,25 DEG C).
Select the sieve mesh number of filtering finishing coat；
The allotment of paint amount：Finishing coat dosage is deployed according to the principle of " a small amount of multiple "；
Control roller speed：Roller speed is 7 ms/min.
Regulating roller away from；
Detect the wet-film thickness of roller coating：Wet-film thickness should be 35 ± 5 microns.
8th step：The drying of finishing coat sets baking temperature：45 to 70 DEG C；
Set baking time：240 to 300 minutes；
The random sampling of drying process：The plate or while drying in batches for randomly selecting 1% from every batch of randomly select 1 block of plate
Material examines paint film pencil hardness；
Detect the solidification situation of paint film：Whether viscous situation is occurred；
Detect hardness of paint film：Not less than 2H.
9th step：It examines, is compared according to content in table.
Tenth step：Overlay film detects whether the protective film of product；
Detect the compression strength of packing case；
Product quality list is detected whether；
Whether high-visible detect mark, work certificate, operation instructions, the text of product quality list and pattern.
Claims (3)
1. a kind of fluorine carbon heat insulation decoration integrated plate production technology, it is characterised in that：The fluorine carbon heat insulation decoration integrated plate produces work
Steps are as follows for skill：
The first step：Substrate inspection, the detection of length and width：Bullet board ends 10 centimetres of left-right positions, midline positions, use coil of strip
Ruler respectively measures at 1, is accurate to 1 millimeter, takes the average value of this 3 measured values as plate face length (width) value；
The detection of thickness：With bow compass and vernier caliper conjunction measuring, each 10 centimetres away from plate both sides, both ends, plotted point respectively surveys one
A value (at 4), respectively surveys 1 value (at 2) with cross central line plotted point, totally 6 measured values, are accurate to 1 by 10 centimetres away from plate both sides
Millimeter；
The detection of edge nonstraightness：Plate is lain against on horizontal platform, is mutually leaned on the side of 2 meters of long guiding rulers with edges of boards, then with minimum
With a thickness of the maximal clearance between the edge and guiding ruler side of 0.01 millimeter of clearance gauge measurement plate；
The detection of warped degree：It lies against plate is concave upright on horizontal platform, it is edge-on above plate with 2 meters of long guiding rulers, then with most
The small clearance gauge with a thickness of 0.01 millimeter measures the maximum chinky altitude between guiding ruler and plate.
Second step：Hair plates sanding detects hair plates sanding finished plate thickness deviation：Extract 10% measurement therein.If there is not conforming to
Lattice product continue checking next block of plate, if any continuous two pieces of rejected products, to expand measurement range to 50%；
The selection in abrasive band：Select the abrasive band of 40 mesh or 80 mesh.
Third step：UV permeates priming paint (primary), detects plate gap and wet-film thickness：Plate gap is no more than 20 centimetres, wet film
With a thickness of 20 ± 5 microns；
Detect UV priming paint levelability；
Detect the aridity of UV priming paint：It is touched by naked hand, whether thoughts and feelings has viscous feel；
Detect the coating surface of plate：The case where having detected whether bubble, shrinkage cavity and being unevenly coated.
4th step：Whether paint film sanding (primary), detection production board base have bright spot：The bright spot of continuous three pieces of plate bases is no more than 10
A/square metre；
It detects whether sand occur show-through；
Select the suitable sand amount of cutting；
Moment checks plate face effect；
The selection in paint film sanding abrasive band：Abrasive band is 320 mesh.
5th step：UV putty (infiltration priming paint is secondary), the gap between detection plate and plate：No more than 20 centimetres；
Detect wet-film thickness：It should be 50 ± 5 microns.
Detect UV levelability；
Detect UV stationary state：It is touched by naked hand, whether thoughts and feelings has viscous feel；
Sampling Detection after paint film sanding：It chooses therein 1% and checks hardness, that is, use the 3H pencil polished with 45 degree of angles along paint film side
Edge point is drawn forward, if can scratch paint film will adjust the intensity of illumination of lamp in time, until the hardness of paint film of continuous two boards closes
Lattice；
Detect curing temperature：Time interval is 30 minutes；
Detect the painting surface layer of every block of plate：The case where having detected whether bubble, shrinkage cavity and being unevenly coated.
6th step：Whether paint film sanding (secondary), detection production board base have bright spot：The bright spot of continuous three pieces of plate bases is no more than 10
A/square metre；
It detects whether sand occur show-through；
Select the suitable sand amount of cutting；
Moment checks plate face effect；
The selection in paint film sanding abrasive band：Abrasive band is 320 mesh.
7th step：It rolls lacquer painting to apply, detects the uniformity of former paint stirring：Precipitation status of the former paint of detection in whipping process, until
It is stirred to no precipitating；
The selection of diluent；
The addition of curing agent；
Adjust viscous viscosity：Diluent additive amount is 15% or so of former paint.Viscosity is in 40-60 seconds/painting -4,25 DEG C (or 80-90
Second/painting -1,25 DEG C).
Select the sieve mesh number of filtering finishing coat；
The allotment of paint amount：Finishing coat dosage is deployed according to the principle of " a small amount of multiple "；
Control roller speed：Roller speed is 7 ms/min.
Regulating roller away from；
Detect the wet-film thickness of roller coating：Wet-film thickness should be 35 ± 5 microns.
8th step：The drying of finishing coat sets baking temperature：45 to 70 DEG C；
Set baking time：240 to 300 minutes；
The random sampling of drying process：Randomly select 1% plate or randomly select the inspection of 1 block of plate from every batch of when drying in batches
Test paint film pencil hardness；
Detect the solidification situation of paint film：Whether viscous situation is occurred；
Detect hardness of paint film：Not less than 2H.
9th step：The case where examining plate coating surface.
Tenth step：Overlay film detects whether the protective film of product；
Detect the compression strength of packing case；
Product quality list is detected whether；
Whether high-visible detect mark, work certificate, operation instructions, the text of product quality list and pattern.
2. a kind of fluorine carbon heat insulation decoration integrated plate production technology according to claim 1, it is characterised in that：7th step
The middle type for selecting diluent is lacquer thinner.
3. a kind of fluorine carbon heat insulation decoration integrated plate production technology according to claim 1, it is characterised in that：7th step
The middle type for selecting curing agent is polyamide curing agent.